Article

Responses of bacterial communities to CuO nanoparticles in activated sludge system Xiaohui Wang, Jing Li, Rui Liu, Reti Hai, Dexun Zou, Xiaobiao Zhu, and Nan Luo Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.6b06137 • Publication Date (Web): 14 Apr 2017 Downloaded from http://pubs.acs.org on April 21, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 40

Environmental Science & Technology

1

Responses of bacterial communities to CuO nanoparticles in activated sludge

2

system

3 4

Xiaohui Wang1, Jing Li1, Rui Liu1, Reti Hai1*, Dexun Zou1, Xiaobiao Zhu1, Nan Luo2

5

1. Beijing Engineering Research Center of Environmental Material for Water

6

Purification, College of Chemical Engineering, Beijing University of Chemical

7

Technology, Beijing 100029, China

8 9

2. China Sciences MapUniverse Technology Co., Ltd. (MAPUNI), Beijing, 100101, China

10 11 12 13

Corresponding author:

14

Reti Hai, Department of Environmental Science and Engineering, Beijing University

15

of Chemical Technology, Beijing 100029, China.

16

E-mail: [email protected]

17

Tel: +86-10-64444924

18

Fax: +86-10-64413170

ACS Paragon Plus Environment

Environmental Science & Technology

19

ABSTRACT

20

The main objectives of this study were to investigate the influence of copper oxide

21

nanoparticles (CuO NPs) on wastewater nutrient removal, bacterial community and

22

molecular ecological network in activated sludge. The results showed that long-term

23

exposure to 1 mg/L CuO NPs induced an increase of effluent concentrations of

24

ammonia and total phosphorus, which was consistent with the inhibition of enzyme

25

activities of ammonia monooxygenase, nitrite oxidoreductase, exopolyphosphatase

26

and polyphosphate in the presence of CuO NPs. MiSeq sequencing data indicated that

27

CuO NPs significantly decreased the bacterial diversity and altered the overall

28

bacterial community structure in activated sludge. Some genera involved in nitrogen

29

and phosphorus removal, such as Nitrosomonas, Acinetobacter and Pseudomonas

30

decreased significantly. Molecular ecological network analysis showed that network

31

interactions among different phylogenetic populations were markedly changed by

32

CuO NPs. For example, β-Proteobacteria, playing an important role in nutrients

33

removal, had less complex interactions in the presence of CuO NPs. These shifts of

34

the abundance of related genera, together with the network interactions may be

35

associated with the deterioration of ammonia and phosphorus removal. This study

36

provides insights into our understanding of shifts in the bacteria community and their

37

molecular ecological network under CuO NPs in activated sludge systems.

38 39

Keywords: Copper oxide nanoparticles, Activated sludge, Bacterial community,

40

Molecular Ecological Network

ACS Paragon Plus Environment

Page 2 of 40

Page 3 of 40

Environmental Science & Technology

41

INTRODUCTION

42

Metal oxide nanoparticles (NPs) have been receiving a lot of attention for their

43

potential applications in optoelectronics, nanodevices, nanoelectronics, nanosensors,

44

information storage, and catalysis1. Among various metal oxide NPs, CuO has

45

attracted particular attention because of its useful physical properties such as high

46

temperature superconductivity, electron correlation effects, and spin dynamics2. CuO

47

NPs are increasingly used in various applications such as in catalysis, pigments,

48

chemical sensors, and bactericidal applications 3. It was reported that the global

49

production of CuO NPs was 570 tons in 2014, and the estimated production would be

50

1600 tons by the year 2025 4. The large production and utilization of CuO NPs

51

inevitably lead to their environmental releases, and their potential health and

52

environmental risks have attracted increasing concerns.

53 54

Previous studies have showed that CuO were highly toxic to some model organisms

55

such as mammalia cells5, aquatic organisms 6, bacteria and algae 7-9. The main reason

56

was attributed to the generation of reactive oxygen species (ROS) 10, which might

57

lead to the DNA lesion or gene regulation 5, 11. Although the toxicities of CuO NPs to

58

paradigm organisms have already been studied, the evaluation of CuO NPs-induced

59

toxicities to microbes in activated sludge was rare 12.

60 61

Since some NPs were observed to enter into wastewater treatment plants (WWTPs) 12,

62

researchers began to consider their possible effects on pollutant removal efficiency

ACS Paragon Plus Environment

Environmental Science & Technology

Page 4 of 40

63

and microbial communities in WWTPs. Previous results indicated that different types

64

of NPs such as, Ag 13, Cu 14, ZnO 15, TiO2 16 and SiO2 17, showed different influences

65

on the performance of the activated sludge systems. Some preliminary studies have

66

evaluated the effect of CuO NPs on activated sludge process

67

bioreactors 3, 21. However, most of the studies mainly focus on the effects of CuO NPs

68

on various pollutant removal efficiencies, and how microbial communities respond to

69

CuO nanoparticles in activated sludge system is still not clear.

18-20

and on anaerobic

70 71

Activated sludge system is a complex ecosystem in which various species interact

72

with each other to form complicated networks 22, 23. Through such network

73

interactions, the activated sludge system is capable of accomplishing system level

74

functions (e.g., removal of oxygen-depleting organics and nutrients) which could not

75

be achieved by individual population 24. It is expected that the entering of

76

nanoparticles could alter the network interactions among activated sludge bacterial

77

populations. However, the effects of CuO NPs on the network interactions of

78

activated sludge bacterial populations are mainly unknown.

79 80

The major objectives of this study were to: (i) investigate the influence of CuO NPs

81

on wastewater nutrient removal, (ii) examine the effects of CuO NPs on the diversity

82

and structure of bacterial communities and (iii) elucidate how molecular ecological

83

network of bacterial community respond to CuO nanoparticles in activated sludge

84

system. For these purposes, we operated three lab-scale sequencing batch reactors

ACS Paragon Plus Environment

Page 5 of 40

Environmental Science & Technology

85

(SBRs) subjected to 1mg/L CuO NPs and three control SBRs over an extended period

86

(180 d).

87 88

MATERIALS AND METHODS

89

Nanoparticles

90

The CuO NPs ( 99%) used in this study were purchased from

91

Sigma-Aldrich (Shanghai, China) as a dry powder. CuO stock solution was prepared

92

by adding 100 mg CuO to 1.0 L Milli-Q (Molsheim, France) water, followed by 1 h of

93

ultrasonication (25℃, 120 W, 40 kHz). Based on the literatures review 3, 12, 1 mg/L

94

was chosen as the environmentally relevant concentration of CuO NPs .

95 96

The stability of the CuO NPs was evaluated by determining the particle size

97

distribution (PSD) and zeta potential in two different liquid media, including

98

deionized water and the influent wastewater of SBR. Samples of CuO NPs (10 mg/L)

99

were dispersed in the appropriate liquid medium and then sonicated (25℃, 120 W, 40

100

kHz) for 60 min and shaken for 2 h to increase their dispersion. The PSD were

101

determined by dynamic light scattering (DLS) using a Zetasizer Nano ZS (Malvern

102

Instruments, USA). The zeta potential of NPs dispersions was measured with the

103

same instrument using laser Doppler velocimetry.

104 105

Activated sludge bioreactors

106

Three SBRs subjected to 1 mg/L CuO NPs (CuO SBRs) and three controls were

ACS Paragon Plus Environment

Environmental Science & Technology

107

operated in parallel. Each SBR has a 4 L working volume, with 1 L of inoculated

108

sludge obtained from a municipal WWTP in Beijing, China. All SBRs were operated

109

on three 8 h cycles every day, and each cycle consisted of a 1.5 h anaerobic and a 3 h

110

aeration period, followed by 1.5 h of settling, then 10 min of decanting, and finally, a

111

110 min idle period. After the settling phase, 2 L of the supernatant was discharged

112

from each SBR, and was replaced with 2 L synthetic wastewater containing 0 (control

113

SBRs) or 1 mg/L CuO (CuO SBRs) during the initial 10 min of a new cycle. The

114

hydraulic retention time (HRT) was 16 h, and the sludge retention time (SRT) was

115

maintained at approximately 20 days by sludge discharging. During the aeration

116

period, DO concentrations in SBRs were maintain between 1.5 and 2.5 mg/L (Fig. S1),

117

while in anaerobic period, DO concentrations were maintain lower than 0.5 mg/L.

118

The initial concentrations of chemical oxygen demand (COD), ammonia (NH4+-N)

119

and total phosphorus (TP) in the influent synthetic wastewater were maintained at

120

approximately 500, 30, and 5 mg/L, respectively. The influent pH was maintained

121

between 7.2 and 7.6. The composition of the synthetic wastewater was described in

122

our previous literature 25.

123 124

Analytical methods

125

The determinations of COD, NH4+-N, nitrate (NO3--N) and TP were conducted in

126

accordance with the Standard Methods 26. CuO in liquid samples was analyzed by

127

inductively coupled plasma-optical emission spectroscopy ICP-OES7700 (Agilent

128

Technologies, USA). CuO in biosolids was determined after microwave-assisted acid

ACS Paragon Plus Environment

Page 6 of 40

Page 7 of 40

Environmental Science & Technology

129

digestion of sludge samples according to previous literature 3. For enzyme activity

130

analysis, the activated sludge samples were collected at the end of the aeration stage

131

during the final week of the study period. The measurements of the activities of

132

ammonia monooxygenase (AMO), nitrite oxidoreductase (NOR), nitrate reductase

133

(NAR), nitrite reductase (NIR), exopolyphosphatase (PPX) and polyphosphate kinase

134

(PPK) were according to the methods of Zheng, et al. 16.

135 136

DNA extraction and PCR amplification

137

Activated sludge samples were weekly collected from each SBR at the aerobic stage

138

during the final three weeks of the study period. Totally, 18 activated sludge samples

139

were collected, and 9 from CuO SBRs and 9 from control SBRs. DNA extraction was

140

performed using a FastDNA SPIN Kit for Soil Kit (MP Biotechnology, USA)

141

according to the manufacturer’s protocol.

142 143

Before sequencing, the extracted DNA samples were amplified with a set of primers

144

targeting the hypervariable V4 region of the 16S rRNA gene. The forward primer is

145

515F (5′-GTGCCAGCMGCCGCGG-3′) and the reverse primer is 806R

146

(5′-GGACTACHVGGGTWTCTAAT-3′). PCR was performed according to the

147

protocol of Hai et al. 25. PCR products were purified using QIAquick PCR

148

Purification Kit (Qiagen, Germany).

149 150

MiSeq sequencing

ACS Paragon Plus Environment

Environmental Science & Technology

151

About 500 ng of purified PCR product for each sample was mixed and sent to a

152

commercial company (Majorbio, China) for Illumina MiSeq sequencing. After

153

sequencing, Python scripts were written to perform quality filtering of the raw reads

154

as follows: (1) to sort sequences exactly matching the specific barcodes into different

155

samples, (2) to check sequencing quality by filtering out the reads with any uncalled

156

bases or two-paired end reads with less than 80 bases overlapping, (3) to trim off the

157

barcodes and primers. Taxonomic classifications of the effective sequences were

158

carried out using the RDP Classifier (Version 2.4) with a set confidence threshold of

159

80% to assign the sequences to different taxonomy levels. The raw reads have been

160

deposited into the NCBI short-reads archive database (Accession Number:

161

SRR1174196).

162 163

Statistical analysis

164

The indices of Shannon-Wiener and Pielou evenness were calculated to assess the

165

bacterial diversity. Detrended correspondence analysis (DCA) was performed to

166

examine the overall variation among bacterial communities of these 18 samples. All

167

the statistical analyses were performed using the VEGAN package in R (v.2.15.1;

168

http://www.r-project.org/).

169 170

Two molecular ecological network (MENs) were constructed using the online MENA

171

pipeline by following these steps 23, 27. First, the MiSeq sequencing data were used to

172

construct MENs. The relative proportions of sequence numbers of individual OTUs

ACS Paragon Plus Environment

Page 8 of 40

Page 9 of 40

Environmental Science & Technology

173

were used for subsequent Pearson correlation analysis. Second, the correlation matrix

174

was then converted to a similarity matrix, which measures the degree of concordance

175

between the abundance profiles of OTUs across different samples by taking the

176

absolute values of the correlation matrix 28. Third, an adjacency matrix encoding the

177

connection strength between each pair of nodes was derived from the similarity

178

matrix by applying an appropriate threshold, st, which was defined using the random

179

matrix theory (RMT)-based network approach 29, 30. Fourth, the modules were

180

detected by the fast greedy modularity optimization 31, 32. Then the modularity value

181

of each network (M) was calculated as previously described 32, which is used to

182

describe how well the modules are separated.

183 184

For network comparison, random networks corresponding to all MENs were

185

constructed using the Maslov-Sneppen procedure 33. For each network, a total of 100

186

randomly rewired networks were constructed and all of the network indexes were

187

calculated individually. Then, the average and standard deviation for each index of all

188

of the random networks were obtained. A standard Z or t test was employed to

189

determine the significance of network indexes between the MENs and random

190

networks and across different experimental conditions. The Cytoscape 3.2.1 software

191

was used to visualize the network graphs.

192 193

RESULTS AND DISCUSSION

194

The stability of CuO NPs

ACS Paragon Plus Environment

Environmental Science & Technology

195

The hydrodynamic particle size distribution in deionized water and wastewater was

196

showed in Fig. S2. A significant aggregation of the CuO NPs was found in both two

197

liquid media and the average sizes were 284 (deionized water) and 336 nm

198

(wastewater), respectively, indicating the aggregation in wastewater was little higher

199

than in deionized water. Additionally, the average zeta potential values of the

200

dispersions were -25.8 mV and -24.6 mV. These values are the typical threshold range

201

that separates unstable dispersions with low charged surfaces from stable dispersions

202

with highly charged surfaces 3.

203 204

Effects of CuO NPs on nutrient removal from wastewater

205

During the study period, the average influent and eluent CuO concentrations were

206

0.99 and 0.31 mg/L, respectively, indicating that an average retention of 69% inside

207

the reactors (Fig. S3). Analysis of acid-digested samples showed that the

208

accumulation of CuO NPs in biosolids increased from 0.21 to 11.3 mg CuO/g volatile

209

suspended solids (VSS) during the operating period.

210 211

As shown in Fig. S4, the effluent COD and NO3−-N concentrations in the presence of 1

212

mg/L CuO NPs were relatively stable, similar to those of the control over a period of

213

180 days. However, the effluent concentrations of NH4+-N and TP in CuO SBR

214

obviously changed with increasing exposure time. The effluent NH4+-N increased

215

abruptly on day 22 and reached the maxim of 7.5 mg/L on day 31. After day 31,

216

NH4+-N fluctuated between 5.3 and 7.5 mg/L. The average effluent concentration of

ACS Paragon Plus Environment

Page 10 of 40

Page 11 of 40

Environmental Science & Technology

217

NH4+-N during the last 30 days was 6.8 mg/L, remarkably higher than that in the

218

control (0.3 mg/L). After day 40, the effluent TP concentration showed a clear

219

increasing trend and reached 2.8 mg/L at day 70. After day 70, the TP concentrations

220

fluctuated between 0.9 and 2.6 mg/L. The average TP removal efficiency during the

221

last 30 days was 63%, remarkably lower than that in the control (91%). This indicated

222

that long-term exposure to CuO NPs had adverse effects on phosphorus removal in

223

activated sludge system.

224 225

Previous studies have showed that some metallic nanoparticles exposure had adverse

226

impacts on a biochemical process. In a lab-scale anaerobic bioreactor, Otero-Gozalez

227

et al. 3 found that long-term exposure to 1.4 mg/L CuO NPs caused severe toxicity

228

and reduced the acetoclastic methanogenic activity by more than 85%. ZnO NPs has

229

also been demonstrated to inhibit nitrogen and phosphorus removal in activated

230

sludge system 15. In the coming text the reasons of the effect of CuO NPs on

231

biological nitrogen and phosphorus removal were further investigated.

232 233

Long-term effects of CuO NPs on the activity of key enzymes

234

Biological nitrogen removal from wastewater depends on the successful nitrification

235

and denitrification, and these processes are relevant to the activities of some key

236

enzymes. Usually, autotrophic AOB uses AMO to catalyze ammonia oxidation, and

237

the subsequent oxidation of nitrite to nitrate is carried out with NOR by nitrite

238

oxidizing bacteria (NOB) 34, 35. Denitrification is mainly catalyzed by NAR and NIR

ACS Paragon Plus Environment

Environmental Science & Technology

239

36

240

polyphosphate-accumulating organisms (PAOs), which are able to use PPX and PPK

241

to perform the anaerobic hydrolysis of polyphosphate and subsequent aerobic uptake

242

of phosphorus, respectively 37. Six key enzymes of activated sludge were investigated

243

after long-term exposure to CuO NP (Fig. 1). The results showed that long-term

244

exposure to 1 mg/L CuO NPs significantly inhibited the activities of AMO and

245

NOR(P