Article pubs.acs.org/Macromolecules
Heterogeneity, Segmental and Hydrogen Bond Dynamics, and Aging of Supramolecular Self-Healing Rubber Rongchun Zhang,§ Tingzi Yan,† Bob-Dan Lechner,† Klaus Schröter,† Yin Liang,‡ Baohui Li,§ Filipe Furtado,† Pingchuan Sun,*,‡ and Kay Saalwac̈ hter*,† †
Naturwissenschaftliche Fakultät II, Martin-Luther Universität Halle-Wittenberg, D-06099 Halle (Saale), Germany Key Laboratory of Functional Polymer Materials, Ministry of Education, College of Chemistry, Nankai University, Tianjin 300071, P. R. China § School of Physics, Nankai University, Tianjin 300071, P. R. China ‡
ABSTRACT: In recent years, self-healing materials have attracted increasing attention due to their potentially spontaneous self-repairing ability after mechanical damage. Here, we focus on a supramolecular self-healing rubber based on fatty acids following the work of Leibler and co-workers. We study the heterogeneous network structure and hydrogen bond dynamics as well as its significant aging properties using several experimental techniques. NMR experiments reveal that the rubber is basically a two-component system, with a ∼85% fraction of material rich in hydrogen-bonded structures and associated aliphatic moieties, undergoing a glass transition just below ambient temperature, and the other one being comprised of more mobile aliphatic chains. Changes in the IR bands corresponding to the NH bending and CO stretching vibrations show that water in the rubber not only takes the role of a plasticizer, reducing the glass transition temperature of the main component, but also is involved in changes of the hydrogen-bonding network. On the basis of shear rheology experiments and proton low-field NMR, we deduce that the rubber undergoes irreversible chemical cross-linking reactions at temperatures above 110 °C, going along with a weakening of its selfhealing ability.
■
INTRODUCTION In the past decades, synthetic polymers have completely changed our daily lives, being widely used in industry due to their low price, easy processing, and their exceptional physical and chemical properties. In addressing the new perspective, self-healing materials have attracted considerable recent attention due to their ability to autonomously and spontaneously repair themselves after suffering from surface or internal damage.1−6 A traditional way of self-repair in resins is realized by embedding repairing chemicals in container capsules within the polymer matrix, initiating the chemical repair reactions by crack formation in the capsules.7,8 In such systems, the chemical reaction can only take place once, and the mechanical properties of the material may be largely influenced or deteriorated by the presence of the capsules. Another elegant self-healing mechanism rests on the introduction of thermally reversible covalent bonds9−11 or noncovalent supramolecular linkages12 into polymers. In these materials, upon heating, the polymers can reversibly rupture and re-form to provide selfhealing. Burnworth et al.13 also synthesized an optically healable metallo-supramolecular polymer, which can convert photonic energy into localized heat, which in turn leads to healing via reversible dissociation of the metal-complex motifs. However, for these materials external energy is required for healing, which limits their application in industry. Recently, Leibler and co-workers2 synthesized a supramolecular rubber based on multivalent fatty acids, which is © XXXX American Chemical Society
able to self-heal at room temperature without the need for external stimuli or embedding chemical substances into the polymer matrix. The self-healing ability was ascribed to a widespread hydrogen-bonding network formed by multifunctional oligomers carrying several associating hydrogen-bonding moieties. Upon fracture, tear, or abrasion, the network breaks by separation of the hydrogen-bonded moieties. As a result, a large number of free and active moieties located at the damaged surface can reassociate when the two surfaces are brought into contact again, thereby causing the interface to heal and the bulk structure to recover its original properties.14 The resulting minimal-maintenance material may thus turn out to be of high economic relevance. This makes it necessary and important to improve our comprehensive understanding of the properties of this self-healing rubber (SHR). In this work, we focus on an SHR sample prepared by following the work of Leibler and co-workers,15 investigating its heterogeneous structure, segmental and hydrogen-bond dynamics, and its aging behavior. We use different low- and high-field proton (1H) NMR methods, IR spectroscopy, and shear oscillation rheology to study the material’s properties on a molecular and macroscopic scale, respectively, and correlate these findings. Importantly, we demonstrate the material’s Received: January 4, 2013 Revised: January 31, 2013
A
dx.doi.org/10.1021/ma400019m | Macromolecules XXXX, XXX, XXX−XXX
Macromolecules
Article
Scheme 1. Molecular Structure of the Raw Materials for SHR
Figure 1. DSC thermograms of the three SHR samples with Tg values indicated. surface water by wiping just before the experiments. The DSC glass transition temperatures for the dried, ambient, and hydrated samples are about 289, 285, and 258 K, respectively, as shown in Figure 1. We note that the dried sample may not be completely water-free, but we wanted to avoid potential structural changes that may occur at higher drying temperatures (vide inf ra). As is apparent from the DSC thermogram in Figure 1, the glass transition of the hydrated sample takes place over a much wider temperature range, indicating significant inhomogeneity. Infrared Experiments. Attenuated total internal reflection (ATR) IR experiments were performed with a Bruker BioATRII cell with Si internal reflective element on a Bruker Tensor27 using an MCT detector. Temperature was adjusted by a Haake Phoenix II thermostat (C25P, Thermo Electron Corporation, Karlsruhe, Germany) and controlled with a Delphi-based home-written software. Since the sample was densely pressed onto the ATR crystal within the sample well, air contact in the investigated area could be effectively avoided. The penetration depth of the IR irradiation is a function of the wavelength and can be estimated to be about 500−1000 nm in the investigated wavelength range. Rheology. The dynamic shear modulus was measured at a frequency of 1 rad/s with an Anton Paar MCR 501 rheometer in the
biphasic nature on the basis of NMR experiments that are sensitive to segmental motions and find that the material undergoes irreversible permanent cross-linking at temperatures above 110 °C, whereby its self-healing ability is compromised.
■
EXPERIMENTAL SECTION
Samples. The raw materials for the synthesis of SHR include a mixture of fatty mono-, di-, and triacids, diethylenetriamine (DETA), 2-aminoethylimidazolidone (UDETA), and urea, whose molecular structures are shown in Scheme 1. SHR was prepared according to published procedures,15 which are shown in Scheme 2. The average number of COOH groups per molecule is navg = 2.03. We used fixed UDETA/DETA compositions, where x/n = 0.2 and y/n = 0.4. The successful synthesis was confirmed by reproducing many of the experimental results published in the related papers, using differential scanning calorimetry (DSC), X-ray diffraction, shear oscillation rheology, etc. A dried sample was obtained by storage in an oven under vacuum at 35 °C for about 2 days. For hydrated samples, we immersed the SHR in water (or D2O) for about 2 days, removing the
Scheme 2. Synthesis of SHR
B
dx.doi.org/10.1021/ma400019m | Macromolecules XXXX, XXX, XXX−XXX
Macromolecules
Article
Figure 2. Pulse sequences. Solid bars denote 90° pulses, the open dashed bars denote 180° pulses, and the shaded areas represent groups of pulses. (a) Single-pulse excitation experiment for detecting the free induction decay (FID) signals, where the initial part is missing due to the dead time of the receiver. (b) Magic-sandwich echo (MSE) pulse sequence for refocusing the loss of rigid-phase signal due to the dead time. (c) Multiplequantum (MQ) pulse sequence. The groups of pulses for the excitation and reconversion of higher spin coherences are the same except for their phases and can consist of the Baum−Pines or three-pulse segments, which both excite and reconvert double-quantum (and to a minor degree higher multiple-quantum) coherences. Multiple-Quantum (MQ) NMR. For a complete account of the principle of MQ NMR as applied to polymers and soft materials we refer to ref 19. Pulse sequences of MQ experiments are shown in Figure 2c. Here we just recall the main procedures of the measurements as well as the data analysis. Depending on the phase cycle used, the MQ experiment yields two signal functions as a function of the double-quantum (DQ) evolution time τDQ, the decaying reference intensity (Iref), and the double-quantum (IDQ) buildup intensity. The sum of both form the sum MQ (IΣMQ) intensity, whose overall decay is dominated by the time scale of segmental orientation fluctuations, while the DQ intensity buildup at shorter times is governed by dipolar couplings between the many protons. These are strong (Dstat ∼ 30 kHz) in a rigid/glassy system, while due to their orientation dependence they are reduced to zero in isotropic liquids or to a finite residual value (Dres) in cases of anisotropic mobility. The latter is realized by entanglement effects as well as crosslinks in true networks, where fluctuations of the end-fixed subchains up to the milliseconds scale lead to a measurable anisotropy on the percent scale (as quantified by a dynamic order parameter S ∼ Dres).20 Dres is the main observable, and in actual rubbers it is proportional to the inverse network chain molecular weight (D r e s ∼ 1/Mc) and thus directly proportional to cross-link density.20 The DQ intensity is subject to a relaxation effect at longer evolution time, which requires an intensity normalization protocol based upon a pointby-point division by the ΣMQ intensity
linear-response range with strains of 0.5%. All measurements were done in parallel plate geometry with 8 mm diameter plates and a gap of around 1 mm. Temperature sweeps were measured from 20 to 160 °C with a temperature increment of 1 K/min. The samples were kept in a chamber under a nitrogen atmosphere. Low-Field 1H NMR. The measurements were performed on a Bruker Minispec mq20 low-field spectrometer at 20 MHz proton resonance frequency. The sample temperature was controlled with a BVT3000 heater working with a flow of heated air. In order to avoid O2-related sample degradation, the NMR tube (10 mm outer diameter) was first flushed with nitrogen gas and then flame-sealed. The minispec has a typical π/2 pulse length of about 1.8 μs and a receiver dead time of about 11 μs. Magic-Sandwich Echo Experiments. As the receiver of the minispec has a rather long dead time of 11 μs, the initial part of the free induction decay (FID) reflecting the rapidly decaying rigid-phase signals is missing, as shown in Figure 2a. This problem is tackled by the magic-sandwich echo (MSE) pulse sequence shown in Figure 2b.16 Through adjusting the finite phase switching time tϕ of the instrument, the final echo time τMSE can be adapted to the receiver dead time, so as to almost fully recover the FID and its shape. In multiphase materials with different molecular mobilities, the FID can be well fitted with a b
combination of stretched or compressed exponential functions, e−(t/τ) . An exponent b = 2 (Gaussian) along with a very short (20−40 μs) τ indicates a rigid component, while b ∼ 1 or even less (indicating a τ distribution) and longer τ indicate a potentially inhomogeneous components with fast mobility. Intermediate dynamics on the time scale of the inverse dipolar broadening of the rigid-limit spectrum (∼20 μs) is reflected in apparent exponents between 2 and 1. In this range, more specific fitting functions apply,17 as discussed below. In fully relaxed samples, using a sufficiently long recycle delay between individual scans, the NMR intensity is proportional to the total proton numer and inversely proportional to the Kelvin temperature according to the Curie law. In this way, the MSE-detected FID intensities were corrected, which allows to estimate intensity losses due to efficiency problems of the MSE related to intermediate mobility and other imperfections.17,18
InDQ =
IDQ IΣ MQ
(1)
The normalization eliminates the effect of temperature-dependent segmental dynamics, so the normalized DQ intensity is exclusively dependent on Dres characterizing the structure of the rubber. However, before the normalization, the signal of usually slowly relaxing isotropically mobile components must be subtracted from the ΣMQ intensity, as shown in eq 2.
IΣ MQ = IDQ + Iref − Be−2τDQ / T2B − C e−2τDQ / T2C C
(2)
dx.doi.org/10.1021/ma400019m | Macromolecules XXXX, XXX, XXX−XXX
Macromolecules
Article
B and C are the fractions of (in our case) two separable mobile components. For a very homogeneous system, after subtraction, the DQ intensity can be calculated and analyzed according to eq 321
InDQ (τDQ , Dres) = 0.5(1 − exp{−(0.378DresτDQ )1.5 } cos[0.583DresτDQ ]
(3)
where Dres is the apparent residual dipolar coupling. Generally, there are two most common excitation schemes for higher-spin coherences in static MQ experiments. One is the Baum− Pines segment,22 and the other is the so-called three-pulse segment.19,23 Both segments are shown in Figure 2c and induce DQ and higher-quantum transitions. In the relevant DQ buildup region, the signal is indeed dominated by double-quantum transitions only, making the experiments sensitive to apparent 1H−1H pair couplings. The most important difference between the two experiments is that the Baum−Pines segment is more robust at long times τDQ and can deal with a multiple-spin weak-coupling situation found in rubbers and melts far above the glass transition,19 while the three-pulse segment suffers from efficiency problems in a multispin system but is more efficient when rather strong couplings are present (the minimum DQ evolution time is 10 μs as opposed to the ∼100 μs minimum cycle time for the Baum−Pines segment). So in general, the three-pulse segment is usually adopted when materials with rather rigid regions are to be characterized.22,24 High-Field 1H Magic-Angle Spinning (MAS) NMR. High-field experiments were performed on a Bruker Avance III 400 spectrometer, using a 4 mm double-resonance probe. The MAS frequency was set between 5 and 8 kHz. A 90° radio-frequency pulse of 3.5 μs was used on the 1H channel. The chemical shift was referenced to external adamantane, whose proton chemical shift was set to 1.63 ppm. Proton single-pulse excitation and rotor-synchronized Hahn-echo experiments were performed for dry, ambient, and hydrated samples as well as for chloroform-swollen pristine and high-temperature aged SHR samples. Rotor synchronization means that the time intervals before and after the 180° pulse were set to integer multiples of the spinning period, which ensures that the results are free of rotor modulations. At moderate MAS rates, weak residual dipolar couplings among mobile protons are averaged out and the echo decay is long, while stronger couplings between multiple protons still lead to signficant dephasing and short apparent T2 despite the MAS as a result of higher-order terms. This enables a similar yet somewhat qualitative mobility distinction as compared to static low-field NMR.
Figure 3. (a) MSE-refocused FID signals (for clarity with 7× reduced point density) as a function of the acquisition time for the dry SHR sample at three different temperatures. All intensities are corrected according to the Curie law. The two-component fitting curves are shown as solid curves, and separate components are shown as dashed curves for the 315 K data. (b) Log-scale plot of the correlation time τc obtained from the fit of the less mobile component (upper part) and the fitted mobile-component apparent 1/T2app (lower part, excluding the highest-temperature values which are challenged by the shim limit) vs inverse temperature. The solid lines are fits to the Vogel−Fulcher equation, and the dashed lines are linear fits covering the hightemperature fast-motion region, yielding a constant apparent activation energy.
corresponding data for the dry sample in Figure 3, with increasing temperature, a motional-narrowing phenomenon is apparent, reflected in an increasingly slower decay of the signal traces. Note that the “NMR Tg”, i.e., the temperature region where the most significant signal shape changes are observed, is located roughly 30−50 K above the calorimetric or hertz-scale dynamic glass transition, as the NMR signal is sensitive to fast motions on the 20 μs scale. Previous work17 has shown that the FID signal of a single polymer phase undergoing the softening transition above Tg can be well described by a function based on Anderson−Weiss (AW) theory.25 The theory relies on a second-moment approximation of the distribution of the spectral frequency ω(θ,τ), and the ensemble- and time-averaged signal function reads
■
RESULTS AND DISCUSSION Heterogeneous Structure and Segmental Dynamics. The SHR was claimed to exhibit an ordering at the nanometer scale arising from a segregation between unpolar and polar domains,14 as suggested by X-ray scattering results.2 The unpolar domains are rich in fatty acids, and the polar domains are rich in hydrogen-bonding moieties. The segregation of unpolar and polar domains reflects the heterogeneous structure of the SHR and possibly comes along with differences in molecular mobility in the different domains. In particular, the question arises whether the glass transition detected by DSC at around 287 K (ambient sample) may be related to only one of the two phases. In principle, the molecular mobility can be investigated by studying simple FID signals. A fast decay indicates the presence of rigid components, while a slow decay corresponds to the response of mobile components. However, due to the dead time problem of the instrument, the acquired FID from singlepulse experiments will suffer from signal missing in the initial period which results in incomplete FID shapes. As the missing part corresponds to the response of very rigid components, it has to be retrieved. Herein, the MSE pulse sequence was used to recover the signal lost during the dead time. As shown in the
IFID(t ) = ⟨cos
∫t
t+τ
ω(θ , τ )⟩
⎡ ⎛ ⎞⎤ t = exp⎢ −M 2τc 2⎜e−t / τc + − 1⎟⎥ ⎢⎣ τc ⎝ ⎠⎥⎦
(4)
This result is based upon the assumption that the glass process can be described by an (almost) isotropic rotational diffusion process with correlation time τc, which should be related to the α relaxation time τα. M2 is the dipolar second moment of the D
dx.doi.org/10.1021/ma400019m | Macromolecules XXXX, XXX, XXX−XXX
Macromolecules
Article
molecular dynamics in the majority phase dominates the mechanical behavior. Upon cooling, the apparent relaxation rate 1/T2app of the mobile component tends toward a plateau value (i.e., a lower T2 limit). In the fast-motion high-temperature branch, an Arrhenius fit (ln cst/T2app = ln τc = ln τ0 + Ea,app/RT; see the dashed line in Figure 3b) yields an apparent activation energy of about 46 kJ/mol describing the motion of the segments in this phase. From the data it is not possible to decide if a separate glass transition (Vogel−Fulcher behavior) exists in this domain, but notably, the segmental dynamics in this domain is obviously coupled to the majority component. Summarizing, the main result of the FID component analysis is the observation that the more mobile components, which may have a Tg much below the DSC temperature ranges investigated so far, take up a (proton) fraction of around 15% of the samples, while the rigid fraction undergoing a glass transition somewhat below ambient temperature amounts to about 85% of the samples. The systematic error associated with ambiguities of the fitting procedure is estimated to around ±5%. Notably, the fitting quality was visibly inferior for the hydrated sample, which is consistent with its more pronounced dynamic inhomogeneity shown by DSC (Figure 1). In order to assess the chemical nature of the two phases, we acquired 1H high-resolution MAS spectra and introduced a rotor-synchronized Hahn echo to allow for a selective relaxation of the less mobile component (see Figure 4).
rigid-limit (glassy) spectral line shape. The data in Figure 3 could not be fitted well to this function, indicating heterogeneity and additional components. We therefore chose a two-component fitting function, with an additional more mobile component modeled by a stretched/compressed b
exponential function, e−(t/T2app) , to describe its decay: ⎡ ⎛ ⎞⎤ t − 1⎟⎥ IFID(t ) = Ag exp⎢ −M 2τc 2⎜e−t / τc + ⎢⎣ τc ⎝ ⎠⎥⎦ b
+ A m e−(t / T2app)
(5)
Ag represents the amplitude of glassy components that soften upon heating, and Am denotes the mobile fraction. For the latter component we analyze the inverse decay time constant 1/ T2app, corresponding to an apparent transverse relaxation rate. In the fast-motion limit (small τc), eq 5 exhibits an exponential limiting behavior with a relaxation rate 1/T2 ≈ M2τc, so the T2app−1 can be used to qualitatively asses the temperature dependence of the associated correlation time. For the lower temperature range up to 325 K, the FID could be stably fitted using the above fitting function with all parameters free. From the fitting of the dry and ambient samples at T = 270 K, we found M2 = 8000 ms−2 for the rigid limit, which was kept constant in all other fits. The mobile amplitude Am was found to be constant in that range, corresponding to a fraction Am/(Am + Ag) of about 15% in the dry and ambient samples. The stability of the fitting deteriorated at higher temperatures due to the limited acquired time window of 0.5 ms (and fitting longer times is not advised due to unknown signal shape related to field inhomogeneities rather than sample properties). Therefore, the amplitude Am was kept fixed at all higher temperatures. Above 345 K the parameter b increased in an uncontrolled fashion and is fixed at a reasonable value of 2. This is the limit above which the intrinsic T2app of the mobile fraction becomes longer than the decay related to the resolution (field inhomogeneity) of the magnet. In this range, the signal decay of a very mobile component indeed appears more or less Gaussian, and T2app is in the milliseconds range, which means that the mobile component merely provides a plateau contribution to the intensity. So for 355 K and above, the amplitude Ag and the correlation time τc remained the only free variables in the fits. For Ag we note an intensity minimum at 315 K (dry sample), which arises because the efficiency of the MSE before detection is compromised by the α process being in the intermediate dynamic range, corresponding to a T2 minimum at the “NMR Tg”.17,18 The intensity minima for the ambient and hydrated samples were found at around 310 and 270 K, respectively, confirming the order of their respective Tgs. The correlation time τc could be fitted with the Vogel−Fulcher (VF) equation, ln τc = ln τ0 + B/(T − TV), as shown in Figure 3b. The Vogel temperature was fixed at an estimated Tg − 50 K = 237 K for the ambient sample, determining B, and with B fixed, TV of the dry and hydrated samples were estimated to 241 and 214 K, respectively, which again nicely reproduces the trend from the DSC values for Tg (Figure 1b). We take this finding as a proof of the validity of our fitting approach. We note that VF fits to the temperature-dependent shift factor obtained from frequency-dependent rheology results for the ambient sample (data not shown) yielded exactly the TV estimated from the DSC Tg. This provides the overall confirmation that the
Figure 4. 1H MAS spectra (8 kHz spinning frequency) of the ambient sample taken at two different temperatures far above Tg, acquired after a single pulse (dashed lines) and after rotor-synchronized Hahn echoes of duration 0.25, 1, and 2 ms.
Sufficiently resolved spectra could be taken around ∼350 K and above, where it is seen that the remaining component after a relaxation delay of 1−2 ms exclusively shows saturated alkyl resonances in the 1−2 ppm range. That means the saturated alkyl signals have the slowest decay rate, while the rigid hydrogen-bonding-related signals decay faster, which proves that the more mobile minority phase is hydrophobic in nature and is composed of long fatty-acid chains. Only at 370 K and above, the mobility of the less mobile majority phase is high enough to lead to resolved signals in the higher ppm range with sufficiently long T2 to partially survive the Hahn echo filter. The heterogeneous structure could be further addressed with MQ NMR experiments, as shown in Figure 5. The aim of these experiments was, initially, to reveal anisotropic mobility of chainlike structures, which would be evidence for entropic rubber elasticity.19 This, however, requires heating of the samples to at least ∼70 K above Tg so as to have segmental E
dx.doi.org/10.1021/ma400019m | Macromolecules XXXX, XXX, XXX−XXX
Macromolecules
Article
Figure 7. Storage and loss moduli (G′, G″) as a function of temperature at constant frequency of 1 rad/s and with a strain amplitude of 0.5% (for clarity with 5× reduced point density). The dry sample was first heated from 20 to 160 °C (red circles) and then cooled to 20 °C (blue triangles) with heating/cooling rates of 1 K/ min.
Figure 5. DQ buildup curve (solid squares) and sum intensity decay data (open circles) of dry SHR at 335 K. The solid curves are obtained from a simultaneous fit of the IΣMQ decay (open squares, after tail subtraction) and IDQ buildup signals. The normalized DQ buildup data are also shown in the inset.
mobility fast enough to minimize the overall signal relaxation (of the ΣMQ intensity) on the time scale of spin evolution due to small residual dipolar couplings (Dres). The aging at these temperatures (see below) prevented a consistent study of the pristine material, so we here focus at a temperature of T = 335 K, where aging is still slow but the α-relaxation is not yet fast on the NMR time scale. This implies rather large apparent Dres and requires the use of the three-pulse segment rather than the more stable Baum−Pines segment in the MQ experiment. The cycle time of the latter is too long, such that stronger coupled moieties are subject to dephasing due to higher-order terms in its average Hamiltonian. The IDQ + Iref decay data shown in Figure 5 reveal a biexponential tail, corresponding to about 44% isotropically mobile molecular segments, subdivided into a long-T 2 component of about 34%, which corresponds to the H-bonded mobile fraction identified above in the FID analysis, and another less mobile ∼10% fraction with a shorter T2. The apparent mobile fraction is higher than in the FID component decomposition discussed above (34% vs 15%) because the relative intensity of the less mobile fraction is reduced due to intensity loss of the more rigid parts before MSE detection, as discussed above. The component fractions are thus not quantitative. The normalized DQ intensity curve as a function of DQ exciting time is shown in the inset of Figure 5. It reaches
the theoretically expected plateau of 50% of the total intensity, and this observation represents a quality-control criterion for the reliability of the tail fit.26 The nice two-step behavior suggests two subcomponents with different motional anisotropy (different Dres). However, this data could not be fitted with a combination of commonly used nDQ buildup functions such as eq 3, as the different components had different relaxation time,27 which means that the point-by-point normalized DQ intensity is distorted. Therefore, we resorted to a simultaneous fit of the raw DQ and ΣMQ signals, the latter after tail subtraction, as discussed in ref 27, taking explicitly into account the different relaxation behavior of the subcomponents. Again, a fit assuming a welldefined Dres for each subcomponent did not describe the data well, so we used a fit based on a Gamma distribution of couplings,19 which is a generic function providing a good fit in heterogeneous scenarios,28 but does not introduce a new fit parameter, as the distribution width depends on its average Dav: P(|Dres|) =
2 π
27|Dres| 8Dav 3
e−3 |Dres| /(2Dav ) (6)
The total DQ buildup is calculated as a numerical finite-step integral according to
Figure 6. (a) ATR-IR spectra of the dry and hydrated samples at room temperature, with the relevant peaks marked by dashed lines. (b) The wavenumber of the N−H bending (around 1545 cm−1) and the amide CO stretching bands (around 1640 cm−1) as a function of temperature for dry and hydrated SHR, restricted to