Highly Carbon-Doped TiO2 Derived from MXene Boosting the

Sep 9, 2018 - The field emission scanning electron microscopy (FESEM) images showed the morphology of the obtained HC-TiO2. Figure 1a showed the ...
0 downloads 0 Views 4MB Size
Subscriber access provided by Kaohsiung Medical University

Article

Highly Carbon-doped TiO2 Derived from MXene Boosting the Photocatalytic Hydrogen Evolution Guangri Jia, Ying Wang, Xiaoqiang Cui, and Weitao Zheng ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.8b03406 • Publication Date (Web): 09 Sep 2018 Downloaded from http://pubs.acs.org on September 9, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Highly Carbon-doped TiO2 Derived from MXene Boosting the Photocatalytic Hydrogen Evolution Guangri Jia a, Ying Wang a, Xiaoqiang Cui, a, * and Weitao Zheng a, *

a

Key Laboratory of Automobile Materials of MOE and School of Materials Science and

Engineering, Jilin University, 2699 Qianjin Street, Changchun 130012, China. *

Corresponding author: Xiaoqiang Cui and Weitao Zheng

E-mail address: [email protected]; [email protected] Tel & Fax: +86-431-85155279

1

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT The effective in-situ carbon-doping of titanium dioxide can greatly improve the lifetime of photogenerated carriers and widen the absorption range of light for photocatalytic reactions. Here, highly carbon-doped TiO2 (HC-TiO2) with hierarchical structure and good crystallization was synthesized by using the exfoliated MXene supernatant at low temperature. The resultant HC-TiO2 was fully characterized, and its catalytic performance for photocatalytic hydrogen evolution was investigated. It was found that the high content carbon-doping induced a valence band tail state that promoted photogenerated carriers’ effective separation and reduced bandgap, which greatly improved the utilization of light for photocatalytic reactions. This band tail was attributed to the strong electron withdrawing carboxylate groups from in-situ carbon doping. The photocatalytic hydrogen production rate of the hierarchical HC-TiO2 exhibited 9.7 times that of the commercial P25 without co-catalyst under simulated sunlight. This work enriched the synthesis method of C-doped TiO2 and the application of MXene based materials.

KEYWORDS: Photocatalyst; Hydrogen evolution; C-TiO2; MXene; Hierarchical structure

2

ACS Paragon Plus Environment

Page 2 of 28

Page 3 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

INTRODUCTION As one of the most promising photocatalytic materials, titanium dioxide (TiO2) plays an important role in the environment, energy, and catalysis.1-5 A lot of photocatalysts have been developed up to now,6-9 but TiO2 is still the most promising photocatalyst10-11 because of its abundance, environmentally friendly, low cost, good thermal and chemical stabilities.12-13 However, it still suffers from the wide bandgap (3.2 eV) and the fast photo-generated carrier recombination velocity (1-10 ps) that hampers its large-scale application in photocatalysis field.14-18 Doping is efficient for changing the band position and the bandgap while enhancing the carrier concentration and lifetime. Transition metal cations (Fe, Cr, Ni, Cu, etc.) and anions (C, N, S, etc.) have been used as dopants,19-26 among which carbon doping provided critically narrow bandgap and high absorption coefficient.27-30 Carboxyl group provided by carbon-doping not only possessed a strong covalent binding ability to TiO2 but also acted as the anchoring group for photocatalysts.19, 31-33 Carbon-doping also broadened the utilization of light and sensitized TiO2 by influencing the electronic environments for Ti cations and O anions.34 Recent studies showed that C-TiO2 could further enhance carrier concentration and the lifetime.32, 35 Many synthetic methods for C-TiO2 materials have been reported, such as sol-gel process,36 heat oxidation of TiC,37 solvothermal synthesis,30 and electrospinning.38-39 These methods usually demand an annealing process at high temperature to remove organics and increase the crystallinity, during which the anatase TiO2 will gradually change to rutile TiO2. Developing a new strategy for preparing HC-TiO2 at a low temperature will be interesting for photocatalytic materials. Here, we chose an ultrathin structure Ti3C2Tx (Tx standing for the surface terminations) as a precursor for the synthesis of HC-TiO2.40-42 A large number of oxygen-containing functional groups (-O and -OH) facilitated the formation of TiO2 and carbon-doping in the strong alkaline environment.43 The stripped Ti3C2Tx dispersed in the organic alkali (tetramethylammonium hydroxide: TMAOH) was raw materials for hydrothermal treatment. The high carbon content changed the electronic structure and adjusted the bandgap of TiO2 for broadening the light absorption range of TiO2. It also increased the lifespan of the 3

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

photo-generated carriers and further inhibited carriers recombination rate. The HC-TiO2 showed a high-efficiency catalytic performance on photocatalytic hydrogen production. This work provided a promising way for preparing high carbon doping TiO2 and broadening the application of MXene. EXPERIMENTAL SECTION Preparation of Ti3C2Tx nanosheets Ti3C2Tx nanosheets precursors were prepared according to the literature.43 2 g Ti3AlC2 crystals were immersed in diluted 20 mL 10% HF for 30 minutes to remove surface oxidant. The above solution is centrifuged three times with deionized water, then attained crystals were dispersed in 20 mL 25% TMAOH aqueous for 24 h. The TMA-intercalated crystals were diluted into 300 mL using water. To achieve complete delamination, the solution was shaken by hand for 10 min repeatedly. And the supernatant was centrifuged at 3500 rpm. Synthesis of HC-TiO2 The attained supernate was encapsulated in the Teflon-lined autoclave and maintained at 160 C for 9 h. The obtained powders were centrifuged and ultrasonic and washed with water and ethanol three times, and then dried at 80 C under vacuum. Photocatalyst tests The experiments were conducted in a quartz container from top-irradiation containing 0.02 g of photocatalyst powder. The photocatalyst was dispersed in 50 mL (10 vol% TEOA, as a holes capture agent) aqueous solution. A 300 W Xe lamp as a full spectrum solar simulator was placed above quartz container. In a typical reaction, the reactor temperature was controlled using a circulating condensate system. The reactor was bubbled for 30 min to completely remove the dissolved oxygen using high purity Ar gas before illumination. The hydrogen produced was detected with GC2014C gas chromatography system equipped with a thermal conductivity detector.

4

ACS Paragon Plus Environment

Page 4 of 28

Page 5 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Photoelectrochemical (PEC) measurements The PEC performance of HC-TiO2 and P25 was measured. The 4 mg/mL samples slurry with 0.5 vol% Nafion was treated with ultrasound for 30 min and dropped onto a fluorine-doped tin dioxide (FTO). The areas of the photoanodes are kept in 1 cm2. After the sample drying, a standard three-electrode system using a Pt foil as the counter electrode, and saturated calomel electrode (SCE) as a reference electrode with 0.5 M Na2SO4 electrolyte was conducted. A 300 W Xe lamp was used. Electrochemical impedance spectra (EIS) were measured over a frequency range of 105 ~ 10-2 Hz with 10 mV amplitude under simulated sunlight. The potential was converted using the Nernst equation: ERHE = ESCE + 0.242 + 0.059 pH. RESULT AND DISCUSSION The Ti3C2Tx nanosheets were first synthesized by etching of the oxidation surface with HF acid and further etching of the Al layers in bulk Ti3AlC2 with TMAOH. The hierarchical structure of carbon doping TiO2 was attained by heating Ti3C2Tx nanosheets supernatant in an autoclave at a suitable temperature. The field emission scanning electron microscopy (FESEM) images showed the morphology of the obtained HC-TiO2. Figure 1a showed the typical SEM images of HC-TiO2 derived from two dimension Ti3C2Tx (Figure S1). The HC-TiO2 samples exhibited multangular flower-like morphology composed of some nanorods tightly aggregated together with diameter dimension of 35 ± 10 nm (Figure S2), which was well less than the diffusion length of photogenerated carriers of TiO2. This small nanorods feature was beneficial to carrier diffusion during the photocatalytic reaction.44 The hierarchical structure was dependent on the reaction temperature (Figure S3). The transmission electron microscope (TEM) image also showed multangular morphology composed of tightly aggregated nanorods in Figure 1b. The HAADF-STEM image and element mappings of the HC-TiO2 sample revealed that the Ti, O, and C distribute uniformly within the HC-TiO2 nanostructure in Figure 1c. The elemental analysis of the HC-TiO2 samples showed a higher carbon weight around 17.78 wt%, 20.93 wt% and 15.01 wt% at 140 C, 160 C, and 180 C, than most of the previously reported works (Table S1). The HRTEM 5

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

image analysis displayed the interplanar spacing of 0.347 nm corresponding to the (101) plane of anatase TiO2 in Figure 1d. The selected area electron diffraction (SAED, inset) revealed the polycrystalline nature and dominant (101), (112), (211), and (200) diffraction planes.

Figure 1. (a) SEM, (b) TEM, (c) HAADF-STEM with Ti, O, C element distribution and (d) HRTEM (inset: SAED pattern) of as-prepared HC-TiO2.

The phase structure and composition of HC-TiO2 was shown in Figure 2a via using X-ray diffraction (XRD) patterns. The results revealed that the as-synthesized HC-TiO2 was mainly composed of anatase matching well with that of polycrystalline tetragonal TiO2 (PDF# 21-1272). There is no observable peak of Ti3C2Tx MXene.43 The facets of HC-TiO2 showed quite sharp strong intensities indicating good crystallinity. Diffraction peaks of HC-TiO2 were not shifted, confirming that carbon atoms did not simply exist as interstitial atoms. And the X-ray photoelectron spectroscopy (XPS) measurements of the C 1s spectra of HC-TiO2 were studied and fitted to three peaks at 284.6, 285.4, and 288.0 eV, which indicated that the carbon element in the HC-TiO2 had different chemical environments in Figure 2b. The peak at 284.6 eV was attributed to adventitious carbon.45 The two peaks at 285.4 and 288.0 eV were characteristic, corresponding to the existence of carbonate-like groups containing carbon and oxygen (C-OOR(H), C-OR(H), or C=O).12 There was no Ti-C bond centered at 281.5 eV in the XPS spectra (Figure S4a),46 indicating the absence of Ti3C2Tx and the lattice oxygen not replaced by the carbon element. The peak at 290.7 eV was not detected, suggesting no 6

ACS Paragon Plus Environment

Page 6 of 28

Page 7 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

graphite-like carbon in the surface of HC-TiO2,47 which indicates that the C element in Ti3C2Tx had not formed graphite carbon. Similarly, XPS of Ti 2p and O1s were conducted to obtain the chemical states and binding energy of elemental composition of HC-TiO2 in Figure 2c and 2d. The high-resolution XPS (HRXPS) spectra of Ti 2p core levels in Figure 2c showed the binding energy of Ti 2p of HC-TiO2 assigned to Ti4+ ions,48 which was different from Ti 2p of Ti3C2Tx (Figure S4b). Compared with P25 (Figure S5), the Ti 2p core levels peak positions for the HC-TiO2 shifted to lower binding energies due to the charge redistribution between O and Ti atoms, respectively, which were resulted from non-stoichiometric TiO2. The change inferred a decrease of electron density in the Ti nucleus by the carbon doping.19 The high-resolution O 1s spectrum clearly evidenced the presence of two major peaks centered at around 529.6 eV and 531.4 eV in Figure 2d. The lower binding energy was assigned to the lattice oxygen of the TiO2 crystal lattice, while the higher was associated with the possible surface H-O bonds and/or C-O and C=O bonds of carbonate species.

Figure 2. (a) XRD patterns of the HC-TiO2 and Ti2C3, (b-d) Ti 2p, O 1s, and C 1s core levels from the XPS spectra of the HC-TiO2 respectively.

The UV-vis spectra were performed, followed by a tauc plot to estimate the bandgap as shown in Figure 3a. The observed bandgaps were 3.10 and 3.26 eV for HC-TiO2 and commercial P25, respectively. Compared with the commercial P25 (380 nm), the as-synthesized HC-TiO2 spectrum significantly had a certain redshift to 400 nm due to the 7

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 28

doping of carbon.35 We also characterized the valence band (VB) for HC-TiO2 and P25 by VB-XPS in Figure 3b. The binding energy of HC-TiO2 was smaller than that of P25 likely because of doping carbon.36 The VB tail states occurred in HC-TiO2, but not in the P25. This band tail was assigned to the carboxylate groups with strong electron withdrawing ability, which induced additional transient electron states above the VB edge, further resulting in narrowed bandgap.12

Figure 3. (a) UV-vis spectra, (b) VB of the samples from XPS, (c) Mott-Schottky curves, and (d) FTIR spectra of as-prepared HC-TiO2 and P25.

To attain the Mott-Schottky (MS) plots, the impedance potential measurement was conducted in Figure 3c. The HC-TiO2 showed a positive slope similar to P25 manifesting an n-type semiconductor. The flat band (FB) potential approximates the conduction band (CB) edge from MS plot, which was generally accepted. The FB potential of HC-TiO2 shifted more negative than commercial P25. The negative FB potential revealed that photogenerated electrons in CB had strong reducibility.49 In other words, HC-TiO2 participated easily in water splitting reaction at the same condition. What’s more, the carrier concentration can also be expressed through the Mott-Schottky equation,50 that is: 1 / C2 = (2 / eεε0Nd) × [V − VFB − kBT / e]

(1)

From the Mott-Schottky plot, the carrier concentration Nd is a correlation with an inverse slope of the range of linearity. Where the electron charge e, relative dielectric constant ε, dielectric constant of vacuum (ε0), temperature (T), the flat-band potential (VFB) and 8

ACS Paragon Plus Environment

Page 9 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Boltzmann constant (kB) were given and obtained. And the carrier concentration of HC-TiO2 is relatively higher than P25. FTIR spectroscopy of HC-TiO2 was further carried out to verify C-doping in TiO2 in the reaction process. As shown in Figure 3d, several new peaks appeared in the spectrum compared with that of P25. The peak at 1460 cm-1 could be assigned to COO symmetric stretching vibration,12, 51 and a shoulder peak at 1380 cm-1 could ascribe to C-H bending modes of the methyl groups derived from TMAOH. The peak at 1630 cm-1 was derived from the stretching vibrations of OH groups and absorbed water on the HC-TiO2 and P25 surface.52-53 The broad peak at 500 cm-1 was attributed to the bonds of Ti-O and Ti-O-Ti.54-55 The results of the FTIR spectrum confirmed that the carbon was doped in TiO2. The transfer behavior of photo-induced carriers of HC-TiO2 was investigated by the photoluminescence (PL) measurements. Compared with P25, the PL intensity was decreased drastically with C doping in TiO2 in Figure 4a, revealing that the recombination rate of photo-induced carriers was decreased significantly, which was hypothetically due to the enhanced charge transfer by the doping of the carbon in TiO2. Significantly, the emission peaks of HC-TiO2 were red-shifted from 367 nm to 384 nm, which was in agreement with the absorption edge 3.10 and 3.26eV for HC-TiO2 and P25, reflecting the band-to-band electron-hole recombination.56-58 To further understand the exciton separation behavior, the time-resolved transient PL (TRPL) spectra of HC-TiO2 and P25 were measured (Figure 4b). The HC-TiO2 exhibited biexponential decay profile.59-60 The average lifetime τave could be attained by integrating slow decay time τ1 and fast decay time τ2 and were summarized in Table S2. The τave for HC-TiO2 and P25 were 5.83 and 4.90 ns, respectively. The difference lifetime in HC-TiO2 and P25 indicated the photoexcited electron-hole of HC-TiO2 had a slower recombination rate than P25. The faster transfer rate of photogenerated electrons in the HC-TiO2 allowed to transport them to the surface and photoreduction process subsequently occurred.61-62

9

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4. (a) PL spectra, (b) TRPL spectra, (c) Electrochemical impedance spectra, (d) Transient photocurrent responses in 0.5 M Na2SO4 aqueous solutions under simulated sunlight irradiation of as-prepared HC-TiO2 and P25.

To study charge transfer ability, electrochemical impedance analysis was operated. The EIS Nyquist plots were shown in Figure 4c, and the inset showed simulated equivalent circuit. The Rt was charge-transfer resistance which can be represented as the diameters of the semicircle. The diameter of HC-TiO2 was much smaller than that of P25, indicating that the HC-TiO2 had superior charge transfer capacity. And the Rs stood for electrolyte solution resistance. Figure 4d showed the on/off photocurrent under simulated sunlight irradiation. It was clear that the HC-TiO2 had remarkably enhanced photocurrents under illumination. The change of the photocurrents was observed during on-off cycles of the irradiation owing to the transient effect of the photon-generated carrier, and a slight drop was found for HC-TiO2 in the 400s, while it was always higher than that of P25. The reason was that the recombination of photogenerated electron-hole carriers was inhibited due to the increase of lifespan of the carriers for HC-TiO2. And the current density increased gradually to 3.20 μA cm-2 when illumination was on for 100s, which was eight times as much as P25. It shows the amounts of photo-induced electrons for HC-TiO2 was more than that of P25. The photocatalytic H2 evolution was investigated under simulated sunlight with 10% TEOA without co-catalysts. As shown in Figure 5, it was found that the steady hydrogen evolution at a 33.04 μmol·h-1·g-1 rate of HC-TiO2 was higher than that of other sample prepared at different temperatures (Figure S6) and 9.7 times of that of commercial P25 10

ACS Paragon Plus Environment

Page 10 of 28

Page 11 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(Table S3). The different H2 evolution performances of these samples were mainly attributed to the variations of the C concentration that affected the electron-holes recombination and the band structure based on their different properties of MS plots (Figure S7) and transient photocurrent (Figure S8). The XRD remained consistent before and after the photocatalyst reaction that showed a good stability of the sample (Figure S9). The N2 adsorption-desorption isotherm was shown in Figure S10, and the BET specific surface area of the sample was attained. The BET specific surface area of HC-TiO2 (1.50 m2/g) was much smaller than that of P25 (46.94 m2/g). The improvement of the photocatalytic property of the HC-TiO2 was not from the specific surface area of TiO2. For the improved photocatalytic property of HC-TiO2, there were two main reasons. First, the C-doping was able to enhance the light absorption range by VB shifting up. Second, the C-doping extended the lifespan of the photo-generated carriers that inhibits carrier recombination rate by trail sensitization.

Figure 5. Typical time course of H2 evolution rates of HC-TiO2 and P25 from water with 10% TEOA under simulated sunlight without co-catalysts over various samples.

Based on the results above, we could briefly summarize that the major processes of the higher hydrogen evolution rate of HC-TiO2 were as follows. Firstly, the size of the nanorods of HC-TiO2 with hierarchical structure was less than the diffusion length of photogenerated carriers of TiO2, which is beneficial to carrier diffusion during the photocatalytic reaction. Secondly, the tail state induced by carbon-doped TiO2 widened the absorption range of light. When the sample was irradiated by light, the photons induced the generation of electron-hole pairs in Figure 6. The electrons in the VB transited to the CB after photons exciting. Due to 11

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

the carbon doping, the new impurity was generated between the CB and the VB, which could further narrow the band gap. Finally, the impurity which tended to induce acceptor level above the VB maximum of TiO2 could be used as an efficient hole transfer medium,63-64 which further achieved the effective separation of electron-holes. Due to enough energy, electrons that were excited to CB could easily reduce protons to produce hydrogen.

Figure 6. Photocatalytic mechanism of HC-TiO2 materials.

CONCLUSIONS In summary, the HC-TiO2 with hierarchical structure was prepared by in situ growth strategy using MXene as the precursor. The HC-TiO2 with high carbon content changed the electronic structure of TiO2 and adjusted the band structure of TiO2, which further inhibited photogenerated carriers recombination rate and broadened the range of TiO2 on the absorption of light. HC-TiO2 exhibited excellent light-driven catalytic activity in photocatalytic water splitting, being better than the commercially available P25. This work paved a new way to fabricate functional materials from two dimensions MXene for extensive photocatalysis and electrocatalysis application. ASSOCIATED CONTENT

12

ACS Paragon Plus Environment

Page 12 of 28

Page 13 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Supporting Information Chemicals and materials, characterization methods, TEM of Ti3C2Tx, SEM after the stripping, size distribution of HC-TiO2 nanorods, SEM of HC-TiO2 at different temperature, XPS spectra of the Ti3C2Tx and the P25, H2 production of HC-TiO2 of different temperature, Mott-Schottky curves and transient photocurrent responses of samples, XRD patterns before and after the photocatalysis, N2 adsorption-desorption isotherm, summary the carbon species in C-doped TiO2, the values estimated PL lifetime τi and corresponding constant Ai and enhancement ratio of H2 production of HC-TiO2 at 140 C, 160 C, 180 C relative to P25 under simulated solar without co-catalyst. ACKNOWLEDGMENTS We greatly acknowledge Natural Science Foundation of China (51702116, 51602305, and 51571100), National Key Research and Development Program of China (2016YFFA0200401), the Fundamental Research Funds for the Central Universities, and Program for JLU Science and Technology Innovative Research Team (JLUSTIRT, 2017TD-09). REFERENCES (1). Zhou, W.; Li, W.; Wang, J. Q.; Qu, Y.; Yang, Y.; Xie, Y.; Zhang, K.; Wang, L.; Fu, H.; Zhao, D., Ordered mesoporous black TiO2 as highly efficient hydrogen evolution photocatalyst, J. Am. Chem. Soc. 2014, 136 (26), 9280-9283. DOI 1021/ja504802q. (2). Tian, J.; Zhao, Z.; Kumar, A.; Boughton, R. I.; Liu, H., Recent progress in design, synthesis,

and

applications

of

one-dimensional

TiO2

nanostructured

surface

heterostructures: a review, Chem. Soc. Rev. 2014, 43 (20), 6920-6937. DOI 10.1039/C4CS00180J. (3). Zhao, Z; Tian, J.; Sang, Y. ; Cabot, A.; Liu, H.; Structure, synthesis, and applications of TiO2 nanobelts, Adv. Mater. 2015, 27 (16), 2557-2582. DOI 10.1002/adma.201405589. (4). Yu, Y.; Zhang, Z.; Yin, X.; Kvit, A.; Liao, Q.; Kang, Z.; Yan, X.; Zhang, Y.; Wang, X., Enhanced photoelectrochemical efficiency and stability using a conformal TiO2 film on a black silicon photoanode, Nat. Energy 2017, 2, 17045. DOI 10.1038/nenergy.2017.45. (5). Hussain, H.; Tocci, G.; Woolcot, T.; Torrelles, X.; Pang, C. L.; Humphrey, D. S.; Yim, C. 13

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 28

M.; Grinter, D. C.; Cabailh, G.; Bikondoa, O.; Lindsay, R.; Zegenhagen, J.; Michaelides, A.; Thornton, G., Structure of a model TiO2 photocatalytic interface, Nat. Mater. 2016, 16, 461-466. DOI 10.1038/nmat4793. (6). Zhao, H.; Ding, X.; Zhang, B.; Li, Y.; Wang, C., Enhanced photocatalytic hydrogen evolution along with byproducts suppressing over Z-scheme CdxZn1−xS/Au/g-C3N4 photocatalysts under visible light, Science Bulletin 2017, 62 (9), 602-609. DOI 10.1016/j.scib.2017.03.005. (7). Zhao, Y.; Zhao, B.; Liu, J.; Chen, G.; Gao, R.; Yao, S.; Li, M.; Zhang, Q.; Gu, L.; Xie, J.; Wen, X.; Wu, L. Z.; Tung, C. H.; Ma, D.; Zhang, T., Oxide-modified nickel photocatalysts for the production of hydrocarbons in visible light, Angew. Chem. 2016, 128 (13), 4287-4291. DOI 10.1002/ange.201511334. (8).Shi, R.; Cao, Y.; Bao, Y.; Zhao, Y.; Waterhouse, G. I. N.; Fang, Z.; Wu, L. Z.; Tung, C. H.; Yin, Y.; Zhang, T., Self-assembled Au/CdSe nanocrystal clusters for plasmon-mediated photocatalytic hydrogen evolution, Adv. Mater. 2017, 29 (27), 1700803. DOI 10.1002/adma.201700803. (9). Yu, H.; Shi, R.; Zhao, Y.; Bian, T.; Zhao, Y.; Zhou, C.; Waterhouse, G. I. N.; Wu, L. Z.; Tung, C. H.; Zhang, T., Alkali-assisted synthesis of nitrogen deficient graphitic carbon nitride with tunable band structures for efficient visible-light-driven hydrogen evolution, Adv. Mater. 2017, 29 (16), 1605148. DOI 10.1002/adma.201605148. (10). Wang, X.; Li, Z.; Shi, J.; Yu, Y., One-dimensional titanium dioxide nanomaterials: nanowires, nanorods, and nanobelts, Chem. Rev. 2014, 114 (19), 9346-9384. DOI 10.1021/cr400633s. (11). Nosaka, Y.; Nosaka, A. Y., Generation and detection of reactive oxygen species in photocatalysis,

Chem.

Rev.

2017,

117

(17),

11302-11336.

DOI

10.1021/acs.chemrev.7b00161. (12). Liu, J.; Han, L.; An, N.; Xing, L.; Ma, H.; Cheng, L.; Yang, J.; Zhang, Q., Enhanced visible-light photocatalytic activity of carbonate-doped anatase TiO2 based on the electron-withdrawing bidentate carboxylate linkage, Appl. Catal. B Environ. 2017, 202, 642-652. DOI 10.1016/j.apcatb.2016.09.057. (13). Chen, J.; Qiu, F.; Xu, W.; Cao, S.; Zhu, H., Recent progress in enhancing photocatalytic 14

ACS Paragon Plus Environment

Page 15 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

efficiency of TiO2-based materials, Appl. Catal. A Gen. 2015, 495, 131-140. DOI 10.1016/j.apcata.2015.02.013. (14). Schneider, J.; Matsuoka, M.; Takeuchi, M.; Zhang, J.; Horiuchi, Y.; Anpo, M.; Bahnemann, D. W., Understanding TiO2 photocatalysis: mechanisms and materials, Chem. Rev. 2014, 114 (19), 9919-9986. DOI 10.1021/cr5001892. (15). Ni, M.; Leung, M. K. H.; Leung, D. Y. C.; Sumathy, K., A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production, Renew. Sustain. Energy Rev. 2007, 11 (3), 401-425. DOI 10.1016/j.rser.2005.01.009. (16). Henderson, M. A., A surface science perspective on TiO2 photocatalysis, Surf. Sci. Rep. 2011, 66 (6), 185-297. DOI 10.1016/j.surfrep.2011.01.001. (17). Chen, X.; Liu, L.; Yu, P. Y.; Mao, S. S., Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals, Science 2011, 331 (6018), 746-750. DOI 10.1126/science.1200448. (18). Tao, J.; Luttrell, T.; Batzill, M., A two-dimensional phase of TiO2 with a reduced bandgap, Nat. Chem. 2011, 3, 296-300. DOI 10.1038/nchem.1006. (19). Wang, P.; Zhou, Q.; Xia, Y.; Zhan, S.; Li, Y., Understanding the charge separation and transfer

in

mesoporous

carbonate-doped

phase-junction

TiO2

nanotubes

for

photocatalytic hydrogen production, Appl. Catal. B Environ. 2018, 225, 433-444. DOI 10.1016/j.apcatb.2017.11.069. (20). Irie, H.; Watanabe, Y.; Hashimoto, K., Nitrogen-concentration dependence on photocatalytic activity of TiO2-xNx powders, J. Phys. Chem. B 2003, 107 (23), 5483-5486. DOI 10.1021/jp030133h. (21). Yu, J. C.; Yu, J.; Ho, W.; Jiang, Z.; Zhang, L., Effects of F-doping on the photocatalytic activity and microstructures of nanocrystalline TiO2 powders, Chem. Mater. 2002, 14 (9), 3808-3816. DOI 10.1021/cm020027c. (22). Ohno, T.; Akiyoshi, M.; Umebayashi, T.; Asai, K.; Mitsui, T.; Matsumura, M., Preparation of S-doped TiO2 photocatalysts and their photocatalytic activities under visible

light,

Appl.

Catal.

A

Gen.

2004,

265

(1),

115-121.

DOI

10.1016/j.apcata.2004.01.007. (23). Pathak, S. K.; Abate, A.; Ruckdeschel, P.; Roose, B.; Gödel, K. C.; Vaynzof, Y.; Santhala, 15

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 28

A.; Watanabe, S. I.; Hollman, D. J.; Noel, N.; Sepe, A.; Wiesner, U.; Friend, R.; Snaith, H. J.; Steiner, U., Performance and stability enhancement of dye-sensitized and perovskite solar cells by Al doping of TiO2, Adv. Funct. Mater. 2014, 24 (38), 6046-6055. DOI 10.1002/adfm.201401658. (24). Inturi, S. N. R.; Boningari, T.; Suidan, M.; Smirniotis, P. G., Visible-light-induced photodegradation of gas phase acetonitrile using aerosol-made transition metal (V, Cr, Fe, Co, Mn, Mo, Ni, Cu, Y, Ce, and Zr) doped TiO2, Appl. Catal. B Environ. 2014, 144, 333-342. DOI 10.1016/j.apcatb.2013.07.032. (25). Ansari, S. A.; Khan, M. M.; Ansari, M. O.; Cho, M. H., Nitrogen-doped titanium dioxide (N-doped TiO2) for visible light photocatalysis, New J. Chem. 2016, 40 (4), 3000-3009. DOI 10.1039/C5NJ03478G. (26). Asahi, R.; Morikawa, T.; Ohwaki, T.; Aoki, K.; Taga, Y., Visible-light photocatalysis in nitrogen-doped

titanium

oxides,

Science

2001,

293

(5528),

269-271.

DOI

10.1126/science.1061051. (27). Dolat, D.; Quici, N.; Kusiak-Nejman, E.; Morawski, A. W.; Li Puma, G., One-step, hydrothermal synthesis of nitrogen, carbon co-doped titanium dioxide (N,C-TiO2) photocatalysts. Effect of alcohol degree and chain length as carbon dopant precursors on photocatalytic activity and catalyst deactivation, Appl. Catal. B Environ. 2012, 115-116, 81-89. DOI 10.1016/j.apcatb.2011.12.007. (28). Chen, X.; Burda, C., The electronic origin of the visible-light absorption properties of C-, N- and S-Doped TiO2 nanomaterials, J. Am. Chem. Soc. 2008, 130 (15), 5018-5019. DOI 10.1021/ja711023z. (29). Lu, Z.; Zeng, L.; Song, W.; Qin, Z.; Zeng, D.; Xie, C., In situ synthesis of C-TiO2/g-C3N4 heterojunction nanocomposite as highly visible light active photocatalyst originated from effective interfacial charge transfer, Appl. Catal. B Environ. 2017, 202, 489-499. DOI 10.1016/j.apcatb.2016.09.052. (30. Liu, B.; Liu, L. M.; Lang, X. F.; Wang, H. Y.; Lou, X.; Aydil, E. S., Doping high-surface-area mesoporous TiO2 microspheres with carbonate for visible light hydrogen production,

Energy

Environ.

Sci.

2014,

10.1039/C4EE00472H. 16

ACS Paragon Plus Environment

7

(8),

2592-2597.

DOI

Page 17 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(31). Zhang, L.; Cole, J. M., Anchoring groups for dye-sensitized solar cells, ACS Appl. Mater. Interfaces 2015, 7 (6), 3427-3455. DOI 10.1021/am507334m. (32). Ganesh, R. S.; Navaneethan, M.; Ponnusamy, S.; Muthamizhchelvan, C.; Kawasaki, S.; Shimura, Y.; Hayakawa, Y., Enhanced photon collection of high surface area carbonate-doped mesoporous TiO2 nanospheres in dye sensitized solar cells, Mater. Res. Bull. 2018, 101, 353-362. DOI 10.1016/j.materresbull.2018.01.018. (33). Khalid, N. R.; Majid, A.; Tahir, M. B.; Niaz, N. A.; Khalid, S., Carbonaceous-TiO2 nanomaterials for photocatalytic degradation of pollutants: A review, Ceram. Int. 2017, 43 (17), 14552-14571. DOI 10.1016/j.ceramint.2017.08.143. (34). Sun, Y. Y.; Zhang, S., Kinetics stabilized doping: computational optimization of carbon-doped anatase TiO2 for visible-light driven water splitting, Phys. Chem. Chem. Phys. 2016, 18 (4), 2776-2783. DOI 10.1039/C5CP07109G. (35). Niu, P.; Wu, T.; Wen, L.; Tan, J.; Yang, Y.; Zheng, S.; Liang, Y.; Li, F.; Irvine, J. T. S.; Liu, G.; Ma, X.; Cheng, H. M.; Substitutional carbon-modified anatase TiO2 decahedral plates directly derived from titanium oxalate crystals via topotactic transition, Adv. Mater. 2018, 30 (20), 1705999. DOI 10.1002/adma.201705999. (36). Wang, S.; Zhao, L.; Bai, L.; Yan, J.; Jiang, Q.; Lian, J., Enhancing photocatalytic activity of disorder-engineered C/TiO2 and TiO2 nanoparticles, J. Mater. Chem. A 2014, 2 (20), 7439-7445. DOI 10.1039/C4TA00354C. (37). Yang, C.; Zhang, X.; Qin, J.; Shen, X.; Yu, R.; Ma, M.; Liu, R., Porous carbon-doped TiO2 on TiC nanostructures for enhanced photocatalytic hydrogen production under visible light, J. Catal. 2017, 347, 36-44. DOI 10.1016/j.jcat.2016.11.041. (38). Matos, J.; García, A.; Zhao, L.; Titirici, M. M., Solvothermal carbon-doped TiO2 photocatalyst for the enhanced methylene blue degradation under visible light, Appl. Catal. A Gen. 2010, 390 (1), 175-182. DOI 10.1016/j.apcata.2010.10.009. (39). Zhang, G.; Sun, M.; Liu, Y.; Lang, X.; Liu, L.; Liu, H.; Qu, J.; Li, J., Visible-light induced photocatalytic activity of electrospun-TiO2 in arsenic(III) oxidation, ACS Appl. Mater. Interfaces 2015, 7 (1), 511-518. DOI 10.1021/am506640k. (40). Ran, J.; Gao, G.; Li, F. T.; Ma, T. Y.; Du, A.; Qiao, S. Z., Ti3C2 MXene co-catalyst on metal sulfide photo-absorbers for enhanced visible-light photocatalytic hydrogen 17

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 28

production, Nat. Commun. 2017, 8, 13907. DOI 10.1038/ncomms13907. (41). Naguib, M.; Kurtoglu, M.; Presser, V.; Lu, J.; Niu, J.; Heon, M.; Hultman, L.; Gogotsi, Y. ; Barsoum, M. W., Two-dimensional nanocrystals produced by exfoliation of Ti3AlC2, Adv. Mater. 2011, 23 (37), 4248-4253. DOI 10.1002/adma.201102306. (42). Yu, M.; Zhou, S.; Wang, Z.; Zhao, J.; Qiu, J., Boosting electrocatalytic oxygen evolution by synergistically coupling layered double hydroxide with MXene, Nano Energy 2018, 44, 181-190. DOI 10.1016/j.nanoen.2017.12.003. (43). Xuan, J.; Wang, Z.; Chen, Y.; Liang, D.; Cheng, L.; Yang, X.; Liu, Z.; Ma, R.; Sasaki, T.; Geng, F., Organic-base-driven intercalation and delamination for the production of functionalized titanium carbide nanosheets with superior photothermal therapeutic performance,

Angew.

Chem.

2016,

128

(47),

14789-14794.

DOI

10.1002/ange.201606643. (44). Leng, W. H.; Barnes, P. R. F.; Juozapavicius, M.; O’Regan, B. C.; Durrant, J. R., Electron diffusion length in mesoporous nanocrystalline TiO2 photoelectrodes during water oxidation, J. Phys. Chem. Lett. 2010, 1 (6), 967-972. DOI 10.1021/jz100051q. (45). Zhang, P.; Shao, C.; Zhang, Z.; Zhang, M.; Mu, J.; Guo, Z.; Sun, Y.; Liu, Y., Core/shell nanofibers of TiO2@carbon embedded by Ag nanoparticles with enhanced visible photocatalytic activity, J. Mater. Chem. 2011, 21 (44), 17746-17753. DOI 10.1039/C1JM12965A. (46). Liu, J.; Zhang, Q.; Yang, J.; Ma, H.; Tade, M. O.; Wang, S.; Liu, J., Facile synthesis of carbon-doped mesoporous anatase TiO2 for the enhanced visible-light driven photocatalysis,

Chem.

Commun.

2014,

50

(90),

13971-13974.

DOI

10.1039/C4CC05544F. (47). Parayil, S. K.; Kibombo, H. S.; Wu, C. M.; Peng, R.; Baltrusaitis, J.; Koodali, R. T., Enhanced photocatalytic water splitting activity of carbon-modified TiO2 composite materials synthesized by a green synthetic approach, Int. J. Hydrogen Energy 2012, 37 (10), 8257-8267. DOI 10.1016/j.ijhydene.2012.02.067. (48). Liu, G.; Yin, L. C.; Wang, J.; Niu, P.; Zhen, C.; Xie, Y.; Cheng, H. M., A red anatase TiO2 photocatalyst for solar energy conversion, Energy Environ. Sci. 2012, 5 (11), 9603-9610. DOI 10.1039/C2EE22930G. 18

ACS Paragon Plus Environment

Page 19 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

(49). Yang, C.; Qin, J.; Xue, Z.; Ma, M.; Zhang, X.; Liu, R., Rational design of carbon-doped TiO2 modified g-C3N4 via in-situ heat treatment for drastically improved photocatalytic hydrogen with excellent

Nano

photostability,

Energy

41,

2017,

1-9.

DOI

10.1016/j.nanoen.2017.09.012. (50). Hsu, Y. K.; Chen, Y. C.; Lin, Y. G., Novel ZnO/Fe2O3 Core-shell nanowires for photoelectrochemical water splitting, ACS Appl. Mater. Interfaces 2015, 7 (25), 14157-14162. DOI 10.1021/acsami.5b03921. (51). Ma, Y.; Han, L.; Ma, H.; Wang, J.; Liu, J.; Cheng, L.; Yang, J.; Zhang, Q., Improving the visible-light

photocatalytic

activity

of

interstitial

carbon-doped

TiO2

with

electron-withdrawing bidentate carboxylate ligands, Catal. Commun. 2017, 95, 1-5. DOI 10.1016/j.catcom.2017.02.025. (52). Nadtochenko, V. A.; Rincon, A. G.; Stanca, S. E.; Kiwi, J., Dynamics of E. coli membrane cell peroxidation during TiO2 photocatalysis studied by ATR-FTIR spectroscopy and AFM microscopy, J. Photochem. Photobiol., A 2005, 169 (2), 131-137. DOI 10.1016/j.jphotochem.2004.06.011. (53). Wei, X.; Shao, C.; Li, X.; Lu, N.; Wang, K.; Zhang, Z.; Liu, Y., Facile in situ synthesis of plasmonic

nanoparticles-decorated

g-C3N4/TiO2

heterojunction

nanofibers

and

comparison study of their photosynergistic effects for efficient photocatalytic H2 evolution, Nanoscale 2016, 8 (21), 11034-11043. DOI 10.1039/C6NR01491G. (54). Tang, J.; Liu, Y.; Hu, Y.; Lv, G.; Yang, C.; Yang, G.; Carbothermal reduction induced Ti3+ Self-doped TiO2/GQD nanohybrids for high-performance visible light photocatalysis, Chem. Eur. J. 2018, 24 (17), 4390-4398. DOI 10.1002/chem.201705637. (55). Li, Y. N.; Chen, Z. Y.; Wang, M. Q.; Zhang, L. Z.; Bao, S. J., Interface engineered construction of porous g-C3N4/TiO2 heterostructure for enhanced photocatalysis of organic

pollutants,

Appl.

Surf.

Sci.

2018,

440,

229-236.

DOI

10.1016/j.apsusc.2018.01.106. (56). Li, B.; Li, J.; Zhao, J., Fine-tuning the fluorescence emission wavelength of gold nanoclusters in the protein-directed synthesis: The effect of silver ions, J. Nanosci. Nanotechnol. 2012, 12 (12), 8879-8885. DOI 10.1166/jnn.2012.6725. (57). Huang, Z. F.; Song, J.; Pan, L.; Wang, Z.; Zhang, X.; Zou, J. J.; Mi, W.; Zhang, X.; 19

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 28

Wang, L., Carbon nitride with simultaneous porous network and O-doping for efficient solar-energy-driven hydrogen evolution, Nano Energy 2015, 12, 646-656. DOI 10.1016/j.nanoen.2015.01.043. (58). Xi, G.; Ouyang, S.; Li, P.; Ye, J.; Ma, Q.; Su, N.; Bai, H.; Wang, C.; Ultrathin W18O49 nanowires with diameters below 1 nm:

Synthesis,

near-infrared absorption,

photoluminescence, and photochemical reduction of carbon dioxide, Angew. Chem. Int. Ed. 2012, 51 (10), 2395-2399. DOI 10.1002/anie.201107681. (59). Liu, Q.; Ai, L.; Jiang, J., MXene-derived TiO2@C/g-C3N4 heterojunctions for highly efficient nitrogen photofixation, J. Mater. Chem. A 2018, 6 (9), 4102-4110. DOI 10.1039/C7TA09350K. (60). Ye, M. Y.; Zhao, Z. H.; Hu, Z. F.; Liu, L. Q.; Ji, H. M.; Shen, Z. R.; Ma, T. Y.; 0D/2D heterojunctions of vanadate quantum dots/graphitic carbon nitride nanosheets for enhanced visible-light-driven photocatalysis, Angew. Chem. Int. Ed. 2017, 56 (29), 8407-8411. DOI 10.1002/anie.201611127. (61). Pan, L.; Muhammad, T.; Ma, L.; Huang, Z. F.; Wang, S.; Wang, L.; Zou, J. J.; Zhang, X., MOF-derived C-doped ZnO prepared via a two-step calcination for efficient photocatalysis,

Appl.

Catal.

B

Environ.

2016,

189,

181-191.

DOI

10.1016/j.apcatb.2016.02.066. (62). Shown, I.; Samireddi, S.; Chang, Y. C.; Putikam, R.; Chang, P. H.; Sabbah, A.; Fu, F. Y.; Chen, W. F.; Wu, C. I.; Yu, T. Y.; Chung, P. W.; Lin, M. C.; Chen, L. C.; Chen, K. H., Carbon-doped SnS2 nanostructure as a high-efficiency solar fuel catalyst under visible light, Nat. Commun. 2018, 9 (1), 169. DOI 10.1038/s41467-017-02547-4. (63). Zhang, C.; Zhou, Y.; Bao, J.; Sheng, X.; Fang, J.; Zhao, S.; Zhang, Y.; Chen, W., Hierarchical honeycomb Br-, N-codoped TiO2 with enhanced visible-light photocatalytic H2 production, ACS Appl. Mater. Interfaces 2018, 10 (22), 18796-18804. DOI 10.1021/acsami.8b04947. (64). Xie, J.; Xie, H.; Su, B. L.; Cheng, Y. B.; Du, X.; Zeng, H.; Wang, M.; Wang, W.; Wang, H.; Fu, Z.; Mussel-directed synthesis of nitrogen-doped anatase TiO2, Angew. Chem. Int. Ed. 2016, 55 (9), 3031-3035. DOI 10.1002/anie.201509906. 20

ACS Paragon Plus Environment

Page 21 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figures Captions: Figure 1. (a) SEM, (b) TEM, (c) HAADF-STEM with Ti, O, C element distribution, and (d) HRTEM (inset: SAED pattern) of as-prepared HC-TiO2. Figure 2. (a) XRD patterns of the HC-TiO2 and Ti2C3, (b-d) Ti 2p, O 1s, and C 1s core levels from the XPS spectra of the as-prepared HC-TiO2 respectively. Figure 3. (a) UV-vis spectra, (b) VB of the samples from XPS, (c) Mott-Schottky curves, and (d) FTIR spectra of as-prepared HC-TiO2 and P25. Figure 4. (a) PL spectra, (b) TRPL spectra, (c) Electrochemical impedance spectra, (d) Transient photocurrent responses in 0.5 M Na2SO4 aqueous solutions under simulated sunlight irradiation of as-prepared HC-TiO2 and P25. Figure 5. Typical time course of H2 evolution rates of HC-TiO2 and P25 from water with 10% TEOA under simulated sunlight without co-catalysts over various samples. Figure 6. Photocatalytic mechanism of HC-TiO2 materials.

21

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 1. (a) SEM, (b) TEM, (c) HAADF-STEM with Ti, O, C element distribution, and (d) HRTEM (inset: SAED pattern) of as-prepared HC-TiO2.

22

ACS Paragon Plus Environment

Page 22 of 28

Page 23 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 2. (a) XRD patterns of the HC-TiO2 and Ti2C3, (b-d) Ti 2p, O 1s, and C 1s core levels from the XPS spectra of the as-prepared HC-TiO2 respectively.

23

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 3. (a) UV-vis spectra, (b) VB of the samples from XPS, (c) Mott-Schottky curves, and (d) FTIR spectra of as-prepared HC-TiO2 and P25.

24

ACS Paragon Plus Environment

Page 24 of 28

Page 25 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 4. (a) PL spectra, (b) TRPL spectra, (c) Electrochemical impedance spectra, (d) Transient photocurrent responses in 0.5 M Na2SO4 aqueous solutions under simulated sunlight irradiation of as-prepared HC-TiO2 and P25.

25

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 5. Typical time course of H2 evolution rates of HC-TiO2 and P25 from water with 10% TEOA under simulated sunlight without co-catalysts over various samples.

26

ACS Paragon Plus Environment

Page 26 of 28

Page 27 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 6. Photocatalytic mechanism of HC-TiO2 materials.

27

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Graphical Abstract

The hierarchical HC-TiO2 induced a valence band tail state that promoted photogenerated carriers’ effective separation and reduced bandgap, which exhibited excellent photocatalytic water splitting.