Recombinant Spidroins Fully Replicate Primary ... - ACS Publications

ligation involve either side chain bonding (e.g. SpyTag-SpyCatcher), which produces branched. 80 structures that could negatively affect material prop...
0 downloads 0 Views 1MB Size
Subscriber access provided by MT ROYAL COLLEGE

Article

Recombinant Spidroins Fully Replicate Primary Mechanical Properties of Natural Spider Silk Christopher H. Bowen, Bin Dai, Cameron J. Sargent, Wenqin Bai, Pranay Ladiwala, Huibao Feng, Wenwen Huang, David L Kaplan, Jonathan M. Galazka, and Fuzhong Zhang Biomacromolecules, Just Accepted Manuscript • DOI: 10.1021/acs.biomac.8b00980 • Publication Date (Web): 06 Aug 2018 Downloaded from http://pubs.acs.org on August 7, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

TITLE: Recombinant Spidroins Fully Replicate Primary Mechanical

2

Properties of Natural Spider Silk

3 4

AUTHORS: Christopher H. Bowen1,†, Bin Dai1,†, Cameron J. Sargent2, Wenqin Bai1, Pranay

5

Ladiwala1, Huibao Feng1, Wenwen Huang4, David L. Kaplan4, Jonathan M. Galazka5, Fuzhong

6

Zhang1-3,*

7 8

AFFILIATIONS:

9

1

Department of Energy, Environmental and Chemical Engineering,

10

2

Division of Biological & Biomedical Sciences,

11

3

Institute of Materials Science & Engineering,

12

Washington University in St. Louis, Saint Louis, MO 63130, USA

13

4

Department of Biomedical Engineering, Tufts University, Medford, MA 02155, USA

14

5

Space Biosciences Division, Ames Research Center, National Aeronautics and Space

15

Administration, Moffett Field, CA 94035, USA

16



17

*

These authors contributed equally. Correspondence to: [email protected]

18 19 20 21 22 23 1 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

24

ABSTRACT:

25

Despite significant efforts to engineer their heterologous production, recombinant spider

26

silk proteins (spidroins) have yet to replicate the unparalleled combination of high strength and

27

toughness exhibited by natural spider silks, preventing their use in numerous mechanically-

28

demanding applications. To overcome this long-standing challenge, we have developed a

29

synthetic biology approach combining standardized DNA part assembly and split intein-

30

mediated ligation to produce recombinant spidroins of previously unobtainable size (556 kDa),

31

containing 192 repeat motifs of the Nephila clavipes dragline spidroin. Fibers spun from our

32

synthetic spidroins are the first to fully replicate the mechanical performance of their natural

33

counterparts by all common metrics, i.e. tensile strength (1.03 ± 0.11 GPa), modulus (13.7 ± 3.0

34

GPa), extensibility (18 ± 6%), and toughness (114 ± 51 MJ/m3). The developed process reveals a

35

path to more dependable production of high-performance silks for mechanically-demanding

36

applications while also providing a platform to facilitate production of other high-performance

37

natural materials.

38 39

INTRODUCTION:

40

Dragline spider silk is among the strongest and toughest biological materials, capable of

41

outperforming most synthetic polymers and even some metal alloys.1-3 These remarkable

42

properties have resulted in a growing list of potential high-performance material applications for

43

spider silks ranging from impact resistant textiles to monofilament surgical sutures;

44

unfortunately, the impracticalities of spider farming have long restricted the practical

45

development of such applications.2,4 The resulting demand for a dependable source of high-

46

performance silk fibers has driven both academic and industrial research toward production of

2 ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

47

recombinant spidroins in engineered hosts including bacteria, yeasts, plants, and animals.5-9

48

While providing significant technical and scientific advances, these efforts have so far been

49

unable to yield recombinant silk fibers that fully replicate natural spider silk's unparalleled

50

combination of mechanical properties (i.e. high strength, modulus, extensibility, and toughness),

51

due in part to an inability to stably produce highly repetitive, high molecular weight (MW)

52

proteins in heterologous hosts.2,4,9

53

Natural dragline spidroins are typically very large (>300 kDa), highly repetitive proteins

54

that contain hundreds of tandem repeats of glycine- and alanine-rich sequences.10,11 As with most

55

polymers, the size of these spidroins is expected to positively correlate with tensile strength (up

56

to a limiting MW) due to an increased density of interchain interactions and entanglements and

57

fewer chain-end defects.9,12 Indeed, previous work has demonstrated a clear correlation between

58

MW and strength for recombinant Nephila clavipes dragline fibers, with the largest spidroin (96-

59

mer, 285 kDa) yielding the strongest recombinant fiber reported to date (σ ≈ 550 MPa).9

60

However, the upper limit for the strength-to-MW relationship in spidroins is currently unclear

61

and despite the apparent need for even larger spidroins to yield fibers with mechanical properties

62

on par with natural spider silk (σ = 0.8-1.2 GPa for N. clavipes dragline, see Table S1),

63

heterologous production of spidroins larger than 285 kDa in quantities sufficient for fiber testing

64

has proven to be extremely difficult.9 Challenges of heterologous production arise from a series

65

of issues including genetic instability of long and highly repetitive DNA sequences, translation

66

inhibition by complex mRNA secondary structures, a high demand for glycine and alanine

67

tRNAs, and overall metabolic burden caused by spidroin overexpression.4,9 To overcome these

68

long-standing challenges, we envisioned a synthetic biology platform employing standardized

69

DNA part assembly to facilitate covalent, post-translational ligation of the largest spidroins that

3 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

70

can be stably expressed in engineered Escherichia coli (i.e. 96-mer), permitting production of

71

spidroins of previously unobtainable MW that can be used to generate fibers with exceptional

72

mechanical properties (Figure 1).

73

Of the various biochemical approaches available for post-translational protein ligation,

74

split inteins (SIs) are perhaps the best suited for generating high MW proteins for material

75

applications. SIs are peptide auto-processing domains that, when fused to separately expressed

76

proteins, catalyze spontaneous splicing reactions, covalently linking their fusion partners via a

77

peptide bond and leaving only a few residues (≤ 6) at the ligation site.13 When SIs are used to

78

ligate 96-mer spidroins, these residues are unlikely to affect the properties of the much larger

79

ligated product (6720 amino acids total). Other common approaches for post translational

80

ligation involve either side chain bonding (e.g. SpyTag-SpyCatcher), which produces branched

81

structures that could negatively affect material properties, or catalysis by separately expressed

82

proteins (e.g. Sortase A), which increases process complexity.14 For these reasons, we chose to

83

employ SI-based ligations for our envisioned platform, such that ligation of an N-intein (IntN)-

84

fused 96-mer spidroin (96N) with a C-intein (IntC)-fused 96-mer (C96) would yield a 556 kDa,

85

192-mer spidroin (Figure 1e).

4 ACS Paragon Plus Environment

Page 4 of 29

Page 5 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

86 87

Figure 1. Process schematic for split intein-mediated ligation of spider silk proteins with

88

unprecedented molecular weight and mechanical properties. (a) The highly repetitive core of

89

natural N. clavipes dragline silk protein MaSp1 (shown as a simplified consensus peptide

90

sequence) was reduced to a single repeat unit (1-mer). Note, while "-mer" often refers to a small

91

molecule or individual amino acid, the abbreviation here refers to the 35 amino acid peptide that

92

constitutes the repeating unit of the larger spidroin. (b) The 1-mer DNA sequence was combined

93

in silico with 5' UTR, RBS, split intein (SI), and terminator sequences, which were then

94

computationally optimized for microbial production. (c) The optimized DNA sequences were

95

assembled within the framework of a standardized DNA part assembly system termed SI-Bricks

96

to yield complementary IntC- or IntN-fused 96-mer constructs. (d) Constructs were transformed

97

to metabolically engineered E. coli for bioproduction. (e) Cell cultures were mixed and lysed to

98

initiate SI-mediated covalent ligation of 96-mer spidroins to yield a 192-mer, 556 kDa product.

99

(f) The ligated product was purified and spun into fibers for mechanical testing. Scale bar

100

indicates 5 µm.

101

5 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

102

MATERIALS AND METHODS:

103

Strains and growth conditions. E. coli NEB 10-beta (NEB10β) was used for all plasmid

104

cloning and protein production. For all cloning, E. coli strains were cultured in Terrific Broth

105

(TB) containing 24 g/L yeast extract, 20 g/L tryptone, 0.4% v/v glycerol, 17 mM KH2PO4, and

106

72 mM K2HPO4 at 37 °C with appropriate antibiotics (50 µg/mL kanamycin and 30 µg/mL

107

chloramphenicol). M9 glucose medium with tryptone supplement (2% w/v glucose, 1x M9 Salts,

108

75 mM MOPS pH 7.4, 12 g/L tryptone, 5 mM sodium citrate, 2 mM MgSO4·7H2O, 100 µM

109

FeSO4·7H2O, 100 µM CaCl2·2H2O, 3 µM thiamine, 1x micronutrients [40 µM ZnSO4·7H2O, 20

110

µM CuSO4·5H2O, 10 µM MnCl2·4H2O, 4 µM H3BO3, 0.4 µM (NH4)6Mo7O24·4H2O, and 0.3 µM

111

CoCl2·6H2O]) was used for protein production in bioreactors.

112

Chemicals and reagents. Unless otherwise noted, all chemicals and reagents were

113

obtained from MilliporeSigma. Plasmid purification and gel extraction kits were purchased from

114

iNtRON Biotechnology. FastDigest restriction enzymes and T4 DNA ligase were purchased

115

from Thermo Fisher Scientific and used for all digestions and ligations following the

116

manufacturer's suggested protocols.

117

Genetic assembly of 64- and 96-mer spidroins. The multimeric spidroin DNA

118

sequences were constructed as SI-Bricks genetic parts based on a method modified from

119

previous work (Supplementary Note 1, Figure S1, Figure S2).5,9 Specifically, an optimized

120

coding sequence of 1-mer N. clavipes MaSp1 was chemically synthesized by Integrated DNA

121

Technologies. To fit the SI-Bricks standard, the DNA sequence was flanked on the 5' end by

122

restriction sites 5'-KpnI/NheI-3' and on the 3' end by restriction sites 5'-SpeI/Kpn2I-3'. The

123

sequence was inserted between restriction sites KpnI/Kpn2I of a medium copy (pBBR1

124

replication origin), chloramphenicol resistance (CmR) SI-Bricks expression vector, resulting in

6 ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

125

plasmid p1 (Figure S2b). To begin the recursive directional genetic assembly, plasmid p1 was

126

linearized by digestion with NheI and ligated with another 1-mer sequence digested by

127

NheI/SpeI. The ligation was transformed to NEB10β for amplification, yielding plasmid p2

128

containing 2-mer spidroin (Figure S2c). The same procedure was repeated for p2, with insertion

129

of a linearized 2-mer sequence, to yield plasmid p4, and the process was repeated until p64 (32-

130

mer + 32-mer) and p96 (64-mer + 32-mer) were obtained (Figure S2d). Because the annealing of

131

NheI/SpeI overhangs produces a non-cutting sequence, digestion with NheI was used to confirm

132

proper insert direction after each ligation iteration.

133

Construction and sequence optimization of silk-SI-fusion proteins. N- and C-intein

134

amino acid sequences (CfaN and CfaC, respectively) were obtained from a recent publication15

135

and prepared as SI-Bricks standard parts as described below. To ensure substantial production of

136

the final SI-fused silk proteins, the SI coding sequences were optimized for E. coli expression

137

within the genetic context of all flanking sequences using a combination of computational

138

approaches.16,17 Specifically, an initial DNA sequence was computationally designed that

139

contains (from 5’ to 3’) a 5' UTR/RBS containing the EcoRI/BglII sites, a short coding sequence

140

(5'-ATGGCTAAGACTAAA-3') intended to increase translation initiation rate as described

141

previously,18 the CfaC coding sequence, the KpnI/NheI sites, and the multimeric silk sequence.

142

Within this genetic context, only the CfaC sequence was set variable and optimized using a

143

modified E. coli codon usage table with extra weight given to 5' mRNA structure minimization

144

within the sequence optimization algorithm.19 The resulting optimized CfaC sequence (including

145

5' UTR/RBS and necessary SI-Bricks restriction sites; Table S2) was synthesized as a gblock

146

fragment by Integrated DNA Technologies and was inserted 5' of the 64-mer or 96-mer

147

sequences by digestion/ligation with EcoRI/KpnI to yield plasmids pC64 and pC96, which encode

7 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 29

148

fusion proteins C64 and C96, respectively (Table S3, Figure S2e). Similarly, to codon-optimize

149

CfaN, an initial DNA sequence was computationally designed containing (from 5’ to 3’) the

150

multimeric silk sequence, the SpeI/Kpn2I restriction sites, a CfaN coding sequence, and the

151

BamHI/XhoI sites. Within this context, only the CfaN coding sequence was subjected to the

152

optimization process. The resulting CfaN sequence (Table S2), including SI-Bricks restriction

153

sites, was synthesized and inserted 3' of the 64-mer and 96-mer sequences by digestion/ligation

154

with Kpn2I/XhoI to yield plasmids p64N and p96N, which encode fusion proteins 64N and 96N,

155

respectively (Figure S2e). The resulting SI-Bricks parts/vectors allow for easy swapping of any

156

IntC, multimeric material protein, or IntN of interest by digestion with EcoRI/KpnI, KpnI/Kpn2I,

157

or Kpn2I/XhoI, respectively. Additionally, the presence of NheI/SpeI sites allows for in situ

158

recursive directional genetic assembly of any large, repetitive material proteins of interest

159

(Supplementary Note 1, Figure S1, Figure S2). Upregulation of GlyV tRNA production. In addition to sequence optimizations, cellular

160 161

glycyl

162

spidroin overexpression. The glyV tRNA coding sequence and its native promoter were PCR-

163

amplified from the NEB10β genomic DNA (Table S2) and cloned between AatII/XhoI sites of a

164

medium copy vector carrying p15A replication origin and Kanamycin resistance (KanR), yielding

165

plasmid pGlyV (Table S3). For all spidroin expression, pGlyV was co-transformed with the

166

spidroin plasmid.

tRNA levels were also upregulated to meet the high demands on

glycyl

tRNA posed by

167

Shake flask cultures. For initial ligation tests (Figure S3), protein production was carried

168

out in shake flasks. Transformants were cultured overnight in 50 mL TB medium at 37 °C on an

169

orbital shaker. Overnight 50 mL cultures were then used to inoculate 500 mL fresh TB medium

170

in Erlenmeyer flasks at an initial OD600 = 0.08. Cultures were grown at 37 °C with orbital

8 ACS Paragon Plus Environment

Page 9 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

171

shaking to OD600 = 6, then induced by addition of 1 mM IPTG and cultured for an additional 6

172

hours at 30 °C with orbital shaking.

173

Bioproduction in fed-batch bioreactors. All spidroins were ultimately produced in 2 L

174

fed-batch bioreactors (Bioflo120, Eppendorf). Transformants were cultured overnight in 50 mL

175

TB medium at 37 °C on an orbital shaker. The overnight cultures were then used to inoculate 1 L

176

glucose M9 medium with tryptone supplement at an initial OD600 = 0.08. After overnight

177

incubation at 37 °C with orbital shaking, 1 L cultures were pelleted by centrifugation at 4500 x g

178

for 10 min and resuspended in 300 mL sterile resuspension medium (250 mM MOPS pH 7.4,

179

2.5% w/v glucose, 60 g/L tryptone, 25 mM sodium citrate, 10 mM MgSO4, 500 µM

180

FeSO4·7H2O, 15 µM thiamine, 5x micronutrients). The resuspended cultures were then added to

181

an autoclaved 2 L Bioflo120 heat-blanketed bioreactor containing 1.2 L water and 1.15x M9

182

salts. Sterile CaCl2·2H2O was added to a final concentration of 100 µM. Antifoam 204 was

183

added as needed to minimize foaming (approximately 0.01% v/v). Agitation and air flow was

184

regulated to maintain approximately 70% dissolved oxygen (DO). After consumption of the

185

initial 0.5% w/v glucose (as judged by ∆DO), a sterile substrate feed (20% w/v glucose, 48 g/L

186

tryptone, and 10 g/L MgSO4·7H2O) was initiated to maintain a linear growth rate. Reactors were

187

induced at OD600 = 80 by addition of 1 mM IPTG and culture temperature was reduced to 30 °C.

188

Cultures were collected four hours after induction. Based on densitometric analysis of

189

Coomassie Blue-stained SDS-PAGE gels (Figure S4), final product titer for 96-mer reactants

190

was estimated at approximately 2 g/L or 63 mg/g cell dry weight.

191

Protein ligation. Cell cultures were pelleted by centrifugation at 4500 x g for 30 min.

192

Pellets from complimentary SI-fused spidroins (e.g. 96N and C96 or 64N and C64) were combined

193

at a 1:1 reactant ratio based on densitometric analysis of Coomassie Blue-stained SDS-PAGE

9 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

194

gels. Mixed pellets were resuspended in sonication buffer (300 mM NaCl, 20 mM MOPS pH

195

7.4, 2 mM TCEP, 1 mM PMSF) and sonicated using a QSonica Q700 sonicator (Qsonica) for 10

196

min (5s on, 10s off). Sonicated resuspensions were pelleted by centrifugation at 25,000 x g for

197

30 min to remove supernatants. Pellets were resuspended in ligation buffer (8 M urea, 20 mM

198

MOPS pH 7.4, 300 mM NaCl, and 2 mM TCEP) and stirred at 37 °C for 24 h to dissolve SI-

199

fused spidroins and ensure complete ligation. The mixtures were then centrifuged at 25,000 x g

200

for 1 h to remove cell debris and undissolved proteins.

201

Protein purification. The purification protocol was modified from previous methods.9

202

Specifically, ligated spidroins in ligation buffer were acidified to pH 4.0 with acetic acid.

203

Ammonium sulfate was then added to a final concentration of 1.2 M. The mixture was then

204

centrifuged at 40,000 x g for 30 min. The pellet was discarded, and additional ammonium sulfate

205

was added to the supernatant to a final concentration of 2.3 M. After stirring for 1 h, the mixture

206

was centrifuged again at 40,000 x g for 15 min., yielding a pellet containing approximately 75%

207

spidroin as estimated by Coomassie Blue-stained SDS-PAGE gels. The supernatant was

208

discarded, and the pellet was resuspended in SEC buffer (8 M urea, 10 mM ammonium

209

bicarbonate pH 10) for further purification by size-exclusion chromatography. SEC purifications

210

were performed on an AKTA Pure Chromatography System (GE Healthcare Life Sciences)

211

using a HiPrep 16/60 Sephacryl S-500 HR column (for 128-mer and 192-mer) or a HiPrep 16/60

212

Sephacryl S-400 HR column (for 96-mer). Proteins were separated using an isocratic elution

213

with SEC buffer at a flow rate of 0.5 mL/min. Fractions containing greater than 90% ligation

214

product, as determined by SDS-PAGE gel densitometry, were collected, resulting in

215

approximately 5% final product recovery as judged by product dry mass. SEC-purified fractions

10 ACS Paragon Plus Environment

Page 10 of 29

Page 11 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

216

were combined and dialyzed in 10K MWCO SnakeSkin dialysis tubing (ThermoFisher

217

Scientific), followed by lyophilization.

218

Ligation kinetics analysis. For kinetics analysis, 64-mer protein concentrations in crude

219

lysates were estimated by densitometric analysis of Coomassie Blue-stained SDS-PAGE gels.

220

Based on estimated concentrations, fully sonicated resuspensions of 64C and N64 in ligation

221

buffer were combined to give final concentrations of 100 µM for both 64C and N64 in a final

222

volume of 500 µL. These mixtures were pelleted by centrifugation, and pellets were resuspended

223

in 500 µL of desired test buffer pre-incubated at the desired test temperature. Reactions were

224

quenched by transferring 5 µL of reaction to 95 µL of Laemmli sample buffer preheated to 100

225

°C and continuing boiling for 10 min.

226

SDS-PAGE and densitometric analysis. All SDS-PAGE gels were 1 mm thick,

227

discontinuous with 3% stacking gel, and hand cast at the indicated percentages. Samples were

228

prepared at 1 mg/mL or 5 µM total protein in Laemmli sample buffer (2% SDS, 10% glycerol,

229

60 mM Tris pH 6.8, 0.01% bromophenol blue, 100 µM DTT). Gels were run on Mini-

230

PROTEAN Tetra Cells (Bio-Rad) in 1x Tris-glycine SDS buffer (25 mM Tris base, 250 mM

231

glycine, 0.1% w/v SDS), until just before the dye front exited the gel. Gels were stained in

232

Coomassie Blue solution (50% methanol, 10% w/v acetic acid, 1 g/L Coomassie Brilliant Blue)

233

for a minimum of one hour at room temperature with gentle agitation and destained in

234

Coomassie Blue destain buffer (40% v/v methanol, 10% v/v acetic acid) for a minimum of one

235

hour. Gels were imaged on an Azure c600 Imager (Azure Biosystems). All densitometry analysis

236

was performed with the AzureSpot Analysis Software (Azure Biosystems). Images were

237

background subtracted with a built-in automatic lane edge subtraction algorithm. Protein band

238

intensities were integrated by the AzureSpot software. Ligation yield was calculated as the

11 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

239

integrated intensity of the product band over the sum of both reactant and product band areas.

240

Purity was calculated as the integrated intensity of the product band over the integrated intensity

241

of all other bands. Spidroin titer was calculated as the integrated intensity of the spidroin band

242

over the integrated intensity of all other bands multiplied by the measured cell density (OD600) of

243

culture at the time of sampling and 150 mg/L/OD600 (150 mg/L/OD600 is an average typical total

244

protein titer for E. coli grown in glucose minimal medium).20

245

Fiber spinning and mechanical testing. Fiber spinning and mechanical testing were

246

performed following a protocol modified from previous methods.9,21,22 Lyophilized spidroin

247

powders were dissolved in hexafluorisopropanol (HFIP) to 17% w/v. This protein dope was

248

loaded to a 100 µL Hamilton gastight syringe (Hamilton Robotics) fitted with a 23s gauge (116

249

µm inner diameter, 1.71 inch length) needle. The syringe was fitted to a Harvard Apparatus

250

Pump 11 Elite syringe pump (Harvard Apparatus), and the dope was extruded into a 95% v/v

251

methanol bath at 5 µL/min. Extruded fibers were then transferred to a 75% v/v methanol bath

252

and carefully extended at approximately 1 cm/s to the maximum draw ratio (~600%) without

253

fiber fracture. Extended fibers were removed from the bath and held under tension until visibly

254

dry. Segments of post-drawn fibers (20 mm) were carefully laid exactly vertical across a 5 mm

255

(vertical) x 15 mm (horizontal) opening cut into a 20 mm x 20 mm piece of cardstock and fixed

256

with adhesive tape at both ends of the opening. Diameters of mounted fibers were then measured

257

by light microscopy, averaging measurements at three points along the fiber axis (Tables S4-S6,

258

Figure S5a). Mechanical properties were measured by axial pull tests on an MTS Criterion

259

Model 41 universal test frame fitted with a 1 N load cell (MTS Systems Corporation). Cardstock

260

holders were mounted between two opposing spring-loaded grips, and the supporting edges were

261

carefully cut. Pull tests were conducted at a relative humidity of 30% and temperature of 22 °C,

12 ACS Paragon Plus Environment

Page 12 of 29

Page 13 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

262

with a constant crosshead speed of 10 mm/min. Stress-strain curves were recorded by the MTS

263

TW Elite test suite at a sampling rate of 50 Hz. Fiber breaks were recorded when a 90% drop

264

from peak stress was detected. All mechanical properties were automatically calculated by the

265

MTS TW Elite test suite. Ultimate tensile strength was calculated as the maximum measured

266

load over the initial fiber cross-sectional area (‫ ݎߨ = ܣ‬ଶ ), as determined from measured initial

267

diameters (see Supplementary Note 2 for an analysis of the validity of this approach). Modulus

268

was calculated as the slope of a linear least squares fit to the stress/strain data of the initial elastic

269

region. Toughness was calculated as the area under the total stress/strain curve divided by the

270

initial fiber volume (ܸ = ߨ‫ ݎ‬ଶ ℎ) as calculated from measured initial fiber diameters and set initial

271

gage length of 5 mm. For each protein, a total of 14 fibers were measured in this manner.

272

Light microscopy. Fiber diameters were measured using images acquired with a Zeiss

273

Axio Observer ZI Inverted Microscope equipped with a phase contrast 20x objective lens and the

274

Axiovision LE software (Zeiss). For morphological analysis and further confirmation of fiber

275

diameters, additional images were acquired with a Nikon Eclipse TiE Inverted Microscope

276

equipped with a 60x objective and analyzed using the Nis-Elements software (Nikon; Figure

277

S5a).

278

Scanning Electron Microscopy. Following tensile tests, silk fibers were mounted onto a

279

sample holder using conductive tape. The sample holder was sputter coated with a 10 nm gold

280

layer using a Leica EM ACE600 high vacuum sputter coater (Leica Microsystems). Fibers were

281

imaged using a Nova NanoSEM 230 Field Emission Scanning Electron Microscope (Field

282

Electron and Ion Company, FEI) at an accelerating voltage of 7-10 kV. Fiber surface roughness

283

(both exterior and interior) was calculated using MountainsMap SEM Topo software (Digital

284

Surf). The root mean square height (Sq) of each surface was determined from single images

13 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 29

285

using greyscale values, normalized by the entire range of values in each micrograph. To remove

286

fiber curvature from consideration, a standard Gaussian filter with a threshold of 2.5 µm was

287

applied when analyzing exterior surfaces. For convenience, exterior and interior surface

288

roughness values are presented relative to each other, with the highest interior value set at 1.

289

Fiber circularity was calculated from cross-sectional areas and perimeters as 4ߨ(௣௘௥௜௠௘௧௘௥ మ ),

290

where a perfect circle gives a value of 1.

௔௥௘௔

291

Polarized Raman spectromicroscopy. The method reported here is adapted from

292

several previous studies of molecular alignment in spider silk fibers.23,24,25 Silk fibers were

293

carefully fixed to glass microscope slides with microscale markings to ensure that spectra were

294

acquired at the same location before and after stage rotation. Raman spectra were acquired with a

295

Renishaw RM1000 InVia Confocal Raman Spectrometer (Renishaw) coupled to a Leica DM LM

296

microscope with rotating stage (Leica Microsystems). Silk fibers were initially oriented along the

297

x-axis. Fibers were irradiated at a fixed point with the 514 nm line of an argon laser with

298

polarization fixed along the x-axis and focused through a 50x objective (NA = 0.75). Spectra

299

were recorded from 1150-1750 cm-1 with an 1800 lines/mm grating. For each acquisition, a total

300

of 16 spectra were accumulated, each for 10 s. The stage was then rotated to orient fibers along

301

the y-axis with the same laser polarization, and spectra were acquired a second time at the same

302

fixed point. No signs of thermal degradation were apparent either visually or within recorded

303

spectra. All recorded spectra were analyzed using Fityk 0.9.8.26 Baselines were subtracted from

304

all spectra using the built-in Fityk automatic convex hull algorithm. For intensity ratio

305

calculations, all spectra were normalized to the intensity of the 1450 cm-1 peak, which arises

306

from CH2 bending and is insensitive to protein conformation.24 For each fiber, the normalized

307

intensity of the peak at 1670 cm-1 when oriented along the Y-axis was divided by the normalized

14 ACS Paragon Plus Environment

Page 15 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules



308

intensity of the peak when oriented along the X-axis to give the intensity ratio (‫ ܫ‬௑). This

309

procedure was performed on a total of three separate fibers and calculated intensity ratios were

310

averaged. Spectra were also averaged and presented in Figure 3d with standard deviations for

311

each point along the spectra.

312

Fourier Transform Infrared Spectroscopy. For secondary structure determination,

313

FTIR spectra were acquired with a Thermo Nicolet 470 FT-IR spectrometer (ThermoFisher

314

Scientific) fitted with a Smart Performer ATR accessory with Ge crystal. Spectra were acquired

315

from 1350-1750 cm-1 at 4 cm-1 resolution. A total of 254 scans were accumulated for each

316

sample. All recorded spectra were analyzed using Fityk 0.9.8. Baselines were subtracted from all

317

spectra using the built-in Fityk convex hull algorithm. The amide I band (1600 - 1700 cm-1) was

318

deconvolved into a set of five Lorentzian peaks centered at 1626.5, 1646.5, 1659, 1679.5, and

319

1700 cm-1 for β-sheet, random coil, α-helix, β-turn, and β-sheet components, respectively.

320

Component peak assignments were based on those used in previous studies.27 Peak areas were

321

integrated and percentages were calculated as the component peak area over the sum of all peak

322

areas. Percentages were averaged from measurements of three fibers.

323

Statistical analysis. GraphPad Prism 7 (GraphPad Software) was used for statistical data

324

analysis, using both two-tailed unpaired t-tests (26 degrees of freedom) and one-way ANOVA

325

tests (41 degrees of freedom) to compare data sets.

326 327

RESULTS AND DISCUSSION:

328

To facilitate microbial production of highly repetitive, SI-fused material proteins, we

329

developed a standardized DNA part assembly system termed SI-Bricks (Supplementary Note 1,

330

Figure S1). SI-Bricks allows for rapid genetic swapping of the core components of the

15 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

331

envisioned SI-mediated ligation platform (i.e. N-inteins, material proteins, C-inteins, and fusion

332

domains/purification tags) in addition to common standardized biological parts (e.g. promoters,

333

ribosomal binding sites, replication origins, and selection markers) (Table S7), all by means of

334

restriction enzyme digestion and enzymatic ligation. To construct the SI-Bricks parts necessary

335

for this study, we first assembled 64-mer and 96-mer spidroin DNA sequences by recursive

336

directional genetic assembly of a single, codon-optimized repeat unit (1-mer) of the N. clavipes

337

dragline spidroin MaSp1.5 The assembled spidroin sequences, flanked by SI-Bricks restriction

338

sites, were genetically combined with codon-optimized SI DNA sequences and other necessary

339

expression parts (Figure S2). Given the tendency of high MW spidroins to form inclusion bodies

340

in microbial hosts, we employed a recently engineered SI pair (Cfa) that retains catalytic activity

341

in the presence of 8 M urea,15 a denaturant often used to extract and solubilize spidroins from E.

342

coli. The resulting SI-fused spidroins (64N, C64, 96N, and C96) were individually expressed in an

343

E. coli host with

344

glycine codons in the spidroin sequences. Using our optimized fermentation conditions, typical

345

titers of the SI-fused spidroins were approximately 2 g/L from a glucose minimal medium with

346

tryptone supplementation after four hours of production (Figure S4).

glycyl

tRNA levels engineered to meet the demands of the most frequently used

347

Spidroin inter- and intramolecular interactions can be highly sensitive to salt and pH,

348

even in the presence of 8 M urea28,29 and we expected that such interactions would lower ligation

349

efficiency of the Cfa SIs. Thus, to test optimum conditions for the ligation of Cfa-fused

350

spidroins, 8 M urea extracts of E. coli expressing 64N or C64 were mixed at several salt

351

concentrations, temperatures, and pH values (Figure S3). Under all tested conditions, SI-

352

mediated spidroin ligation was both rapid and robust, with the highest ligation yields observed at

353

37 °C, 300 mM NaCl, pH 7. Thus, for all subsequent ligations, these conditions were maintained,

16 ACS Paragon Plus Environment

Page 16 of 29

Page 17 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

354

giving ligation yields of 68% and 62% for 128-mer and 192-mer spidroins, respectively (Figure

355

2a,b).

356

Ligation products were initially separated from most cellular proteins by selective

357

ammonium sulfate precipitation and then further separated from unreacted 64-mer or 96-mer by

358

size exclusion chromatography (SEC) for a final product purity ≥90% (Figure S6). As a standard

359

for mechanical properties, a 96-mer spidroin with no SIs was also expressed and purified

360

following identical procedures. Spinning dope was prepared from lyophilized powder of each

361

purified protein and fibers were spun and mechanically tested following well-documented wet-

362

spinning protocols detailed in the Materials and Methods section.

363

Comparing post-drawn 96-mer and 192-mer fibers, mechanical testing revealed

364

significant, nearly two-fold increases in both tensile strength (from 525 to 1031 MPa, P