Organic Alkali Metal Salt Derived 3D N-Doped Porous Carbon/ CNTs Composites with Superior Li-S Battery Performance Zhenpu Shi, Yange Yang, Yan Huang, Hongyun Yue, Zhaoxia Cao, Hongyu Dong, Yanhong Yin, and Shu-Ting Yang ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.8b05305 • Publication Date (Web): 17 Jan 2019 Downloaded from http://pubs.acs.org on January 18, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 21 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Organic Alkali Metal Salt Derived 3D N-Doped Porous Carbon/CNTs Composites with Superior Li-S Battery Performance Zhenpu Shi 123﬩, Yange Yang 123﬩, Yan Huang 123, Hongyun Yue 123*, Zhaoxia Cao 123, Hongyu Dong 123, 1 2

Yanhong Yin 123and Shuting Yang 123*

College of Physics and Material Science, Henan Normal University, Xinxiang Henan 453007, China

National and Local joint Engineering Laboratory of Motive Power and Key Materials, Xinxiang Henan 453007, China; 3

Collaborative Innovation Center of Henan Province for Motive Power and Key Materials, Xinxiang Henan 453007, China) ﬩These

authors contributed equally to this work.

*E-mail: [email protected]; [email protected];

Abstract The organic alkali metal salt of sodium 4-(methylamino)butanoate has been synthesized and used as precursor for N-doped porous carbon/CNTs composite (NPC/CNTs). The cheap and easy obtained CNTs slurry and metal Na were used as raw materials. NPC provided polysulfides (LiPS) adsorption sites and CNTs constructed the conductive network. The obtained S/NPC/CNTs cathode material which has strong adsorption capacity and high conductivity restrained the shuttle effect to a large extent and enhanced the sulfur utilization, especially at high current density. The synergy of N doping, CNTs adding and mesopores existing enhanced the suppression of shuttle effects. When the S/NPC/CNTs material was used as cathode electrode for Li-S battery, a reversible capacity of 785 mA h g−1 was obtained after 500 cycles, with an average fading rate of 0.08% per cycle at the current density of 0.3 C. The S/NPC/CNTs material also showed superior rate performance, and the specific discharge capacity maintained at 880 mA h g−1 at 2 C rate. Moreover, the single layered pouch cell with a nominal capacity of 200 mA h was assembled and could discharge at a current of 38.6 mA stably. The S/NPC/CNTs cathode material is promising in application of Li-S battery. Keywords: Organic alkali metal salt; N-doped porous carbon; Interconnected CNTs; Sulfur host; LiS battery; Pouch Cell. Introduction

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 21

The increasing power sources demand for mobile electronic equipment has urged the exploration of advanced energy storage devices to replace the conventional lithium-ion batteries (LIBs). [1-3] Among various rechargeable battery systems, the high energy density lithium–sulfur (Li–S) batteries (2600 W h kg−1 in theory) have drawn considerable attention.

[4-6]

Moreover, the elemental sulfur cathode

express high theoretical specific capacity of 1675 mA h g−1, and material is natural abundance and low cost. Despite their great potential advantages, several technical challenges still need to be overcome before the large scale commercialization of Li–S batteries.

[7-9]

The so-called “shuttle effect” is the

major issue associated with Li–S batteries. During cycling processes, the soluble discharge intermediate products polysulfides (LiPS) migrate to the Li anode through the separator.

[10, 11]

The

diffusion and runoff of LiPS lead to low coulombic efficiency, poor cycling stability, and severe selfdischarge. Moreover, the insulated nature of elementary sulfur and its final discharge products (Li2S/Li2S2) blocks the electron transferring, which makes the interruption of the electrochemical reaction.

[12, 13]

In order to overcome the abovementioned challenges associated with Li–S batteries,

encapsulating sulfur into host materials, such as carbonaceous materials, [14, 15] conducting polymers, [16, 17] metal oxides or sulfide,[18] and metal or covalent organic frameworks, [19-21] has been used widely.

Carbonaceous materials are considered as most promising sulfur hosts materials, which can provide the electronic conductive network of sulfur based cathodes and immobilize LiPS.

[9, 22]

Carbon

nanotubes (CNTs) have been extensively used as the sulfur host because of the superior electronic conductivity and mechanical strength. [23, 24] However, the CNTs host with a low specific surface area (typically