Impact of Surface Charge on Cerium Oxide Nanoparticle Uptake

Shifts in N and δ15N in wheat and barley exposed to cerium oxide nanoparticles. Cyren M. Rico , Mark G. Johnson , Matthew A. Marcus , Christian P. An...
2 downloads 0 Views 942KB Size
Subscriber access provided by Binghamton University | Libraries

Article

Impact of surface charge on cerium oxide nanoparticle uptake and translocation by wheat (Triticum aestivum) Eleanor Spielman-Sun, Enzo Lombi, Erica Donner, Daryl L Howard, Jason M Unrine, and Gregory V. Lowry Environ. Sci. Technol., Just Accepted Manuscript • Publication Date (Web): 02 Jun 2017 Downloaded from http://pubs.acs.org on June 2, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

Environmental Science & Technology

1

Impact of surface charge on cerium oxide nanoparticle uptake and

2

translocation by wheat (Triticum aestivum)

3 4

Eleanor Spielman-Sun§, Enzo Lombi‡, Erica Donner‡, Daryl Howard⊥,

5

Jason M. Unrine˟, Gregory V. Lowry*§

6 7

§

8 9 10

Civil & Environmental Engineering, Carnegie Mellon University, Pittsburgh, Pennsylvania, 15213, United States



Future Industries Institute, University of South Australia, Mawson Lakes, South Australia, 5095, Australia

11

⊥Australian

12

˟ University of Kentucky, Department of Soil and Plant Science, Lexington, Kentucky 40546,

13

Synchrotron, Clayton, Victoria, 3168 Australia

United States

14 15 16

*Corresponding author:

17

Address: Carnegie Mellon University, Pittsburgh, PA 15213

18

Phone: (412) 268-2948

19

Fax: (412) 268-7813

20

Email: [email protected]

21

ACS Paragon Plus Environment

Page 1

Environmental Science & Technology

22

Page 2 of 30

TOC ART

23 24 25

ABSTRACT

26

Nanoparticle (NP) physiochemical properties, including surface charge, affect cellular uptake,

27

translocation, and tissue localization. To evaluate the influence of surface charge on NP uptake

28

by plants, wheat seedlings were hydroponically exposed to 20 mg/L of ~4nm CeO2 NPs

29

functionalized with positively charged, negatively charged, and neutral dextran coatings. Fresh,

30

hydrated roots and leaves were analyzed at various time points over 34h using fluorescence X-

31

ray absorption near-edge spectroscopy to provide laterally resolved spatial distribution and

32

speciation of Ce. A 15-20% reduction from Ce(IV) to Ce(III) was observed in both roots and

33

leaves, independent of NP surface charge. Due to its higher affinity with negatively charged cell

34

walls, CeO2(+) NPs adhered to the plant roots the strongest. After 34h, CeO2(-) and CeO2(0) NP

35

exposed plants had higher Ce leaf concentrations than the plants exposed to CeO2(+) NPs. While

36

Ce was found mostly in the leaf veins of the CeO2(-) NP exposed plant, Ce was found in clusters

37

in the non-vascular leaf tissue of the CeO2(0) NP exposed plant. These results provide important

38

information for understanding mechanisms responsible for plant uptake, transformation, and

39

translocation of NPs, and suggest that NP coatings can be designed to target NPs to specific parts

40

of plants.

ACS Paragon Plus Environment

Page 2

Page 3 of 30

41

Environmental Science & Technology

INTRODUCTION

42

Nanotechnology has the potential to play a critical role in global food production.1–5 The

43

unique properties of nanoparticles (NPs) can be harnessed for developing formulations that

44

contain nanoscale active ingredients designed for direct use on agricultural soils or crops. These

45

products have the capacity to reduce the energy and water inputs for food production by

46

providing a more targeted and efficient delivery system for fertilizers and pesticides. However,

47

properly utilizing the characteristics of these nanoparticles, such as particle size, coating,

48

chemical composition, and shape, requires an understanding of the factors influencing the

49

fundamental interactions between plant tissues and engineered NPs.

50

Several hydroponic studies have investigated the accumulation and translocation of bare

51

cerium dioxide nanoparticles (CeO2 NPs) in plants.6–19 Most of these studies demonstrated a

52

dose-dependent increase of cerium (Ce) in the roots of various plant species and limited

53

translocation of Ce to the shoots. There are a few studies that have specifically documented the

54

speciation and transformation of CeO2 NPs in plant tissue. Hernandez-Viezcas et al. grew

55

soybean in soil amended with 1000 mg/L CeO2 NPs and used Micro X-Ray Fluorescence (μ-

56

XRF) and X-Ray Absorption Near Edge Structure (XANES) spectroscopy to determine that

57

while most of the Ce(IV) remained untransformed in the plant, there was a small percentage of

58

Ce(III) in the pod.20 Zhang et al. used XANES and Scanning Transmission X-ray Microscopy

59

(STXM) analysis and found accumulation in cucumber of both CeO2 NPs and Ce(III) as cerium

60

phosphate in roots and as cerium carboxylates in shoots.14 Similar dissolution and transformation

61

of CeO2 NPs has been observed in hydroponically grown wheat, pumpkins and sunflowers8 as

62

well as in soil cultivated corn.21

ACS Paragon Plus Environment

Page 3

Environmental Science & Technology

Page 4 of 30

63

Surface charge is a key property that can control NP transport in environmental and

64

biological systems. Zhu et al. compared the uptake of functionalized gold nanoparticles (AuNPs)

65

with well-defined surface charges into various terrestrial plants, including radish, ryegrass, rice,

66

and pumpkin, and confirmed that while positively-charged NPs more readily attach to plant

67

roots, negatively-charged NPs are most efficiently translocated into the plant roots.22 The same

68

trend has been observed for AuNPs coated with variously charged organic ligands on rice and

69

tomato23 and for cationic or anionic coated CdSe/ CdSnS quantum dots on poplar trees.24 There

70

are a few studies focused on surface charge dependent CeO2 NP plant uptake, including Zhao et

71

al. who exposed corn to alginate coated CeO2 NPs21 and Barrios et al. who exposed tomato to

72

citric acid coated CeO2 NPs.25 However these studies focus more on the effects of uptake with

73

and without coating, and less on the translocation and spatial distribution of Ce in the plant. Here

74

we studied NP surface charge in a well-controlled hydroponic system to gain a better

75

understanding of the influence of surface charge on NP uptake, transformation, and translocation

76

to leaves, and tissue localization in wheat plants.

77

In situ imaging of metal distribution in hydrated biological systems can provide mechanistic

78

details of plant uptake and translocation, but is challenging because target metal concentrations

79

are low (mg/kg dry plant tissue) and element speciation and distribution can be altered during

80

sample preparation (including drying, embedding, and staining) as well as by the analytical

81

process itself (e.g. X-ray beam damage).26,27 Furthermore, in the case of most biological samples,

82

the highly hydrated nature of the specimens is not compatible with most major analytical

83

techniques operating under vacuum such as TEM and non-environmental SEM. However,

84

advances in synchrotron-based techniques now allow the in situ examination of metals and

85

metalloids in hydrated and fresh plant tissues at low metal concentrations.28–30 In this

ACS Paragon Plus Environment

Page 4

Page 5 of 30

Environmental Science & Technology

86

experiment, we obtained spatially resolved 2D maps of metal speciation in plant samples by

87

XANES mapping, i.e. scanning the same area repeatedly with decreasing energies across an

88

absorption edge, thus collecting a XANES spectra for each pixel of an entire image.31,32 This

89

approach differs from other studies where a μ-XRF map is obtained and μ-XANES spectra are

90

then collected from specific regions of interest within that map, or where XANES is performed

91

on the bulk, freeze-dried tissue.26,28–30,33 XANES mapping has the advantage of providing more

92

detailed information on speciation distribution for the entire sample. This technique has

93

previously been performed on plant tissues by Wang et al. to compare selenate and selenite

94

exposed wheat and rice plants32, Kopittke et al. to compare arsenate and arsenite exposed wheat

95

and rice plants, 34 and De Brier et al. to study iron speciation in mature wheat grains.35

96

The main goals of the present study were to evaluate the influence of surface charge on

97

CeO2 NP uptake, distribution, and speciation in a model plant, specifically wheat (Triticum

98

aestivum), and elucidate details about the reduction of Ce(IV) to Ce(III) in the different plant

99

compartments. CeO2 NPs were chosen as a model NP because they are easy to synthesize in a

100

narrow size distribution, to coat with various charges, and to disperse in aqueous solution;

101

cerium also has a low background level in plants. We used fluorescence-XANES imaging to

102

investigate the in situ laterally resolved speciation of Ce within fresh wheat roots and leaves with

103

the overarching goal of gaining a better understanding of how NPs can be engineered to increase

104

translocation and to target specific parts of plants through functionalization.

105 106

MATERIALS AND METHODS

107

ACS Paragon Plus Environment

Page 5

Environmental Science & Technology

Page 6 of 30

108

CeO2 Nanoparticles. Cerium dioxide NPs with three different charges were synthesized as

109

reported previously in Collin et al.36 Briefly, uncharged dextran coated CeO2 NPs (CeO2 NP (0))

110

with a nominal 4 nm primary particle diameter were produced via alkaline precipitation from a

111

solution of cerium chloride salt and dextran. This coating was then further functionalized, either

112

with diethylaminoethyl groups to create a net positive charge (CeO2 (+)) or with carboxymethyl

113

groups to create a net negative charge (CeO2 (-)). The particles were diluted to 20 mg/L as Ce in

114

the exposure medium (¼ strength Hoagland’s) and probe sonicated (550 Sonic Dismembrator,

115

Fisher Scientific) for 1 min at 10 s intervals to ensure dispersion. The hydrodynamic diameter

116

and electrophoretic mobility of the NPs in the exposure medium (20 mg/L as Ce in ¼ strength

117

Hoagland’s) were measured using a Nano Zetasizer (Malvern Instruments, Malvern). The initial

118

pH and ionic strength of the exposure medium were 5.6 and 5.2 mM, respectively, and these

119

were not further adjusted. The apparent zeta potential was calculated from the electrophoretic

120

mobility using the Hückel approximation. NP dosing concentrations were selected to avoid acute

121

toxicity while ensuring adequate signal for µ-XRF imaging.

122 123

Plant Growth: For µ-XRF, wheat (Triticum aestivum cv. shield) seeds were surface sterilized

124

with 10% w/v bleach (VWR Analytical) for 10 min and then thoroughly rinsed with DI water.

125

The sterilized seeds were germinated on deionized water-moistened filter paper in a Petri dish.

126

After four days, the seedlings were transferred to 100-mL plastic containers. Each container was

127

filled with 80 mL of ¼ strength Hoagland’s medium37 and covered with a plastic lid with five

128

holes. Five seedlings were transplanted to five of the holes with the roots suspended in a

129

continuously aerated solution. Plants were grown at 25 °C under alternating conditions of 12 h of

130

light and 12 h of dark. Nutrient solution was renewed every 3 days. After 7 days, the plants were

ACS Paragon Plus Environment

Page 6

Page 7 of 30

Environmental Science & Technology

131

transferred from the University of South Australia (Adelaide, Australia) to the Australian

132

Synchrotron (Melbourne, Australia) where the plants were hydroponically exposed to 20 mg-

133

Ce/L of CeO2 NPs. Plant tissue was removed at 1 h, 8 h, and 34 h to analyze by µ-XRF.

134

Total Ce determination experiments were conducted at Carnegie Mellon University

135

(Pittsburgh, PA). Plant growth conditions were replicated to match those used for the

136

synchrotron experiment. At the various time points, plants were harvested in triplicate and roots

137

and shoots separated for determination of fresh and dry mass. Briefly, dried plant tissue samples

138

were digested overnight at room temperature in a 2:1 ratio of concentrated HNO3 and 30% H2O2,

139

then heated to 100 °C for 30 minutes (protocol adapted from EPA Method 3050b38). Following

140

digestion, the samples were diluted to 5% HNO3 using deionized water before analysis using

141

inductively coupled plasma mass spectrometry (ICP-MS) (Agilent 7700x, Santa Clara, CA).

142

Further details are provided in the supporting information.

143 144

µ-XRF and Fluorescence XANES Imaging: Following exposure, roots were rinsed in a Ce free

145

hydroponic solution and placed between two pieces of 4 µm-thick Ultralene, which formed a seal

146

around the plant tissue to minimize dehydration. For each exposure solution, two replicate roots

147

were examined, with all roots positioned vertically in the sample holder and scanned

148

simultaneously. The tips and bases of the plant leaves were scanned separately due to the size of

149

the sample mount. Samples were prepared and examined at the XFM beamline at the Australian

150

Synchrotron, where an in-vacuum undulator is used to produce an X-ray beam. A Si(111)

151

monochromator and Kirkpatrick-Baez (KB) mirror microprobe are used to obtain a

152

monochromatic beam focused onto the specimen. The X-ray fluorescence emitted by the

153

specimen was collected using the 384-element Maia detector (Rev C) placed in a backscatter

ACS Paragon Plus Environment

Page 7

Environmental Science & Technology

Page 8 of 30

154

geometry.39,40 For all scans, samples were analyzed continuously “on-the-fly” in the horizontal

155

direction.

156

An initial large area survey scan at 15.8 keV was conducted to identify the area of interest

157

and obtain overall elemental distributions. Step sizes and scanning velocities were adjusted so

158

each scan took around 2 h. Details are provided in the supporting information. Subsequently, a

159

smaller area was chosen to conduct fluorescence XANES imaging with the XANES stack itself

160

consisting of 108 individual maps at decreasing energies across the Ce LIII edge. Details

161

regarding the energy steps are provided in the supporting information.

162

The three nanoparticle types as standards were also analyzed as suspensions using

163

fluorescence-XANES imaging. All standards were prepared to a final Ce concentration of 20

164

mg/L. Further details about the preparation and imaging of these standards are provided in the

165

supporting information. These XANES spectra and that of Ce(III) acetate, which was used as the

166

model compound for Ce(III), are presented in the supporting information (Figure S1). The large

167

peak at 5727 eV is a characteristic peak of the Ce(III) oxidation state; the two peaks at 5730 and

168

5737 eV are characteristic of Ce(IV). These spectral differences are an important criterion for

169

distinguishing Ce compounds of the two different oxidation states.

170

µ-XRF spectra were analyzed using GeoPIXE.31 For the fluorescence-XANES stacks, the

171

GeoPIXE “energy association” module was used to compare the ‘concentration’ ratios between

172

two energies: 5,727 and 5,737 eV, which are the white lines for Ce(III) and Ce(IV) respectively.

173

Because pixels were generally parallel to the 1:1 line, particularly at the highest Ce

174

concentrations, selected pixel populations represented absolute changes in Ce(III) and Ce(IV)

175

concentration. (See Figures S3, S5-6 in supporting information for more details). From the

176

selected pixel populations, XANES spectra were extracted, background subtracted, and

ACS Paragon Plus Environment

Page 8

Page 9 of 30

Environmental Science & Technology

177

normalized using SIXPack (Version 1.4).41 Linear combination fitting (LCF) was performed

178

using the collected CeO2 NP standards above and a Ce(III) acetate spectrum from Auffan et al.42

179

Because the exact oxidation state of CeO2 NPs is difficult to characterize,43 we assume for the

180

purposing of fitting that the starting materials are all Ce(IV) oxidation state.

181 182

RESULTS AND DISCUSSION

183 184

Characterization of CeO2 NPs: NPs have been previously characterized by TEM, FTIR and

185

XRD by Collin et al.36 TEM indicated the CeO2 core of the particles was ~4 nm. Additional

186

characterization of the particles at 20 mg/L as Ce in the nutrient solution was performed as

187

follows. The number weighted average hydrodynamic diameter of the particles in the exposure

188

medium were 12.0 ± 3.4, 19.4 ± 5.7, and 14.5 ± 3.3 nm, for the CeO2(+), CeO2(0), and CeO2(-)

189

particles, respectively. The electrophoretic mobility of the particles in the nutrient solution were

190

1.15 ± 0.30, -0.02 ± 0.21, and -1.59 ± 0.41 µm·cm·V-1·s-1 for the CeO2(+), CeO2(0), and CeO2(-)

191

particles respectively. At pH of 5.6 and an ionic strength of 5.2 mM, this corresponds to an

192

apparent zeta potential of +22.0 ± 6.1 mV, -0.5 ± 3.9 mV, and -30.3 ± 6.6 mV, for the CeO2(+),

193

CeO2(0), and CeO2(-) particles respectively. The particles were stable in the exposure medium;

194

less than 0.1 % dissolution was observed over 34 hours (Table S1); organic acid root exudates

195

induced a small shift in the measured hydrodynamic diameter for all three particle types, but no

196

significant difference in the aggregation behavior for the three particle types was observed

197

(Figure S2).

198

ACS Paragon Plus Environment

Page 9

Environmental Science & Technology

Page 10 of 30

199

Total Ce Association/Uptake in Roots and Shoots: The surface charge of the CeO2 NPs had a

200

substantial impact on the accumulation and translocation of Ce. The Ce concentrations

201

associated with the wheat roots and shoots from the three different treatments are shown in

202

Figure 1. These values include all Ce that was associated with the plant roots (internal and

203

external) after collection and rinsing in NP-free Hoagland’s medium. As exposure time

204

increased, total Ce uptake increased for all NP types in both the roots and shoots. The majority of

205

the plant-associated Ce was sorbed on/in the roots rather than in the shoots, irrespective of the

206

charge of the NPs (note the 1000-fold higher concentrations in the roots compared to the shoots

207

in Figure 1). Du et al.44 and Rico et al.45 observed significantly less uptake of CeO2 NPs in their

208

soil exposures with wheat, which is a common difference between hydroponic and soil

209

exposures.46 Unlike our study, Schwabe et al. observed no translocation of CeO2 NPs in

210

hydroponic wheat,8 though this is likely attributed to NP size differences. Numerous studies have

211

demonstrated that smaller NPs are more likely to be internalized by plants than larger ones.47,48

212

The smallest CeO2 NPs used by Schwabe et al. were 9 nm by TEM, which is more than twice the

213

diameter of the particles used in this study. Thus we attribute the observed differences to a NP

214

size effect.

215

With regards to surface charge,, there was an overall greater mass of the positively charged

216

NPs associated with the roots than the neutral or negatively charged NPs, which is consistent

217

with other studies comparing the impact of surface charge on NP uptake by plants.22–24,49 This

218

difference in association between the differently charged particles is likely due to electrostatic

219

interactions between the charged particles and the root surface. It is well established that plant

220

cell walls, including epidermal cells on the root surface, are negatively charged because of the

221

abundance of polysaccharides containing galacturonic acid residues.50,51 Thus, CeO2(+) NPs

ACS Paragon Plus Environment

Page 10

Page 11 of 30

Environmental Science & Technology

222

accumulated on the root surface due to electrostatic attraction between the positively charged NP

223

and the negatively charged root surface, while CeO2(-) NPs accumulated the least due to

224

electrostatic repulsions. The uncharged particles had an intermediate degree of interaction

225

(possibly limited by steric impediment). While the negatively charged and neutral particles had

226

the lowest accumulation in/on the roots, these NPs were still able to overcome this electrostatic

227

and/or electrosteric repulsion by forming strong hydrogen or covalent bonds with the root

228

surface, through polyvalent cation bridging, or by diffusing into the mucilage.52 This distribution

229

was confirmed with Ce maps on the wheat plant roots (Figure 2). Sufficient Ce was present on

230

the roots exposed to negative and neutral NPs for 1h to allow elemental mapping; the neutral

231

particles showed some regions of concentrated Ce, likely from particle adhesion (Figure 2).

232

Overall, the leaves contained less than 1% of the total plant associated Ce, indicating that very

233

little of the adhered Ce was translocated from the roots to the shoots. While there was no

234

statistically significant difference in Ce accumulation in the leaves for each treatment after 8 h,

235

by 34 h the CeO2(-) and CeO2(0) NP exposed plants had accumulated significantly more Ce in

236

the leaves than the CeO2(+) NP exposed plants. This is particularly noteworthy since both had

237

accumulated significantly less Ce on/in the roots than the CeO2(+) NP exposed plants.

238

ACS Paragon Plus Environment

Page 11

Environmental Science & Technology

239

Page 12 of 30

Figure 1. Total Ce concentrations in dried wheat plant roots (bottom) and leaves (top) after 1 h, 8 h, and 34 h. Note different scales for the roots and leaves. Total Ce uptake in the leaves after 1 h of exposure was not measured. Significant differences (based on ANOVA and Tukey HSD post hoc tests (p