Properties Enhancement of Room Temperature ... - ACS Publications

Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Properties Enhancement of Room Temperature Vulcanized Silicone Rubber by Rosin Modified Aminopropyltriethoxysilane as a Crosslinking Agent Qiaoguang Li, Xujuan Huang, He Liu, Shibin Shang, Zhanqian Song, and Jie Song ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.7b01943 • Publication Date (Web): 25 Sep 2017 Downloaded from http://pubs.acs.org on September 27, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Properties Enhancement of Room Temperature Vulcanized Silicone Rubber by Rosin Modified Aminopropyltriethoxysilane as a Crosslinking Agent Qiaoguang Li † , Xujuan Huang † , He Liu†*, Shibin Shang†‡*, Zhanqian Song†‡* and Jie Song§ †

Institute of Chemical Industry of Forestry Products, Chinese Academy of Forestry, Key

Laboratory of Biomass Energy and Material, National Engineering Laboratory for Biomass Chemical Utilization, Key and Laboratory on Forest Chemical Engineering, State Forestry Administration, Nanjing, Jiangsu Province 210042, China ‡

Institute of New Technology of Forestry, Chinese Academy of Forestry, Beijing 100091, China

§

Department of Chemistry and Biochemistry, University of Michigan-Flint, Flint, Michigan

48502, United States Mailing address: †

No.16 Suojinbei Road, Xuanwu District, Nanjing, Jiangsu Province 210042, China.

‡

NO.1 Xiangshan Road, Haiding District, Beijing, 100091, China.

§

303 E. Kearsley Street, Michigan, 48502, United States.

⁑

These authors contributed equally to this work.

ACS Paragon Plus Environment

1


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 38

*

Corresponding author Email: [email protected], [email protected] &

[email protected] Phone: 086-25-85482452. Fax: 086-25-85482499.


2

Page 3 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


ABSTRACT: Rosin modified aminopropyltriethoxysilane (RA) was prepared via an epoxide ring opening reaction of rosin based glycidyl ester with aminopropyltriethoxysilane. The structure of RA was confirmed by Fourier transform infrared spectroscopy (FT-IR), 1H-NMR and 13C-NMR. RA was used as a crosslinking agent to prepare room temperature vulcanized (RTV) silicone rubber with hydroxy terminated polydimethylsiloxane (PDMS) matrix in the presence of an organotin catalyst. Morphology, thermal, and mechanical properties of the rosin modified RTV silicone rubbers were characterized by scanning electron microscope (SEM), thermal gravimetric analysis (TG), universal testing machine, and dynamic mechanical analysis (DMA), respectively. Compared to the silicone rubber using tetraethoxysilane (TEOS) as the crosslinking agent, the RA modified RTV silicone rubber exhibited a significant enhancement in thermal stabilities and mechanical properties due to the strong rigidity and polar hydrogenated phenanthrene ring structure of rosin and the uniform distribution of RA in the RTV silicone rubber. KEYWORDS: Crosslinking agent, Rosin, RTV silicone rubber


3


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 38

INTRODUCTION Silicone rubber has characteristics of both inorganic and organic materials and offers many advantages not found in other organic rubbers.1 It has better heat resistance, ozone resistance, weather resistance, chemical stability, electrical insulating, and low surface tension compared to organic rubber.2-3 Because of these unique properties, silicone rubber has been widely applied in aerospace, munitions industry, construction, electricity, medical and so on.4-5 However, the low intermolecular force results in lower mechanical properties and limits its practical applications.2 Therefore, improving the mechanical properties of silicone rubber has attracted more attention. Incorporation of fillers and modification of the polydimethylsiloxane (PDMS) matrix are two effective procedures to reinforce the silicone rubber.

6-8

In addition, using new types of

crosslinking agents to improve the properties of silicone rubber is effective as well.9-10 Han et al. found that the thermal and mechanical properties of silicone rubber were improved significantly by using a novel polymethylmethoxysiloxane (PMOS) as the crosslinking agent because of the improvement effect of PMOS phases in-situ at microscale.11 Ramli et al. synthesized α, ω-bis(trimethoxysilane)-polydimethylsiloxane as a crosslinking agent which induced the elevated thermal properties and improved the hardness of silicone rubber by the incrementing crosslinking density.12 In addition, the rigid and polar inorganic materials were also used as crosslinking agents to improve the thermal and mechanical properties of silicone rubber. Chen et al. investigated the effects of two types of polyhedral oligomeric silsesquioxanes (POSS) crosslinking agents on the RTV silicone rubber. The remarkable improvement in thermal and mechanical properties of silicone rubber are attributed to the effective three-dimensional network structures and the uniform distribution of POSS.13-15 Shi et al. prepared a series of silicone rubbers using tetra-silanol-phenyl-polyhedral oligomeric silsesquioxane (TOPO) as a


4

Page 5 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


crosslinking agent and the thermal stability was enhanced because of the nano-reinforcement effect of the POSS cage.9 These studies indicate that thermal stabilities and mechanical properties of silicone rubber are improved significantly by the chemical incorporation of rigid and polar inorganic materials as crosslinking agents. In recent years more attention has been paid to research about polymer materials from the biomass.16-21 In nature some renewable biomass resources have strong rigidity and polar rings as well, which are good alternatives for the preparation of polymers. Rosin is a solid form of resin obtained directly from the exudates of pines and conifers or as a byproduct from the pulping process.22 It is a mixture of natural products which is composed of 40-60 wt% of mainly isomeric abietic-type acids, 9-27 wt% of pimaric-type acids and 10 wt% of neutral compounds.23-25 Rosin, which is similar to cyclic aliphatic or aromatic compounds in molecule rigidity, has a large hydrogenated phenanthrene ring structure, a carboxylic acid group and a conjugated carbon-carbon double bond of active functional groups.22,

26

Therefore, rosin

derivatives can be easily prepared via esterification, D-A addition, acylation, disproportionation, and amination reactions.22, 26-28 Rosin derivatives may serve as alternatives to the petroleumbased cyclic aliphatic or aromatic monomers used in polymers including polyesters, epoxy resin, silicone rubber, adhesives, coating, and bio-based plastics to obtain better mechanical and thermal stabilities.22, 25-27, 29-32 Deng et al. prepared a series of novel rosin-based siloxane epoxy resins using ethylene glycol diglycidyl ether modified acrylpimaric acid (AP-EGDE) with poly(methylphenylsiloxane).32 In our previous study rosin and its derivatives were grafted with vinyl polysiloxane via the reaction of carboxyl with the primary amino at high temperature.29, 3334

Then, these rosin modified polysiloxanes were used as raw materials to prepare silicone rubber

via the free radical vulcanization reaction. Rigid and polar hydrogenated phenanthrene rings of


5


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 38

rosin on the side chain of polysiloxane have remarkable effects on the mechanical and thermal stabilities of silicone rubber. Although rosin derivatives have attracted more attention in the synthesis of polymers in recent years, they have rarely been employed as crosslinking agents of silicone rubber.29

Figure 1. Synthetic route of RTV silicone rubber. Rosin (RO), glycidyl ester of rosin acid (ER), and rosin modified aminopropyltriethoxysilane (RA) In this work, a novel crosslinking agent was synthesized from glycidyl ester of rosin acid and aminopropyltriethoxysilane. RTV silicone rubbers were prepared using different amounts of rosin modified aminopropyltriethoxysilane (RA) as a crosslinking agent with the hydroxy terminated polydimethylsiloxane (PDMS) matrix (Figure 1). The effects of RA on the morphology, thermal properties, mechanical properties, and dynamic mechanical properties of RTV silicone rubber were explored.


6

Page 7 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


MATERIALS AND METHODS Materials Purified rosin (RO) composed of rosin acids (ca ≥ 95 wt%) was purchased from Hunan pine forest Technologies Co., Ltd. Aminopropyltriethoxysilane was purchased from Wanda Chemical Co., Ltd. Hydroxy terminated polydimethylsiloxane (PDMS, 5000 mpa.s) was obtained from Hubei new Universal Chemical Co., Ltd. Sodium hydroxide (NaOH), calcium oxide (CaO), celite, tetraethoxysilane (TEOS), epichlorohydrin, toluene, benzyltriethyl ammonium chloride, and dibutyltin dilaurate were obtained from Nanjing Chemical Reagent Co., Ltd. Deionized water was obtained at a conductivity of 18.3 MΩ·cm on a Hitech-Sciencetool Master-Q (Shanghai Hetai Reagent Co., Ltd). All chemicals were used without further purification. Synthesis of glycidyl ester of rosin acid (ER) A 500 mL flask equipped with a stirrer, a thermometer, and a condenser pipe was filled with 50.0 g rosin, 157.3 g epichlorohydrin, and 0.381 g benzyltriethyl ammonium chloride under the protection of a nitrogen atmosphere.26, 35 The mixture was held around 117 oC for 2 h and then cooled to 60 oC. The two parameters 6.62 g sodium hydroxide and 9.272 g calcium oxide were added to the flask and the mixture was kept at 60 oC for another 3 h. The mixture was filtered by celite and filter paper, then the filtrate was distilled under vacuum at 100 oC to remove excess epichlorohydrin. Finally, 54.5 g (92 wt% yield, Figure 1) brown and viscous glycidyl ester of rosin acid with an epoxide equivalent weight of 352 g/mol (theory gives 358 g/mol) was obtained without further purification. Synthesis of rosin modified aminopropyltriethoxysilane (RA)


7


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 38

A flask equipped with a stirrer, an inert gas inlet, a thermometer, and a reflux condenser was filled with 48g ER and 29.6g aminopropyltriethoxysilane and the mixture was kept at 80 oC for about 1 h at which time the appearance of mixture changed from turbid to transparent. 77.6 g brown and viscous rosin modified aminopropyltriethoxysilane (100 wt% yield, Figure 1) were obtained. The RA products were directly applied in the following experiments without further purification. Preparation of modified RTV silicone rubber PDMS and crosslinking agents (TEOS and RA) were added into a three-necked flask and stirred by mechanical stirrer for 15 min at room temperature under dry nitrogen protection. Then, a dibutyltin dilaurate catalyst was added into the flask and vigorously stirred for 15 min. Finally, the mixture was quickly poured into a mold after removing the air bubbles. The mixture was cured for 7 d at room temperature to obtain a RTV silicone rubber sheet with smooth surface. Table 1. The components of RTV silicone rubbers

0

Oxethyl of RA (mmol) 0

Oxethyl of TEOS (mmol) 51.9

Total Oxethyl (mmol) 51.9

100

5

8.8

43.1

51.9

1.75

100

10

18.3

33.6

51.9

5.51

1.21

100

15

28.5

23.4

51.9

7.66

0.64

100

20

39.7

12.2

51.9

Sample

PDMS (g)

RA (g)

TEOS (g)

Catalyst (µL)

RA (wt%)

SRTE-1

30

0

2.70

100

SRRA-1

30

1.70

2.24

SRRA-2

30

3.53

SRRA-3

30

SRRA-4

30

The RTV silicone rubber sheets cured with different contents of RA are presented in Table 1. PDMS (30 g) and dibutyltin dilaurate (100 µL) catalyst were used to prepare the RTV silicone


8

Page 9 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


rubber in all samples. RA was used as the crosslinking agent to replace TEOS partially and the total oxyethyl group amount of RA and TEOS was kept constant at 51.9 mmol. With the increase of RA from 0 to 7.66 g, the mass of TEOS decreased from 2.70 to 0.64 g. The increase from 0 to 20 wt% in the mass fraction of RA the silicone rubber allowed us to study the effects of RA on the morphologies, thermal, and mechanical properties of RTV silicone rubber. Characterizations and measurements FT-IR Fourier transform infrared (FT-IR) spectra were carried out on a Thermo Scientific Nicolet IS10 spectrometer (Nicolet, USA) by ATR (attenuated total reflectance). The spectra were recorded over the range 4000-600 cm-1 at 4 cm-1 resolution and averaged over 16 scans per sample. NMR 1H-NMR and

13

C-NMR spectra for RA were recorded at 40 oC on a AV400

spectrometer (Bruker, Germany) with frequency of 400.13 and 100.61 MHz, respectively. Deuterochloroform (CDCl3) were used as the solvent, tetramethylsilane (TMS) as an internal standard. The chemical shift values were referenced to the signals of CDCl3 and TMS. Density The density of samples was taken using pycnometer. Hardness The hardness of samples was measured using an LX-A durometer (Eide fort, China) at 23 oC and around 50% relative humidity (RH). TG The thermal stability analysis of samples was carried out on a TG209F1 (Netzsch, Germany). About 10 mg of the sample was heated from 25 oC to 800 oC at a heating rate of 10 o

C/min in an Al2O3 crucible in a nitrogen atmosphere.


9


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 38

Mechanical properties Five dumb-bell shape specimens were prepared and performed using a capacity 500 N of UTM6502 universal testing machine (Suns, China). The samples were characterized at 23 oC and around 50% RH using a cross-head speed of 500 mm/min and an average value of five time measurements was reported. SEM New sections of the silicone rubber were coated with gold. Then morphology studies were performed using a QUANTA 200 (FEI, Holland) scanning electron microscope at a voltage of 10 KV. EDS The element composition of silicone rubber was performed using X-ACT energy dispersive X-ray spectroscopy (OXFORD, England). DMA The dynamic mechanical analysis of the samples was performed using a DMA Q800 (TA, USA). The DMA characterized the samples at a frequency of 1 Hz from -135 oC to -75 oC with a heating rate of 3 oC/min by stretching mode. Average crosslinking density The cross-linking density of RTV silicone rubber was recalculated by using the equilibrium swelling method. RTV silicone rubber (about 0.2 g) and toluene (25 mL) were put into a sealed vessel at 25 oC. After being immersed in toluene for 48 h, the samples were weighed after being blotted with filter paper to remove the excess toluene, and then immersed into toluene again. The above step was repeated every 3 h until the swelling equilibrium was obtained. The crosslinking density is calculated using the following equations (1-2).37-38

ϕ = ( wo / ρ ) /[(ws − wo ) / ρ1 + wo / ρ ]

[

](

(1)

γ e = ρ / M C = − ln (1 − ϕ ) + ϕ + χ 1ϕ 2 / v o ϕ 1 / 3


)

(2)

10

Page 11 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Here, ϕ is the volume fraction. wo is the weight of the original sample. ρ is the density of the RTV silicone rubber before swelling. ws is the swollen weight of the RTV silicone rubber.

ρ1 is the density of the toluene and the value is 0.87 g/cm3. γ e is the crosslinking density. M C is the average molecular weight between crosslinking point. χ 1 is the interaction parameter of polymer and solvent, and the value is 0.465. vo is the molar volume of toluene and the value is 106.54 cm3/mol. RESULTS AND DISCUSSION Characterization of RA FT-IR analysis

Figure 2. FT-IR characterization. (a) RO, (b) ER, (c) aminopropyltriethoxysilane, and (d) RA. The FT-IR spectra of RO, ER, aminopropyltriethoxysilane, and RA are shown in Figure 2. From spectrum a and b in Figure 2, we note the disappearance of the C=O peak at 1688 cm-1 and the new characteristic peak of carbonyl groups at 1726 cm-1 which indicates that the ring opening


11


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 38

reaction of epoxy groups with carboxyl groups was completely accomplished. In addition, new characteristic peak of epoxide group at 910 cm-1 can be preliminary evidence for the appearance of epoxide groups in ER. In Figure 2d the absorption peak of epoxide groups at 910 cm-1 disappeared because of the epoxy ring opening reaction of ER with aminopropyltriethoxysilane. From spectrum c in Figure 2 we note the characteristic peak for the stretching vibration of N-H, bending vibration of N-H, and Si-O-C of aminopropyltriethoxysilane which are displayed at 3364 cm-1, 1593 cm-1, 957 cm-1, respectively. From spectrum c and d in Figure 2 we can see a wide characteristic peak for the N-H and -OH functional group at 3319 cm-1, and the characteristic peak for N-H at 1593 cm-1 moved to 1624 cm-1 which provided further evidences for the reaction of ER with aminopropyltriethoxysilane. NMR analysis The structure of RA was further confirmed by the 1H-NMR and 13C-NMR spectra in CDCl3 (see supporting information Figure S1). In the 1H-NMR spectrum clusters of signal peaks at 5.7 ppm and 5.3 ppm are related to the protons of the carbon-carbon double bond of rosin. Clusters of signal peaks at 1.2 ppm and 3.8 ppm are attributed to the chemical shifts of Si-O-CH2-CH3 protons, respectively. In the

13

C NMR spectrum the peaks at 120 ppm and 123 ppm that are

observed correspond to the carbon-carbon double bond of rosin. The characteristic peak at 178 ppm belongs to the carbonyl carbon. The two peaks at 58 ppm and 18 ppm are due to the chemical shifts of Si-O-C-C carbons. Characterization of RTV silicone rubber RTV silicone rubber was synthesized via a condensation reaction between PDMS and crosslinking agents with an organotin catalyst in a moist environment at room temperature. The


12

Page 13 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


crosslinking process was affected by cured catalysts, crosslinking agents, PDMS, moisture, and temperature under ambient conditions. In our experiments a certain amount of dibutyltin dilaurate catalyst and 5000 mpa.s PDMS were used in all samples, and the RTV silicone rubber showed better mechanical performances when the total oxyethyl group content of TEOS was 51.9 mmol. Hence, in order to study the effect of RA on the thermal and mechanical properties of RTV silicone rubber, RA was used as the crosslinking agent to replace TEOS partially and the total oxyethyl group amount of RA and TEOS was kept constant at 51.9 mmol. Morphologies The RTV silicone rubber with TEOS as a single crosslink agent is clear and colorless (Figure 3a). However, when RA partially replaces TEOS, the silicone rubber is opaque and the color becomes yellow (Figure 3b-3c), which is caused by the change of microstructure. Morphologies of the RTV silicone rubbers were investigated by scanning electron microscopy. The SEM images of SRTE-1, SRRA-3, and SRRA-4 RTV silicone rubber are presented in Figure 3d-3f. The surfaces of the silicone rubber become rough with the increase of RA. This can be attributed to the stronger polarity and rigid fused ring structures of RA, which increase the molecular chain rigidity of the polymer matrix.26 The rigid fused ring groups of rosin tend to aggregate by molecular polarity and rigidity which result in a microphase separation in silicone rubber.29, 39 The EDS spectra and elemental composition of SRRA-3 are presented in Figure 3g3i. The C element content (61.87%) of point A is higher than that of point B (28.94%). Point A represents the hard segment which is formed by the aggregation of rosin groups from RA. Point B represents the soft segment which is composed of polysiloxane with low C element content.39 The hard segment domains of rosin are well dispersed in the soft segment of polysiloxane.


13


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 38

Figure 3. Morphology and microstructure of RTV silicone rubber. (a) Photo image of SRTE-1. (b) Photo image of SRRA-3. (c) Photo image of SRRA-4. (d) SEM images of SRTE-1. (e) SEM images of SRRA-3. (f) SEM images of SRRA-4. (g) EDS spectra and element composition of point A in h. (h) EDS detection domain of SRRA-3. (i) EDS spectra and element composition of point B in h. Thermal properties The effects of the RA crosslinking agent on the thermal degradation behavior of RTV silicone rubber were characterized by TGA. The TG and DTG curves of RTV silicone rubber are presented in Figures 4a and 4b. The temperature of the 10% mass loss is delayed from 363 oC (SRTE-1) to 439 oC (SRRA-1), and it begins to decrease with increasing RA content (Figure 4c).


14

Page 15 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Furthermore, the temperatures of the 10% mass loss of all SRRA silicone rubbers are higher than that of SRTE-1 due to the introduction of RA with a phenanthrene ring structure. It is known that the polysiloxanes exhibit dissociation routes with low energy in the presence of hydroxylcontaining impurities.36 The hydroxyl groups can participate in a “back-biting” reaction to form volatile cyclic products at elevated temperatures.9, 36 The stable phenanthrene ring structure of RA increases the chain entanglements which restricted the molecular motion of polysiloxane chain.3, 40 These may result in preventing the rearrangement of Si-O bonds of polysiloxane to degrade the formation of cyclic oligomers and in decreasing the rate of thermal degradation.8 However, the C-N bond energy of amine groups is relatively lower so it breaks first at a given temperature.41 Therefore, the thermal stability of SRRA silicone rubbers decreases with increasing RA content because the amine groups increase as well. The greatest rate of mass loss temperature is also delayed from 400 oC (SRTE-1) to 653 oC (SRRA-1), which is an enhancement of 253 oC (Figure 4d). Because of the weak intermolecular force, the trace of residual hydroxyl groups in SRTE-1 silicone rubber could accelerate decomposition of PDMS, leading to rapid degradation at 400 oC.13-14 The incorporation of RA in silicone rubber results in restricting the mobility of the PDMS chains and preventing the rearrangement of Si-O bonds in polysiloxane. Therefore, polysiloxane is inhibited from degrading into forming cyclic oligomers.36 As a result, the decomposition temperature of RA modified silicone rubber increases to 653 oC. Note that these higher temperatures might facilitate random degradation because the chain mobility and molecular motion are relatively enhanced.1314

Ultimately the SRTE-1 cured without RA completely degraded into cyclic oligomers with no

residue left at 800 oC. But the silicone rubber cured with RA have more residual yield than that of the SRTE-1 (Figure 4e).32


15


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 38

Figure 4. Thermal stabilities of RTV silicone rubber. (a) TG curves of RTV silicone rubber. (b) DTG curves of RTV silicone rubber. (c) 10% mass loss temperature of RTV silicone rubber. (d) The greatest rate of mass loss temperature of RTV silicone rubber. (e) Residual yield at 800 o

C of RTV silicone rubber.

Mechanical properties The effects of RA on the mechanical properties of RTV silicone rubber were evaluated as illustrated in Figure 5. The test for mechanical properties of SRTE-1 and SRRA-3 (Figure 5a) and the stress-strain curves of RTV silicone rubber (Figure 5b) directly show that RTV silicone rubber using RA as the crosslinking agents possesses better mechanical properties. The tensile strength and the elongation at break of the rosin modified RTV silicone rubber are improved


16

Page 17 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


significantly (Figure 5c-5d). The tensile strength and the elongation at break of SRRA-3 are 1.25 MPa and 355%, respectively. Both of them increase more than double compared with the SRTE1 sample. The tensile modulus at 100% elongation of RTV silicone rubber improves from 0.352 MPa to 0.454 MPa (Figure 5e). These increases in tensile strength, elongation at break, and tensile modulus of the silicone rubber could be due to the positive role of hydrogen bonds between the N-H and C=O groups and the hydrogenated phenanthrene ring of RA which increases the amounts of formed rigid segments and promotes the chain entanglements.22, 25, 42 Although all the samples have the same total amount of oxyethyl groups, the crosslinking densities increases from 1.07×10-4 (SRTE-1) to 1.28×10-4 mol/cm3 (SRRA-2) when the RA crosslinking agent content increases from 0 to 10 wt%. In addition, the crosslinking densities of SRRA-3 and SRRA-4 decrease to 1.25×10-4 and 1.18×10-4 mol/cm3 with increasing the RA crosslinking agent content to 15 and 20 wt%, respectively. It indicates that the RA crosslinking agent can promote the crosslinking degree of silicone rubber. This should be attributed to the enhancement of the chain entanglement by the rigid and polar hydrogenated phenanthrene rings of rosin on the side chain of polysiloxane.22 Butane modified aminopropyltriethoxysilan (BA) crosslinking agent was synthesized to prepare BA cured silicone rubber (SRBA-1) to confirm this speculation (see supporting information). The crosslinking densities of the SRBA-1 and SRRA-3 silicone rubber are calculated by using the equilibrium swelling method and shown in Figure S3. The crosslinking density of SRRA-3 is 1.25×10-4 mol/cm3, which is higher than that of SRBA-1. Compared to the SRBA-1 silicone rubber, SRRA silicone rubbers were cured by the RA crosslinking agent with hydrogenated phenanthrene ring. The ethyl group (red color in Figure S2a) of BA crosslinking agent is smaller and more flexible than the hydrogenated phenanthrene ring group (blue color in Figure S2b) of


17


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 38

RA crosslinking agent. Therefore, the improved cross-linking density of SRRA is attributed to the enhancement of chain entanglement as the rigid and polar hydrogenated phenanthrene ring of the RA crosslinking agent. These results indicate that the incorporation of hydrogenated phenanthrene ring into the silicone rubber via the crosslinking reaction is an effective approach to enhance chain entanglement and increase the crosslinking density of the silicone rubber. Since crosslinking density is an important factor to influence the mechanical properties of silicone rubber, the effect of hydrogenated phenanthrene ring on the crosslinking density must be reflected in the mechanical properties of silicone rubber. The mechanical properties of SRBA-1 and SRRA-3 RTV silicone rubber were evaluated as illustrated in Figure S4. The tensile strength and the elongation at break of SRRA-3 are increased significantly to 1.25 MPa and 355%, respectively. The incorporation of RA as crosslinking agent caused the increase of crosslinking density of silicone rubber, while the tensile strength and the elongation at break increase significantly. This indicates that the RA crosslinking agent possesses both reinforcing and toughening effects on the silicone rubber, which cause the tensile modules of all SRRA samples are higher than that of the SRTE-1. However, when the toughening effect plays primary role to the silicone rubber, the increment of strain is more significant than the stress, which results in the decrease of the modulus (SRRA-2) while the crosslinking density and tensile strength both increase. These characterizations prove that the incorporation of hydrogenated phenanthrene ring into the silicone rubber result in the increase of crosslinking density and the improvement of mechanical properties as well. When the silicone rubbers are cured with lower RA crosslinking agent content (SRRA-1, SRRA-2 and SRRA-3), RA is found to be uniformly dispersed in the matrix, even though microphase separation is formed (From Figure S5b to Figure S5d). The mechanical properties of


18

Page 19 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


SRRA-1, SRRA-2 and SRRA-3 are improved with the increase of RA and higher than that of SRTE-1. However, the crosslinking density, the tensile strength and the elongation at break of the silicone rubber start to decrease when the RA crosslinking agent content exceeds 15 wt% (Figure 5b-5d and 5g). This can be due to the agglomeration and self-crosslinking from an overdose of RA crosslinking agent, which lead to inhomogeneous RA-rich domains and serious microphase separation in silicone rubber supported by SEM (Figure 3f).14, 29 Meanwhile, the agglomeration and self-crosslinking of RA crosslinking agent also induce losing many active sites, which results in the decrease of the crosslinking density. This indicates that uniform distribution of RA in the silicone rubber is beneficial for the improvement of mechanical properties. In addition, the density and the Shore hardness increase from 0.984 to 1.027 g/cm3 and from 18 to 26 A, respectively (Figure 5f and 5h). Therefore, the RA can effectively improve the mechanical properties of RTV silicone rubber which can be attributed to the strong rigidity of the phenanthrene ring structure of rosin, the increment of crosslinking density, and the uniform distribution of RA in silicone rubber as well.


19


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 38

Figure 5. Mechanical properties of RTV silicone rubber with different RA content. (a) Photos of mechanical properties test of SRTE-1 and SRRA-3. (b) Stress-train curves of RTV silicone rubber. (c) Tensile strength of RTV silicone rubber. (d) Elongation at break of RTV silicone rubber. (e) Tensile modulus at 100% elongation of RTV silicone rubber. (f) Density of RTV silicone rubber. (g) Crosslinking density of RTV silicone rubber. (h) Shore hardness of RTV silicone rubber.


20

Page 21 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Dynamic mechanical properties Figure 6a shows the E' curves for RTV silicone rubbers. The crosslinking density and the chemical structure play a key role in the E' of silicone rubber. The E' values of RTV silicone rubbers increase from 4050 MPa (SRTE-1) to 4577 MPa (SRRA-2) with the increase of the RA crosslinking agent. This is because the increment of the chain entanglements and the molecular chain rigidity impose considerable restrictions on the polysiloxane chain mobility of silicone rubber.22 When the RA crosslinking agent content reaches more than 15 wt%, the agglomeration and self-crosslinking from an overdose of RA crosslinking agent can lead to inhomogeneous RA-rich domains and serious microphase separation in silicone. Meanwhile, the agglomeration and self-crosslinking of RA crosslinking agent also induces losing many active sites, which results in the decrease of the cross-linking density. The inhomogeneous RA-rich domains, serious microphase separation and decrease of the cross-linking density cause the decrease of E’.

Figure 6. Dynamic mechanical properties of silicone rubber. (a) Storage modulus (E') curves of RTV silicone rubber. (b) Tan δ curves of RTV silicone rubber. (c) Tg of the RTV silicone rubber. The peak temperature of tan δ corresponds to the glass transition temperature (Tg). The tan δ curves show that each sample has only one clearly single Tg from -135 oC to -75 oC (Figure 6b).


21


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 38

The Tg of RTV silicone rubbers increased from -116.6 oC (SRTE-1) to -113.5 oC (SRRA-4) with the increase of the RA crosslinking agent because of the more rigid hydrogenated phenanthrene ring structure and correspondingly less flexible polysiloxane chains that impose restriction on the polysiloxane chain mobility (Figure 6c).20, 40, 43 CONCLUSION In summary, a novel crosslinking agent to RTV silicone rubber was prepared via an epoxide ring opening reaction of rosin based glycidyl ester with aminopropyltriethoxysilane. The thermal and mechanical properties of RTV silicone rubber are improved significantly by using RA as a crosslinking agent. Compared with SRTE-1 samples, the 10% mass loss temperature and the greatest rate of mass loss temperature of SRRA are delayed by 76 oC and 253 oC, respectively. In addition, the tensile strength and the elongation at break of SRRA-3 increase significantly. These phenomena are attributable to the synergistic effect of the hydrogenated phenanthrene ring structure of rosin, increment of crosslinking density, and uniform distribution of RA in the RTV silicone rubber. This study may facilitate an increase in the use of renewable bio-resource rosin to improve properties of RTV silicone rubber. ASSOCIATED CONTENT Supporting Information 1

H-NMR and 13C-NMR spectra of rosin modified aminopropyltriethoxysilane (RA); Synthesis of

butane modified aminopropyltriethoxysilane crosslinking agent (BA); Preparation of BA cured silicone rubber (SRBA-1); Crosslinking densities of SRBA-1 and SRRA-3; Mechanical properties of SRBA-1and SRRA-3; Morphology of SRRA RTV silicone rubbers.


22

Page 23 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


AUTHOR INFORMATION Corresponding Authors: He Liu, Email: [email protected] Shibin Shang, Email: [email protected] Zhanqian Song, Email: [email protected] Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. Qiaoguang Li⁑ and Xujuan Huang⁑ contributed equally to this work. Funding Sources National Natural Science Foundation of China, Key Laboratory of Biomass Energy and Materials of Jiangsu Province of China and Discipline Group Construction Project of CAFICIFP. Notes The authors declare no competing financial interest. ACKNOWLEDGMENT


23


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 38

This work was supported by National Natural Science Foundation of China (31570562), Key Laboratory of Biomass Energy and Materials of Jiangsu Province of China (JSBEM-S-201504) and Discipline Group Construction Project of CAF-ICIFP (LHSXKQ1). REFERENCES (1) Wang, D.; Klein, J.; Mejía, E. Catalytic Systems for the cross-linking of organosilicon polymers. Chem-Asian. J. 2017, 12, 1180-1197 DOI: 10.1002/asia.201700304 (2) Sun, Z.; Huang, Q.; Wang, Y.; Zhang, L.; Wu, Y. Structure and properties of silicone rubber/styrene–butadiene rubber blends with in situ interface coupling by thiol-ene click reaction. Ind. Eng. Chem. Res. 2017, 56, 1471-1477 DOI: 10.1021/acs.iecr.6b04146 (3) Zhao, Q.; Liu, Q.; Xu, H.; Bei, Y.; Feng, S. Preparation and characterization of room temperature vulcanized silicone rubber using α-amine ketoximesilanes as auto-catalyzed crosslinkers. RSC Adv. 2016, 6, 38447-38453 DOI: 10.1039/C6RA04445J (4) Ragheb, A. M.; Brook, M. A.; Hrynyk, M. Highly active, lipase silicone elastomers. Biomaterials 2005, 26, 1653-1664 DOI: 10.1016/j.biomaterials.2004.07.004 (5) Kumar, A.; Mollah, A. A.; Keshri, A. K.; Kumar, M.; Singh, K.; Rallabhandi, K. D. V. S.; Seelaboyina, R. Development of macroporous silicone rubber for acoustic applications. Ind. Eng. Chem. Res. 2016, 55, 8751-8760 DOI: 10.1021/acs.iecr.6b02051 (6) Wahba, L.; D'Arienzo, M.; Donetti, R.; Hanel, T.; Scotti, R.; Tadiello, L.; Morazzoni, F. In situ sol–gel obtained silica–rubber nanocomposites: influence of the filler precursors on the improvement of the mechanical properties. RSC Adv. 2013, 3, 5832-5844 DOI: 10.1039/C3RA22706E (7) Dong, X.; Niu, C.; Qi, M. Enhancement of electrorheological performance of electrorheological elastomers by improving TiO2 particles/silicon rubber interface. J. Mater.


24

Page 25 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Chem. C. 2016, 4, 6806-6815 DOI: 10.1039/C6TC01447J (8) Liu, Y.; Shi, Y.; Zhang, D.; Li, J.; Huang, G. Preparation and thermal degradation behavior of room temperature vulcanized silicone rubber-g-polyhedral oligomeric silsesquioxanes. Polymer 2013, 54, 6140-6149 DOI: 10.1016/j.polymer.2013.08.041 (9) Shi, Y.; Gao, X.; Zhang, D.; Liu, Y.; Huang, G. Synthesis and thermal properties of modified room temperature vulcanized (RTV) silicone rubber using polyhedral oligomeric silsesquioxane (POSS) as a cross linking agent. RSC Adv. 2014, 4, 41453-41460 DOI: 10.1039/C4RA06706A (10) Rezakazemi, M.; Vatani, A.; Mohammadi, T. Synergistic interactions between POSS and fumed silica and their effect on the properties of crosslinked PDMS nanocomposite membranes. RSC Adv. 2015, 5, 82460-82470 DOI: 10.1039/C5RA13609A (11) Han, Y.; Zhang, J.; Yang, Q.; Shi, L.; Qi, S.; Jin, R. Novel polymethoxylsiloxane-based crosslinking reagent and its in-situ improvement for thermal and mechanical properties of siloxane elastomer. J. Appl. Polym. Sci. 2008, 107, 3788-3795 DOI: 10.1002/app.27505 (12) Ramli, M. R.; Othman, M. B. H.; Arifin, A.; Ahmad, Z. Cross-link network of polydimethylsiloxane via addition and condensation (RTV) mechanisms. Part I: Synthesis and thermal

properties.

Polym.

Degrad.

Stabil.

2011,

96,

2064-2070

DOI:

10.1016/j.polymdegradstab.2011.10.001 (13) Chen, D.; Yi, S.; Fang, P.; Zhong, Y.; Huang, C.; Wu, X. Synthesis and characterization of novel room temperature vulcanized (RTV) silicone rubbers using octa[(trimethoxysilyl)ethyl]POSS

as

cross-linker.

React.

Funct.

Polym.

2011,

71,

502-511

DOI:

10.1016/j.reactfunctpolym.2010.12.010 (14) Chen, D.; Yi, S.; Wu, W.; Zhong, Y.; Liao, J.; Huang, C.; Shi, W. Synthesis and characterization of novel room temperature vulcanized (RTV) silicone rubbers using Vinyl-POSS


25


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

derivatives

as

cross

linking

agents.

Polymer

2010,

Page 26 of 38

51,

3867-3878

DOI:

10.1016/j.polymer.2010.06.028 (15) Chen, D.; Nie, J.; Yi, S.; Wu, W.; Zhong, Y.; Liao, J.; Huang, C. Thermal behaviour and mechanical properties of novel RTV silicone rubbers using divinyl-hexa[(trimethoxysilyl)ethyl]POSS

as

cross-linker.

Polym.

Degrad.

Stabil.

2010,

95,

618-626

DOI:

10.1016/j.polymdegradstab.2009.12.002 (16) Li, J.; Li, J.; Gao, Y.; Shang, S.; Song, Z.; Xiao, G. Taking advantage of a sustainable forest resource in agriculture: a value-added application of volatile turpentine analogues as botanical pesticides based on amphipathic modification and QSAR study. ACS Sustain. Chem. Eng. 2016, 4, 4685-4691 DOI: 10.1021/acssuschemeng.6b00819 (17) Gao, Y.; Tian, X.; Li, J.; Shang, S.; Song, Z.; Shen, M. Study on amphipathic modification and QSAR of volatile turpentine analogues as value-added botanical fungicides against cropthreatening pathogenic fungi. ACS Sustain. Chem. Eng. 2016, 4, 2741-2747 DOI: 10.1021/acssuschemeng.6b00236 (18) Jiang, F.; Hsieh, Y. L. Self-assembling of TEMPO oxidized cellulose nanofibrils as affected by protonation of surface carboxyls and drying methods. ACS Sustain. Chem. Eng. 2016, 4, 1041-1049 DOI: 10.1021/acssuschemeng.5b01123 (19) Zhuo, X.; Liu, C.; Pan, R.; Dong, X.; Li, Y. Nanocellulose mechanically isolated from amorpha

fruticosa

linn.

ACS

Sustain.

Chem.

Eng.

2017,

5,

4414-4420

DOI:

10.1021/acssuschemeng.7b00478 (20) Xin, J.; Li, M.; Li, R.; Wolcott, M. P.; Zhang, J. Green epoxy resin system based on lignin and tung oil and its application in epoxy asphalt. ACS Sustain. Chem. Eng. 2016, 4, 2754-2761 DOI: 10.1021/acssuschemeng.6b00256


26

Page 27 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(21) Liu, W.; Liu, T.; Liu, T.; Liu, T.; Xin, J.; Hiscox, W. C.; Liu, H.; Liu, L.; Zhang, J. Improving grafting efficiency of dicarboxylic anhydride monomer on polylactic acid by manipulating monomer structure and using comonomer and reducing agent. Ind. Eng. Chem. Res. 2017, 56, 3920-3927 DOI: 10.1021/acs.iecr.6b05051 (22) Rahman, M. A.; Lokupitiya, H. N.; Ganewatta, M. S.; Yuan, L.; Stefik, M.; Tang, C. Designing block copolymer architectures toward tough bioplastics from natural rosin. Macromolecules 2017, 50, 2069-2077 DOI: 10.1021/acs.macromol.7b00001 (23) Zheng, Y.; Yao, K.; Lee, J.; Chandler, D.; Wang, J.; Wang, C.; Chu, F.; Tang, C. Welldefined renewable polymers derived from gum rosin. Macromolecules 2010, 43, 5922-5924 DOI: 10.1021/ma101071p (24) Wang, H.; Liu, X.; Liu, B.; Zhang, J.; Xian, M. Synthesis of rosin-based flexible anhydridetype curing agents and properties of the cured epoxy. Polym. Int. 2009, 58, 1435-1441 DOI: 10.1002/pi.2680 (25) Ganewatta, M. S.; Ding, W.; Rahman, M. A.; Yuan, L.; Wang, Z.; Hamidi, N.; Robertson, M. L.; Tang, C. Biobased plastics and elastomers from renewable rosin via “living” ring-opening metathesis

polymerization.

Macromolecules

2016,

49,

7155-7164

DOI:

10.1021/acs.macromol.6b01496 (26) Huang, K.; Zhang, J.; Li, M.; Xia, J.; Zhou, Y. Exploration of the complementary properties of biobased epoxies derived from rosin diacid and dimer fatty acid for balanced performance. Ind. Crop. Prod. 2013, 49, 497-506 DOI: 10.1016/j.indcrop.2013.05.024 (27) Sacripante, G. G.; Zhou, K.; Farooque, M. Sustainable polyester resins derived from rosins. Macromolecules 2015, 48, 6876-6881 DOI: 10.1021/acs.macromol.5b01462 (28) Deng, L.; Ha, C.; Sun, C.; Zhou, B.; Yu, J.; Shen, M.; Mo, J. Properties of bio-based epoxy


27


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 38

resins from rosin with different flexible chains. Ind. Eng. Chem. Res. 2013, 52, 13233-13240 DOI: 10.1021/ie4005223 (29) Xu, T.; Liu, H.; Song, J.; Shang, S.; Song, Z.; Zou, K.; Yang, C. Synthesis and characterization of novel fluorosilicone rubber using imide modified vinyl-containing fluorosilicone resin as cross-linker. J. Polym. Sci. Pol. Chem.

2015, 53, 1769-1776 DOI:

10.1002/pola.27619 (30) Lee, S.; Lee, K.; Kim, Y. W.; Shin, J. Preparation and characterization of a renewable pressure-sensitive adhesive system derived from ε-decalactone,l-lactide, epoxidized soybean oil, and

rosin

ester.

ACS

Sustain.

Chem.

Eng.

2015,

3,

2309-2320

DOI:

10.1021/acssuschemeng.5b00580 (31) Ganewatta, M. S.; Miller, K. P.; Singleton, S. P.; Mehrpouya-Bahrami, P.; Chen, Y. P.; Yan, Y.; Nagarkatti, M.; Nagarkatti, P.; Decho, A. W.; Tang, C. Antibacterial and biofilm-disrupting coatings from resin acid-derived materials. Biomacromolecules 2015, 16, 3336-3344 DOI: 10.1021/acs.biomac.5b01005 (32) Deng, L.; Shen, M.; Yu, J.; Wu, K.; Ha, C. Preparation, characterization, and flame retardancy of novel rosin-based siloxane epoxy resins. Ind. Eng. Chem. Res. 2012, 51, 81788184 DOI: 10.1021/ie201364q (33) Xu, T.; Liu, H.; Song, J.; Shang, S. B.; Song, Z. Q.; Chen, X. J.; Yang, C. Synthesis and characterization of imide modified poly(dimethylsiloxane) with maleopimaric acid as raw material. Chinese Chem. Lett. 2015, 26, 572-574 DOI: 10.1016/j.cclet.2015.01.011 (34) Xu, T.; Liu, H.; Song, J.; Shang, S. B.; Song, Z. Q.; Zou, K.; Yang, C. Synthesis and characterization of maleated rosin-modified fluorosilicone resin and its fluorosilicone rubber. J. Appl. Polym. Sci. 2015, 132, 41888 DOI: 10.1002/app.41888


28

Page 29 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(35) Huang, K.; Zhang, P.; Zhang, J.; Li, S.; Li, M.; Xia, J.; Zhou, Y. Preparation of biobased epoxies using tung oil fatty acid-derived C21 diacid and C22 triacid and study of epoxy properties. Green Chem. 2013, 15, 2466-2475 DOI: 10.1039/C3GC40622A (36) Han, Y.; Zhang, J.; Shi, L.; Qi, S.; Cheng, J.; Jin, R. Improvement of thermal resistance of polydimethylsiloxanes with polymethylmethoxysiloxane as crosslinker. Polym. Degrad. Stabil. 2008, 93, 242-251 DOI: 10.1016/j.polymdegradstab.2007.09.010 (37) Xu, Q.; Pang, M.; Zhu, L.; Zhang, Y.; Feng, S. Mechanical properties of silicone rubber composed of diverse vinyl content silicone gums blending. Mater. Design. 2010, 31, 4083-4087 DOI: 10.1016/j.matdes.2010.04.052 (38) Pal, K.; Rajasekar, R.; Kang, D. J.; Zhang, Z. X.; Pal, S. K.; Das, C. K.; Kim, J. K. Effect of fillers on natural rubber/high styrene rubber blends with nano silica: morphology and wear. Mater. Design. 2010, 31, 677-686 DOI: 10.1016/j.matdes.2009.08.014 (39) Kang, D. W.; Kim, Y. M. Preparation and properties of poly(methyltrifluoropropylsiloxaneb-imide) copolymer. I. J. Appl. Polym. Sci. 2002, 85, 2867-2874 DOI: 10.1002/app.10885 (40) Liu, X.; Xin, W.; Zhang, J. Rosin-derived imide-diacids as epoxy curing agents for enhanced

performance.

Bioresource

Technol.

2010,

101,

2520-2524

DOI:

10.1016/j.biortech.2009.11.028 (41) Jiao, L.; Xiao, H.; Wang, Q.; Sun, J. Thermal degradation characteristics of rigid polyurethane foam and the volatile products analysis with TG-FTIR-MS. Polym. Degrad. Stabil. 2013, 98, 2687-2696 DOI: 10.1016/j.polymdegradstab.2013.09.032 (42) Dai, X.; Zhang, Y.; Gao, L.; Bai, T.; Wang, W.; Cui, Y.; Liu, W. A mechanically strong, highly stable, thermoplastic, and self-healable supramolecular polymer hydrogel. Adv. Mater. 2015, 27, 3566-3571 DOI: 10.1002/adma.201500534


29


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 38

(43) Wang, H.; Wang, H.; Zhou, G. Synthesis of rosin-based imidoamine-type curing agents and curing behavior with epoxy resin. Polym. Int. 2011, 60, 557-563 DOI: 10.1002/pi.2978


30

Page 31 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


For Table of Contents Use Only

SYNOPSIS: Rosin modified aminopropyltriethoxysilane is an efficient crosslinking agent to significantly improve the properties of room temperature vulcanized silicone rubber.

ABSTRACT GRAPHIC


31


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 1. Synthetic route of RTV silicone rubber. Rosin (RO), glycidyl ester of rosin acid (ER), and rosin modified aminopropyltriethoxysilane (RA) 99x57mm (300 x 300 DPI)


Page 32 of 38

Page 33 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 2. FT-IR characterization. (a) RO, (b) ER, (c) aminopropyltriethoxysilane, and (d) RA. 68x58mm (300 x 300 DPI)



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 34 of 38

Figure 3. Morphology and microstructure of RTV silicone rubber. (a) Photo image of SRTE-1. (b) Photo image of SRRA-3. (c) Photo image of SRRA-4. (d) SEM images of SRTE-1. (e) SEM images of SRRA-3. (f) SEM images of SRRA-4. (g) EDS spectra and element composition of point A in h. (h) EDS detection domain of SRRA-3. (i) EDS spectra and element composition of point B in h. 115x78mm (300 x 300 DPI)


Page 35 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 4. Thermal stabilities of RTV silicone rubber. (a) TG curves of RTV silicone rubber. (b) DTG curves of RTV silicone rubber. (c) 10% mass loss temperature of RTV silicone rubber. (d) The greatest rate of mass loss temperature of RTV silicone rubber. (e) Residual yield at 800 oC of RTV silicone rubber. 107x67mm (300 x 300 DPI)



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 5. Mechanical properties of RTV silicone rubber with different RA content. (a) Photos of mechanical properties test of SRTE-1 and SRRA-3. (b) Stress-train curves of RTV silicone rubber. (c) Tensile strength of RTV silicone rubber. (d) Elongation at break of RTV silicone rubber. (e) Tensile modulus at 100% elongation of RTV silicone rubber. (f) Density of RTV silicone rubber. (g) Crosslinking density of RTV silicone rubber. (h) Shore hardness of RTV silicone rubber. 158x139mm (300 x 300 DPI)


Page 36 of 38

Page 37 of 38

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Figure 6. Dynamic mechanical properties of silicone rubber. (a) Storage modulus (E') curves of RTV silicone rubber. (b) Tan δ curves of RTV silicone rubber. (c) Tg of the RTV silicone rubber. 48x14mm (300 x 300 DPI)



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Rosin modified aminopropyltriethoxysilane is an efficient crosslinking agent to significantly improve the properties of room temperature vulcanized silicone rubber. 48x31mm (300 x 300 DPI)


Page 38 of 38