Parahydrogen-Induced Polarization Study of SilicaSupported Vanadium Oxo organometallic Catalyst Vladimir Valeryevich Zhivonitko, Ivan Vladimirovich Skovpin, Kai C. Szeto, Mostafa Taoufik, and Igor V. Koptyug J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.7b12069 • Publication Date (Web): 15 Feb 2018 Downloaded from http://pubs.acs.org on February 15, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry C is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Parahydrogen-Induced Polarization Study of SilicaSupported Vanadium Oxo Organometallic Catalyst Vladimir V. Zhivonitko,*,¶,†,‡, Ivan V. Skovpin,†,‡ Kai C. Szeto,§ Mostafa Taoufik § and Igor V. Koptyug†,‡ ¶

NMR Research Unit, University of Oulu, P.O.Box 3000, 90014 Oulu, Finland.

†

Laboratory of Magnetic Resonance Microimaging, International Tomography Center SB RAS,

Institutskaya St. 3A, 630090 Novosibirsk, Russia. E-mail: [email protected] ‡

Department of Natural Sciences, Novosibirsk State University, Pirogova St. 2, 630090

Novosibirsk, Russia. §

Laboratoire de Chimie, Catalyse, Polymères et Procédés, UMR 5265 CNRS/ESCPE-

Lyon/UCBL, ESCPE Lyon, F-308-43, Boulevard du 11 Novembre 1918, F-69616 Villeurbanne Cedex, France

ABSTRACT Parahydrogen can be used in catalytic hydrogenations to achieve substantial enhancement of NMR signals of the reaction products and in some cases of the reaction reagents as well. The corresponding nuclear spin hyperpolarization technique, known as parahydrogeninduced polarization (PHIP), has been applied to boost the sensitivity of NMR spectroscopy and MRI by several orders of magnitude. The catalyst properties are of paramount importance for

ACS Paragon Plus Environment

1

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 35

PHIP, since the addition of parahydrogen to a substrate must be pairwise. This requirement significantly narrows down the range of the applicable catalysts. Herein, we study an efficient silica-supported vanadium oxo organometallic complex (VCAT) in hydrogenation and dehydrogenation reactions in terms of efficient PHIP production. This is the first example of Group 5 catalyst used to produce PHIP. Hydrogenations of propene and propyne with parahydrogen over VCAT demonstrated production of hyperpolarized propane and propene, respectively. The achieved NMR signal enhancements were 200-300-fold in the case of propane and 1300-fold in the case of propene. Propane dehydrogenation in the presence of parahydrogen produced no hyperpolarized propane, but instead the hyperpolarized side product 1-butene was detected. Test experiments of other Group 5 (Ta) and Group 4 (Zr) catalysts showed a much lower efficiency in PHIP as compared to that of VCAT. The results prove the general conclusion that vanadium-based catalysts and other Group 4 and Group 5 catalysts can be used to produce PHIP. The hydrogenation/dehydrogenation processes, however, are accompanied by side reactions leading, for example, to C4, C2 and C1 side products. Some of the side products like 1butene and 2-butene were shown to appear hyperpolarized, demonstrating that the reaction mechanism includes pairwise parahydrogen addition in these cases as well.

INTRODUCTION Parahydrogen-induced polarization (PHIP) is a nuclear spin hyperpolarization technique based on the use of parahydrogen-enriched H2 (para-H2) in catalytic reactions.1-3 Upon hydrogenations with para-H2, strong NMR signals of specific shape amplified by several orders of magnitude can be observed, revealing the high nuclear spin hyperpolarization in the reaction products. The hyperpolarized products obtained this way can be used for substantial sensitivity boosting in


2

Page 3 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


NMR spectroscopy and MRI, which often suffer from an insufficient sensitivity. PHIP does not require remarkably sophisticated equipment necessary in other spin hyperpolarization methods like dynamic nuclear polarization (DNP).4 The efficiency of PHIP, however, crucially depends on the catalyst mediating para-H2 interaction with substrates. The para-H2 addition process must be pairwise, meaning that the two hydrogen atoms must follow each other throughout the catalytic cycle, and end up together in the same product molecule. The requirement of the pairwise mechanism, therefore, provides a unique type of labeling, which is sensitive to pairwise catalytic processes. It also sets, however, some limitations on the catalytic system if one wishes to get strong spin hyperpolarization by using PHIP. So far, the most efficient catalysts providing high contribution of pairwise mechanism are dissolved precious metal complexes, which are unfortunately difficult to rapidly separate from the hyperpolarized substances. As solid heterogeneous catalysts are easy to separate from reaction mixtures, heterogeneous hydrogenations using parahydrogen is considered as an efficient approach for producing pure hyperpolarized gases and liquids. For the last decade, many heterogeneous catalytic systems were found to produce PHIP in hydrogenations with parahydrogen.5-9 In most cases, the catalysts were based on the Group 8 metal nanoparticles10-12 or complexes supported on oxides.7-9,13 Metal nanoparticle based catalysts provided high stability but moderate enhancements, while immobilized complexes are typically unstable under reaction conditions.8,9 Vanadium-based catalysts are used in a number of important industrial processes.14-17 Recent developments led to a vanadium oxo organometallic complex supported on silica as a new efficient catalyst for non-oxidative dehydrogenation of propane (Scheme 1).18 This catalyst, designated in the text as VCAT, demonstrates high activity, selectivity and stability, and it is well characterized under propane dehydrogenation reaction conditions. On the other hand,


3


Page 4 of 35

VCAT can be potentially used in hydrogenation reactions, because hydrogenation reaction is the reverse of dehydrogenation and, thus, it can be catalyzed by the same catalyst. In principle, sequential dehydrogenation-hydrogenation can also lead to the spin hyperpolarization if para-H2 addition proceeds in a pairwise manner, as was reported previously.8,11,19,20 This route of production of hyperpolarized substances is referred to in the literature as “pairwise replacement”.19,20 Thus, propane dehydrogenation over VCAT may produce hyperpolarized propane. Thus, both hydrogenation and dehydrogenation using VCAT in the presence of para-H2 are of great interest to explore. At the same time, observation of hyperpolarization effects can provide important mechanistic information about these chemical reactions catalyzed by VCAT. Scheme 1. VCAT structure.

Herein, we show that surface-grafted vanadium complex VCAT can provide hyperpolarized compounds in hydrogenations with parahydrogen. In particular, it is shown that in spite of a relatively low activity, this catalyst demonstrates high stability over long reaction runs, providing continuous production of hyperpolarized propane in propene hydrogenation with parahydrogen. It is demonstrated that the production of hyperpolarized propane takes place over a wide range of temperatures (250-500 ºC). On the other hand, propane dehydrogenation in the presence of paraH2 led to observation of hyperpolarization effects for the side product 1-butene, whereas propane itself remained not polarized, implying that H2 pairwise replacement process is likely inefficient. It is shown that in comparison to several other surface-grafted complexes of Group 5 and 4 metals (Ta- and Zr-based complexes), VCAT catalyst demonstrates higher activity and efficiency


4

Page 5 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


in the production of hyperpolarized substances. It was demonstrated that the catalytic activity of VCAT catalyst in hydrogenations is the highest among the examined catalysts. In contrast to Group 5 catalysts (VCAT and Ta-based one), Group 4 catalysts (Zr-based) were more active at low temperatures (below 0 ºC), but their activity was still low. EXPERIMENTAL Catalysts VCAT catalyst was prepared by the synthetic procedure described elsewhere.18 Prior to grafting reactions, the molecular precursor [V(=O)(Mes)3] was synthesized in two steps.21,22 A mixture of the molecular complex (300 mg, 0.70 mmol) and the support SiO2-(700) (2 g) in pentane (10 mL) was stirred at 25 °C for 2 hours. After filtration, the solid, VCAT, was washed 5 times with pentane. The resulting red powder was dried under vacuum (10-5 Torr). FTIR, UVVis and solid state NMR (1H and 13C) spectra (Figures S6-S8) as well as the metal loading of 1.4 wt% determined by elemental analysis were in agreement with literature data.18 In addition, several other Group 4 and 5 catalysts presented in Table 1 were tested. These catalysts were synthesized according to the methods described in Ref. [23]. All catalyst treatments were performed under Ar atmosphere. Table 1. Labels and structures of other studied Group 4 and 5 complexes. Label

Formula

TaCAT

Ta(H)3(SiO2)n

Structure

SiO2-Al2O3-500


5


ZrCAT

Page 6 of 35

Zr(CH2tBu)3(SiO2)n SiO2-700

PHIP experiments The parahydrogen-enriched H2 was produced using Bruker parahydrogen generator BPHG-90 (the actual parahydrogen content in H2 was ca. 80-90 %). This gas is referred to as para-H2 in the text. NMR experiments were performed on a Bruker AV-300 spectrometer operating at 300 MHz 1

H resonance frequency.

In most cases, investigated hydrogenation and dehydrogenation reactions in the presence of paraH2 were carried out in a quartz reactor operating in the temperature range from 25 to 650 oC outside the NMR magnet (Figure 1, right branch). The gas mixture after the reactor was flowing through a capillary into a 10 mm NMR tube inside the NMR magnet to acquire 1H NMR spectra. This experimental procedure involving adiabatic transfer of the products of reaction with para-H2 from low to high magnetic fields leads to the so-called ALTADENA24 effect. In a common run, 3-5 mg of catalyst packed in the reactor were used. The gas flow rate through the reactor was 2.1 or 4.1 scc/s.


6

Page 7 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 1. Experimental setup and procedure. The reagent gas flow controlled by a flowmeter was supplied either to the packed bed reactor outside and then to the empty sample tube inside the NMR magnet (right branch, ALTADENA experiment), or directly into the sample tube with catalyst inside the NMR magnet (left branch, PASADENA experiment). In selected experiments when heating to high temperatures was not required, the reactions with para-H2 were performed inside the NMR magnet in a 10 mm tube containing 3-5 mg of catalyst (Figure 1, left branch). The NMR spectra were acquired during the reaction. The gaseous reagents were passed through the catalyst layer at the bottom of the tube using a 1/16’’ Teflon capillary with the flow rate of 2.1 scc/s in the temperature range from –20 to +130 oC. As products were formed in the high magnetic field, the so-called PASADENA1 hyperpolarization effect was observed in this case.


7


Page 8 of 35

In propene hydrogenation with VCAT, several gas mixtures of differing propene/para-H2 ratios were used in the experiments: 1/3, 1/4 and 1/6. In the experiments with other substrates (propane, propyne, 1,3-butadiene, 1-butyne) and other catalysts (Table 1), the substrate/para-H2 ratio was 1/4. RESULTS To the best of our knowledge, neither Group 4 nor Group 5 heterogeneous catalysts are presented in the literature in the context of PHIP studies. Herein, main results are obtained for the vanadium VCAT catalyst (Scheme 1). For comparison, other Group 5 and additionally Group 4 catalysts were tested in hydrogenations with para-H2, see Table 1 and Supporting Information. Thus, the following discussion of the results is divided into two parts describing VCAT results first and comparing it to other catalysts, respectively. VCAT catalyst Propene hydrogenation 1

H NMR spectra acquired for propene hydrogenation catalyzed by VCAT catalyst at 350 oC are

shown in Figure 2. The use of para-H2 as a reagent led to the enhanced NMR signals of the product propane molecules when gas mixture was flowing through the catalyst at 4.1 scc/s, Figure 2a. The signals appeared in the form of two multiplets of opposite signs; negative sign (emission) for methyl group and positive sign (absorption) for methylene group. For comparison, the spectrum representing thermally polarized signals acquired after an abrupt termination of gas flow followed by a 5 s relaxation delay is shown in Figure 2b. The signal enhancements can be seen clearly from the comparison to the thermal 1H NMR spectrum. The observation of the


8

Page 9 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


enhanced signals provides an additional insight into the mechanism of hydrogenation over VCAT catalyst since hyperpolarized signals indicate the addition of para-H2 molecules to propene in a pairwise manner. The contribution of pairwise mechanism to the overall propene hydrogenation process was estimated from the observed enhancements as 1-2 %. We should note, however, that this estimate constitutes a lower bound because nuclear spin relaxation processes decreasing originally produced hyperpolarization were not taken into account.

Figure 2. 1H NMR spectra of the gaseous reaction mixture from propene hydrogenation catalyzed by VCAT. Spectrum (a) was detected while the propane was produced in the reactor at 350 oC and the reagent gas flow rate of 4.1 scc/s and the mixture was flowing through the sample tube, whereas spectrum (b) was detected 5 seconds after the gas flow was abruptly stopped. The initial propene/para-H2 ratio in the reagent gas mixture was equal to 1/4. It should be noted that some less pronounced PHIP effects in the NMR spectra were also evident for reagent propene molecules. Indeed, the ratios of the amplitudes of H1b and H1c signals to the amplitude of H1a signal in Figure 2a reveal a significant difference compared to the corresponding ratios in the spectrum of thermally polarized propene in Figure 2b. H1b and H1c signals have much lower intensity in comparison to H1a signal in the former case. This observation indicates that in addition to propene hydrogenation the replacement of two vicinal


9


Page 10 of 35

hydrogens in the reagent propene molecules by hydrogens of a para-H2 molecule takes place. It also gives a new insight to the mechanism of propene hydrogenation over VCAT and side processes accompanying it. Such pairwise replacement in propene molecules was reported earlier with Rh, Pt and Ir metal nanoparticles,8,19 and possible mechanisms leading to this effect are discussed in the literature.19 The hyperpolarization levels were somewhat dependent on the composition of the reagent gas mixture, with higher content of parahydrogen providing on average slightly higher hyperpolarization levels, Figure 3. This was likely influenced by the conversion between para-H2 and ortho-H2 accompanying the hydrogenation over VCAT. The higher concentration of para-H2 resulted in higher probability that parahydrogen is added to propene before it is converted to orthohydrogen. The higher flow rates on average also resulted in higher detected hyperpolarization as the influence of the nuclear relaxation during the gas transport is reduced, Figure 3b and 3c.


10

Page 11 of 35

Enhancement factor

(c)

propene/para-H2 = 1/6 450 400 350 300 250 200 150 100 50 0 250

300

350 400 Temperature, oC

2.1 scc/s

Enhancement factor

(b)

450

500

450

500

450

500

4.1 scc/s

propene/para-H2 = 1/4 300 250 200 150 100 50 0 250

300


2.1 scc/s

(a) Enhancement factor

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


4.1 scc/s

propene/para-H2 = 1/3 200 150 100 50 0 250

300

350 400 Temperature, oC 2.1 scc/s

Figure 3. 1H NMR signal enhancements measured as a function of the reactor temperature for hyperpolarized propane produced in propene hydrogenation with para-H2 over VCAT. Average enhancement values over CH2 and CH3 groups are presented. The bar charts shown in (a), (b) and (c) correspond to the reagent mixtures with 1/3, 1/4 and 1/6 propene/para-H2 ratios, respectively. The reagent gas flow rates in the reactor are indicated in the legends. We note that catalytic activity of VCAT in propene hydrogenation was evident clearly at 250 oC and higher temperatures. In the activity tests, the temperature was increased stepwise from 50 to 500 oC under continuous flow of reagent gas mixtures having propene/para-H2 ratio of 1/4 and


11


1/6 (Figure 4). Experiments were also done with the mixture of 1/3 propene/para-H2 ratio, but conversion of propene was hard to quantify precisely in this case (below 1 %). The initial activity increased slightly in time over the period of ca. 2 h at the elevated temperature of 500 oC and reached some constant value, which was in accord with previous observations in the study of catalytic performance over this catalyst in propane dehydrogenation.18 For a stability check, the temperature was decreased from 500 to 300 oC, and then gradually increased to 500 oC again. The catalytic activity was preserved on the same level, which confirmed the thermal stability of the catalyst after a 2 h activation treatment. In the course of the activation, the color of the catalyst changed from orange to black.

(b) Propene conversion, %

propene/para-H2 = 1/6 10 9 8 7 6 5 4 3 2 1 0 250

(a)

300

350 400 Temperature, oC 2.1 scc/s 4.1 ssc/s

450

500

450

500

propene/para-H2 = 1/4 Propene conversion, %

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 35

8 7 6 5 4 3 2 1 0 250

300


2.1 scc/s

4.1 scc/s

Figure 4. Propene conversion as a function of temperature in propene hydrogenation over VCAT. The results are shown for the reagent gas mixtures of (a) 1/4 and (b) 1/6 propene/p-H2 ratios, and two different gas flow rates (2.1 and 4.1 scc/s).


12

Page 13 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Importantly, PHIP signal amplitudes changed accordingly with the changes of the temperature described above: the higher the yield, the stronger the signal from the hyperpolarized propane. This means that the hyperpolarization degree was not significantly dependent on the temperature, and the signal intensity was determined majorly by the number of produced molecules. The observation serves as an extra evidence of the active center stability under reaction conditions. In the vast majority of cases, immobilized complexes are unstable at such high temperatures,8,9 which is clear from irreversible changes of hyperpolarization degree of the products. Our experience in the field tells that Group 8 metal complexes (Rh, Ir, Pd) tend to degrade rapidly under propene hydrogenation conditions above 150 oC with the formation of metal nanoparticles, while VCAT demonstrates high stability even at 500 oC. These results suggest that vanadium species have been transformed to tripodal V(III) (Scheme S1 in Supporting Information) upon the heat treatment, because such isolated species are expected to be stable similarly to unsaturated tripodal tantanlum surface species.25 Furthermore, they can easily conduct oxidative addition of H2 molecules (Scheme S2). The catalytic cycle is completed after an insertion of propene into the resulting H-V-H center followed by the reductive elimination of propane. The propane molecule should be hyperpolarized in this case as the hydrogenation is pairwise (see Scheme S2 in Supporting Information). Recently, a similar vanadium complex (VIII(Mes)3·THF) has been grafted onto silica and investigated in alkene and alkyne hydrogenations.26 This bipodal vanadium complex was catalytically active in 1-octene hydrogenation at 70 °C and diphenyl acetylene at 100 °C. The mechanism of these reactions was proposed to be either oxidative addition/reductive elimination or heterolytic activation. However, no direct evidence was given. For VCAT at relatively low temperature (< 250 °C), no significant hyperpolarization was observed, while the catalytic activity was low. This result may indicate that at the low


13


Page 14 of 35

temperatures VCAT can undergo a transfer of hydride to the support,25 giving a bipodal vanadium(V) oxo species (Scheme S1) which can complete the catalytic cycle only by nonpairwise heterolytic activation (Scheme S3). We note, however, that the formation of the tripodal V(III) at high temperatures is a tentative conclusion based on the literature data and our experience with Group 5 catalysts. More data about the nature of the active species can be obtained by using a combination of ex-situ, in-situ and operando characterization methods, which will be addressed in our future study of VCAT. Such experiments are beyond the scope of this paper, which describes mostly the observation of hyperpolarization effects with this catalyst. Finally, we can conclude that the 1H NMR signal enhancements observed for propane in the propene hydrogenation with parahydrogen are on the order of 100-300-fold depending on the experimental conditions (Figure 3). These numbers are lower than the theoretically expected ones (ca. 104-fold at 7 T), but they do demonstrate that orders of magnitude signal enhancements are possible with VCAT. As mentioned above, the enhancements can be converted into the fractions of pairwise addition in the overall hydrogenation process, which constitute the lowest values possible, providing the fraction of pairwise addition on the order of 1-2 %. The nuclear relaxation processes in this case may lead to a severe underestimation of the pairwise addition fractions, especially considering that vanadium center is paramagnetic in certain oxidation states. The paramagnetic relaxation can significantly accelerate the nuclear spin relaxation, leading to quenching of hyperpolarization. In the case of VCAT, however, this process seems to be not extremely fast as to prevent an observation of substantial nuclear hyperpolarization in propene hydrogenation. Propane dehydrogenation


14

Page 15 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Propane dehydrogenation over VCAT was carried out using propane/para-H2 mixture with the ratio of the reagents equal to 1/4. In principle, dehydrogenation in the presence of para-H2 molecules may result in hyperpolarized products if pairwise hydrogen replacement or dehydrogenation followed by rehydrogenation take place.11,19,20 Formally, these processes can lead to hyperpolarized propane or propene as represented in Scheme 2. Scheme 2. A formal mechanism of pairwise replacement leading to the formation of hyperpolarized propane.

In our experiments, signals of hyperpolarized products at 4.7 and 5.7 ppm in 1H NMR spectra were initially detected upon heating to 400 oC when the reaction mixture was passed through VCAT layer at the flow rate of 2.1 scc/s (Figure 5). These signals were also observed at 450, 500 and 550 oC at the same flow rate. As it was determined from a thorough analysis of the NMR spectra, these signals correspond to hyperpolarized 1-butene, namely to the CH (5.7 ppm) and CH2 (4.7 ppm) groups of its vinyl fragment. This was an interesting and unexpected result indicating that complex side processes take place during interaction of propane molecules with VCAT in the presence of para-H2. The NMR spectra show also the presence of ethylene along with 1-butene in the temperature range 400-550 oC. The formation of the C2 and C4 reaction products from C3 propane molecules on VCAT under these conditions implies likely that the reaction mechanism includes a C-C coupling step resulting in C6 chain which in turn is split into C2 and C4 parts. Alternatively, the C4 and C2 hydrocarbons could be formed as a result of metathesis of two propene molecules. At the same time, no signals of 1-butene were detected in


15


Page 16 of 35

the 1H NMR spectra of reaction mixture if reaction was carried out at 600 and 650 oC. Moreover, at these high temperatures, propene was the main reaction product, while ethylene and methane were detected as side-products (Figure 5e and 5f). At these temperatures the thermodynamics is favorable for the formation of propene, while formation of C1 methane and C2 ethylene is the result of propane molecule splitting. The change in the catalytic behavior of VCAT with the temperature was also apparent from the propane conversion, which for the mixture flowing at 2.1 scc/s increased as follows: 1-2 % at 400 oC, 9% at 600 oC and 14% at 650 oC. It should be noted that after cooling down the reactor from 650 oC to 450 oC the formation of hyperpolarized 1butene as well as ethylene was again observed, implying that the catalyst was stable under applied high temperature conditions.


16

Page 17 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 5. 1H NMR spectra of reaction mixture formed in propane dehydrogenation on VCAT when propane/para-H2 (1/4) gas mixture was passed through reactor at different rector temperatures of (a) 400, (b) 450, (c) 500, (d) 550, (e) 600 and (f) 650 oC. It should be noted that the observed hyperpolarization of 1-butene protons at the double carboncarbon bond, H5a and H5b, is rather unexpected because we would instead expect to see hyperpolarization of propane or propene as represented in Scheme 2. The mechanism of hyperpolarized 1-butene formation is unclear, but undoubtedly it includes pairwise addition of two hydrogen atoms originating from one para-H2, which is evidenced by the observation of PHIP signals itself. It is possible that the dehydrogenation goes deeper, and a triple carboncarbon bound is formed, which is then hydrogenated with para-H2. Indeed, in the tests with 1butyne hydrogenation catalyzed by VCAT at 500 oC it was shown that hyperpolarized 1-butene can be formed from 1-butyne and para-H2 (see Figure S1 in Supporting Information). However, in this case the enhanced hyperpolarization signals are observed for all hydrogens at 1-butene double bond, whereas in propane dehydrogenation only H5a and H5b hydrogens got hyperpolarized (Figure 5a). This test indicates that there are likely some differences in the mechanisms of formation of hyperpolarized 1-butene in the propene dehydrogenation and in the 1-butyne hydrogenation. The NMR signal enhancement for H5a hydrogen of 1-butene was about 25 in the propane dehydrogenation, which was determined by comparing the amplitudes of the hyperpolarized and thermal signals (see Figure S2 in Supporting Information). This value corresponds to less than 1 % fraction of the pairwise addition, meaning that the pairwise replacement of hydrogens is not very efficient in the complex process of 1-butene formation from propane, which must include also processes such as oligomerization or metathesis. In our previous study, we have


17


Page 18 of 35

demonstrated the possibility to observe PHIP for C4 oligomerization products during acetylene hydrogenation with para-H2 over palladium nanoparticles,11 wherein the signal enhancements generated for H2a of 1-butene molecule were an order of magnitude higher than the value observed for the same product produced over VCAT in propane dehydrogenation in this work. Additionally, in case of VCAT, PHIP was observed only for hydrogens H5a and H5b but not for H5c (i.e., for the pair of protons cis to each other with respect to the double bond), whereas there was no such selectivity in the case of Pd nanoparticles. Apparently, the pathways of C4 product formation and hyperpolarization significantly differ for these catalytic systems. In contrast, propane signals didn’t reveal any noticeable hyperpolarization under propane dehydrogenation conditions, implying that pairwise hydrogen replacement process19 drawn in Scheme 2 for propane is not efficient. However, one should consider that the polarized signals of propane could be possibly masked by the strong signals of thermally polarized propane. The inefficiency of pairwise hydrogen replacement in propane is in accord with previously reported tests performed using Pt and Ir nanoparticles as catalysts.19 Propyne hydrogenation A significant hyperpolarization of propene was observed in the hydrogenation of propyne with para-H2 over VCAT, Figure 6.


18

Page 19 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 6. 1H NMR spectra of the reaction mixture produced in propyne hydrogenation with para-H2 over VCAT at 500 oC. Spectrum (a) was detected in the continuous flow mode using a single scan, whereas (b) is detected using 256 scan accumulations after the flow was abruptly stopped. The reagent mixture of 1/4 propyne/para-H2 ratio was used, which was supplied to the reactor at the flow rate of 2.1 scc/s. The measured NMR signal enhancement for proton H1a of produced propene is ca. 1300, which is an order of magnitude higher compared to that observed for methyl and methylene groups of propane in propene hydrogenation. In contrast to propene hydrogenation, however, VCAT was much less active in propyne hydrogenation, providing typical reaction yields of less than 1 % under similar experimental conditions. Moreover, the higher temperatures around 500 oC were required to observe detectable signals of the hyperpolarized propene. In addition to propene, hyperpolarized 2-butene was visible in the 1H NMR spectra acquired from the reaction mixture in continuous reaction mode (Figure 6a). Moreover, thermally polarized ethylene was also detected (Figure 6b). Such observations imply that like in propane


19


Page 20 of 35

dehydrogenation the side reactions leading to the C4 and C2 hydrocarbons took place, meaning that in propyne hydrogenation over VCAT catalyst is accompanied either by oligomerization and hydrogenolysis processes or metathesis, since the initial feed contained only the C3 hydrocarbon. Since the high temperatures were used, to verify that the hyperpolarized butene and propene were produced because of reaction on VCAT, but not due to pyrolysis, we performed test experiments with no catalyst loaded in the reactor, but otherwise under the same reaction conditions (same temperatures and flow rates). No hyperpolarized/thermally polarized butene or propene products were detected at the same level of accuracy, implying that the catalytic action of VCAT was the source of the hyperpolarized substances. Other Group 4 and 5 catalysts Some selected catalysts based on immobilized complexes of other Group 4 and Group 5 elements were tested in hydrogenation reactions with para-H2. The structures of the catalysts are shown in Table 1. Tantalum belongs to the same group as vanadium. Immobilized TaCAT complex was studied in the hydrogenation of propene in the temperature range of 25-400 oC. The complex was found to become active at 200 oC in propene hydrogenation with parahydrogen. Moreover, the formation of hyperpolarized propane was detected at this temperature by acquiring 1H NMR spectra of the flowing reaction mixture in the ALTADENA-type experiments (see Figure S3, Supporting Information). The signals of the hyperpolarized propane were also detected when the reaction was carried out at 250-400 oC. The measured signal enhancement factors and propene conversion data are presented in Figure 7.


20

Page 21 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 7. Enhancement factors and propene conversions obtained in propene hydrogenation with para-H2 over TaCAT in the temperature range of 200-400 oC. The gas reagent flow rate was 2.1 scc/s. The enhancement factors are calculated for protons of CH3 group of propane. It can be seen that the signal enhancement factors varied in the range of 70-90, which means that the enhancement was practically constant in the examined temperature range. The conversion, however, changed significantly with the highest value at 200-250 oC (4 %) and the lowest value at 350-400 oC (1 %). Thus, TaCAT produced lower levels of hyperpolarization (Scheme S4 in Supporting Information), but comparable reaction yields as compared to the data for VCAT catalyst (Figures 3 and 4). The decrease in activity at the high temperatures is likely due to partial transformation of bipodal monohydride Ta-H species to tripodal Ta species,25 which are inactive in hydrogenations (Scheme S5 in Supporting Information). ZrCAT immobilized complex was used as an example of Group 4 based catalyst in propene hydrogenation with para-H2. This complex became active at 150 oC reaction temperature, and hyperpolarized propane was detected in 1H NMR spectra of the reaction mixture under continuous flow conditions (Figure S4 in Supporting Information). It was found that temperature increase to 300-500 oC leads to decrease in the hyperpolarization of propane and deactivation of the catalyst. The signal enhancement factor measured for the hyperpolarized propane was 20 at


21


Page 22 of 35

150 oC and 6 at 300 oC. At the same time, no propane signals were detected at 400 oC or higher. This observation likely indicates a restructuring of the surface species (Scheme S6 in Supporting Information). The hyperpolarization is likely produced by bipodal zirconium bis-hydride species (Scheme S7). The number of such species declines with the temperature due to a gradual transformation to tripodal zirconium monohydride. The mechanism of the hydrogenation reaction with the latter species is such that the hydrogen insertion cannot be pairwise, (Scheme S8) and consequently no hyperpolarization of propane is expected. At the higher temperature (400 °C), the zirconium completely transforms to tetrapodal species without any possibility to insert propene. It should be noted that in addition to propane, hyperpolarized 1-butene was formed at 300-350 oC over ZrCAT. However, temperature increase led to vanishing of 1-butene at 400 oC as well from the reaction mixture. The enhancement factor for 1-butene 1H NMR signal was likely very high, since corresponding thermal signals were not observed after 128 accumulations when the reaction mixture flow was stopped. We note also that thermally polarized 1,3-butadiene was detected in 1H NMR spectrum of the reaction mixture when the flow was stopped (Figure S4b* in Supporting Information). The observation of 1,3-butadiene suggests that the hyperpolarized 1butene produced in continuous flow conditions could be formed by hydrogenation of 1,3butadiene, which is initially generated by the reaction of propene with ZrCAT catalyst. This assumption is supported by the production of hyperpolarized 1-butene with a similar 1H NMR signal shape to that detected in propene hydrogenation when 1,3-butadiene hydrogenation with para-H2 was tested at 300 oC with the same catalyst (Figure S5 in Supporting Information). DISCUSSION


22

Page 23 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


The observation of PHIP effects demonstrated in this work for the hydrogenations of propene, propyne and 1-butyne with para-H2 over VCAT constitutes a solid evidence for the presence of pairwise addition mechanistic pathways in these reactions. This is an important feature of VCAT, making vanadium based catalysts worth considering for an efficient production of hyperpolarized substances. It is also interesting in terms of understanding of the mechanistic aspects of hydrogenation catalyzed by the complex. Basically, two ways of para-H2 activation can lead to the pairwise addition and eventually to the formation of the spin hyperpolarization. In the first case, the hydrogenation proceeds through the oxidative addition of para-H2.27 This way is well exemplified by the formation of dihydride compounds from transition metal complexes and para-H2 molecules in homogeneous hydrogenations. In the second case, the reaction proceeds through a heterolytic activation of molecular hydrogen, meaning that the charge separation occurs under para-H2 activation.6,28 This way is characteristic, for instance, for oxidebased catalytic systems like activated ZnO,29 in which one of the hydrogen atoms from para-H2 molecule goes to the metal ion whereas another goes to the oxygen. The presence of PHIP on propane produced from propene and para-H2 may be the result of any of these two mechanistic pathways as soon as vanadium center can interact to form a dihydride complex, and also this center contains oxygen as a ligand which may facilitate the heterolytic activation. It is worth to note that to produce hyperpolarized propane efficiently in propene hydrogenation with para-H2, the time scale of transfer of the two hydrogens to the substrate should be relatively fast compared to the lifetime of the hyperpolarization. In other words, the transfer time should be preferably much shorter than the time during which the hyperpolarization is destroyed. Depending on conditions, the NMR signal enhancements observed for CH2 and CH3 groups of propane produced over VCAT varied in the range of 100-350-fold. The reaction temperature had


23


Page 24 of 35

only a weak effect on the enhancement factors (Figure 3). This observation indicates that the reaction step responsible for the transfer of para-H2 to the substrate is not the rate-limiting one, or it is rate-limiting but always much faster than the nuclear spin relaxation. We note also that the amplitude of ortho-H2 signal visible in the NMR spectra was relatively low and temperature independent in the studied hydrogenations over VCAT, indicating the absence of a fast orthopara conversion process in the studied temperature range and implying that the addition of H2 to VCAT is likely an irreversible step. In addition, mechanistic aspects of propene hydrogenation over VCAT are reflected by the observed weak hyperpolarization of H1a, H1b and H1c hydrogens of propene when it was hydrogenated to propane with para-H2 (Figure 2). This observation most likely indicates the presence of side reactions leading to pairwise replacement of pairs of hydrogens at the double bond in propene with the ones originating from para-H2. Such processes were observed in several studies with supported Rh, Pt and Pd metal catalysts and in situ reduced immobilized complexes.8,11,19,20 On the other hand, we cannot entirely exclude the polarization transfer from para-H2 to the catalyst-bound propene on the catalytic center which may also occur as the reaction was performed at the low magnetic field, i.e., under conditions which are known to lead to a SABRE effect.30 Based on the enhancement factors, the contribution of pairwise addition of para-H2 to propene in the overall hydrogenation process catalyzed by VCAT is around 1-2%. This value is the lower limit estimate of the contribution, because relaxation of the hyperpolarization is hard to account for correctly in the evaluation, and the actual value of the pairwise contribution can be significantly higher. This estimated value is comparable to those observed in propene hydrogenation over immobilized Vaska’s complex and the immobilized Wilkinson’s complex


24

Page 25 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


reduced in situ.7-9 VCAT, however, has the highest stability compared to the Rh and Ir immobilized complexes. Supported Pt and Rh metal catalysts also provide comparable values of the pairwise addition in propene hydrogenation with para-H2.5 As was discussed above, the NMR signal enhancements are practically unchanged in the temperature range 250-500 oC, meaning that the temperature does not significantly influence the contribution of pairwise addition to the overall propene hydrogenation over VCAT. On the other hand, the temperature had an effect on the propene conversion. In particular, it can be seen that largest propene conversions of 7 % and 9 % at 2.1 scc/s flow rate were observed at 250 oC for 1/4 and 1/6 propene/para-H2 mixtures, respectively. At the same time, the propene conversion rapidly drops with increasing temperature, and at 500 oC the conversion didn’t exceed 3 % for both mixtures. This observation most likely spotlights the shift of thermodynamic equilibrium to the formation of propene and H2 at such a high temperature due to the exothermic nature of the hydrogenation reaction, when hydrogenation is no longer favorable. We should note that other immobilized complexes of Group 4 and 5 elements (Ta and Zr) studied in this work have shown only weak activity in propene hydrogenation. Some promising conversion of propene to hyperpolarized propane was obtained with TaCAT, but the NMR signal enhancement of the product was several times lower as compared to what was observed with VCAT. The hyperpolarization of propane produced with ZrCAT was in turn several times lower than for TaCAT. Therefore, among all studied catalysts VCAT was the best catalyst to produce hyperpolarized propane, which also demonstrated a noticeable stability over long reaction runs. Interestingly, switching the substrate hydrogenated with para-H2 from propene to propyne had a significant effect on both the observed NMR signal enhancement of the reaction product,


25


Page 26 of 35

propene, and the catalytic activity of VCAT. A dramatically increased signal enhancement observed for the product molecules of 1300-1500-fold was recorded, which is almost an order of magnitude larger value as compared to the signal enhancement for propane in propene hydrogenation with para-H2. These values correspond to at least 10-12 % of pairwise addition. Thus, the contribution of pairwise addition to the overall hydrogenation of propyne over VCAT is significant, especially if we take into account the effects of relaxation processes leading to underestimation of the fraction of pairwise addition. The significant difference in the NMR signal enhancements observed in the hydrogenations of propene and propyne indicates a significant difference in hydrogenation mechanisms for these substrates. A detailed elucidation of these differences is currently not possible as it requires sophisticated in situ VCAT studies not accessible at the current state-of-the-art, and this is beyond the scope of this article. We note, however, that such a significant enhancement considerably distinguishes this complex from previously studied heterogeneous catalysts. Indeed, hydrogenation on supported metal catalysts or oxides usually provides NMR signal enhancements between 100-200, while the use of immobilized Ir catalysts makes it possible to obtain enhancements of about 500-700-fold under similar experimental conditions.5,6 Catalytic activity of VCAT in propyne hydrogenation was much lower as compared to that in propene hydrogenation with VCAT catalyst. Propyne conversion was less than 1 % in the temperature range from 250-500 oC. Indeed, in propyne hydrogenation, reliably detectable NMR signals of thermally polarized propene after an abrupt stop of the reaction mixture flow were acquired upon heating up to 500 oC after extensive scan accumulations, whereas in propene hydrogenation under the similar reaction conditions propane was easily detected with a single scan.


26

Page 27 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


The propane dehydrogenation over VCAT in the presence of para-H2 didn’t lead to a production of hyperpolarized propane. This initial expectation was based on the idea that pairwise replacement may be an efficient process taking place on the catalyst as shown in Scheme 2. Instead, we detected hyperpolarized 1-butene produced because of side processes taking place during the activation of propane molecules in the presence of para-H2. In addition to 1-butene, ethylene and methane molecules were detected in the NMR spectra of reaction mixture as side products (Figure 5). The formation of the C4 hydrocarbon product indicated the presence of propane oligomerization or metathesis processes taking place over VCAT, whereas the presence of C2 and C1 hydrocarbons indicates that carbon chain scission is also taking place. The main reaction product at temperatures above 500 oC was non-polarized propene. CONCLUSIONS In conclusion, we have examined a new silica-supported vanadium oxo organometallic complex VCAT in hydrogenation and dehydrogenation reactions in the presence of para-H2. It was found that the catalyst provides the formation of hyperpolarized propane in propene hydrogenation by means of parahydrogen-induced polarization (PHIP), demonstrating significant NMR signal enhancements of more than two orders of magnitude compared to thermal polarization. This is the first observation of PHIP effects over vanadium-based catalysts. On the other hand. no hyperpolarized propane was detected in propane dehydrogenation in the presence of para-H2, indicating that pairwise replacement of two hydrogens from propane with the ones originating from para-H2 is not an efficient process over VCAT. Instead, the side product 1-butene was found hyperpolarized in this process, illuminating complexity of the dehydrogenation process.


27


Page 28 of 35

Substantial hyperpolarization of more than three orders of magnitude was produced by VCAT as a catalyst in propyne hydrogenation with para-H2. Such a high enhancement factor deserves considering it as a record value observed among heterogeneous catalysts like immobilized complexes and supported metal catalysts of various metals known to produce PHIP. VCAT demonstrates also exceptionally high stability over long use in reaction conditions. It also has a relatively high activity in comparison to other Group 4 and 5 immobilized complexes (Ta, Zr), which, however, is not supreme, with the best result obtained of around 9 % conversion in the continuous flow mode in propene hydrogenation. We believe that further investigations of vanadium-based immobilized complexes are of significant importance for new breakthrough developments in the field of production of hyperpolarized substances in hydrogenations with para-H2. ASSOCIATED CONTENT Supporting Information. The following files are available free of charge. Additional supporting figures about 1-butyne hydrogenation and propane dehydrogenation over VCAT, propene and 1,3-butadiene hydrogenation over ZrCAT and propene hydrogenation over TaCAT (file type PDF). AUTHOR INFORMATION Corresponding Author *E-mail: [email protected]. Funding Sources


28

Page 29 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Russian Foundation for Basic research, RFBR (17-54-33037, 16-33-60198). FASO Russia (0333-2017-0002) ABBREVIATIONS ALTADENA, adiabatic longitudinal transport after dissociation engenders nuclear alignment; DNP, dynamic nuclear polarization; PASADENA, parahydrogen and synthesis allow dramatically enhanced nuclear alignment; para-H2, parahydrogen; PHIP, parahydrogen-induced polarization; rf, radio frequency; SABRE, signal amplification by reversible exchange. ACKNOWLEDGMENTS IVS thanks RFBR (16-33-60198) and IVK and VVZ thank RFBR (17-54-33037) for financial support of the research. The authors thank FASO Russia (0333-2017-0002) for basic funding. VVZ thanks University of Oulu (Kvantum Institute) for financial support. REFERENCES (1)

Bowers, C. R.; Weitekamp, D. P. Parahydrogen and Synthesis Allow

Dramatically Enhanced Nuclear Alignment. J. Am. Chem. Soc. 1987, 109, 5541-5542. (2)

Bowers, C. R.; Weitekamp, D. P. Transformation of Symmetrization Order to

Nuclear-Spin Magnetization by Chemical Reaction and Nuclear Magnetic Resonance. Phys. Rev. Lett. 1986, 57, 2645-2648. (3)

Natterer, J.; Bargon, J. Parahydrogen Induced Polarization. Prog. Nucl. Magn.

Reson. Spectrosc. 1997, 31, 293-315.


29


(4)

Page 30 of 35

Leggett, J.; Hunter, R.; Granwehr, J.; Panek, R.; Perez-Linde, A. J.; Horsewill, A.

J.; McMaster, J.; Smith, G.; Kockenberger, W. A Dedicated Spectrometer for Dissolution DNP NMR Spectroscopy. Phys. Chem. Chem. Phys. 2010, 12, 5883-5892. (5)

Kovtunov, K. V.; Zhivonitko, V. V.; Skovpin, I. V.; Barskiy, D. A.; Koptyug, I.

V. In Hyperpolarization Methods in NMR Spectroscopy; Kuhn, L. T., Ed.; Springer: Berlin, Heidelberg, 2013; Topics in Current Chemistry,Vol. 338, pp 123-180. (6)

Kovtunov, K. V.; Barskiy, D. A.; Salnikov, O. G.; Khudorozhkov, A. K.;

Bukhtiyarov, V. I.; Prosvirin, I. P.; Koptyug, I. V. Parahydrogen-Induced Polarization (PHIP) in Heterogeneous Hydrogenation over Bulk Metals and Metal Oxides. Chem. Commun. 2014, 50, 875-878. (7)

Skovpin, I. V.; Zhivonitko, V. V.; Prosvirin, I. P.; Khabibulin, D. F.; Koptyug, I.

V. Gas-Phase Hydrogenation with Parahydrogen Over Immobilized Vaska’s Complex. Z. Phys. Chem. 2016, 231, 575-592. (8)

Skovpin, I. V.; Zhivonitko, V. V.; Koptyug, I. V. Parahydrogen-Induced

Polarization in Heterogeneous Hydrogenations over Silica-Immobilized Rh Complexes. Appl. Magn. Reson. 2011, 41, 393-410. (9)

Skovpin, I. V.; Zhivonitko, V. V.; Kaptein, R.; Koptyug, I. V. Generating

Parahydrogen-Induced Polarization Using Immobilized Iridium Complexes in the Gas-Phase Hydrogenation of Carbon–Carbon Double and Triple Bonds. Appl. Magn. Reson. 2013, 44, 289300.


30

Page 31 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(10)

Zhivonitko, V. V.; Kovtunov, K. V.; Beck, I. E.; Ayupov, A. B.; Bukhtiyarov, V.

I.; Koptyug, I. V. Role of Different Active Sites in Heterogeneous Alkene Hydrogenation on Platinum Catalysts Revealed by Means of Parahydrogen-Induced Polarization. J. Phys. Chem. C 2011, 115, 13386-13391. (11)

Zhivonitko, V. V.; Skovpin, I. V.; Crespo-Quesada, M.; Kiwi-Minsker, L.;

Koptyug, I. V. Acetylene Oligomerization over Pd Nanoparticles with Controlled Shape: A Parahydrogen-Induced Polarization Study. J. Phys. Chem. C 2016, 120, 4945-4953. (12)

Kovtunov, K. V.; Beck, I. E.; Zhivonitko, V. V.; Barskiy, D. A.; Bukhtiyarov, V.

I.; Koptyug, I. V. Heterogeneous Addition of H2 to Double and Triple Bonds over Supported Pd Catalysts: a Parahydrogen-Induced Polarization Technique Study. Phys. Chem. Chem. Phys. 2012, 14, 11008-11014. (13)

Kovtunov, K. V.; Zhivonitko, V. V.; Corma, A.; Koptyug, I. V. Parahydrogen-

Induced Polarization in Heterogeneous Hydrogenations Catalyzed by an Immobilized Au(III) Complex. J. Phys. Chem. Lett. 2010, 1, 1705-1708. (14)

Bauer, G.; Güther, V.; Hess, H.; Otto, A.; Roidl, O.; Roller, H.; Sattelberger, S. In

Ullmann's Encyclopedia of Industrial Chemistry; Wiley-VCH Verlag GmbH & Co. KGaA: 2000, pp 49-69. (15)

Chalupka, K.; Thomas, C.; Millot, Y.; Averseng, F.; Dzwigaj, S. Mononuclear

pseudo-Tetrahedral V Species of VSiBEA Zeolite as the Active Sites of the Selective Oxidative Dehydrogenation of Propane. J. Catal. 2013, 305, 46-55.


31


(16)

Page 32 of 35

Cheng, L.; Ferguson, G. A.; Zygmunt, S. A.; Curtiss, L. A. Structure–Activity

Relationships for Propane Oxidative Dehydrogenation by Anatase-Supported Vanadium Oxide Monomers and Dimers. J. Catal. 2013, 302, 31-36. (17)

Takahara, I.; Saito, M.; Inaba, M.; Murata, K. Dehydrogenation of Propane over a

Silica-Supported Vanadium Oxide Catalyst. Catal. Lett. 2005, 102, 201-205. (18)

Szeto, K. C.; Loges, B.; Merle, N.; Popoff, N.; Quadrelli, A.; Jia, H.; Berrier, E.;

De Mallmann, A.; Delevoye, L.; Gauvin, R. M.; et al. Vanadium Oxo Organometallic Species Supported on Silica for the Selective Non-oxidative Dehydrogenation of Propane. Organometallics 2013, 32, 6452-6460. (19)

Zhou, R.; Zhao, E. W.; Cheng, W.; Neal, L. M.; Zheng, H.; Quiñones, R. E.;

Hagelin-Weaver, H. E.; Bowers, C. R. Parahydrogen-Induced Polarization by Pairwise Replacement Catalysis on Pt and Ir Nanoparticles. J. Am. Chem. Soc. 2015, 137, 1938-1946. (20)

Burueva, D. B.; Salnikov, O. G.; Kovtunov, K. V.; Romanov, A. S.; Kovtunova,

L. M.; Khudorozhkov, A. K.; Bukhtiyarov, A. V.; Prosvirin, I. P.; Bukhtiyarov, V. I.; Koptyug, I. V. Hydrogenation of Unsaturated Six-Membered Cyclic Hydrocarbons Studied by the Parahydrogen-Induced Polarization Technique. J. Phys. Chem. C 2016, 120, 13541-13548. (21) Vanadium(III)

Gambarotta, S.; Floriani, C.; Chiesivilla, A.; Guastini, C. A Tri-σ-aryl Derivative

–

Structural

Determination

of

Trimesitylvanadium(III)-

Tetrahydrofuran. J. Chem. Soc. Chem. Comm. 1984, 886-887.


32

Page 33 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(22)

Vivanco, M.; Ruiz, J.; Floriani, C.; Chiesivilla, A.; Rizzoli, C. Chemistry of the

Vanadium Carbon σ Bond .2. Oxovanadium(IV) and Oxovanadium(V) Containing Metal-toCarbon σ Bonds. Organometallics 1993, 12, 1802-1810. (23)

Norsic, S.; Larabi, C.; Delgado, M.; Garron, A.; de Mallmann, A.; Santini, C.;

Szeto, K. C.; Basset, J. M.; Taoufik, M. Low Temperature Hydrogenolysis of Waxes to Diesel Range Gasoline and Light Alkanes: Comparison of Catalytic Properties of Group 4, 5 and 6 Metal Hydrides Supported on Silica–Alumina. Catal. Sci. Technol. 2012, 2, 215-219. (24)

Pravica, M. G.; Weitekamp, D. P. Net NMR Alignment by Adiabatic Transport of

Para-Hydrogen Addition-Products to High Magnetic-Field. Chem. Phys. Lett. 1988, 145, 255258. (25)

Saggio, G.; de Mallmann, A.; Maunders, Barry; Taoufik, M.; Thivolle-Cazat, J.;

Basset, J.-M. Synthesis, Characterization, and Reactivity of the Highly Unsaturated SilicaSupported Trisiloxy Tantalum: (⋮SiO)3Ta(III). Organometallics 2002, 21, 5167-5171. (26)

Sohn, H.; Camacho-Bunquin, J.; Langeslay, R. R.; Ignacio-de Leon, P. A.; Niklas,

J.; Poluektov, O. G.; Liu, C.; Connell, J. G.; Yang, D.; Kropf, J.; et al. Isolated, Well-Defined Organovanadium(III) on Silica: Single-Site Catalyst for Hydrogenation of Alkenes and Alkynes. Chem.Commun. 2017, 53, 7325-7328. (27)

Eisenberg, R.; Eisenschmid, T. C.; Chinn, M. S.; Kirss, R. U. Parahydrogen-

Induced Polarization and Polarization Transfer in Hydrogenation and Oxidative AdditionReactions - a Mechanistic Probe. Adv. Chem. Ser. 1992, 230, 47-74.


33


(28)

Page 34 of 35

Zhivonitko, V. V.; Sorochkina, K.; Chernichenko, K.; Kotai, B.; Foldes, T.;

Papai, I.; Telkki, V.-V.; Repo, T.; Koptyug, I. Nuclear Spin Hyperpolarization with ansaAminoboranes: A Metal-Free Perspective for Parahydrogen-Induced Polarization. Phys. Chem. Chem. Phys. 2016, 18, 27784-27795. (29)

Anderson, A. B.; Nichols, J. A. Hydrogen on zinc oxide. Theory of its Heterolytic

Adsorption. J. Am. Chem. Soc. 1986, 108, 4742-4746. (30)

Adams, R. W.; Aguilar, J. A.; Atkinson, K. D.; Cowley, M. J.; Elliott, P. I.;

Duckett, S. B.; Green, G. G.; Khazal, I. G.; Lopez-Serrano, J.; Williamson, D. C. Reversible Interactions with para-Hydrogen Enhance NMR Sensitivity by Polarization Transfer. Science 2009, 323, 1708-1711.


34

Page 35 of 35 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


TOC graphic