Graphene Ingestion and Regrowth on âCarbon ... - ACS Publications

Subscriber access provided by Gothenburg University Library

Article

Graphene Ingestion and Regrowth on “Carbon-Starved” Metal Electrodes Ming-Sheng Wang, Yong Cheng, Longze Zhao, Ujjal K. Gautam, and Dmitri Golberg ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b06078 • Publication Date (Web): 27 Sep 2017 Downloaded from http://pubs.acs.org on September 29, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Nano is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Graphene Ingestion and Regrowth on “CarbonStarved” Metal Electrodes Ming-Sheng Wang1,2*, Yong Cheng 1, Longze Zhao 2, Ujjal K. Gautam 3, Dmitri Golberg 4,5*

1

Department of Materials Science and Engineering, College of Materials, Xiamen University,

Xiamen, Fujian 361005, China. 2

Pen-Tung Sah Institute of Micro-Nano Science and Technology, Xiamen University, Xiamen,

Fujian 361005, China. 3

Department of Chemical Sciences, Indian Institute of Science Education and Research (IISER)-

Mohali, Sector 81, Mohali, SAS Nagar, Punjab 140306, India 4

International Centre for Materials Nanoarchitectonics (MANA), National Institute for Materials

Science (NIMS), Namiki 1-1, Tsukuba, Ibaraki 3050044, Japan. 5

School of Chemistry, Physics and Mechanical Engineering, Queensland University of

Technology (QUT), 2 George str., Gardens Point, Brisbane, QLD 4000, Australia *Address correspondence to: [email protected], [email protected]

KEYWORDS Graphene-metal interaction, sp2 carbon catalytic growth, carbon diffusion, metal carbide, interfacial thermochemistry, in situ TEM

ACS Paragon Plus Environment

1

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 22

ABSTRACT

The interaction between graphene and various metals plays a central role in future carbon-based device and synthesis technologies. Herein, three different types of metal nanoelectrodes (W, Ni, Au) were employed to in situ study the graphene-metal interfacial kinetic behaviors in a highresolution transmission electron microscope. Three metals exhibit distinctly different interactions with graphene when driven by a heating current. Tungsten tips, the most carbon-starved ones, can ingest a graphene sheet continuously; nickel tips, less carbon starved, typically “eat” graphene only by taking a “bite” from its edge; gold, however, is non-active with graphene at all, even in its molten state. The ingested graphene atoms finally precipitate as freshly-formed graphitic shells encapsulating the catalytic W and Ni electrodes. Particularly, we propose a periodic extension/thickening graphene growth scenario by atomic-scale observation of this process on W electrodes, where the propagation of the underlying tungsten carbide (WC) dominates

the

growth

dynamics.

This

work

uncovers

the

complexity of

carbon

diffusion/segregation processes at different graphene/metal interfaces that would severely degrade the device performance and stability. Besides, it also provides detailed and insightful understanding of the sp2 carbon catalytic growth, which is vital in developing efficient and practical graphene synthetic routes.


2

Page 3 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Graphene has attracted worldwide attention owing to its appealing properties and great promise for building future carbon-based device architectures.1 Among the diverse graphenebased applications, the interaction between graphene sheets and various metals plays a central role, since the performance of every single graphene-based device is greatly influenced by the electronic/mechanical coupling and chemical/structural stability at the graphene-electrode interfaces.

This

is

particularly

true

for

graphene

applications

in

nanoelectronic,

nanoelectromechanical and energy storage devices, etc.1-6 These graphene/metal (abbreviated as “G/M” hereafter) interfaces are also critical for the large-area growth of high-quality graphene suitable for commercial purposes, since the graphene growth is strongly linked to the kinetic behavior between epitaxial graphene and metal (or carbide) substrates during metal catalytic syntheses.7-16 Although previous studies based on postsynthesis characterizations and theoretical considerations have been carried out to pursue detailed understanding of the graphene nucleation and growth mechanisms,12-16 the complexity of the interactions between growing graphene and underlying metals is not completely uncovered. To date, the direct high-resolution observations of graphene growth on different metals and study of their interplay at elevated temperatures are still lacking. In this contribution, we present the systematic in situ transmission electron microscopy (TEM) investigation of G/M interfacial kinetics stimulated by a heating current. The G/M interfacial reaction processes were observed in real time and at the atomic level resolution, which gave a rare opportunity to mimic and study the real process of graphene layers growth. Instead of gaseous raw materials (e.g. CH4 or C2H2) that are widely used in conventional CVD methods,7,17 in this work, graphene itself served as a solid carbon source for its regrowth on metal surfaces. Different metals were fabricated into nanosized tips, thus naturally offering the cross-section of


3

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 22

G/M interfaces required for TEM observations. During a typical G/M kinetic process, a graphene sheet is first “ingested” into a heated liquid-like metal tip, and then segregated as new graphitic layers surrounding the tip surface. Three representative metals (tungsten, nickel and gold) were used in the experiments, and their reactivities with graphene, referred to as “carbon-starved” degrees, were ultimately compared. Our findings would be extremely valuable for design of efficient graphene-metal contacts with a high thermal stability for device purposes, and for indepth understanding of the general growth mechanism of sp2 carbon structures.

RESULTS AND DISCUSSION

The graphene sheets used in our experiment were produced by adopting a supercritical fluid exfoliation method of graphite powder, in which ~90% of the exfoliated sheets are under 8 layers.18 The electrochemically etched metal tips usually have an initial diameter of less than 50 nm at the tip end (see Method or Refs.19-21 for the preparation details of W, Ni and Au nanotips, respectively). Both graphene sheets and metal tip were mounted on a TEM-scanning tunneling microscopy (STM) holder,22,23 followed by an in situ manipulation to make contact between a single graphene sheet and a metal tip inside the TEM, as depicted in Figure 1a. The G/M interfacial reaction was initiated when this heterostructure was Joule-heated to high temperature simply by increasing the applied bias up to 1~3 V, which depends on metal species, tip sizes and G/M contact conditions, etc. We firstly chose tungsten, a typical refractory metal, as the metal tip. As shown in Figure 1(b), when the bias was increased to 1.4 V, with a current of ~600 µA, the graphene near the G/W contact began to be absorbed into W tip, resulting in obvious wrinkling of the formerly smooth graphene surface (marked by the arrow in Fig. 1b). A closer examination of the enlarged


4

Page 5 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

image at the G/W contact reveals that a few surface layers, close to the W tip, were ingested preferentially. The brighter contrast area in the inset of Fig. 1b indicates a void formed within these surface layers with its edge highlighted by the yellow dashed line. In the following process, the W tip worked like an arm to grasp the graphene sheet firmly (Fig. 1c), and later, like a straw to suck the right side of the graphene sheet entirely into its body (Fig. 1d-e and Supporting Information, Movie S1). It should be noted that the W tip actually remains crystalline throughout the whole process, though it behaves somewhat like a liquid. The W tip finally broke under tensile stress caused by the graphene absorption (Fig. 1f), indicating a strong adhesive force at the G/W interface. The ingested carbon transformed W tip into tungsten carbide (α-WC), which was confirmed by high-resolution TEM (HRTEM) imaging and selected area electron diffraction (SAED) patterns taken from the newly-formed tip-end (Fig. 1g). This carbide phase usually exhibits a distinctly different optical contrast from pure tungsten. As indicated by the arrowheads in Figure 1f, tungsten carbide has expanded about 500 nm deep into the W tip body. Interestingly, the carbide region can even extend up to micrometers if the W tip is continuously pushed forward to keep contact with a large graphene sheet that could provide enough carbon feedstock. The continuous graphene ingestion leads to carbide extension within W tip body, which subsequently causes the precipitation of new graphitic layers surrounding the tip surface where C concentration exceeds the supersaturation level. Figure 2a shows a typical as-obtained W electrode with a part of its surface covered by segregated graphitic layers (see Supporting Information Fig. S4 and Video S2 for the graphite segregation process). The carbon distribution within this heterostructure was analyzed under elemental mapping using spatially resolved electron energy loss spectroscopy (EELS) (Fig. 2b). The sharp boundary between the brighter


5

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 22

and darker regions marked by the arrowheads in the C map agrees well with the carbide/metal interface marked by arrowheads in Figure 2a. The brightest region in C map corresponds to the graphitic layers surrounding carbide region. This clearly shows that the intermediate tungsten carbide, instead of pure tungsten, plays the actual catalytic role during the present graphitic layer growth. Figure 2c presents EEL spectra showing the C K-edge obtained from three typical regions marked with circles A, B, C in Figure 2a. The well-known π* peak at ~284.5 eV indicating the sp2 carbon bonding, which shows up only in the spectrum from region A, confirms the formation of graphite structures; whereas, the carbon concentration in tungsten, as expected, is negligible, as shown in the spectrum from region C. In some cases, in order to reveal the details of graphene nucleation, the G/W reaction was terminated at the early stage of graphene segregation by switching off the bias. As documented by the HRTEM image in Figure 2d, graphene nucleation had been found to be associated with the formation of morphological defects on WC surface. The 4-layer graphene seems to nucleate at the surface step (indicated by the arrowhead 1), extend along the surface plane, and terminate at a slightly concaved step that is more distant from the W tip end (indicated by the arrowhead 2). This strongly suggests that the graphene growth on WC would be accompanied by W atom desorption from the WC substrate, leaving behind concaved steps on the surface. It is more evident in Fig. 2a, compared to the pure WC region (region B), that the graphene growth has led the underlying WC (region A) to shrink drastically in the radial direction due to W atom desorption. The desorbed W atoms could migrate toward the tip end, or more likely, be evaporated into the vacuum at a high local temperature, quite similar to the process of graphene fabrication by vacuum annealing of silicon carbide via Si sublimation.8 Differently, the graphite growth during our graphene-metal reaction process can not solely be attributed to the W


6

Page 7 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

desorption from WC substrate. A simple calculation reveals that the C atoms derived from the missing part of WC make less than a half of what is actually needed to build the graphite as observed in Fig. 2a. This apparently means that more C atoms in the grown graphite come directly from the ingested source graphene via carbon diffusion through the bulk WC and segregation at the graphite/WC interface.22 In spite of the complexity of the carbon supply mode in our experiments, the graphite growth on WC and SiC also share some common features. First, these two types of carbides are both hexagonal crystals with C and W/Si atomic planes alternately stacked along the c-axis. Second, the graphite growth on WC is found to proceed in a bottom-up manner, as proposed for the epitaxial graphene growth on SiC.13 As indicated in Fig. 2d, the top layer of a 4-layer graphene has extended beyond the right-hand side concave step, whereas the layers below terminate into the concave step, forming the growth front for their further extension. Here, the extent of layer formation is inversely related to the distance from the top layer of graphene, which is consistent with the bottom-up growth where each subsequent graphene layer is formed between the above layer and the underlying carbide substrate. The G/W reaction was then controlled to proceed slowly by adjusting the applied bias, which facilitates the tracking of graphene growth fronts and the study of its growth dynamics. As shown in Fig. 2e-g, the bottom-up graphene thickening is found to alternate with its lateral extension during the graphene growth on WC. In the lateral extension step, as indicated by the rightward arrow in Fig. 2e, single or bilayer graphene propagates first from the site of its former termination (black arrowhead 1). In the following thickening step, the top layer extension stops at the new graphene termination (arrowhead 2 in Fig. 2f), and the layers below extend successively, resulting in a vertical growth of graphene, as indicated by the upward arrow. In the


7

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 22

next growth cycle, the top layer(s) propagates once again; its new termination is marked by arrowhead 3 in Fig. 2g. This periodic extension/thickening growth scenario can be repeated until the G/W reaction is halted. Notably, the graphene extension never surpasses the propagation of the underlying carbide region, highlighting the dominant role of carbide substrate for graphene lateral growth. Besides, the discontinuous top layer, due to the formation of a large void (as pointed by the white arrowhead in Fig. 2e), has been repaired during the subsequent graphene thickening. This suggests that the segregated carbon atoms not only incorporate into the carbon network to form graphene at the G/WC interface, but can also diffuse along the graphene plane and participate in its reconstruction at elevated temperature. It is worth noting that during the above-discussed graphene growth process, the WC substrate changes marginally without notable W desorption from its surface. Actually, graphene growth and the associated WC morphology are highly influenced by the growth conditions. During the controlled growth with a relatively low heating current, the graphene growth proceeds via alternating extension and thickening, and the WC can largely maintain its morphology. By contrast, by increasing the applied heating current, the growth can be remarkably accelerated, resulting in the graphene formation up to tens of layers within a few seconds. Such instantlyformed graphene usually displays an improved structural quality due to the significantly increased growth temperature (see the case in Fig. 2h and Supporting Information Fig. S3). Meanwhile, the increase in temperature also accelerates the process of W desorption (via its sublimation or migration), leading to a drastic morphological change of tungsten carbide encapsulated in the grown graphite, as seen in Fig. 2a and 2h. Nickel, a typical transition metal for catalytic growth of graphene, was also employed to study its interaction with graphene using the present in situ technique. A Ni tip was brought into


8

Page 9 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

contact with the surface of a graphene sheet to initiate the G/M reaction (Figure. 3a). In contrast to W, the increasing current did not cause interfacial reaction on graphene surface, though the Ni tip was locally melted and swelled at the end due to Joule heating (Fig. 3b). However, in the case when a Ni tip was made to contact the edge of a graphene sheet, the applied current heating could readily initiate graphene edge etching, as seen in Fig. 3c-h or Supplementary Video S3. The G/Ni interfacial reaction usually leads to the formation of the irregularly notched edge on graphene as if gnawed by the Ni tip. Unlike the continuous graphene ingestion by the W tip, the G/Ni reaction is often interrupted due to the relatively week adhesion between the molten Ni tipend and the etched graphene edge. The local temperature at the G/M interface upon graphene “eating” is likely around the melting point of bulk Ni (1450 oC). At such high temperature, the Ni tip-end always slightly changes its morphology after each “bite” of graphene, thus frequently detaching from the graphene sheet (Fig. 3f). The Ni tip, therefore, needs to be made in contact with the graphene sheet again to continue the G/Ni reaction (Fig. 3g-h). Actually, the Ni tip can also be strongly bonded to a graphene edge so as to pull the graphene sheet in case that the tip is cooled down to form covalent bonds at the G/Ni interface (see Video S4 in Supporting Information).24 The above experiments unambiguously demonstrate that the graphene edge is more reactive with Ni than its surface. This can be primarily attributed to the different bonding coordination of C atoms located at the graphene edge and those within the basal plane. Each C atom within the honeycomb network is bound to three neighboring C atoms by strong covalent sp2 bonds, which keeps them non-active with Ni, even in the case of extremely curved sp2 carbon network. This can be verified by a fullerene-like particle that maintains its integrity during its two reactions with the Ni tip, as indicated by the arrows in Fig. 3e-h. In contrast, at the open


9

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 22

edge of graphene, the reduced bonding coordination of C atoms and their dangling bonds make them more susceptible to the call from Ni metal: they dissolve into the molten Ni or form strong bonding with the crystalized Ni. The etched graphene should be primarily dissolved into the Ni tip, since we can not fully rule out the possibility that a small quantity of lost carbon may be oxidized (by residual oxygen in the TEM column) into carbon monoxide or carbon dioxide at the G/Ni interface.25, 26 (Another graphene etching mechanism through Ni-nanoparticle catalytic hydrogenation of carbon should not be involved due to the absence of H2).27 When a certain amount of graphene was “eaten” by the Ni tip, as seen in the case in Figure. 4a, it became saturated with carbon. Once the Ni tip detached from graphene, it became cooled instantly to the ambient temperature, leading to the multilayer graphene segregated on Ni surface, as indicated by the arrow in Fig. 4b. No existence of metastable nickel carbide phase (Ni3C) was detected, as revealed by the corresponding SAED pattern in Fig.4c (or see the HRTEM image of another Ni tip after reaction in Fig. S6). This is in line with the binary phase diagram of Ni-C in which C has a limited solubility in Ni metal without the presence of a carbide compound.7, 9 In a particular situation, the molten Ni tip end can also be bonded to the graphene edge due to the larger contact area, thus offering opportunity of the growth of thicker graphite on Ni tip due to a constant heating current and a continuous carbon supply from the source graphene. As in the case shown in Fig. 4d, the Ni tip portion has been encapsulated by a thick layer of graphite. The quick segregation of graphite has expelled a part of the melted Ni into the tip end (or partly evaporated), leaving behind a much thinner Ni core wire. The segregated graphite is estimated to be of 200 layers and its morphology is highly dependent on the deformation of the underlying Ni catalyst (Fig. 4e). When the Ni core wire was largely removed upon further


10

Page 11 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

reaction, this segment of graphite actually turned into a carbon nanotube (CNT) or nanofiber, as seen in Fig. 4f. Finally, gold, a typical noble metal, was tried to study its interfacial reaction with graphene. Gold was found to have a very weak reactivity with graphene. Except for local melting of a gold nanoelectrode at the G/M contact at a high current, no dissolution of graphene into gold or formation of graphitic layers on the gold surface were detected, irrespective of whether the gold tip contacts the graphene surface or its edge (see Supporting Information Fig. S7 and Video S5). These results are consistent with the previous reports that gold has very low catalytic activity toward the decomposition of a C feedstock.28 The experimental results of the interfacial reactions of three types of metals with graphene are summarized in Table 1. Obviously, these three metals can be lined up with respect to their carbon-starved degree as follows: W>Ni>Au. Compared to Ni and Au, the higher reactivity of tungsten with graphene may probably stem from a chemical driving force due to the negative Gibbs free energy of the carbide formation.29 Although the transformation from a flat graphene sheet to a curved or tubular structure causes an increase in bending energy, what governs this transformation is the driving force to form bonding of the curved graphene surface onto catalyst metal substrate and to reduce dangling bonds on the graphene edges, which can significantly reduce the energy of the whole system. Besides, the polarity of an applied bias was found to have little influence on the reaction behaviors, suggesting a thermal or thermochemical activated process rather than an electrical driven one. All three metals exhibit liquid-like behaviors and their morphologies change strikingly at G/M interfaces at the elevated temperatures estimated to be over ~1000 oC (for W, the formation


11

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 22

of WC was observed at a temperature more than 1200 K 30). However, the degree of damage brought to graphene during the reactions varies a lot for different metals. As seen in Table 1, a heated W tip can cause severe graphene damage and carbon loss wherever it touches the graphene; for Ni, graphene etching only starts for its edge; whereas in the case of Au, no real damage is found on graphene, though its shape could be altered slightly due to gold melting. These results highly suggest that the nonactive noble metals can remain the maximum integrity of graphene, whereas carbide-forming metals may cause the maximum damage to the graphene that would drastically influence the performance of G/M contacts and even the entire devices. We believe that using this in situ technique, it would be of great interest to further analyze the interface dynamics between graphene and other metals, such as Ti, Pd, and Sc, which have demonstrated great promise as high-performance electrode materials in the recently developed graphene and CNT device technologies.31-33 The present in situ experiments also demonstrate an entirely condensed phase transformation between different sp2 carbon allotropes, from graphene to nanotube (i.e. tubular graphene), with the assistance of a heated W and Ni catalyst (interestingly, the reverse process, i.e. from nanotube to graphene, has been achieved using several other approaches34,35). In recent years, the graphene growth from solid carbon sources through a high-temperature process has attracted an increasing research interest. In addition to the above-mentioned SiC annealing approach, graphite, amorphous carbon and polymer films, for example, can also be transformed into graphene on Ni, Co or Cu substrates in this way.9-12 Our in situ observation provides many valuable details of the graphene growth dynamics that may represent the actual situation during any ex situ graphene growth processes on a metal or carbide surface.


12

Page 13 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

CONCLUSIONS

To sum up, three different metal nanotips (W, Ni, Au) were employed to study the graphene-metal interfacial kinetic behaviors by using in situ TEM technique. Driven by a heating current, a graphene sheet is “ingested” into a liquid-like tungsten tip at the G/W interface, followed by the segregation of new graphitic layers surrounding the tip surface. The periodic extension/thickening scenario is proposed to describe the graphene growth on W tip surface, where the formation of WC and its propagation was observed to dominate the growth process. Nickel tips, showing a lower reactivity, can “eat” graphene only from its edge, leading to the graphene segregation on Ni surface without carbide formation. Au, however, seems to be not carbon-starved at all, even in its molten state. These findings provide detailed and valuable information with respect to the degraded structural stability of G/M contacts at a high working current, as well as the growth dynamics of sp2 carbon structures with metal catalyst involved, which should be vital for graphene-based device and synthesis technologies.

METHODS Tungsten, nickel and gold nanotips were prepared by DC electrochemical etching of the corresponding metal wires (0.2 mm in diameter) with 2M NaOH, 2M KCl and HCl/ethanol (1:1) solutions as the electrolytes, respectively (see Refs.1-3 for more technical details). The graphene sheets were assembled onto a freshly cut gold wire (0.25 mm in diameter) before each experiment by rubbing the gold wire in the graphene powder. This gold wire was then transferred and fixed by inserting the wire into a small-diameter pipe welded to the TEM-STM sample holder frame. An electrochemically etched metal wire was inserted into the three-dimensional movable part of the piezo-driven holder. The in situ TEM manipulation, electrical probing, EELS analysis and structural observations were performed in a JEM-3100FEF HRTEM (Omega Filter)


13

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 22

equipped with a “Nanofactory” TEM-STM holder; a part of the in situ experiments was conducted in a JEM-2100 TEM by using a “PicoFemto” TEM-STM holder as well. Experimental videos were obtained by recording sequential TEM images using a CCD camera with a rate of 2frames/s.

Supporting Information. Details of experimental procedures; Additional data for metalgraphene interactions (Figures S1-S7); In-situ TEM videos showing the structural evolution at the metal-graphene interfaces (Videos S1-S5). This material is available free of charge via the Internet at http://pubs.acs.org.”

Corresponding Author *E-mail: [email protected]; [email protected] Acknowledgements This work was financially supported by the National Natural Science Foundation of China (No. 61471307), the National Key R&D Program of China (Grant No. 2016YFA0202602), the Specialized Research

Fund for the Doctoral Program of Higher Education (No.

20130121120009), the Fundamental Research Funds for the Central Universities, National Program for Thousand Young Talents of China. It was also supported by the International Center for Materials Nanoarchitectonics (MANA) of the National Institute for Materials Science (NIMS), Tsukuba, Japan. D.G. is also grateful to the Australian Research Council for granting a Laureate Fellowship (Grant No. FL 160100089).


14

Page 15 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

REFERENCES AND NOTES (1) Novoselov, K. S.; Falko, V. I.; Colombo, L.; Gellert, P. R.; Schwab, M. G.; Kim, K. A Roadmap for Graphene. Nature 2012, 490, 192-200. (2) Lin, Y. M.; Valdes-Garcia, A.; Han, S.; Farmer, D. B.; Meric, I.; Sun, Y.; Wu, Y.; Dimitrakopoulos, C.; Grill, A.; Avouris, P.; Jenkins, K. A. Wafer-Scale Graphene Integrated Circuit. Science 2011, 332, 1294-1297. (3) Leong, W. S.; Nai, C. T.; Thong, J. T. L. What Does Annealing Do to Metal−Graphene Contacts? Nano Lett. 2014, 14, 3840-3847. (4) Mathew, J. P.; Patel, R. N.; Borah, A.; Vijay, R.; Deshmukh, M. M. Dynamical Strong Coupling and Parametric Amplification of Mechanical Modes of Graphene Drums. Nat. Nanotechnol. 2016, 11, 747-752. (5) Raccichini, R.; Varzi, A.; Passerini, S.; Scrosati, B. The Role of Graphene for Electrochemical Energy Storage. Nat. Mater. 2015, 14, 271-279. (6) Lin, D.; Liu, Y.; Liang, Z.; Lee, H. W.; Sun, J.; Wang, H.; Yan, K.; Xie, J.; Cui, Y. Layered Reduced Graphene Oxide with Nanoscale Interlayer Gaps as a Stable Host for Lithium Metal Anodes. Nat. Nanotechnol. 2016, 11, 626-633. (7) Li, X.; Cai, W.; Colombo, L.; Ruoff, R. S. Evolution of Graphene Growth on Ni and Cu by Carbon Isotope Labeling. Nano Lett. 2009, 9, 4268-4272. (8) Emtsev, K. V.; Bostwick, A.; Horn, K.; Jobst, J.; Kellogg, G. L.; Ley, L.; McChesney, J. L.; Ohta, T.; Reshanov, S. A.; Röhrl, J.; Rotenberg, E. A.; Schmid, K.; Waldmann, D.; Weber, H. B.; Seyller, T. Towards Wafer-Size Graphene Layers by Atmospheric Pressure Graphitization of Silicon Carbide. Nat. Mater. 2009, 8, 203-207. (9) Amini, S.; Garay, J.; Liu, G.; Balander, A. A.; Abbaschian, R. Growth of Large-Area Graphene Films from Metal-Carbon Melts. J. Appl. Phys. 2010, 108, 094321. (10) Zheng, M.; Takei, K.; Hsia, B.; Fang, H.; Zhang, X.; Ferralis, N.; Ko, H.; Chueh, Y. L.; Zhang, Y.; Maboudian, R.; Javey, A. Metal-Catalyzed Crystallization of Amorphous Carbon to Graphene. Appl. Phys. Lett. 2010, 96, 063110. (11) Orofeo, C. M.; Ago, H.; Hu, B.; Tsuji, M. Synthesis of Large Area, Homogeneous, Single Layer Graphene Films by Annealing Amorphous Carbon on Co and Ni. Nano Res. 2011, 4, 531– 540. (12) Sun, Z. Z.; Yan, Z.; Yao, J.; Beitler, E.; Zhu, Y.; Tour, J. M. Growth of Graphene from Solid Carbon Sources. Nature 2009, 468, 549-522. (13) Robinson, J.; Weng, X.; Trumbull, K.; Cavalero, R.; Wetherington, M.; Frantz, E.; LaBella, M.; Hughes, Z.; Fanton, M.; Snyder, D. Nucleation of Epitaxial Graphene on SiC(0001). ACS Nano 2010, 4,153-158.


15

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 22

(14) Poon, S. W.; Chen, W.; Tok, E. S.; Wee, A. T. S. Probing Epitaxial Growth of Graphene on Silicon Carbide by Metal Decoration. Appl. Phys. Lett. 2008, 92, 104102. (15) Saadi, S.; Abild-Pedersen, F.; Helveg, S.; Sehested, J.; Hinnemann, B.; Appel, C. C.; Nørskov, J. K. On the Role of Metal Step-Edges in Graphene Growth. J. Phys. Chem. C 2010, 114, 11221-11227. (16) Ding, F.; Larsson, P.; Larsson, J. A.; Ahuja, R.; Duan, H.; Rosén, A.; Bolton, K. The Importance of Strong Carbon−Metal Adhesion for Catalytic Nucleation of Single-Walled Carbon Nanotubes. Nano Lett. 2008, 8, 463–468. (17) Reina, A.; Jia, X.; Ho, J.; Nezich, D.; Son, H.; Bulovic, V.; Dresselhaus, M. S.; Kong, J. Large Area, Few-Layer Graphene Films on Arbitrary Substrates by Chemical Vapor Deposition. Nano Lett. 2009, 9, 30-35. (18) Rangappa, D.; Sone, K.; Wang, M. S.; Gautam, U. K.; Golberg, D.; Itoh, H.; Ichihara, M.; Honma, I. Rapid and Direct Conversion of Graphite Crystals into High-Yielding, Good-Quality Graphene by Supercritical Fluid Exfoliation. Chem. Eur. J. 2010, 16, 6488-6494. (19) Ibe, J. P.; Bey, P. P.; Brandow, S. L.; Brizzolara, R. A.; Burnham, N. A.; Dilella, D. P.; Lee, K. P.; Marrian, C. R. K.; Colton, R. J. On the Electrochemical Etching of Tips for Scanning Tunneling Microscopy. J. Vac. Sci. Technol. A 1990, 8, 3570-3575. (20) Cavallini, M.; Biscarini, F. Electrochemically Etched Nickel Tips for Spin Polarized Scanning Tunneling Microscopy. Rev. Sci. Instrum. 2000, 71, 4457-4460. (21) Ren, B.; Picardi, G.; Pettinger, B. Preparation of Gold Tips Suitable for Tip-Enhanced Raman Spectroscopy and Light Emission by Electrochemical Etching. Rev. Sci. Instrum. 2004, 75, 837-841. (22) Wang, M. S.; Golberg, D.; Bando, Y. Interface Dynamic Behavior between a Carbon Nanotube and Metal Electrode. Adv. Mater. 2010, 22, 93–98. (23) Zhang, B.; Zhao, L. Z.; Cheng, Y.; Golberg, D.; Wang, M. S. Reversible Tuning of Individual Carbon Nanotube Mechanical Properties via Defect Engineering. Nano Lett. 2016, 16, 5221−5227. (24) Rodríguez-Manzo, J.; Banhart, F.; Terrones, M.; Terrones, H.; Grobert, N.; Ajaya, P. M.; Sumpter, B. G.; Meunier, V.; Wang, M. S.; Bando, Y.; Golberg, D. Heterojunctions between Metals and Carbon Nanotubes as Ultimate Nanocontacts. Proc. Natl. Acad. Sci. U. S. A. 2009, 106, 4591–4595. (25) Wei, J.; Xu, Z.; Wang, H.; Tian, X.; Yang, S.; Wang, L.; Wang, W.; Bai, X. In-Situ TEM Imaging of the Anisotropic Etching of Graphene by Metal Nanoparticles. Nanotechnology 2014, 25, 465709. (26) Severin, N.; Kirstein, S.; Sokolov, I. M.; Rabe, J. P. Rapid Trench Channeling of Graphenes with Catalytic Silver Nanoparticles. Nano Lett. 2009, 9, 475-461.


16

Page 17 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

(27) Campos, L. C.; Manfrinato, V. R.; Sanchez-Yamagishi, J. D.; Kong, J.; Jarillo-Herrero, P. Anisotropic Etching and Nanoribbon Formation in Single-Layer Graphene. Nano Lett. 2009, 9, 2600-2604. (28) Yoshihara, N.; Ago, H.; Tsuji, M. Growth Mechanism of Carbon Nanotubes over GoldSupported Catalysts. Jpn. J. Appl. Phys. 2008, 47, 1944. (29) Kostorz, G. Phase Transformations in Materials. Wiley-VCH, Germany 2001, Ch. 7. (30) Luthin, J.; Linsmeier, C. Carbon Films and Carbide Formation on Tungsten. Surf. Sci. 2000, 454, 78-82. (31) Xu, H.; Zhang, Z.; Xu, H.; Wang, Z.; Wang, S.; Peng, L. M. Top-Gated Graphene FieldEffect Transistors with High Normalized Transconductance and Designable Dirac Point Voltage. ACS Nano 2011, 5, 5031–5037. (32) Xu, H.; Zhang, Z.; Wang, Z.; Wang, S.; Liang, X.; Peng, L. M. Quantum Capacitance Limited Vertical Scaling of Graphene Field-Effect Transistor. ACS Nano, 2011, 5, 2340–2347. (33) Zhang, Z.; Liang, X.; Wang, S.; Yao, K.; Hu, Y.; Zhu, Y.; Chen, Q.; Zhou, W.; Li, Y.; Yao, Y.; Zhang, J.; Peng, L. M. Doping-Free Fabrication of Carbon Nanotube Based Ballistic CMOS Devices and Circuits. Nano Lett. 2007, 7, 3603-3607. (34) Kosynkin, D. V.; Higginbotham, A. L.; Sinitskii, A.; Lomeda, J. R.; Dimiev, A.; Price, B. K.; Tour, J. M. Longitudinal Unzipping of Carbon Nanotubes to Form Graphene Nanoribbons. Nature 2009, 458, 872-876. (35) Jiao, L.; Zhang, L.; Wang, X.; Diankov, G.; Dai, H. Narrow Graphene Nanoribbons from Carbon Nanotubes. Nature 2009, 458, 877-880.


17

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 22

Figure 1. Morphology and structure changes of a graphene/W-tip heterostructure under biasing and Joule heating. (a-e) The series of TEM images showing the structural transformation of the G/W interface. In (b) the arrow indicates a wrinkle on the graphene surface, and the inset shows the enlarged image of the contact region with a void formed within the surface layers highlighted by a yellow dashed line. (f) The W tip finally broke at the carbide region under tensile stress caused by graphene ingestion. The black arrows indicate the positions of the interface between the tungsten carbide and pure tungsten domains. (g) A high-resolution TEM image of the WC domain and the corresponding SAED pattern (inset).


18

Page 19 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 2. Structural characterization of the W/WC heterostructure encapsulated with the segregated graphite layers. TEM image (a) and the corresponding spatially resolved carbon map (b) of a G/W/WC heterostructure. (c) EEL spectra of the domains indicated in (a). (d) HRTEM image of the indicated region in the inset showing the nucleated graphene layers on the WC substrate. The inset shows the overall image of the G/W interface. (e-g) The alternating graphene layer lateral extension and vertical thickening growth on WC substrate. Black arrowheads 1-3 display the advance of graphene termination. (h) A typical case of W-tip encapsulated with a thick graphite layer with improved structural quality.


19

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 22

Figure 3. Interfacial reaction between Ni tips and graphene sheets with different contact conditions. (a-b) Local melting of a nickel tip on the surface of a graphene sheet at a large heating current. (c-h) The series of TEM images showing the etching of graphene edge by a Ni tip with its end locally melted. The black arrows indicate a fullerene-like carbon particle that maintains its integrity during two reactions (e-f and g-h) with the Ni tip.


20

Page 21 of 22

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Figure 4. Structural characterization of Ni tips encapsulated with a layer of segregated graphite obtained by G/Ni reaction. (a-c) Low- and high-magnification TEM images showing the graphene/Ni heterostructure and the corresponding SAED pattern. (d) A graphitic tube encapsulating a thin Ni core wire during G/Ni reaction. (e) A magnified image of the boxed region in d. (f) The carbon tube with the Ni core being largely removed upon further G/Ni reaction.

Table 1. The summarized experimental results and their comparison with respect to the interfacial reaction of three types of metals with graphene. Metal type

Reactivity with G

Reaction site on G

Carbide formation

C shell formation

W

High

Everywhere

Yes

Yes

Ni

Medium

Edge

No

Yes

Au

Low

None

No

No


21

ACS Nano

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 22

ToC Figure

Synopsis Interface dynamic behavior between individual graphene sheets and various metal electrodes is observed directly at a nearly atomic resolution. The W/Ni tip-end absorbs the source graphene atoms, which then penetrate deep into its body, and finally precipitate as freshly formed graphitic tubular shells encapsulating the electrode. A periodic extension/thickening graphene growth scenario is proposed based on atomic-scale observation of this process on W electrodes.


22

Graphene Ingestion and Regrowth on âCarbon ... - ACS Publications