Organometal Halide Perovskites as Visible-Light Sensitizers for

Apr 14, 2009 - Japan, Graduate School of Engineering, Toin UniVersity of Yokohama, and Peccell Technologies, Inc., 1614. Kurogane-cho, Aoba, Yokohama,...
0 downloads 0 Views 458KB Size
Published on Web 04/14/2009

Organometal Halide Perovskites as Visible-Light Sensitizers for Photovoltaic Cells Akihiro Kojima,† Kenjiro Teshima,‡ Yasuo Shirai,§ and Tsutomu Miyasaka*,†,‡,| Graduate School of Arts and Sciences, The UniVersity of Tokyo, 3-8-1 Komaba, Meguro-ku, Tokyo 153-8902, Japan, Graduate School of Engineering, Toin UniVersity of Yokohama, and Peccell Technologies, Inc., 1614 Kurogane-cho, Aoba, Yokohama, Kanagawa 225-8502, Japan, and Graduate School of Engineering, Tokyo Polytechnic UniVersity, 1583 Iiyama, Atsugi, Kanagawa 243-0297, Japan Received December 9, 2008; Revised Manuscript Received April 1, 2009; E-mail: [email protected]

Light-energy conversion by photoelectrochemical cells has been extensively studied in the past 50 years using various combinations of inorganic semiconductors and organic sensitizers.1 Dye-sensitized mesoscopic TiO2 films have been established as high-efficiency photoanodes for solar cells.2 As cost-effective devices, dyesensitized photovoltaic cells suit vacuum-free printing processes for cell fabrication; such processes enable researchers to design thin, flexible plastic cells by low-temperature TiO2 coating technology.3 With a thin photovoltaic film, optical management is an important key for harvesting light while ensuring high efficiency. Organic sensitizers often limit light-harvesting ability because of their low absorption coefficients and narrow absorption bands. To overcome this, researchers have examined quantum dots such as CdS,4a,b CdSe,4c-e PbS,4f,g InP,4h and InAs4i for photovoltaic cells in both electrochemical and solid-state structures. Intense bandgap light absorption by these inorganic sensitizers, however, has not allowed high performance in quantum conversion and photovoltaic generation; significant losses in light utilization and/or charge separation are found at the semiconductor-sensitizer interface. We have studied the photovoltaic function of the organic-inorganic lead halide perovskite compounds CH3NH3PbBr3 and CH3NH3PbI3 as visible-light sensitizers in photoelectrochemical cells. In addition to being synthesized from abundant sources (Pb, C, N, and halogen), these perovskite materials have unique optical properties,5 excitonic properties,6 and electrical conductivity.7 In this report, we show a photovoltaic function of the perovskite nanocrystalline particles selforganized on TiO2 as n-type semiconductors. Solar energy was converted with an efficiency of 3.8% on a CH3NH3PbI3-based cell, while a high photovoltage of 0.96 V was obtained with a CH3NH3PbBr3-based cell. Each photoelectrode was prepared on a fluorine-doped SnO2 transparent conductive glass (FTO, 10 Ω/sq, Nippon Sheet Glass) as a substrate, the surface of which had been pretreated by soaking in a 40 mM TiCl4 aqueous solution at 70 °C for 30 min to form a thin TiO2 buffer layer. A mesoporous film of TiO2 (n-type semiconductor) was prepared on the above-treated FTO by coating with a commercial nanocrystalline TiO2 paste (see the Supporting Information) using a screen printer and sintering at 480 °C for 1 h in air. The resultant TiO2 film had a thickness of 8-12 µm. Nanocrystalline particles of CH3NH3PbX3 (X ) Br, I) were deposited on the TiO2 surface by a self-organization process starting with the coating of a precursor solution containing stoichiometric amounts of CH3NH3X and PbX2. CH3NH3Br and CH3NH3I were synthesized from HBr and HI, respectively, by reaction with 40% †

The University of Tokyo. Peccell Technologies, Inc. Tokyo Polytechnic University. | Toin University of Yokohama. ‡ §

6050

9

J. AM. CHEM. SOC. 2009, 131, 6050–6051

methylamine in methanol solution followed by recrystallization. Synthesis of CH3NH3PbBr3 on the TiO2 surface was carried out by dropping onto the TiO2 film a 20 wt % precursor solution of CH3NH3Br and PbBr2 in N,N-dimethylformamide; subsequent film formation was done by spin-coating.8 For CH3NH3PbI3, an 8 wt % precursor solution of CH3NH3I and PbI2 in γ-butyrolactone was employed. The liquid precursor film coated on the TiO2 gradually changed color simultaneously with drying, indicating the formation of CH3NH3PbX3 in the solid state. A vivid color change from colorless to yellow occurred for CH3NH3PbBr3 and from yellowish to black for CH3NH3PbI3. X-ray diffraction analysis (Rigaku RINT2500) for CH3NH3PbBr3 and CH3NH3PbI3 prepared on TiO2 showed that both materials have crystalline structures that can be assigned to the perovskite form. CH3NH3PbBr3 gave diffraction peaks at 14.77, 20.97, 29.95, 42.9, and 45.74°, assigned as the (100), (110), (200), (220), and (300) planes, respectively, of a cubic perovskite structure with a lattice constant of 5.9 Å.9 CH3NH3PbI3 gave peaks at 14.00 and 28.36° for the (110) and (220) planes, respectively, of a tetragonal perovskite structure with a ) 8.855 Å and c ) 12.659 Å.9 Scanning electron microscopy (SEM) observation of the CH3NH3PbBr3-deposited TiO2 showed nanosized particles (2-3 nm) that existed here and there on the TiO2 and/or CH3NH3PbBr3 surface (Figure 1).

Figure 1. (a) Crystal structures of perovskite compounds. (b) SEM image of particles of nanocrystalline CH3NH3PbBr3 deposited on the TiO2 surface. The arrow indicates a particle, and the scale bar shows 10 nm.

A photovoltaic cell was constructed by combining the CH3NH3PbX3deposited TiO2 electrode (CH3NH3PbX3/TiO2) as the photoelectrode (anode) and a Pt-coated FTO glass as the counter electrode (cathode) with insertion of a 50 µm thick separator film. The gap between the electrodes was filled with an organic electrolyte solution containing lithium halide and halogen as a redox couple; the CH3NH3PbBr3/TiO2-based cell employed an electrolyte consisting of 0.4 M LiBr and 0.04 M Br2 dissolved in acetonitrile, while the CH3NH3PbI3/TiO2-based cell employed 0.15 M LiI and 0.075 M I2 dissolved in methoxyacetonitrile. A sandwich-type open cell had an effective light-exposure area of 0.238 cm2 with the use of a black mask. Incident photon-to-current quantum conversion efficiency (IPCE) and photocurrent-voltage (I-V) performance were measured on an action spectrum measurement setup (PEC-S20) and 10.1021/ja809598r CCC: $40.75  2009 American Chemical Society

COMMUNICATIONS

a solar simulator (PEC-L10, Peccell Technologies), respectively, the latter irradiating simulated sunlight of AM 1.5 and 100 mW/ cm2 intensity. Light irradiation of the photocells caused generation of anodic photocurrents with amplitudes of 5-11 mA/cm2. After optimization of the average TiO2 thickness for short-circuit photocurrent density (Jsc), the maximum Jsc occurred with 8 µm for CH3NH3PbI3/TiO2 and 12 µm for CH3NH3PbBr3/TiO2. Figure 2a compares action spectra of the IPCE for the photocells based on CH3NH3PbBr3/ TiO2 and CH3NH3PbI3/TiO2. With CH3NH3PbBr3/TiO2, the photocurrent occurred in the visible wavelength region (λ < 600 nm). The IPCE exhibited a sharp rise at ∼570 nm with saturation at