Low-Temperature Pre-Synthesized Crystalline Tin Oxide for Efficient Flexible Perovskite Solar Cells and Modules Tongle Bu, Shengwei Shi, Jing Li, Yifan Liu, Jielin Shi, Li Chen, Xueping Liu, Junhao Qiu, Zhiliang Ku, Yong Peng, Jie Zhong, Yi-Bing Cheng, and Fuzhi Huang ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b02624 • Publication Date (Web): 10 Apr 2018 Downloaded from http://pubs.acs.org on April 10, 2018
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 13 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
ACS Applied Materials & Interfaces
Low-Temperature Pre-Synthesized Crystalline Tin Oxide for Efficient Flexible Perovskite Solar Cells and Modules Tongle Bu,a† Shengwei Shi,a† Jing Li,a Yifan Liu,a Jielin Shi,a Li Chen,a Xueping Liu,a Junhao Qiu,a Zhiliang Ku,a Yong Peng,a Jie Zhong,a* Yi-Bing Chenga,b and Fuzhi Huanga* a
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of
Technology, Wuhan 430070, PR China b
Department of Materials Science and Engineering, Monash University, VIC 3800, Australia
†
These authors contributed equally to this work
*Corresponding Email:
[email protected];
[email protected].
Abstract Organic-inorganic metal halide perovskite solar cells (PSCs) have been emerging as one of the most promising next generation photovoltaic technologies with a breakthrough power conversion efficiency (PCE) over 22%. However, aiming for commercialization, it still encounters challenges for the large-scale module fabrication, especially for flexible devices which have attracted intensive attention recently. Low-temperature processed high-performance electron transporting layers (ETLs) are still difficult. Herein, we present a facile lowtemperature synthesis of crystalline SnO2 nanocrystals (NCs) as efficient electron transporting layers (ETLs) for flexible PSCs including modules. Through thermal and UV-Ozone treatments of the SnO2 ETLs, the electron transporting resistance of the ETLs and the charge recombination at the interface of ETL/perovskite were decreased. Thus, the hysteresis-free highly efficient rigid and flexible PSCs were obtained with PCEs of 19.20% and 16.47%, respectively. Finally, a 5 × 5 cm2 flexible PSC module with a PCE of 12.31% (12.22% for forward scan and 12.40% for reverse scan) was fabricated with the optimized perovskite/ETL interface. Thus, employing pre-synthesized SnO2 NCs to fabricate ETLs has showed promising for future manufacturing. Keywords: tin oxide, interface optimization, hysteresis, flexible perovskite solar cells, modules Introduction Hybrid organic-inorganic metal halide perovskite materials with their outstanding properties such as moderate band-gap, high light extinction coefficient, long charge diffusion length, and high charge mobility, have emerged as very promising photovoltaic materials and attracted more and more attentions.1-3 Since it was first used as light absorber in solar cells, the up to date certificated power conversion efficiency (PCE) of perovskite solar cells (PSCs) has been over 22% just in few years.4 The feasibility of solution and low temperature processability makes it possible to fabricate flexible devices,5-7 which opens more applications compared to
ACS Paragon Plus Environment
ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
silicon or GaAs solar cells. However, before the real commercial application, there are still some fatal problems that need to be highly concerned such as hysteresis, stability, and up-scaling.8-12 In particularly, for flexible PSCs, the low temperature process is vital because the flexible plastic substrate cannot stand high temperature even over 150 ℃.13, 14 Although organic semiconductors such as phenyl-C61-butyric acid methyl ester (PCBM), poly(bis(4-phenyl)(2,4,6-trimethylphenyl)amine) (PTAA), Poly(3-hexylthiophene) (P3HT) and Spiro-OMeTAD, can be directly applied in flexible PSCs, they are still quite expensive and somehow unstable, especially for large area perovskite solar modules (PSMs). 15-18 Li et al. reported a large area (16 cm2, no mask) flexible PSM with PCE over 8% recently based on a vacuum evaporation of C60, this low PCE and expensive process would retard the commercial application.19 In the other hand, inorganic semiconductors, such as TiO2, SnO2 and ZnO, show more promising, despite of the difficulty in low temperature processing.20-22 For example, Dagar et al. employed a low temperature processed SnO2/meso-TiO2 composite film as the ETL and obtained a PCE of 8.8% for a large area (12 cm2, no mask) flexible PSM.23 As recent reports demonstrated, SnO2 has shown superior performances such as high conductivity, proper energy band and good ultraviolet (UV) resistance. Thus, SnO2 has been widely studied in PSCs. There are various routes to fabricate SnO2 ETLs, such as atomic layer deposition (ALD), spin coating, and chemical bath deposition (CBD).24-26 Recently, Wang et al. have reports a low temperature plasma enhanced ALD processed SnO2 ETL sand achieved a high PCE over 18% with the water vapor treatment, although the device still had non-negligible hysteresis.21 However, a wet chemical processed SnO2 has more advantages as it does not involve a vacuum process, and is a promising route for future low-cost production. For example, SnO2 ETLs can be spin coated with precursor solutions such as SnCl4•5H2O and SnCl2•2H2O, however, the prepared films normally need to be sintered at a higher temperature usually at 180 ℃ that is not suitable for the flexible plastic substrate. Thus, a UV annealing process was employed to facilitate the annealing of such films at a low temperature for the flexible PSCs.23 Also, CBD methods with the addition of acids to control the hydrolysis rate of SnO2 has been employed. Unfortunately, the flexible conducting substrate (ITO) would be etched by the acids.
25, 27, 28
Therefore, using of pre-synthesized SnO2 nanocrystals (NCs) to prepare the films under low
temperature (150 ℃) is a smart route to fabricate efficient ETLs for the flexible PSCs. There are a lot of ways to synthesize SnO2 NCs, Zhu et al. have reported highly crystalline SnO2 NCs via a hydrothermal method at 200 ℃.29 Asdim et al. also reported microwave synthesis of SnO2 NCs with average size over 10 nm.30 Liu et al. developed a dual-fuel combustion method to create a milder exothermic process allowing the grow of uniform SnO2 films at low temperature.31 Herein, we obtained uniform SnO2 NCs with small size (