Postsynthesis Transformation of Insulating Cs4PbBr6 Nanocrystals into Bright Perovskite CsPbBr3 through Physical and Chemical Extraction of CsBr Francisco Palazon,† Carmine Urso,† Luca De Trizio,† Quinten Akkerman,†,‡ Sergio Marras,§ Federico Locardi,‡ Ilaria Nelli,†,‡ Maurizio Ferretti,‡ Mirko Prato,§ and Liberato Manna*,† †
Nanochemistry Department, and §Materials Characterization Facility, Istituto Italiano di Tecnologia, Via Morego 30, 16163 Genova, Italy ‡ Dipartimento di Chimica e Chimica Industriale, Università degli Studi di Genova, Via Dodecaneso 31, 16146 Genova, Italy S Supporting Information *
ABSTRACT: Perovskite-related Cs4PbBr6 nanocrystals present a “zerodimensional” crystalline structure where adjacent [PbBr6]4− octahedra do not share any corners. We show in this work that these nanocrystals can be converted into “three-dimensional” CsPbBr3 perovskites by extraction of CsBr. This conversion drastically changes the optoelectronic properties of the nanocrystals that become highly photoluminescent. The extraction of CsBr can be achieved either by thermal annealing (physical approach) or by chemical reaction with Prussian Blue (chemical approach). The former approach can be simply carried out on a dried film without addition of any chemicals but does not yield a full transformation. Instead, reaction with Prussian Blue in solution achieves a full transformation into the perovskite phase. This transformation was also verified on the iodide counterpart (Cs4PbI6).
H
demonstrated that the 0D to 3D conversion can be carried out by extraction of CsX in an immiscible polar solvent (water).25 In the present work, we study the postsynthesis conversion of insulating 0D NCs into bright photoluminescent 3D perovskite NCs by extraction of CsBr either through thermal annealing or by reaction with Prussian Blue (PB). Also, the 3D CsPbBr3 NCs remain stable in PB, a finding that can be used to enhance the stability of these materials in devices. 0D Cs4PbBr6 NCs were synthesized as previously reported.13 The structural evolution of these NCs upon annealing in vacuum was monitored by in situ X-ray diffraction (XRD), as shown in Figure 1a. The diffractogram of the pristine NCs at room temperature (Figure 1a, bottom) matches that of bulk Cs4PbBr6 (ICSD 162158). As the sample is annealed above 150 °C, the new CsPbBr3 phase appears, with additional peaks matching the reference ICSD 97851 pattern for bulk CsPbBr3. Both phases coexist from 150 to 350 °C (in Figure 1a, the diffractograms where both phases are present are shown in green). Then, upon further annealing at 400 °C, the peaks corresponding to the 3D perovskite vanish and only the original Cs4PbBr6 phase remains. In order to gain more insight into
alide perovskites have emerged as very interesting materials for a wide range of optoelectronic devices ranging from photovoltaics to light-emission applications.1−3 Fully inorganic cesium lead halide colloidal nanocrystals (NCs) have attracted considerable attention in this context owing, among others, to their remarkable chemical and structural versatility. Several syntheses have been reported yielding different chemical compositions, sizes, and shapes.4−9 Although for NCs the main focus has been on the perovskite CsPbX3 (X being mostly Br but also I and Cl) structure, recent works have demonstrated the synthesis of CsPb2X510−12 and Cs4PbX6 NCs.13−20 These three structures can be named “3D” (CsPbBr3), “2D” (CsPb2Br5), and “0D” (Cs4PbBr6), based on the way the [PbBr6]4− octahedra are networked (see Scheme S1). Clear proof of the aforementioned versatility in these ternary compounds is that they can be interconverted by postsynthesis physical and chemical treatments. It has been shown, for instance, that thermal annealing of a dried NC film triggers a 3D to 2D phase transformation (3D → 2D), presumably through temperature-induced extraction of CsBr.21 Furthermore, postsynthesis 0D → 3D conversion as well as the 3D → 2D one has been demonstrated through insertion of PbBr2,13,22 while amine- and thiol-mediated extraction of PbBr2 from 3D NCs has been reported to yield 0D NCs (3D → 0D).23,24 During the review process of this Letter, it was © 2017 American Chemical Society
Received: September 5, 2017 Accepted: September 19, 2017 Published: September 19, 2017 2445
DOI: 10.1021/acsenergylett.7b00842 ACS Energy Lett. 2017, 2, 2445−2448
Letter
http://pubs.acs.org/journal/aelccp
Letter
ACS Energy Letters
is known that these species are difficult to identify unambiguously by MS as they undergo degradation and strong interaction with the stationary phase in the column.26 Therefore, the signal attributed to “ligands” in Figure 2 is derived from the total ion current (TIC) measured in MS. This desorption of ligands is concomitant with the reverse transformation of CsPbBr3 to Cs4PbBr6, as seen by XRD. Two different reaction pathways can be contemplated for this transformation: (i) the reinsertion of CsBr into CsPbBr3 to form Cs4PbBr6 or (ii) further extraction of PbBr2 from CsPbBr3 following the reaction 4CsPbBr3 → Cs4PbBr6 + 3PbBr2. It must be noted that the melting point of PbBr2 is around 357 °C, yet no signal for the melting of PbBr2 is seen by differential thermal analysis (DTA) around these temperatures (see Figure S1). Thus, we can rationalize the XRD (Figure 1a) and TG-DTAMS (Figures 2 and S1) data as follows: thermal annealing above 150 °C leads to the complete desorption of residual solvent (toluene) and partial extraction of Cs+ and Br−, which are complexed by residual long-chain ligands (stable up to ca. 300 °C), and a fraction of the Cs4PbBr6 NCs is transformed to CsPbBr3. Upon further annealing at around 250−350 °C, ligands are desorbed from the film, freeing the previously extracted Cs+ and Br− ions, which are inserted back into CsPbBr3 to form Cs4PbBr6, which is the only visible phase at 400 °C. This mechanism explains the evidence that the weight loss in the RT to 450 °C range is very moderate (6.7% as determined from TG) and no inorganic material is detected by MS. Melting of Cs4PbBr6 is detected by DTA at 507 °C (Figure S1),27 and significant weight losses above 500 °C can be attributed to the vaporization of PbBr2 followed by vaporization of CsBr above 600 °C.28 These chemical transformations upon annealing have a direct consequence on the photoluminescence (PL) of the film. Indeed, when thermal annealing is stopped before 400 °C (e.g., at 200 °C) and the sample is cooled down to roomtemperature, the mixed-composition sample (0D/3D) exhibits bright PL at 520 nm (and a respective drop of transmittance at 500 nm; see Figure S2), typical of the perovskite phase and clearly seen by the eye under a UV lamp (see Figure 1b with inset). Indeed, several reports have shown that even a small fraction of CsPbBr3 in a CsPbBr3/Cs4PbBr6 mixture yields bright PL.13 The bright PL of the mixed film annealed at 200 °C is especially striking because annealing a film of pristine CsPbBr3 NCs up to a similar temperature is known to almost fully quench its PL.29−31 Eventually, it must be noted that the evolution of samples annealed ex situ in nitrogen under ambient pressure (see Figure S3) is similar to that observed in situ under vacuum. Thermal annealing also leads to NC sintering, as can be seen by the narrowing of the XRD peaks (Figures 1a and S4) as well as by direct observation under scanning electron microscopy (Figure 1c−e). As the above transformation of Cs4PbBr6 NCs into CsPbBr3 is only partial and causes sintering and ripening of the particles, we have developed an alternative path to this transformation, involving chemical extraction of CsBr, which achieves full conversion and prevents particle sintering. The reaction employs FeIII4[FeII(CN)6]3, also known as Prussian blue (PB), a chemical known to intercalate Cs+ ions interstitially.32 PB powder was added to a colloidal dispersion of Cs4PbBr6 NCs in toluene and left to react for 1 day at room temperature. PB is immiscible in toluene, but extraction of CsBr can be achieved through interfacial reactions, as recently shown.25 After 24 h, the NCs were isolated by centrifugation and
Figure 1. (a) XRD diffractograms of NCs upon annealing in vacuum and reference patterns of bulk CsPbBr3 (ICSD 97851) and Cs4PbBr6 (ICSD 162158). (b) Photoluminescence spectra and photographs under a UV lamp (inset) of the reference sample and sample annealed at 200 °C. SEM images of samples at RT (c), 200 °C (d), and 400 °C (e). Scale bars are 100 nm.
these transformations, we also performed thermogravimetric (TG) analysis coupled with mass spectrometry (MS), as presented in Figure 2. From these data, we can infer that, from
Figure 2. TG (black) curve and evolved gas analysis of Cs4PbBr6 NCs; the signals are related to toluene (red, m/z = 91) and organic ligands (blue, TIC). Note: the blue intensity is five times magnified.
RT to 150 °C, a slight weight loss is due to the evaporation of residual solvent (toluene), as evidenced by MS. Around 150− 250 °C, as we have seen by XRD, CsPbBr3 is formed. This transformation implies the extraction of Cs and Br from the original Cs4PbBr6. Indeed, it has recently been shown that CsBr can easily depart from Cs4PbBr6 NCs to form CsPbBr3 NCs.25 In our case, we did not observe the appearance of CsBr XRD peaks upon annealing. Nonetheless, it is unlikely that it vaporizes at this low temperature (the melting point of CsBr is over 600 °C). Indeed, TG shows only a very low weight loss, and no signal for Cs or Br is seen by MS (Figure 2). Furthermore, at these temperatures, the long-chain molecules used for the synthesis of the NCs (oleylamine, octadecene, and oleic acid) are stable (boiling points are above 300 °C). Therefore, the most likely explanation is that the extracted Cs+ and Br− ions are complexed by residual organics, or form very small clusters hardly detectable by XRD. Upon further annealing, a small step in TG translating a weight loss can be seen at around 300−400 °C. This weight loss can be attributed to desorption/decomposition of the aforementioned ligands. It 2446
DOI: 10.1021/acsenergylett.7b00842 ACS Energy Lett. 2017, 2, 2445−2448
ACS Energy Letters
■
filtration. Figure 3b reports the evolution of the optical properties from a sharp absorption at 314 nm and no PL, as is
Letter
ASSOCIATED CONTENT
S Supporting Information *
The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsenergylett.7b00842. Experimental details, 3D schemes of crystal structures, XRD, DTA, TEM, absorption, and photoluminescence spectra (PDF)
■
AUTHOR INFORMATION
Corresponding Author
*E-mail:
[email protected]. ORCID
Francisco Palazon: 0000-0002-1503-5965 Luca De Trizio: 0000-0002-1514-6358 Mirko Prato: 0000-0002-2188-8059 Liberato Manna: 0000-0003-4386-7985
Figure 3. XRD (a), optical (b) and TEM (c,d) characterization of 0D NCs transformed to 3D by PB. Black and green bars in (a) are reference patterns for 0D and 3D phases. Scale bars in (c,d) are 50 nm.
Notes
The authors declare no competing financial interest.
■
ACKNOWLEDGMENTS We thank Muhammad Imran for support with NC synthesis. The research leading to these results has received funding from the seventh European Community Framework Programme under Grant Agreement No. 614897 (ERC Consolidator Grant “TRANS-NANO”).
characteristic of the 0D phase, to an absorption onset at around 500 nm with the corresponding Stokes-shifted PL at 515 nm of the resulting 3D phase. This transformation is further verified by TEM (Figure 3c,d), which evidences a shape evolution and corresponding XRD peaks (Figure 3a) matching the bulk patterns of Cs4PbBr6 (before) and CsPbBr3 (after 24 h). These data highlight the successful conversion of the initial 0D NCs into 3D ones. The shrinkage in size of the NCs following this treatment supports the hypothesis that CsBr was extracted from the NCs rather than the overall sample undergoing a dissolution-recrystallization. On the other hand, the CsPbBr3 NCs are smaller than expected and slightly more polydisperse than the starting Cs4PbBr6 NCs (average size goes from 9.8 ± 1.1 to 6.3 ± 1.4 nm; see Figure S5), suggesting that the transformation is accompanied by etching of the sample. This is not surprising as there is considerable reorganization of the lattice when going from Cs4PbBr6 to CsPbBr3. Evidently, the extraction of Cs+ ions is accompanied by that of Br− ions to maintain charge neutrality both in the NCs and in PB. It is worth noting that the resulting 3D NCs did not react further with PB, even after several days in solution (see Figure S6), meaning that PB is unable to extract additional CsBr from the 3D perovskite to yield the CsPb2Br5 phase. The same conversion could be achieved on iodide NCs, transforming Cs4PbI6 NCs into red-emitting CsPbI3 NCs (see Figure S7). This is seen both by the change in morphology evidenced by TEM (Figure S7a,b) and by the evolution of absorption and PL spectra (Figure S7c). Indeed, the initial sample shows a sharp absorption peak at 368 nm and no PL, while the resulting NCs after reaction with PB for 20 min at 80 °C show an absorption onset at around 647 nm with a Stokesshifted PL peak at 667 nm. These features are typical of Cs4PbI6 (before reaction) and CsPbI3 (after reaction).4,13 In summary, we have shown that Cs4PbBr6 NCs can be transformed either by thermal annealing or by reaction with PB into bright-emitting perovskite CsPbBr3 NCs. These postsynthesis reactions represent a new tool to tailor the stoichiometry and optical properties of cesium lead halide NCs. Especially the use of PB as an additive in 3D perovskite films may help to stabilize the 3D phase by preventing its transformation to other phases.
■
REFERENCES
(1) Sessolo, M., Gil-Escrig, L.; Longo, G.; Bolink, H. J. Perovskite Luminescent Materials. In Photoluminescent Materials and Electroluminescent Devices; Armaroli, N., Bolink, H. J., Eds.; Springer International Publishing: Cham, 2017, pp 241−268. (2) Stranks, S. D.; Eperon, G. E.; Grancini, G.; Menelaou, C.; Alcocer, M. J.; Leijtens, T.; Herz, L. M.; Petrozza, A.; Snaith, H. J. Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber. Science 2013, 342, 341− 344. (3) Sutherland, B. R.; Sargent, E. H. Perovskite Photonic Sources. Nat. Photonics 2016, 10, 295−302. (4) Protesescu, L.; Yakunin, S.; Bodnarchuk, M. I.; Krieg, F.; Caputo, R.; Hendon, C. H.; Yang, R. X.; Walsh, A.; Kovalenko, M. V. Nanocrystals of Cesium Lead Halide Perovskites (CsPbX3, X= Cl, Br, and I): Novel Optoelectronic Materials Showing Bright Emission with Wide Color Gamut. Nano Lett. 2015, 15, 3692−3696. (5) Akkerman, Q. A.; Gandini, M.; Di Stasio, F.; Rastogi, P.; Palazon, F.; Bertoni, G.; Ball, J. M.; Prato, M.; Petrozza, A.; Manna, L. Strongly Emissive Perovskite Nanocrystal Inks for High-Voltage Solar Cells. Nat. Energy 2016, 2, 16194. (6) Akkerman, Q. A.; Motti, S. G.; Srimath Kandada, A. R.; Mosconi, E.; D’Innocenzo, V.; Bertoni, G.; Marras, S.; Kamino, B. A.; Miranda, L.; Angelis, De.; et al. Solution Synthesis Approach to Colloidal Cesium Lead Halide Perovskite Nanoplatelets with Monolayer-Level Thickness Control. J. Am. Chem. Soc. 2016, 138, 1010−1016. (7) Bekenstein, Y.; Koscher, B. A.; Eaton, S. W.; Yang, P.; Alivisatos, A. P. Highly Luminescent Colloidal Nanoplates of Perovskite Cesium Lead Halide and Their Oriented Assemblies. J. Am. Chem. Soc. 2015, 137, 16008−16011. (8) Zhang, D.; Eaton, S. W.; Yu, Y.; Dou, L.; Yang, P. Solution-Phase Synthesis of Cesium Lead Halide Perovskite Nanowires. J. Am. Chem. Soc. 2015, 137, 9230−9233. (9) Nedelcu, G.; Protesescu, L.; Yakunin, S.; Bodnarchuk, M. I.; Grotevent, M. J.; Kovalenko, M. V. Fast Anion-Exchange in Highly Luminescent Nanocrystals of Cesium Lead Halide Perovskites (CsPbX3, X= Cl, Br, I). Nano Lett. 2015, 15, 5635−5640. 2447
DOI: 10.1021/acsenergylett.7b00842 ACS Energy Lett. 2017, 2, 2445−2448
Letter
ACS Energy Letters (10) Wang, K.-H.; et al. Large-Scale Synthesis Of Highly Luminescent Perovskite-Related CsPb2Br5 Nanoplatelets and Their Fast Anion Exchange. Angew. Chem., Int. Ed. 2016, 55, 1−6. (11) Tang, X.; Hu, Z.; Yuan, W.; Hu, W.; Shao, H.; Han, D.; Zheng, J.; Hao, J.; Zang, Z.; Du, J.; et al. Perovskite CsPb2Br5 Microplate Laser with Enhanced Stability and Tunable Properties. Adv. Opt. Mater. 2017, 5, 1600788. (12) Zhang, X.; Xu, B.; Zhang, J.; Gao, Y.; Zheng, Y.; Wang, K.; Sun, X. W. All-Inorganic Perovskite Nanocrystals for High-Efficiency Light Emitting Diodes: Dual-Phase CsPbBr3-CsPb2Br5 Composites. Adv. Funct. Mater. 2016, 26, 4595−4600. (13) Akkerman, Q. A.; Park, S.; Radicchi, E.; Nunzi, F.; Mosconi, E.; De Angelis, F.; Brescia, R.; Rastogi, P.; Prato, M.; Manna, L. Nearly Monodisperse Insulator Cs4PbX6 (X= Cl, Br, I) Nanocrystals, Their Mixed Halide Compositions, and Their Transformation into CsPbX3 Nanocrystals. Nano Lett. 2017, 17, 1924−1930. (14) Zhang, Y.; Saidaminov, M. I.; Dursun, I.; Yang, H.; Murali, B.; Alarousu, E.; Yengel, E.; Alshankiti, B. A.; Bakr, O. M.; Mohammed, O. F. J. Zero-Dimensional Cs4PbBr6 Perovskite Nanocrystals. J. Phys. Chem. Lett. 2017, 8, 961−965. (15) Yang, L.; Li, D.; Wang, C.; Yao, W.; Wang, H.; Huang, K. Room-Temperature Synthesis of Pure Perovskite-Related Cs4PbBr6 Nanocrystals and Their Ligand-Mediated Evolution into Highly Luminescent CsPbBr3 Nanosheets. J. Nanopart. Res. 2017, 19, 258. (16) Seth, S.; Samanta, A. Fluorescent Phase-Pure Zero-Dimensional Perovskite Related Cs4PbBr6 Microdisks: Synthesis and Single Particle Imaging Study. J. Phys. Chem. Lett. 2017, 4461−4467. (17) De Bastiani, M.; Dursun, I.; Zhang, Y.; Alshankiti, B. A.; Miao, X.-H.; Yin, J.; Yengel, E.; Alarousu, E.; Turedi, B.; Almutlaq, J. M.; et al. Inside Perovskites: Quantum Luminescence from Bulk Cs4PbBr6 Single Crystals. Chem. Mater. 2017, 29, 7108−7113. (18) Cha, J.-H.; Han, J. H.; Yin, W.; Park, C.; Park, Y.; Ahn, T. K.; Cho, J. H.; Jung, D.-Y. Photoresponse of CsPbBr3 and Cs4PbBr6 Perovskite Single Crystals. J. Phys. Chem. Lett. 2017, 8, 565−570. (19) Saidaminov, M. I.; Almutlaq, J.; Sarmah, S.; Dursun, I.; Zhumekenov, A. A.; Begum, R.; Pan, J.; Cho, N.; Mohammed, O. F.; Bakr, O. M. Pure Cs4PbBr6: Highly Luminescent Zero-Dimensional Perovskite Solids. ACS Energy Lett. 2016, 1, 840−845. (20) Chen, D.; Wan, Z.; Chen, X.; Yuan, Y.; Zhong, J. Large-Scale Room-Temperature Synthesis and Optical Properties of PerovskiteRelated Cs4PbBr6 Fluorophores. J. Mater. Chem. C 2016, 4, 10646− 10653. (21) Palazon, F.; Dogan, S.; Marras, S.; Locardi, F.; Nelli, I.; Rastogi, P.; Ferretti, M.; Prato, M.; Krahne, R.; Manna, L. From CsPbBr3 Nano-Inks to Sintered CsPbBr3-CsPb2Br5 Films via Thermal Annealing: Implications on Optoelectronic Properties. J. Phys. Chem. C 2017, 121, 11956−11961. (22) Li, G.; Wang, H.; Zhu, Z.; Chang, Y.; Zhang, T.; Song, Z.; Jiang, Y. Shape and Phase Evolution from CsPbBr3 Perovskite Nanocubes to Tetragonal CsPb2Br5 Nanosheets with an Indirect Bandgap. Chem. Commun. 2016, 52, 11296−11299. (23) Liu, Z.; Bekenstein, Y.; Ye, X.; Nguyen, S. C.; Swabeck, J.; Zhang, D.; Lee, S. T.; Yang, P.; Ma, W.; Alivisatos, A. P. Ligand Mediated Transformation of Cesium Lead Bromide Perovskite Nanocrystals to Lead Depleted Cs4PbBr6 Nanocrystals. J. Am. Chem. Soc. 2017, 139, 5309−5312. (24) Palazon, F.; Almeida, G.; Akkerman, Q. A.; De Trizio, L.; Dang, Z.; Prato, M.; Manna, L. Changing the Dimensionality of Cesium Lead Bromide Nanocrystals by Reversible Postsynthesis Transformations with Amines. Chem. Mater. 2017, 29, 4167−4171. (25) Wu, L.; Hu, H.; Xu, Y.; Jiang, S.; Chen, M.; Zhong, Q.; Yang, D.; Liu, Q.; Zhao, Y.; Sun, B.; et al. From Nonluminescent Cs4PbX6 (X = Cl, Br, I) Nanocrystals to Highly Luminescent CsPbX3 Nanocrystals: Water-Triggered Transformation through a CsX-Stripping Mechanism. Nano Lett. 2017, 17, 5799−5804. (26) Kataoka, H. Derivatization Reactions for the Determination of Amines by Gas Chromatography and Their Applications in Environmental Analysis. J. Chromatogr. A 1996, 733, 19−34.
(27) Velázquez, M.; Ferrier, A.; Péchev, S.; Gravereau, P.; Chaminade, J.-P.; Portier, X.; Moncorgé, R. Growth and Characterization of Pure and Pr3+-Doped Cs4PbBr6 Crystals. J. Cryst. Growth 2008, 310, 5458−5463. (28) Kulbak, M.; Gupta, S.; Kedem, N.; Levine, I.; Bendikov, T.; Hodes, G.; Cahen, D. Cesium Enhances Long-Term Stability of Lead Bromide Perovskite-Based Solar Cells. J. Phys. Chem. Lett. 2016, 7, 167−72. (29) Palazon, F.; Di Stasio, F.; Lauciello, S.; Krahne, R.; Prato, M.; Manna, L. Evolution of CsPbBr3 Nanocrystals upon Post-Synthesis Annealing under an Inert Atmosphere. J. Mater. Chem. C 2016, 4, 9179−9182. (30) Yuan, X.; Hou, X.; Li, J.; Qu, C.; Zhang, W.; Zhao, J.; Li, H. Thermal Degradation of Luminescence in Inorganic Perovskite CsPbBr3 Nanocrystals. Phys. Chem. Chem. Phys. 2017, 19, 8934−8940. (31) Diroll, B. T.; Nedelcu, G.; Kovalenko, M. V.; Schaller, R. D. High-Temperature Photoluminescence of CsPbX3 (X = Cl, Br, I) Nanocrystals. Adv. Funct. Mater. 2017, 27, 1606750. (32) Ishizaki, M.; Akiba, S.; Ohtani, A.; Hoshi, Y.; Ono, K.; Matsuba, M.; Togashi, T.; Kananizuka, K.; Sakamoto, M.; Takahashi, A.; et al. Proton-Exchange Mechanism of Specific Cs+ Adsorption via Lattice Defect Sites of Prussian Blue Filled with Coordination and Crystallization Water Molecules. Dalton Trans. 2013, 42, 16049− 16055.
2448
DOI: 10.1021/acsenergylett.7b00842 ACS Energy Lett. 2017, 2, 2445−2448