646

Macromolecules 1985,18, 646-650

Milan, for supplying some samples and m a n y useful suggestions and to Dr. M. Dell’Eva and Mr. A. Tealdi for valuable help. This investigation was supported by the Italian Research Council through its “Chimica Fine e Secondaria” project. Registry No. Cellulose, 9004-34-6; LiCl, 7447-41-8; DMAc, 127-19-5.

References and Notes G. Conio, E. Bianchi, A. Ciferri, A. Tealdi, and M. A. Aden, Macromolecules, 16, 1264 (1983). M. A. Aden, E. Bianchi, A. Ciferri, G. Conio, and A. Tealdi, Macromolecules, 17, 2010 (1984). P. J. Flory, Macromolecules, 11, 1141 (1978). A. Ciferri, in “Polymer Liquid Crystals”, A. Ciferri, W. R. Krigbaum, and R. B. Mayer, Eds., Academic Press, New York, 1982. G. Conio, P. Corazza, E. Bianchi, A. Tealdi, and A. Ciferri, J . Polym. Sci., Polym. Lett. Ed. 22, 273 (1984). M. Marx, Makromol. Chem. 16, 157 (1955); M. Marx-Figini and G. V. Schulz, ibid. 54,102 (1962); J. Brandrup and E. H. Immergut, Eds., “Polymer Handbook”,Wiley, New York, 1975, V-107.

(7) A. F. Turbak, A. El-Kafrawy, F. W. Snyder, and A. B. Auerbach, U. K. Pat. App. GB 2055 107A, 1981. C. L. McCormick and T. S. Shen, “Macromolecular Solutions”, R. B. Seymour and G. A. Stahl, Eds., Pergamon Press, New York, 1982. (9) D. Frdlich, D. Strazielle, G. Bernardi, and H. Benoit, Biophys. J., 3, 115 (1963). (10) G. Cohen and H. Eisenberg, Biopolymers, 4, 429 (1966). (11) E. F. Casassa and H. Eisenberg, J . Phys. Chem., 65, 1106 (1961). (12) M. Marx-Figini, Angew. Makromol. Chem. 72, 161 (1978). (131 A. El-Kafrawy, J . Appl. Polym. Sci., 27, 2435 (1982). ii4j C. P. Rao, P. Balaram, and C. N. R. Rao, J. Chem. SOC.,Faraday Trans. I , 76, 1008 (1980). (15) H. G. Elias, “Light Scattering from Polymer Solutions”, M. B. Huglin, Ed., Academic Press, London, 1972, p 397. (16) Cf., e.g., A. G. Walton and J. Blackwell, “Biopolymers”,Academic Press, New York 1973, p 470. (17) Ch. Tanford, ”Physical Chemistry of Macromolecules”, Wiley, New York, 1967, p 306. (18) E. Bianchi, A. Ciferri, G. Conio, A. Cosani, and M. Terbojevich, Macromolecules, following paper in this issue. (19) J. A. Hearst and Y. Tagami, J. Chem. Phys., 42,4149 (1965). (20) A. Sharples, “Cellulose and Cellulose Derivatives”, N. M. Bikales and L. Segal, Eds., Wiley-Interscience, New York, 1971, Part V, p 991.

Mesophase Formation and Chain Rigidity in Cellulose and Derivatives. 4. Cellulose in N,N-Dimethylacetamide-Lithium Chloride qstella Bianchi,’ Albert0 Ciferri,*tGiuseppina Conio,*Alessandro Cosani,$ and Maria Terbojevichs Istituto di Chimica Industriale, Uniuersitd di Genova, 16132 Genoua, Italy, and Centro Studi Biopolimeri, CNR,Istituto di Chimica Organica, Uniuersitd di Padoua, 35100 Padoua, Italy. Received May 17, 1984 ABSTRACT A study of the solubility and mesophase formation of cellulose in N,N-dimethylacetamide (DMAc) containing from 2% to 10% LiCl is reported. The cellulose samples and the method of preparation of the solutions are those described in the preceding paper where a study of dilute solution parameters and of aggregation was reported. T h e solubility of all samples increases with LiCl concentration. However, for several samples the solubility is too low to allow the attainment of the critical concentration for mesophase formation. Aggregated samples prepared by acid hydrolysis never attain the mesophase. The possibility of observing the latter a t high LiCl content is confined to samples which show molecular dispersion in dilute solution and DP below -600. Even in these cases the cholesteric phase is often metastable with respect to the crystal. The critical concentration increases with LiCl content. From the preceding paper we know that irregular patterns of association occur a t these concentrations. The interpretation of this complex situation in terms of independent or associated particles is discussed.

In the first two papers of this series we investigated the liquid crystallinity of (hydroxypropy1)cellulose(HPC) i n N,N-dimethylacetamide (DMAc)’ and in dichloroacetic acid (DCA).2 The results could be interpreted in terms of existing theories for semiflexible chains composed of rigid segments connected b y flexible joints? Basically, the HPC/DMAc system approached the behavior expected for independent and monodjsperse rods3having an axial ratio corresponding to the Kuhn statistical link. The occurrence of a small degree of soft interaction4 had to be postulated in order to obtain complete agreement between the theoretical and experimental values of the critical volume fraction.

In the accompanying paper5(part 3) we reported a light scattering and viscosity s t u d y of unsubstituted cellulose dissolved in DMAc LiC1. Cellulose does not present the

+

Istituto di Chimica Industriale, Universitl di Genova.

* Istituto di Chimica Organica, Universitl di Padova. 5 Centro

Studi Macromolecule, CNR.

0024-9297/85/2218-0646$01.50/0

problems associated with the nonuniform substitution of HPC and also appears to be a somewhat more rigid polymer than the latter. However, the above results show that considerable aggregation occurs depending, in a nonanticipated manner, upon sample preparation, molecular weight, LiCl concentration, and polymer concentration. Studies with cellulose, particularly with its concentrated solutions, have been hampered b y its poor solubility. Exotic solvents such as N-methylmorpholine N - o ~ i d e , ~ , ~ trifluoroacetic acid + chlorinated alkanes: liquid ammonia + NH4SCN,gand DMAc + LiCl’O have been reported to dissolve cellulose at concentrations at which the mesophase may be formed. For some of the above solvents, however, degradation is appreciable, while for others the occurrence of a true mesophase was not fully investigated. In no case was an attempt made to correlate the critical volume fraction with dilute solution data obtained in the same solvent. In this paper we report a study of mesophase formation of cellulose i n DMAc + LiCl and discuss the problems associated with the occurrence of aggregation. 0 1985 American Chemical Society

Cellulose in DMAc-LiC1 647

Macromolecules, Vol. 18, No. 4, 1985

sample G D A L C I E

Table I Characteristics of Samples Investigated [SI," dL/g DP M, supplier 102 16500 Snia Fibre' 0.63 155 25100 Avicel 0.92 288 46700 Snia Fibred 1.61 1.62 290 47000 Snia Fibred 449 72800 Buckeye Corp' 2.40 460 74500 SSCC, Miland 3.45 3.85 760 123000 Snia Fibrd

biphasic. f ibers

[SI?

dL/g 15-

3.0 3.0 4.9 5.0 7.5

s.

A

3

btphash fibers

'

aIn 0.5 M cupriethylenediamine at 25 O C . *In DMAc-5% LiCl at 25 O C . 'Sample E, hydrolyzed with HCl. dCellulose I1 regenerated. e V68 prehydrolyzed Kraft. 'Mischia latifoglia Kraft. Preliminary data concerning t h e phase diagram have already been reported." T h e cellulose/DMAc LiCl system was described i n a patent b y T u r b a k et al.,l0 who showed that no appreciable degradation occurs. Although they did n o t prove the occurrence of a mesophase, spinning from concentrated solutions produced ultrahigh-modulus fibers. Our own study of fiber spinning from the present system will be presented at a later date.

+

Experimental Section Materials. Seven cellulose samples similar to the corresponding ones described in the preceding pape@ were used. Their characteristics are collected in Table I. Molecular weights were evaluated from the intrinsic viscosities5 measured in 0.5 M cupriethylenediamine (CED) using the relationship12

5-

6b

B

c1449

A / 288

L b

2

5

1

I

4

6

I

I

8

1

1

0

,

I

I

L

6

8

cs ,%

Figure 1. Phase diagrams for cellulose, samples A and C, in DMAc with varying LiCl concentration at 20 O C : (0) isotropic solution; (a)isotropic solution solid; (A)biphasic solution; (A) biphasic solution + solid. Broken line indicates the upper limit 1.3. of the biphasic gap if C{/Cd

+

-

1.0187 mL/g. The latter data were used to convert C, into polymer volume fraction. Solutions in CED, obtaining by stirring for 24 h small pieces of dried cellulose, exhibit molecular dispersion and virtual absence of degradation.6 Phase Diagram. Solutions in DMAc/LiCl were prepared following the method described by Turbak et al.,1° as described in more detail in the preceding paper.5 Polymer concentration, C,, is given as grams of cellulose per 100 g of ternary solution. C, varied between -0.3% and 17%. Salt concentration, C,, is given as grams of LiCl per 100 g of binary (LiC1 + DMAc) solution. C, varied between -2% and 10%. Virtual absencelo of degradation of cellulose in DMAc/LiCl solutions was confirmed5 by measurement of [ s ] in CED on samples which had been reprecipitated from the former solvent. Solutions were observed under the polarizing microscope at room temperature (-20 "C) at various times (up to 3 months) following the preparation of the solutions. Situations observed were (i) isotropic solutions, (ii) isotropic solutions containing a solid in the form of small fibers, (iii) solutions containing an isotropic and a birefringent phase, and (iv) solutions of the latter type containing also undissolved fibers. In no case was a single anisotropic phase observed. The birefringent phase observed in case iii was separated from the isotropic one for a solution with C, = 11.5% and C, = 7% in the following way 14 mL of the latter solution was centrifugated at 44000 rpm at 20 "C as previously described.' After about 350 h, the birefringent phase sedimented at the bottom of the polyallomer tube and occupied about 10% of the total volume. However, even after this extensive centrifugation, a little birefringent phase remained above the boundary, its amount increasing as the boundary was approached. The clear part of the isotropic phase and the bottom part of the anisotropic one were separated. From aliquots of these phases, the polymer was precipitated and the corresponding C/ (anisotropic)and C,l (isotropic) were determined along with the respective intrinsic viscosities. Optical rotatory dispersion was performed on the phases separated by centrifugation (the large amount of LiCl prevented circular dichroism measurements). The rotation angle was measured by using a Jasco ORD UV/5 spectropolarimeter between 500 and 700 nm a t room temperature.' The polymer partial specific volume, ij2, was determined pycnometrically at 25 OC using sample A. In DMAc + 3.5 LiC1, u2 = 0.615 mL/g. In DMAc + 5% LiC1, u2 = 0.621 mL/g. The molar volume Vlof DMAc + 5% LiCl was found to be equal to

Results and Discussion T h e phase diagram for samples A a n d C are plotted in Figure 1as polymer concentration vs. LiCl concentration. T h e curves represent the boundaries between t h e various phases and t h e experimental points indicate the appearance of t h e solutions a long time after preparation. T h e dotted line, describing the composition of the pure anisotropic phase for sample A, was drawn by taking t h e ratio C,,"/C,,' of t h e composition of t h e pure anisotropic phase and isotropic phase equal to 1.33. This ratio is obtained from the results of the determination of C,,' (=11.0) and C/ (=14.7%) in the case of a solution having overall C, = 11.5% and C, = 7 % (cf. Experimental Section). T h i s ratio, describing the width of the biphasic gap,3 is larger than that determined for HPC in DMAc and DCA1i2and that expected for a rather narrow molecular weight distribution.lJ3J4J5 (A more extensive discussion of these relationships and of theories relating t h e critical volume fraction to t h e axial ratio may be found i n ref 15.) It is evident from Figure 1that for sample A the solubility line is rather close to t h e line describing t h e composition of t h e anisotropic solution. Therefore, formation of t h e anisotropic phase is associated with ~rystallization.'~Situations in which the solubility line crosses the narrow region have been described by Balbi et al.,16Papkov," and Ciferri and Krigbaum.18 Since t h e rate of nucleation of t h e liquid crystal is generally larger than that of t h e crystalline material, t h e former may be observed even under metastable conditions. In t h e case of sample C, t h e anisotropic phase is not observed unless extremely high C, (Xi%) are used. It is seen that t h e solubility of sample C is considerably smaller t h a n for sample A, preventing t h e former from attaining the critical concentration for mesophase formation. We note t h a t for both samples t h e solubility is increased b y increasing C,. A closer inspection of Figure 1reveals t h a t t h e solubility difference between samples A and C decreases with C, (the difference is -100% at C, = 5 % a n d -50% a t C, = 8%).

Macromolecules, Vol. 18, No. 4 , 1985

648 Bianchi et al. Table I1 Axial Ratios Uib

sample (DP)

A (288) L (290) I(460)

L," A 1480 1490 2364

C, = 5% 0.058

xexptlc

C, = 7.8%

C, = 5%

0.079

137

C, = 7.8% 99 96 120

0.082 0.066

x = L/5.€id

x = 2q/5.8O

x = L/17f

255 257 408

43 43 43

87 88 139

Data from Figure 3. 'Derived by using eq 2. Axial ratio corresponding to rod of length L. e Axial ratio a Contour length = DP X 5.14 A. corresponding to q = 125 A. !Axial ratio corresponding to aggregate of length L and d = 17 A.

150

1

0

->w

500

600 A , nm

Figure 2. Optical rotation vs. wavelength for coexisting isotropic and anisotropic layers of cellulose in DMAc + 7% LiCl separated by centrifugation. Overall C , is 11.5%. 0.01-mm-thick quartz cell.

Thus, the lower solubility of sample C with respect to sample A cannot be entirely ascribed to its higher DP. In fact, we found (unreported) that samples such as D and G having a DP smaller than sample A (Table I) had very low solubility and could not attain the critical concentration. From the results in the accompanying paper5 we know that hydrolyzed samples such as C, D, and G may exhibit stable aggregation even at c 0. In contrast, samples such as A, L, I, and E (not subject to acid hydrolysis) exhibited molecular dispersion at c 0. Sample C was peculiar because, when prepared at C, > 3%, it exhibited aggregation at C, = 5% and molecular dispersion at C, = 7.8%. It thus appears that the solubility of cellulose in DMAc/LiCl is conditioned by both aggregation and DP, making it unlikely for both aggregated samples and samples exhibiting molecular dispersion, but too large DP (e.g., sample E), to attain the critical concentration. In the case of sample A, the proof that the phase separated by centrifugation is indeed a cholesteric one is given by the ORD data reported in Figure 2. Here, while the rotation of the pure isotropic phase is extremely small, the pure anisotropic phase exhibits a large negative rotation typical of cholesteric mesophases. The effect observed is of the same order of magnitude as that observed with HPC.'y2 We note that often the shape of the ORD curve exhibited considerable irreproducibility, probably due to incomplete equilibrium or too thick samples. Other features of the phase equilibria include the determination of [17] for the coexisting isotropic and anisotropic phases (overall C, = 11.5%; C, = 7%). The results, [77lmisO N [77liaON 1.30 f 0.05 g/dL, fail to reveal the selective enrichment of high molecular weight species in the anisotropic phase which was observed with other systems.'v2J6 The dependence of the critical volume fraction u2' upon the DP of cellulose in DMAc + 7.8% LiCl is exhibited in Figure 3. The only samples which could be included are regenerated cellulose I1 (samples A, L, and I) having a relatively low DP (sample C exhibited some evidence of mesophase only at C, > 7.8%). In Figure 3 we have included the previously reported2 behavior of semirigid HPC

-

-

. -- - ---*. I

~

- - - - - - Rods,d=17A - -- - - - - - - - - ROd5,d=58A -*_

I

I

in DCA to show the considerable difference between the critical volume fraction of HPC and cellulose. The behavior of cellulose is closer in several respects (including poor solubility and LiCl effect) to that observed with rigid poly(p-benzamide).16 To describe the various theoretical curves represented in Figure 3, we explore the correlation between the critical concentration and axial ratio. The critical concentration C,' increases with salt content in analogy with the case of poly@-benzamide).16 Sample A, for instance (cf. Figure l), at C, = 5% has C,' = 9.2 f 0.3%, which corresponds to a polymer volume fraction 1121 = 0.058 f 0.002. A t C, = 8%, C ' is between 10.8% and 11.3% or u2' = 0.079 f 0.002. d i n g the relationship3J9

we can evaluate the apparent axial ratio of cellulose which conforms with the hard rod theory.lg At C, = 5 % , we obtain x = 137 and at C, = 8%, x = 99. These data, and similar evaluation of x for the samples in Figure 3, are included in Table 11. In previous work, values of x have been determined a priori from either the contour length (for rods) or the persistence length (for semirigid chains) in the assumption that molecular dispersion pre~ailed.'?~J~ In view of the association and aggregation phenomena occurring in the present ~ y s t e m it , ~is appropriate to consider x as a parameter to be determined using eq 2, as indicated above, and then compared with various models of molecularly dispersed and aggregated species. Assuming a rodlike model and nonaggregated chains, the axial ratio is simply the contour length L divided by the chain diameter d. On

Cellulose in DMAc-LiC1 649

Macromolecules, Vol. 18,No.4,1985

sample (DP) c (449) I(460) E (760) OContour length = DP

X

L,”A

Table I11 Persistence Length Data (It&’/*: A 9CL,C 8,

2308 2364 3906

375 f 20% 400 f 20% 490 f 20%

qm,d A

qYF;

140-(420) 160-(500) 130-(330)

117-(263) 130-(292) 118-(265)

A

110 f 10 110 f 10

110 f 10

5.14 A. *From ref 5. CUsingeq 4. dUsing eq 5. eFrom Figure 4.

the basis of the density of rayonzoa( p = 1.52 g/cm3), the diameter, calculated according to13 d = (MO/pNALo)1/2

(3)

where Lo is the projection of the residue unit on the chain axis, turns out to be 5.8 A. (The density of cellulose 1I2Ob from X-ray analysis is 1.6 g/cm3, corresponding to d = 5.7 A.) Results, included in the fifth column of Table I1 and represented by the lower line in Figure 3, show that this model is untenable. The persistence length can be evaluated by using the light scattering and viscosity data determined in the accompanying paper5 under conditions in which molecular dispersion occurs. The intrinsic viscosities in DMAc + 5% LiCl listed in Table I for the samples investigated here correspond to molecularly dispersed cellulose (data were obtained when c 0 and C, was smaller than the value at which stable aggregation occurs5). These data are compared in Figure 4 with theoretical [q]-Mw curves calculated according to the theory of Yamakawa and Fujii’l for wormlike cilinders

q,i

,140 1.01

120 110 100 90

80

70 0.71

/

-

[q] =

CPL’3/2/X3M (4) where L‘= xM/ML is a reduced contour length (MLbeing the mass per unit length), X = 1/2q, and CP is a function of L‘ and the reduced cilinder diameter d’ tabulated by Yamakawa and Fujii. ML was taken to be equal to 31.5 daltons/A (correspondingto a residue vector of 5.14 A2za). The unreduced diameter d was allowed to varym between 4.5 and 6.0 A. The experimental points in Figure 4 suggest q y F = 110 f 10 A. Evaluation of the possible errors on q from the diameter and other sources, as described elsewhere,’ gave indeterminations which do not exceed the indetermination caused by the scatter of the data point in Figure 4. Alternative determinations of q are possible using the light scattering data.5 For samples C, I, and E the radii of gyration determined in the preceding paper5 are reported in Table I11 (third column). They are affected by a large indetermination, on the order of 20%. From (RG’), the persistence length in the Gaussian coil limit is given by qCL = 3(RG2)/L (5) Values of qcL are reported in the fourth column of Table III. Using the Benoit-Doty treatment of wormlike chainsu it also possible to obtain the persistence length, qBD, according to ( R G ~=) q2(Y3(L/q) - 1 + (2q/L) - (2s2/L2)[1 - exp(-L/q)lI (6) The results of this calculation are reported in the fifth column of Table 111. The comparison of the various estimates of q collected in Table I11 reveals that QYF < q?i < qBD. This result is at variance with out data for HPC. ~ QBD, by However, Sai@ found that in several cases q y < a factor up to -2. He suggested that the neglect of a free-draining effect in the Yamakawa-Fujii theory is responsible for the lower value of qYF. YamakawaZ6has recently commented on the problems associated with the

4.6

4.9

5.2

l o g MV

Figure 4. Full lines represent the theoretical intrinsic viscosity-molecular weight dependence for wormlike cylinders having the indicated values of q and diameter 5.8 A. ML = 16215.14 daltons/A. Black points are the experimentalvalues of [ v ] for cellulose in DMAc + 5% LiCl for molecularly dispersed samples.

proper value of the chain diameter required for the wormlike cylinder. We observe, however, that the large error affecting (RG’) is primarily responsible for the large scatter of qcL and qBD. The lower limits of these quantities are rather close to the q y F values. By averaging the lowest figures obtained by light scattering with the viscosity result, we obtain q 125 A, which represents a lower limit for q in DMAc + 5% LiC1. Using q = 125 A we have calculated the axial ratio of the Kuhn segment given by x = 2q/d. According to Flory’s treatment of semirigid chains3(cf. introduction), the latter axial ratio should be related to u i using eq 2. The results, shown in Table I1 (sixth column) and by the horizontal line in Figure 3, indicate that the Kuhn model does not represent the experimental variation of ud with DP and overestimate the absolute values of u i . The deviation between the Kuhn model and the experimental data for cellulose in DMAc/LiCl is in the same direction as that previously observed for HPC in DMAc and in DCA.’p2 In the latter cases-when molecular dispersion likely prevailed-we postulated the occurrence of soft interactions4 to secure agreement between experiment and theory. In che present case, a P 130 K (already within the wide region) would be required4 to fit the Kuhn model to the u i measured for the sample with largest DP. The large indetermination affecting q (which for the present system is even larger than the indetermination affecting dl,’) prevents, however, a too strict assessment of the deviation between experiment and the Kuhn model. Although, with proper adjustment of q, and possibly T*, the Kuhn model might represent the limiting value of u i at a given C,, it is unlikely that the variation of u i with C, could be explained by the effect of LiCl on q. Both the viscosity and light scattering data in the accompanying paper5 rule out a significant decrease of q when C, is increased from 5% to

-

-

Macromolecules, Vol. 18, No. 4, 1985

650 Bianchi et al.

7.8%. A decrease of T* with C, would be required to justify the observed trend, making rather unsatisfactory the interpretation based on molecularly dispersed species. We therefore consider the axial ratio to be expected without the assumption of molecular dispersion. The results in the accompanying paper5 reveal the existence, under given conditions, of stable aggregate particles composed of about 7 extended molecules with a side-by-side organization. The axial ratio for such particles should be given by the contour length divided by a diameter on the order of 17 A. Data thus obtained for samples A, L, and I are included in the last column of Table 11. They show better agreement with the values of x deduced from eq 2 than the values calculated by assuming molecular dispersion (compare the last four columns in Table I1 and Figure 3). There are, however, at least two considerations which cast doubts on the validity of this simple model. The first consideration is that, as indicated earlier, the instances in which such an aggregate was observed correspond to situation of low solubili,y, in fact preventing the attainment of the critical concentration. The second consideration is that the model of the aggregated particle does not readily explain the smooth increase of v i with C,. I t was shown5 that increasing C, results in the disruption of the aggregates. However, molecularly dispersed species were observed at high C,, but only at low polymer concentration. A t large C, and C,, association equilibria set in, with a more irregular pattern of interchain contacts than observed with the stable aggregates, making the evaluation of x a rather problematic task. The occurrence of an association equilibria could be handled in the following manner. With proper choice of a model, the size distribution of associated species could be evaluated (the pattern of association could include side-by-side organization with partial overlap along the chain axis). The corresponding axial ratio distribution could be related to the critical volume fraction using an approach similar to that used by Flory and Frost14for the most probable distribution of molecularly dispersed rods (neglecting a shift in the association equilibrium upon crossing the narrow region). Although we do not propose a quantitative analysis along the above lines, we observe that some of the present results would be qualitatively in line with the model. In particular, the observation of a biphasic gap wider than exhibited by HPC, coupled with a negligible disproportion of high and low molecular weight species between the conjugated phases, would not be surprising. The pronounced increase of u i with C, would be compatible with a reduction of asymmetry resulting

from the experimentally observed5increase of association with C,.

Acknowledgment. We express our appreciation to Mrs. G . Bitossi, Mr. A. Tealdi, and Dr. P. Corazza for their cooperation. This investigation was supported by the Italian Research Council through its “Chimica Fine e Secondaria” project. Registry No. Cellulose, 9004-34-6; LiCl, 7447-41-8; DMAc, 127-19-5.

References and Notes (1) G. Conio, E. Bianchi, A. Ciferri, A. Tealdi, and M. A. Aden, Macromolecules, 16, 1264 (1983). (2) M. A. Aden, E. Bianchi, A. Ciferri, G. Conio, and A. Tealdi, Macromolecules, 17, 2010 (1984). (3) P. J. Flory, Macromolecules, 11,1141 (1978); R. R. Matheson and P. J. Flory, ibid., 14,954 (1981). (4) P. J. Flory and G . Ronca, Mol. Cryst. Liq. Cryst., 54, 311 (1979). (5) M. Terbojevich, A. Cosani, G. Conio, A. Ciferri, and E. Bianchi,

Macromolecules, preceding paper in this issue. (6) C. McCorsley and J. Varga, US.Pat. 4 142 913 and 4 144 080

(to Akzona Co.).

(7) M. Chanzy and A. Peguy, J.Polym. Sci., Polym. Phys. Ed., 18, 1137 (1980). (8) D. L. Patel and R. D. Gilbert, J.Polym. Sci., Polym. Phys. Ed., 19, 1449 (1981). (9) S. M. Hudson and J. A. Cuculo, J. Polym. Sci., Polym. Chem. Ed., 18, 3469 (1980). (10) A. F. Turbak, A. El-Kafrawy, and A. Auerbach, U.K. Pat. Appl. GB 2055 107A, 1981. (11) G. Conio, P. Corazza, E. Bianchi, A. Tealdi, and A. Ciferri, J. Polym. Sci., Polym. Lett. Ed., 22, 273 (1984). (12) M. Marx, Makromol. Chem., 16, 157 (1955). (13) P. J. Flory, Adu. Polym. Sci. 59, 1 (1984). (14) P. J. Flory and R. S. Frost, Macromoles, 11, 1126 (1978). (15) A. Ciferri, “Polymer Liquid Crystals”, A. Ciferri, W. R. Krig-

baum, and R. B. Meyers, Eds., Academic Press, New York, 1982. (16) C. Balbi, E. Bianchi, A. Ciferri, A. Tealdi, and W. R. Krigbaum, J. Polym. Sci., Polym. Phys. Ed., 18, 2037 (1980). (17) S. P. Papkov, Contemp. Top. Polym. Sci., 2 (1977). (18) A. Ciferri and W. R. Krigbaum, Mol. Cryst. Liq. Cryst., 69,273 (1981). (19) P. J. Flory, Proc. R. SOC. London, Ser. A., 234,73 (1956); P. J. Flory and G . Ronca, Mol. Cryst. L ~ QCryst., . 54, 289 (1979). (20) (a) W. E. Morton and J. W. S. Hearle, “Physical Properties of

Textile Fibers”, The Textile Institute-Heinemann, London, 1975. (b) J. Brandrup and E. H. Immergut, Eds., “Polymer Handbook”, Wiley, New York, 1975. (21) H. Yamakawa and M. Fujii, Macromolecules, 7, 128 (1974). (22) D. A. Brant and K. D. Goebel, Macromolecules, 5,536 (1972). (23) R. H. Marchessault and A. Sarko, Adu. Carbohydr. Chem., 22,

421 (1967). (24) H. Benoit and P. Doty, J. Phys. Chem., 57, 958 (1953). (25) M. Saito, Polym. J., 15, 213 (1983). (26) H. Yamakawa, Macromolecules, 16, 1928 (1983).