Ordered Mesoporous Carbonaceous Materials with Tunable Surface Property for Enrichment of Hexachlorobenzene Jianwei Fan, Xianqiang Ran, Yuan Ren, Chun Wang, Jianping Yang, Wei Teng, Liyin Zou, Yu Sun, Bin Lu, Yonghui Deng, and Dongyuan Zhao Langmuir, Just Accepted Manuscript • DOI: 10.1021/acs.langmuir.6b02258 • Publication Date (Web): 06 Sep 2016 Downloaded from http://pubs.acs.org on September 7, 2016
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
Langmuir is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
Ordered Mesoporous Carbonaceous Materials with Tunable
2
Surface Property for Enrichment of Hexachlorobenzene
3
Jianwei Fan,† Xianqiang Ran,† Yuan Ren,‡ Chun Wang,‡ Jianping Yang,†,‡ Wei Teng,†
4
Liyin Zou,§ Yu Sun,§ Bin Lu,†,* Yonghui Deng‡,ψ *, Dongyuan Zhao‡
5
†
6
Environmental Science and Engineering, Tongji University, Shanghai 200092, P.R.
7
China
8
‡
9
Polymers, Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials,
10
iChEM (Collaborative Innovation Center of Chemistry for Energy Materials), Fudan
11
University, Shanghai 200433, China
12
§
13
Company Limited, Shanghai, 200092, P.R. China
14
ψ
15
Information Technology, Chinese Academy of Sciences, Shanghai 200050, China
State Key Laboratory of Pollution Control and Resource Reuse, College of
Department of Chemistry, State Key Laboratory of Molecular Engineering of
Shanghai Tongji Clearon Environmental-Protection Equipment Engineering
State Key Lab of Transducer Technology, Shanghai Institute of Microsystem and
16
17
Corresponding author:
[email protected],
[email protected] 18
1
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 2 of 29
1
Abstract
2
A gradient pyrolysis approach has been adopted for synthesis of ordered mesoporous
3
carbonaceous materials with different surface and textural properties for removal of hexachlorobenzene. The resultant ordered mesoporous carbonaceous materials possess high surface areas (364 ~ 888 m2/g), large pore volumes (0.23 ~ 0.47 cm3/g),
4 5 6 7 8 9 10 11 12
uniform pore sizes (2.6 ~ 3.8 nm), and tunable hydrophobic properties. They show high-efficiency removal performances for hexachlorobenzene with high adsorption capacity of 594.2-992.1 µg/g. An enhanced removal rate (> 99 %) can be obtained with the increasing of pyrolysis temperature (900 °C), due to strong hydrophobic-hydrophobic interaction between the carbon framework and hexachlorobenzene molecules. Furthermore, the adsorption behaviors follow the Langmuir equation and obey the pseudo-first-order kinetic model.
13 14 15 16
Keywords: Mesoporous materials, Hexachlorobenzene, Water treatment
Carbonization
temperature,
2
ACS Paragon Plus Environment
Adsorption,
Page 3 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
1. Introduction
2
Hexachlorobenzene (HCB) is one kind of typical persistent organic pollutants
3
(POPs). It was considered as a commonly efficient fungicide which was once widely
4
used in the last century and still could be frequently found in soil, sediment, water, air,
5
and also in biota nowadays [1-4].The presence of HCB in environment do great harm
6
to human beings and ecosystem [5, 6], causing dermatitis, severe numb in
7
cardiovascular and nervous system, and even cancer [7-9].Therefore, it is urgent to
8
develop efficient and economical methods for removal of HCB.
9
Up to now, various techniques such as chemical enhanced washing, electrokinetic
10
(EK) remediation, reductive/oxidation dechlorination, thermal decomposition and
11
radiolytic reduction have been adopted for the treatment of HCB in soil and sediment
12
[10-20]. However, there are few reports on the removal of HCB in water. In fact, HCB
13
accumulated in soil and sediment mainly comes from the surface water, for this
14
reason the treatment of HCB in aquatic environment maybe relatively crucial and
15
should deserve more attentions [21, 22]. While chemical properties of HCB, such as
16
hydrophobic property, bring a great challenge to researchers. Therefore, it is still very
17
difficult to find an effective approach for the removal of HCB in water.
18
Ordered mesoporous carbonaceous materials are emerged as the promising
19
candidates for pollutants adsorption and removal, because of their stable,
20
environmentally friendly properties, the ideal space for the fast accumulation of
21
organic pollutants, tunable ordered mesopore sizes ranging from 1.5 to 10 nm [23, 24],
22
and the remarkable properties such as high surface areas and large pore volumes 3
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1
[25-27]. Especially, ordered mesoporous carbons are considered as ideal adsorbents in
2
treating environmental issues [28] due to the fast mass transfer in their mesochannels.
3
In addition, mesoporous carbons display the excellent adsorption ability for organic
4
pollutants, such as reactive dyes (Remazol Red, methylthionine chloride and
5
rhodamine B), alcohol biofuel, chloroacetic acid, aminoacids, toluene, lysozyme and
6
naphthalene from aqueous solutions [29-33]. However, there are rare reports
7
concerning removal of persistent organic pollutants (POPs) using ordered mesoporous
8
carbons as the adsorbents. Furthermore, there is a lack of systematic research about
9
the effect of different surface properties of mesoporous carbon on their adsorption
10
capacities.
11
Herein, we detailedly investigate the removal of HCB from aqueous solutions using
12
ordered mesoporous carbonaceous materials calcinated at different temperatures (350,
13
600 and 900 °C) as adsorbents, which denoted as OMC-350, OMC-600, and
14
OMC-900, respectively. All these materials have ordered two-dimensional (2-D)
15
hexagonal mesostructure, open mesopore channels, and hydrophobic properties.
16
While the hydrophobic property of ordered mesoporous carbonaceous materials
17
endow the superior HCB adsorption efficiency (> 99 %). The sorption capacity and
18
kinetics were studied using the batch method. The results can provide necessary
19
information for a better understanding of the POPs adsorption and separation
20
involving mesoporous carbonaceous materials.
4
ACS Paragon Plus Environment
Page 4 of 29
Page 5 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
2. Materials and methods
2
2.1. Chemicals
3
Triblock
copolymer
poly(ethylene
oxide)-block-poly(propylene
4
oxide)-block-poly(ethylene oxide) copolymer, Pluronic F127 (EO106PO70EO106, Mw =
5
12,600) was purchased from Aldrich. Hexachlorobenzene (HCB) (100 mg/mL) was
6
purchased from J&K Chemical Ltd. Pure water was deionized with a Milli-Q water
7
purification system (Millipore). Phenol, n-hexane, formaldehyde and ethanol were
8
purchased from Sinopharm Chemical Reagent Co., Ltd.
9
2.2 . Preparation of ordered mesoporous materials
10
The carbon precursor, phenolic resin ethanolic solution (20 wt. %), was prepared
11
referring to the method of Meng et al [34]. The ordered mesoporous materials were
12
prepared by organic-organic self-assembly approach with phenolic resin as carbon
13
source and triblock copolymer Pluronic F127 as the structure-directing agent. The
14
synthesis procedure for ordered mesoporous materials was as follows. First, 1.0 g of
15
triblock copolymer Pluronic F127 was dissolved in 20.0 g of ethanol with stirring for
16
3 h to obtain a clear solution. Then, 5.0 g of phenolic resins ethanolic solution was
17
added with stirring for 3 h. After that, the mixture was poured into dishes to evaporate
18
ethanol completely at 25 °C for 8 h, and heated at 100 °C for 24 h to obtain the
19
as-made samples. Then, it was carbonized at different temperature (350, 600 or
20
900 °C) for 3 h under N2 to obtain the samples denoted as OMC-350, OMC-600, and 5
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1
OMC-900, respectively. The heating rate was 1 °C/min below 600 °C and 5 °C/min
2
above 600 °C.
3
2.3 . Characterization
4
Small-angle X-ray scattering (SAXS) patterns were collected on a Nanostar U
5
small-angle X-ray scattering system using Cu Kα radiation at 40 kV and 35 mA. The
6
d-spacing values and unit cell parameters (a0) were calculated by the formula
7
d = 2π / q and a0 = 2d10 ( 3)−1 , respectively. Transmission electron microscopy
8
(TEM) experiments were carried out using a JEOL 2011 microscope operated at 200
9
kV. The ground samples for TEM measurements were suspended in ethanol and
10
supported on a carbon-coated copper grid. The N2 adsorption-desorption at 77 K was
11
performed on a Micromeritics Tristar 3000 analyzer. Before the measurements, all
12
samples were degassed at 180 °C in vacuum for more than 6 h. The pore size
13
distributions were derived by using the Barrett-Joyner-Halenda (BJH) model. The
14
total pore volume (Vp) was estimated from the adsorbed amount at p/p0 of 0.995. The
15
specific surface areas were calculated by the Brunauer-Emmett-Teller (BET) method.
16
13
17
spectrometer. The
18
and the contact time was 1 ms. Adamantane was used as a reference for 13C chemical
19
shift. Infrared Spectrum scanned from 4000 ~ 400 cm-1 was detected at ambient
20
temperature on a Nicolet Fourier transform infrared spectrometer.
21
2.4. Adsorption experiments
C NMR spectrum was recorded at room temperature on a Bruker MSL-300 13
C resonance frequency was 75 MHz. Their cycle time was 2 s,
6
ACS Paragon Plus Environment
Page 6 of 29
Page 7 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
Experiments
were
carried
out
to
investigate
adsorption
behaviors
of
2
hexachlorobenzene using the ground samples in batch mode. The absorbate solution
3
was prepared by diluting HCB standard solution (100 mg/mL in methanol) to a series
4
of certain concentrations. All adsorption studies were conducted as follows: a fixed
5
mass of adsorbent was added into a conical flask with 50 mL of HCB solution with
6
various initial concentrations. Each flask was sealed, and stirred in a rotary shaker at
7
150 rpm under different constant temperatures (± 0.5 °C) for 24 h. After that, the
8
mixture was taken out and filtered using a membrane filter for further analysis. All the
9
experiments were carried out with repeated trials.
10
In order to screen out the optimal adsorbent with maximum adsorption ability, three
11
kinds of ordered mesoporous materials (10 mg) calcined at 350, 600, and 900 °C and
12
commercial active carbon (surface area of ~1900 m2/g, pore size of 0.99), indicating that the diffusion including
8
liquid film and intra-particle diffusion are the rate-controlling steps for the HCB
9
adsorption on OMC-900 material. The coefficient of determination (R2 = 0.996) for
10
pseudo-first-order model is higher than that for Lagergren-second-order model (R2 =
11
0.994), suggesting that the kinetic process can be better explained by
12
pseudo-first-order model. Additionally, the value of qe (933.30 µg/g) calculated using
13
the pseudo-first-order model is closer to the experimental data (962.31 µg/g).
14
4. Conclusions
15
In summary, ordered mesoporous carbonaceous materials with different surface
16
properties have been successfully synthesized by organic-organic self-assembly
17
method with phenolic resin as carbon source, triblock copolymer Pluronic F127 as
18
structure-directing agent at different pyrolysis temperature. The obtained OMC-350,
19
OMC-600 and OMC-900 have ordered hexagonal mesostructures, uniform pore size
20
distribution, high surface area for adsorption removal of HCB. OMC-900 material
21
show the highest adsorption capacity (992.09 µg/g), which is higher than that of 17
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1
commercial active carbon at 25 °C (809.05 µg/g). Theoretical fitted results based on
2
thermodynamics data indicate that the adsorption of HCB is physical adsorption with
3
an exothermic process. Meanwhile, these equilibrium data fit well with the Sip’s
4
isotherm model and demonstrate a heterogeneous adsorption. The adsorption of HCB
5
by OMC-900 can be well explained by a pseudo-first-order kinetic model. This new
6
kind of ordered mesoporous carbon (OMC-900) with high surface area and
7
hydrophobic characteristic is supposed to be applied in the adsorption of hydrophobic
8
pollutants from water.
9 10
5. Acknowledgments
11
This work was supported by the National Natural Science Foundation of China
12
(21377096, 51372041, 51422202), the State Key Laboratory of Pollution Control and
13
Resource Reuse Foundation (NO. PCRRK16009), the Shanghai Committee of
14
Science and Technology (14ZR1400600), the “Shu Guang” Project (13SG02) of
15
Shanghai Municipal Education Commission, Shanghai Municipal Science and
16
Technology Commission (13140902401, 14JC1400700), and National Youth
17
Top-notch Talent Support Program in China.
18
19
References
20
[1] Meijer, S. N.; Ockenden, W. A.; Sweetman, A.; Breivik, K.; Grimalt, J. O.; Jones, K. C.;
21
Global distribution and budget of PCBs and HCB in background surface soils: Implications for
22
sources and environmental processes. Environ. Sci. Technol. 2003, 37 (4), 667–672. 18
ACS Paragon Plus Environment
Page 18 of 29
Page 19 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
[2] Bailey, R.E. Global hexachlorobenzene emissions. Chemosphere. 2001, 43, 167-182.
2
[3] Barber, J. L.; Sweetman, A. J.; Wijk, D.V.; Jones, K. C. Hexachlorobenzene in the global
3
environment: Emissions, levels, distribution, trends and processes. Sci. Total Environ. 2005, 349,
4
1-44.
5
[4] Falcó, G.; Llobet, J. M.; Bocio, A.; Domingo, J. L. Exposure to hexachlorobenzene through
6
fish and seafood consumption in Catalonia, Spain. Sci. Total Environ. 2008, 389, 289-295.
7
[5] Liu, X.; Zhang, G.; Li, J.; Yu, L. L.; Xu, Y.; Li, X.D.; Kobara, Y.; Jones, K.C. Seasonal patterns
8
and current sources of DDTs, chlordanes, hexachlorobenzene, and endosulfan in the atmosphere
9
of 37 Chinese cities. Environ. Sci. Technol. 2009, 43 (5), 1316-1321.
10
[6] Howe, T.; Billings, S.; Stolzberg, R. J. Sources of polycyclic aromatic hydrocarbons and
11
hexachlorobenzene in spruce needles of eastern Alaska. Environ. Sci. Technol. 2004, 38,
12
3294-3298.
13
[7] Jarrel, J.; Gocmen, A. A review of human and sub-human primate toxicity of
14
hexachlorobenzene. Pure Appl. Chem. 2000, 72, 1015-1022.
15
[8] Pohl, H. R.; McClure, P. R.; Fay, M.; Holler, J.; De Rosa, C. T. Public health assessment of
16
hexachlorobenzene. Chemosphere. 2001, 43, 903-908.
17
[9] Hou, H.; Zhao, L.; Zhang, J.; Xu, Y. F.; Yan, Z. G.; Bai, L. P.; Li, F. S. Organochlorine
18
pesticides and polychlorinated biphenyls in soils surrounding the Tanggu Chemical Industrial
19
District of Tianjin, China. Environ. Sci. Pollut. Res. 2013, 20, 3366-3380.
20
[10] Tong, M.; Yuan, S. Physiochemical technologies for HCB remediation and disposal: A review.
21
J. Hazard Mater. 2012, 229-230, 1-14.
22
[11] Deane, G.; Chroneer, Z.; Lick, W. Diffusion and sorption of hexachlorobenzene in sediments
23
and saturated soils. J. Environ. Eng. 1999, 125, 689-696.
24
[12] Chu, W.; Chan, K. H. The mechanism of the surfactant-aided soil washing system for
25
hydrophobic and partial hydrophobic organics. Sci. Total Environ. 2003, 307, 83-92.
26
[13] Yuan, S. H.; Wu, X. F.; Wan, J. Z.; Long, H. Y.; Lu, X. H.; Wu, X. H.; Chen, J. Enhanced
27
washing of HCB and Zn from aged sediments by TX-100 and EDTA mixed solutions. Geoderma
28
2010, 156, 119-125.
29
[14] Li, T. P.; Yuan, S. H.; Wan, J. Z.; Lu, X. H. Hydroxypropyl-β-cyclodextrin enhanced
30
electrokinetic remediation of sediment contaminated with HCB and heavy metals. J. Hazard.
31
Mater. 2010,176, 306-312.
32
[15] Oonnittan, A.; Shrestha, R. A.; Sillanpää, M. Removal of hexachlorobenzene from soil by
33
electrokinetically enhanced chemical oxidation. J. Hazard. Mater. 2009,162, 989-993.
34
[16] Gomes, H. I.; Dias-Ferreira, C.; Ribeiro, A. B. Electrokinetic remediation of organochlorines
35
in soil: Enhancement techniques and integration with other remediation technologies.
36
Chemosphere 2012, 87, 1077-1090.
37
[17] Zhu, N.; Luan, H.; Yuan, S.; Chen, J.; Wu, X.; Wang, L. Effective dechlorination of HCB by
38
nanoscale Cu/Fe particles. J. Hazard. Mater. 2010,176, 1101-1105. 19
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1
[18] Lundin, L.; Marklund, S. Thermal degradation of PCDD/F, PCB and HCB in municipal solid
2
waste ash. Chemosphere 2007, 67, 474-481.
3
[19] He, F.; Zhao, D. Y. Preparation and characterization of a new class of starch-stabilized
4
bimetallic nanoparticles for degradation of chlorinated hydrocarbons in water. Environ. Sci.
5
Technol. 2005, 39, 3314-3320.
6
[20] Zacheis, G. A.; Gray, K. A.; Kamat, P. V. Radiolytic reduction of hexachlorobenzene in
7
surfactant solutions: a steady-state and pulse radiolysis study. Environ. Sci. Technol. 2000, 34,
8
3401-3407.
9
[21] Bashkova, S.; Bagereev, A.; Bandosz, T. Adsorption of methyl mercaptan on activated
10
carbons. Environ. Sci. Technol. 2002, 36, 2777-2782.
11
[22] Lillo-Ródenasa, M. A.; Fletcher, A. J.; Thomas, K. M.; Cazorla-Amorós, D.; Linares-Solano,
12
A. Competitive adsorption of a benzene–toluene mixture on activated carbons at low
13
concentration. Carbon 2006, 44, 1455-1463.
14
[23] Wu, Z. X.; Zhao, D. Y. Ordered mesoporous materials as adsorbents. Chem. Commun. 2011,
15
47, 3332-3338.
16
[24] Zhai, Y. P.; Dou, Y. Q.; Liu, X. X.; Tu, B.; Zhao, D. Y. One-pot synthesis of magnetically
17
separable ordered mesoporous carbon. J. Mater. Chem. 2009, 19, 3292-3300.
18
[25] Wu, Z. X.; Webley, P. A.; Zhao, D. Y. Comprehensive study of pore evolution,
19
mesostructural stability, and simultaneous surface functionalization of ordered mesoporous carbon
20
(FDU-15) by wet oxidation as a promising adsorbent. Langmuir 2010, 26, 10277-10286.
21
[26] Luo W.; Wang Y. X.; Chou S. L.; Xu Y. F.; Li W.; Kong B.; Dou S. X.; Liu H. K.; Yang, J. P.
22
Critical Thickness of Phenolic Resin-Based Carbon Interfacial Layer for Improving Long Cycling
23
Stability of Silicon Nanoparticle Anodes. Nano Energy. 2016, 27, 255-264.
24
[27] Yang, J. P.; Wang, Y. X.; Chou, S. L.; Zhang, R. Y.; Xu, Y. F.; Fan, J. W.; Zhang, W. X.; Liu,
25
H. K.; Zhao, D. Y.; Dou. S. X. Yolk-shell silicon-mesoporous carbon anode with compact solid
26
electrolyte interphase film for superior lithium-ion batteries. Nano Energy 2015, 18, 133-142.
27
[28] Yang, J. P.; Chen, W. Y.; Shen, D. K.; Wei, Y.; Ran, X. Q.; Fan, J. W.; Zhang , W. X.; Zhao,
28
D. Y. Controllable fabrication of dendritic mesoporous silica-carbon nanospheres for anthracene
29
removal. J. Mater. Chem. A 2014, 2, 11045-11048.
30
[29] Asouhidou, D. D.; Triantafyllidis, K. S.; Lazaridis, N. K.; Matis, K. A.; Kim, S. S.; Pinnavaia,
31
T. J. Sorption of reactive dyes from aqueous solutions by ordered hexagonal and disordered
32
mesoporous carbons. Micropor. Mesopor. Mater. 2009, 117, 257-267.
33
[30] Kim, D. J.; Lee, H. I.; Yie, J. E.; Kim, S. J.; Kim, J. M. Ordered mesoporous carbons:
34
Implication of surface chemistry, pore structure and adsorption of methyl mercaptan. Carbon 2005,
35
43, 1868-1873.
36
[31] Deng, Y. H.; Qi, D. W.; Deng, C. H.; Zhang, X. M.; Zhao, D. Y. Superparamagnetic
37
high-magnetization microspheres with an Fe3O4@SiO2 core and perpendicularly aligned
38
mesoporous SiO2 shell for removal of microcystins. J. Am. Chem. Soc. 2008, 130, 28-29. 20
ACS Paragon Plus Environment
Page 20 of 29
Page 21 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
[32] Wang, T. B.; Liang, L.; Wang, R. W.; Jiang, Y. Q.; Lin, K. F.; Sun, J. M. Magnetic
2
mesoporous carbon for efficient removal of organic pollutants. Adsorption 2012, 18, 439-444.
3
[33] Nevskaia, D. M.; Lopez, E. C.; Munoz, V.; Guerrero-Ruiz, A. Adsorption of aromatic
4
compounds from water by treated carbon materials. Environ. Sci. Technol. 2004, 38, 5786-5796.
5
[34] Meng, Y.; Gu, D.; Zhang, F. Q.; Shi, Y. F.; Cheng, L.; Feng, D.; Wu, Z. X.; Chen, Z. X.;
6
Wan, Y.; Stein, A.; Zhao, D. Y. A family of highly ordered mesoporous polymer resin and carbon
7
structures from organic-organic self-assembly. Chem. Mater. 2006, 18, 4447-4464.
8
[35] Kauzmann, W. Some factors in the interpretation of protein denaturation. Adv. Protein. Chem.
9
1959, 14, 1-63.
10
[36] Wang, X.; Xing, B. Sorption of organic contaminants by biopolymer-derived chars. Environ
11
Sci Technol. 2007, 41, 8342-8348.
12
[37] Papageorgiou, S. K.; Katsaros, F. K.; Kouvelos, E. P.; Nolan, J. W.; Deit, H. L.;
13
Kanellopoulos, N. K. Heavy metal sorption by calcium alginate beads from Laminaria digitata. J.
14
Hazard. Mater. 2006, 137, 1765-1772.
15
[38] Freundlich, H. M. F., Die adsorption in lusungen. J. Phys. Chem. 1906, 57, 385-470.
16
[39] Shahryari, Z.; Goharrizi, A. S.; Azadi, M. Experimental study of methylene blue adsorption
17
from aqueous solutions onto carbon nanotubes. Int. J. Water Res. Environ. Eng. 2010, 2, 16-28.
18
[40] Gautham P. J., T. Prabhakar C. A modified Langmuir-Freundlich isotherm model for
19
simulating pH-dependent adsorption effects. J. Contam. Hydrol. 2012, 129-130, 46-53.
20
[41] Fujiwara, A.; Ishii, K; Suematsu, H.; Kataura, H.; Maniwa, Y.; Suzuki, S.; Achiba, Y. Gas
21
adsorption in the inside and outside of single-walled carbon nanotubes. Chem. Phys. Lett. 2001,
22
336, 205–211.
23
[42] Rowsell, J. L. C.; Yaghi, O. M. Effects of functionalization, catenation, and variation of the
24
metal oxide and organic linking units on the low-pressure hydrogen adsorption properties of
25
metal-organic frameworks. J. Am. Chem. Soc. 2006, 128, 1304-1315.
26
[43] Dinca, M.; Dailly, A.; Liu, Y.; Brown, C. M.; Neumann, D. A.; Long, J. R. Hydrogen storage
27
in a microporous metal-organic framework with exposed Mn2+ coordination sites. J. Am. Chem.
28
Soc. 2006, 128, 16876-16883.
29
[44] Hamdaoui O, Chiha M. Removal of methylene blue from aqueous solutions by wheat bran.
30
Acta Chim. Slov. 2007, 54, 407-418.
31
[45] Ho, Y. S.; Mckay, G. Pseudo-second order model for sorption processes. Process Biochem.
32 33
1999, 34, 451-465.
21
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1 2 3 4
Page 22 of 29
Table 1. Properties of the samples prepared at different pyrolysis temperature. SBET is the BET specific surface area; a0 is the unit-cell parameter; D is the pore diameter; T is the thickness of pore walls; VP is the total pore volume; qe is the adsorption capacity.
pyrolysis temperature
a
SBET
b
a0
c
D
d
T
e
Vp
q e
sample
(°C)
(m2/g)
(nm)
(nm)
(nm)
(cm3/g)
(µg/g)
OMC-350
350
364
10.85
3.82
7.03
0.23
594.18
OMC-600
600
596
10.00
2.65
7.35
0.31
875.78
OMC-900
900
888
9.27
2.61
6.66
0.47
992.09
5
a
6
b
7
c
8
d
9
e
Calculated by the BJH model from sorption data in a relative pressure range from 0.04 to 0.2. Calculated from SAXS results.
Calculated by the BJH model from the adsorption branches of the isotherms. Calculated by the formulas T= a0-D.
Estimated from the adsorbed amount at p/p0 of 0.995.
10 11 12 13 14 15
22
ACS Paragon Plus Environment
Page 23 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1
Table 2. Equilibrium and thermodynamics parameters for the adsorption of hexachlorobenzene
2
(HCB) by ordered mesoporous carbon (OMC-900).
Langmuir T
R2
°C
Feundlich Qm
a
R2
µg/g
L/µg
b
Sips b
kf
c
nf
R2
Qm
d
µg/g
L/µg
ks
e
ms
25
0.98
530.02
2.16
0.94
287.69
0.30
0.96
637.22
0.87
1.05
35
0.97
528.87
0.38
0.93
175.19
0.34
0.98
560.68
0.32
1.11
45
0.94
523.52
0.22
0.92
120.02
0.43
0.95
557.90
0.19
1.18
3
a
b is a Langmuir constant relating to the energy of adsorption for an adsorbent
4
b
kf is a Freundlich constant relating to the adsorption capacity
5
c
nf is an empirical parameter relating to the adsorption intensity
6
d
7
e
ks is a median association constant of Sips model
ms is a heterogeneity factor of Sips model
8 9
23
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1 2
3 4 5 6 7 8
Figure 1. Synthetic procedure of ordered carbonaceous materials (a). Small-angle X-ray scattering (SAXS) patterns (b), N2 adsorption-desorption isotherms (c), and the corresponding pore size distribution curves (d) of OMC-350, OMC-600, and OMC-900. The isotherms for OMC-600 and OMC-900 are offset vertically by 115 and 175 cm3/g, respectively.
9 10
24
ACS Paragon Plus Environment
Page 24 of 29
Page 25 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1 2 3 4
5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30
Figure 2. SEM (a-c) and TEM (d-f) images of ordered mesoporous carbonaceous materials: (a, d) OMC-350, (b, e) OMC-600, and (c, f) OMC-900.
25
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1 2 3
4 5 6
Figure 3. The 13C solid-state NMR (a) and the Fourier transform infrared spectra (b) of ordered mesoporous polymer (OMC-350) and ordered mesoporous carbon (OMC-900).
7 8 9 10 11 12 13 14 15 16 17 18 19 26
ACS Paragon Plus Environment
Page 26 of 29
Page 27 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1 2 3
4 5 6 7 8 9
Figure 4. (a) Removal percentage and adsorption amount of hexachlorobenzene (HCB) on the ordered mesoporous carbonaceous materials at different carbonization temperatures of 350, 600, and 900 °C (OMC-350, OMC-600, and OMC-900) and the commercial active carbon. The initial concentration of HCB is 200 µg/L. (b) the image of adsorption mechanism.
10 11 12 13 14 15 16 17 18 19 20 21 22 27
ACS Paragon Plus Environment
Langmuir
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
1 2
3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22
Figure 5. Adsorption isotherms of hexachlorobenzene (HCB) by using ordered mesoporous carbon material (OMC-900) as adsorbent in Milli-Q water at 25, 35 and 45 °C with experimental data (dots), Langmuir model curves (full line in (a)) and Freundlich model curves (full line in(b)). Hexachlorobenzene (HCB) adsorption isotherms (c) according to Sips model at 25, 35 and 45 °C. The adsorption capacity (d) of HCB versus contact time on OMC-900 with initial concentration of 200 µg/L in deionized water.
28
ACS Paragon Plus Environment
Page 28 of 29
Page 29 of 29
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Langmuir
1 2
TOC graphic
3 4 5 6 7 8 9 10 11 12 13 14
29