Self-driven photoelectrochemical splitting of H2S ... - ACS Publications

Subscriber access provided by Service des bibliothèques | Université de Sherbrooke

Article

Self-driven photoelectrochemical splitting of H2S for S and H2 recovery and simultaneous electricity generation Tao Luo, Jing Bai, Jinhua Li, qingyi zeng, youzhi ji, li qiao, xiaoyan li, and Baoxue Zhou Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b03116 • Publication Date (Web): 03 Oct 2017 Downloaded from http://pubs.acs.org on October 10, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24

Environmental Science & Technology

1

Self-driven photoelectrochemical splitting of H2S for S and H2

2

recovery and simultaneous electricity generation

3

Tao Luo a, Jing Bai

4

Zhou a,b∗

5

a

6

800 Dongchuan Rd, Shanghai 200240, China

7

b

8

Shanghai 200240, PR China

9

Abstract:

a∗

, Jinhua Li a, Qingyi Zeng, Youzhi Ji, Li Qiao, Xiaoyan Li, Baoxue

School of Environmental Science and Engineering, Shanghai Jiao Tong University No.

Key Laboratory of Thin Film and Microfabrication Technology, Ministry of Education,

10

A novel, facile self-driven photoelectrocatalytic (PEC) system was established for

11

highly selective and efficient recovery of H2S and simultaneous electricity production.

12

The key ideas were the self-bias function between a WO3 photoanode and a Si/PVC

13

photocathode due to their mismatched Fermi levels and the special cyclic redox reaction

14

mechanism of I-/I3-. Under solar light, the system facilitated the separation of holes in the

15

photoanode and electrons in the photocathode, which then generated electricity. Cyclic

16

redox reactions were produced in the photoanode region as follows: I- was transformed

17

into I3- by photoholes or hydroxyl radicals, H2S was oxidized to S by I3-, and I3- was then

∗

Corresponding authors: [email protected] (J. Bai) [email protected] (B. Zhou)

ACS Paragon Plus Environment


18

reduced to I-. Meanwhile, H+ was efficiently converted to H2 in the photocathode region.

19

In the system, H2S was uniquely oxidized to sulfur but not to polysulfide (Sxn-) because of

20

the mild oxidation capacity of I3-. High recovery rates for S and H2 were obtained up to

21

~1.04 mg h-1 cm-1 and ~0.75 mL h-1 cm-1, respectively, suggesting that H2S was

22

completely converted into H2 and S. In addition, the output power density of the system

23

reached ~0.11 mW cm-2. The proposed PEC-H2S system provides a self-sustaining,

24

energy-saving method for simultaneous H2S treatment and energy recovery.

25

Key words: Self-driven; H2S decomposition; PEC; S recovery; electricity generation

26

For Table of Contents Only

27

28

INTRODUCTION

29

H2S is an extremely flammable, colorless, toxic, irritating, and corrosive gas with a

30

strong odor of rotten eggs produced from the fast progress of industrialization, resulting

31

in serious environmental pollution and bodily injury1-5. In fact, H2S is a potentially

32

valuable chemical that is rich with H2 and elemental sulfur (S)4. Hence, there is a


Page 2 of 24

Page 3 of 24


33

pressing need to dispose of H2S, while simultaneous recycling its waste. In fact, the best

34

way to dispose of H2S is to recover H2 and S since the thermodynamic decomposition of

35

H2S is only 33 kJ mol-1 (∆G0)4, and some methods, including the thermal decomposition

36

method5, 6, the electrochemical decomposition method1, the plasma method4, 7, and other

37

methods, have been reported. However, the existing methods have several shortcomings.

38

For instance, the thermal decomposition method requires a temperature higher than

39

1,000 °C for the reaction5, 6, the electrochemical decomposition method requires external

40

power1, and the plasma method requires complex equipment7. Therefore, an

41

environmentally friendly, sustainable and low consumption method for decomposing H2S

42

into S and H2 is highly desirable.

43

In recent years, photocatalytic8-10 and photoelectrocatalytic (PEC) techniques for

44

dealing with environmental pollution have attracted wide attention because these methods

45

provide great insight into the utilization of solar energy for degrading pollutants,

46

producing hydrogen, and generating electricity11-17. However, in addition to the organic

47

waste, few other inorganic pollutants are as concerning as H2S. Traditional PEC

48

techniques require an external bias to carry out the PEC process, which means additional

49

cost for the external power18-22. Another problem is that S2- can be easily oxidized to

50

polysulfide (Sxn-) by the hydroxyl radical (E0 = ~3.2 V vs. NHE) or photoholes (E0 = 3.0

51

V vs. NHE) due to their high oxidation potential, resulting in new secondary

52

environmental pollution23. Therefore, a specific PEC system for H2S recovery is required.



53

Herein, we propose a self-driven PEC H2S system with a special cyclic redox

54

reaction mechanism of I-/I3- for the first time. In this system, a WO3 nanoplate was

55

selected as the photoanode due to its good visible light absorption and superior

56

photoelectronic performance24. A Pt-decorated Si photovoltaic cell (Pt/SiPVC) was

57

chosen as the photocathode due to its suitable valence band edge of the p-type Si

58

substrate, which will result in a good visible light response25. Together, the photoanode

59

and photocathode created a basic self-driven PEC system due to the mismatched Fermi

60

levels between the two photoelectrodes. Under illuminating solar light, the system

61

facilitated the separation of electron/hole pairs in the two photoelectrodes, and thus, the

62

holes of the WO3 photoanode and the electrons of the Si/PVC photocathode could be

63

effectively released and generate electricity26. The cyclic redox reactions were set up in

64

the photoanode region where I- can be oxidized into I3- 27, 28 (E0 (I3-/I-) = 0.535 V vs. NHE)

65

by photoholes or hydroxyl radicals. H2S can be oxidized into S (E0 S/H2S = 0.142 V vs.

66

NHE) by I3-, and I3- can then be reduced into I-. Meanwhile, H+ can be reduced very

67

efficiently into H2 in the photocathode region. In the system, H2S is uniquely oxidized

68

into elemental sulfur (S) but not polysulfide (Sxn-) because I- is a well-known hole or

69

hydroxyl-trapping agent29, 30, and the products of I3- are only gentle oxidizers, not strong

70

oxidizers31. We also designed an S collection system that was integrated in the PEC

71

system to maintain its continuous operation. Overall, the proposed self-driven PEC-H2S

72

system provides a sustainable way to recover H2S into S and H2 and to simultaneous

73

generate electricity.


Page 4 of 24

Page 5 of 24

74


MATERIALS AND METHODS

75

Materials. All chemical reagents used in this work were purchased from Sinopharm

76

Group CO. LTD and were analytically pure. All solutions were prepared using

77

high-purity DI water.

78

Synthesis of the nanostructured WO3 nanoplate photoanode. The purchased

79

F-doped tin oxide (FTO) substrate (13 Ω cm-1) was cut into 20 mm × 60 mm slides and

80

washed under ultrasonication with acetone and deionized water for 30 min. The WO3

81

photoanode was prepared via a modified chemical bath deposition method (CBD) 32. In a

82

typical process, 0.4 g of Na2WO4•2H2O and 0.15 g of ammonium oxalate were first

83

dissolved in 33 mL of deionized water. Then, HCl (9 mL, 37%), H2O2 (8 mL, 30%) and

84

ethanol (30 mL) were each subsequently added with strong agitation to obtain the

85

precursor solution. The precipitates were dissolved to form a clear solution, and the

86

prepared FTO glass (13 Ω cm-1) was dipped into the precursor solution with the FTO side

87

facing down. Then, the mixtures were heated to 85 °C in a constant temperature bath and

88

naturally cooled down. Finally, the as-prepared sample was rinsed and dried, followed by

89

calcination at 500 °C in air for 2 h.

90

Fabrication of the Pt/SiPVC photocathode. The Pt/SiPVC photocathode was

91

prepared according to our previous work32-34. The backing Al ohmic metal of the

92

crystalline Si photovoltaic cell (Shenzhou New Energy) Development Co., Ltd., Shanghai,

93

China) was first soldered with a Cu wire and then sealed using an insulating epoxy resin.



94

Then, Pt black was decorated on the Ag grids of the Si/PVC via an electrode position

95

process in a solution of 1 mM K2PtCl6 and 0.5 M K2SO4 adjusted to pH 1 with H2SO4 at

96

-0.4 V.

97

Structural Characterization. A field emission scanning electron microscope

98

(FE-SEM; Zeiss, Germany, ULTRA PLUS) was used to characterize the surface

99

morphology of the WO3 nanoplate photoanode. The crystal phase of the samples was

100

characterized via X-ray diffractometry (XRD) (Bruker, Germany, AXS-8 Advance).

101

Optical absorption measurements were performed in a Lamda 750 UV-Vis-IR

102

spectrophotometer using an integrating sphere.

103

Photoelectrochemical Measurements. The photo response of the WO3/FTO

104

photoanode and Pt/SiPVC photocathode was determined using a three-electrode system

105

with an Ag/AgCl electrode as the reference, platinum foil as the auxiliary electrode and

106

the samples as the working electrode. The working electrode potential and current were

107

controlled by an electrochemical workstation (CHI 660c, CH Instruments Inc. 3700

108

Tennison Hill Drive Austin, USA). A 350-W Xe lamp was used as the simulated light

109

source, without further modification, and all experiments were performed under visible

110

light irradiation (light intensity, 100 mWcm−2). The linear sweep voltammograms (LSV)

111

were conducted at a scan rate of 10 mV s-1 under chopped light irradiation.

112

Apparatus and methods of hydrogen sulfide splitting. A customized double

113

chamber reactor with a proton membrane (Bofeilai Technology Co., Ltd.) and a specific


Page 6 of 24

Page 7 of 24


114

accessory for S collection was applied for establishing the self-biasing PFC cell. The

115

nanostructured WO3 photoanode and Pt photoanode were placed in the anodic and

116

cathodic compartments, respectively. The back of WO3/FTO was pressed to the outer

117

wall of the anodic compartment to ensure stable light absorption during the entire process.

118

Then, 100 mL of 0.5 M H2SO4 containing 0.05-0.3 M KI was used as the electrolyte in

119

the anodic compartment and 100 mL of 0.5 M H2SO4 was used as the electrolyte in the

120

cathodic compartment. Before operation, nitrogen was piped into the PEC cell for 10 min

121

to eliminate air. Under illumination, H2S gas was intermittently pumped into the anodic

122

cell, followed by filtration via an S collection accessory, and the filtered solution was

123

reinjected into the anodic cell. H2 was gathered and tested using an online gas system

124

(Bofeilai Technology Co., Ltd.) connected to a gas chromatograph (GC2010 plus,

125

SHIMADZU, Japan).

126

RESULTS AND DISCUSSION

127

Characterization of the WO3 photoanode and Si The electrodes (photoanode and

128

photocathode) used to construct the self-driven PEC system were characterized (Figure 1).

129

In terms of the photoanode, Figure 1a shows top-view and cross-section SEM images of

130

the WO3 nanoplates. As shown, the WO3 film has a very homogeneous plate-like

131

morphology that is perpendicular to the substrate with a thickness of ~850 nm. The

132

nanoplate films tightly adhered to the FTO substrate, and the film was directly grown on

133

the substrate. As previously reported32, the WO3 nanoplate has an orthorhombic



134

crystalline phase and an absorption wavelength of ~450 nm (Figure S1 and Figure S2).

135

The IPCE behavior of the WO3 NPA film exhibited in the range of 350 to 470 nm in 0.5

136

M H2SO4 solution with 0.2 M KI, which is roughly consistent with the light absorption of

137

the WO3 NPA film. This means that the conversion of the incident photons into

138

photocurrent occurred successfully in the photoanodes. An IPCE value of ~49% was

139

obtained for WO3 at 400 nm (Figure S3). Figure 1c shows the schematic illustration and

140

digital photo of the commercial Pt/SiPVC that was used as the photocathode. As shown,

141

the backing Al ohmic metal of the PVC was first connected to Cu wires and then

142

protected by an epoxy resin. It was subsequently modified using the Pt catalyst via a

143

photoassisted electrodeposition method. The Pt catalyst was only deposited on the Ag

144

grids, and no Pt catalyst was found on the residual SiNx coating.

145

Figures 1b and 1d show the typical LSV curves of the WO3 photoanode and

146

Pt/SiPVC photocathode, respectively, in the dark and under AM 1.5 solar light

147

illumination (light intensity, 100 mW cm-2) with a 0.5 M H2SO4 electrolyte. Figure 1b

148

shows that the WO3 nanoplate has a good photocatalytic capacity under solar light

149

irradiation, and the JSC-potential curve of ~0.70 mA cm−2 at a bias of 0.6 V vs. the

150

Ag/AgCl reference electrode was observed. The plot in Figure 1d also reveals that

151

Pt/SiPVC has an excellent solar light response due to its very short band gap (~2.2 V) due

152

to the Si substrate. The ideal onsets of WO3 and Si for photooxidation and photoreduction

153

reactions are ~0.65 V and ~-0.4 V, respectively. In view of the JSC-Potential (Figure 1b


Page 8 of 24

Page 9 of 24


154

and Figure 1d) and I-T plots (Figure S4), both the photoanode and photocathode show

155

favorable photoresponses and good stability for the construction of the H2S-PFC system.

156

The self-driven PEC was performed due to matched Fermi levels between the

157

photoanode and photocathode, which accounts for the generation of photovoltage in the

158

PEC34, 35. Unlike metal electrodes, the Fermi level is located at different positions for

159

different types of semiconductors: it is near the conduction band (CB) edge for an n-type

160

semiconductor and near the valence band (VB) edge for a p-type semiconductor.

161

Therefore, the VOC values could have a difference of Fermi levels between the two

162

electrodes. As reported elsewhere36-39, the conduction band and valence band edge of

163

WO3 are located at approximately -0.5 V to 0 V and 2.5 V to 3.0 V, respectively, vs.

164

NHE. The band gap of WO3 is approximately 3 V. The n-type semiconductor photoanode

165

should have a positively located VB edge with an energy level that is sufficient for water

166

oxidation. In contrast, a p-type semiconductor photocathode should have a negatively

167

located CB edge with an energy level that is sufficient for water reduction. The

168

band-edge positions of the WO3 and Si photoelectrodes can be matched to allow

169

electrons to migrate from the photoanode to the photocathode. According to the optical

170

absorption spectra and the reported energy band level of the semiconductors, the energy

171

band positions of the photoanode and photocathode are illustrated in Figure 2a. As shown,

172

the Fermi level of WO3 is more negative than that of Si/PVC (0.3 V vs. NHE vs 0.6 V vs.

173

NHE) so the electrons generated from WO3 and the holes generated from Si/PVC can be



174

driven to be combined with each other by an interior bias through the external circuit.

175

Meanwhile, the holes of the photoanode and the electrons of the photocathode can be

176

released to produce redox reactions in the solution. This process could be very efficient

177

considering the high self-bias, consequently reducing the combination of photogenerated

178

electron-hole pairs in both the photoanode and photocathode.

179

Figure 2b shows the configuration and operating mechanism of the PEC-H2S system.

180

The photoanode and photocathode were placed in the anodic cell and cathodic cell,

181

respectively and were separated by a proton exchange membrane. During the operation,

182

both photoelectrodes were simultaneous illuminated, and H2S gas was injected into the

183

anodic cell while elemental S was collected via an external portion. Special I-/I3- cyclic

184

redox reactions40, 41, 21 were set up in the photoanode region, in which I- can be oxidized

185

into I3- by photoholes or hydroxyl radicals, H2S can be oxidized into S by I3-, and I3- can

186

then be reduced into I-. Meanwhile, H+ was reduced to H2 in the photocathode region.

187

The mechanisms of the reactions in the PEC-H2S system can be summarized as equations

188

(1)-(9), which were conducted in the two cells. In the anodic cell, the redox couple of

189

I-/I3- plays a key role that links the photoelectrochemical reaction and chemical reaction.

190

Under illumination, the photogenerated holes (h+) and hydroxyl radical from WO3 first

191

oxidize I- to I3- (Eq.1-4); then, I3- efficiently traps and selectively converts H2S to S and

192

protons and finally converts into I- (Eq.5). In the cathodic cell, the photogenerated

193

electrons (e-) from Pt/SiPVC can reduce protons to generate H2 (Eq.7-8). Overall, with


Page 10 of 24

Page 11 of 24


194

the connected redox couples (I-/I3-), the released holes of the WO3 photoanode and the

195

released electrons of the Si PVC photocathode can make H2S splitting and energy

196

recovery possible using solar energy. WO3 + hv → e- + h+

(1)

198

H2O + h+ → HO⋅ + H+

(2)

199

3I- + 2 h+ → I3-

(3)

200

3I- + 2⋅OH → I3- + 2OH-

(4)

201

I3- + H2S → 3I- + 2H+ + S↓

202

OH- + H+ → H2O

(6)

SiPVC + hv → e- + h+

(7)

2H+ + 2e- →H2↑

(8)

197

203

Anodic cell:

Cathodic cell:

204

H2S → H2↑+ S↓

(5)

205

Overall:

(9)

206

Figure 3a shows the ion percentages of I- and I3- during the operation of the system

207

in 100 mL of 0.5 M H2SO4 solution with 0.2 M KI, and Figure 3b shows the contrasting

208

experiment conducted in 100 mL of 0.5 M H2SO4 solution containing 0.2 M KI with 0.1

209

mM methyl alcohol as the scavenger. According to the equations above (Eq.1-Eq.9), I3-

210

was accumulated, and I- was simultaneous consumed during the initial operation over



211

6000 seconds. When H2S was introduced into the anodic cell, I3- reacted with H2S and

212

turned back into I-; meanwhile, S was produced. Afterwards, the system ran into the

213

second cycle (Figure 3a), and the concentration ratio between I- and I3- presented a

214

dynamic equilibrium. In contrast, a scavenger, which can capture photogenerated holes

215

(h+) as well as hydroxyl radicals (OH⋅), was added into the anodic cell to investigate the

216

effect of the photogenerated holes (h+) and the hydroxyl radicals (OH⋅) on the oxidation

217

of I-. As indicated in Figure 3b, the I3- formation rate was far smaller with the existence of

218

methyl alcohol, which means that I- can easily oxidize into I3- via photogenerated holes

219

(h+) and hydroxyl radicals (OH⋅).

220

Based on the proposed principle, H2SO4 was chosen as the basic electrolyte in both

221

cells, and KI was added into the anodic cell for H2S oxidation. Thus, we first investigated

222

the photoelectric properties of the PEC system under different concentrations of H2SO4

223

and KI. The change of the photocurrent density in the system depends on the

224

concentration of I- and H2SO4, higher concentration of H2SO4 and I- would both lead to

225

higher photocurrent density. In order to show the influence of those two factors on the

226

photocurrent density intuitively, we draw a three-dimensional stereogram (Figure 4a). As

227

shown in Figure 4a, with the same concentration of sulfuric acid, the photocurrent tended

228

to increase as the concentration of KI gradually increased and reached the highest value

229

of 0.95 mA cm-2 at 0.25 M KI. Although the current density under 0.25 M KI is slightly

230

higher than that under 0.2 M KI, the increment is not considerable. However, KI is


Page 12 of 24

Page 13 of 24


231

expensive. We used 0.2 M KI, taking economic factors into account. Since I- can be

232

easily oxidized by H+, more electrons could be generated and transferred to the electrode,

233

leading to an increase in the photocurrent. However, the nature of the photoanode limited

234

the amount of H+, thus further increasing the concentration of I- could not increase the

235

photocurrent. Similarly, a higher concentration of H+ led to a higher photocurrent. The

236

stability of the electrode was tested, and the results show that the current density reduced

237

from 0.95 mA cm-2 to 0.70 mA cm-2 during the initial progress, and the current density

238

tended to be stable (Figure S5).

239

Accordingly, the concentration of electrolyte also determines the bias potential

240

between the photoanode and photocathode. As a key index, the open-circuit voltage (VOC)

241

was therefore investigated, and the results are shown in Figure 4b. The VOC values were

242

-0.1 V under dark and increased to 0.2 V under illumination without KI. Then, the VOC

243

gradually increased with the addition of KI. As shown, the VOC values were 0.27 V, 0.3 V,

244

0.33 V and 0.45 V at 0.05 M KI, 0.1 M KI, 0.15 M KI and 0.2 M KI, respectively. In

245

particular, the instantaneous open-circuit voltage at 0.2 M KI is ~0.45 V, which is close to

246

the theoretical VOC (0.53 V) of the WO3-Si/PVC system. This result indicates that the

247

WO3/FTO-Si/PVC system can be driven by the interior bias between the two

248

photoelectrodes.

249

Figure 5 shows the variation in the photocurrent and the corresponding color change

250

of the solution during the entire process under visible light illumination. In the initial



251

stage, the photocurrent was approximately 0.7 mA cm-2, and H2 bubbles were observed in

252

the cathode cell as the color of solution in the anodic cell gradually turned from

253

transparent to light yellow and to bright red, indicating the generation of I3-. After a

254

quantity of H2S was injected into the anodic cell, the photocurrent sharply dropped to 0.1

255

mA cm-2 as the bright red solution rapidly turned to a turbid solution that was milky white

256

(Figure 5, Figure S6). This finding is attributed to the formation of elemental S, which is

257

known to be insoluble in water, and its density is bigger than that of water. This result

258

also explained that the oxidation of H2S by I3- is much faster than the oxidation of I-. The

259

solution was then rapidly filtered out, and a colorless and transparent solution was

260

obtained again. simultaneous, the photocurrent returned to 0.7 mA cm-2. As shown in

261

Figure 5, this phenomenon may be constantly proceeded by a long-term and more

262

substantial elemental collection of S (Figure 5b). During the entire process, the

263

photocurrent was maintained at 0.7 mA cm-2, except when H2S was injected into the

264

solution, leading to a sharp drop. Thus, the I3- could react with H2S to rapidly recover S,

265

which, meanwhile, was restored to the reduced state of I- at the end of the cycle. A control

266

trial was conducted without the I-/I3- cycle in the anodic cell to determine the formation

267

of polysulfide (Sxn-). A yellow-clear but turbid solution was only obtained during the

268

operation, which is the typical feature of polysulfide solutions (Figure S7). The

269

polysulfide could be further confirmed via qualitative analysis of hydrochloric acid in

270

which milky-white turbidity was produced when the yellow-clear solution reacted with

271

the dilute solution of hydrochloric acid. The result illustrated that H2S was easily


Page 14 of 24

Page 15 of 24

272


converted into polysulfide (Sxn-) without the existence of I-/I3-.

273

To evaluate the performance of the PEC-H2S system, hydrogen and sulfur were

274

continuously collected during long-term operation. Figure 6a shows the production rate

275

of H2 and S by the PEC-H2S system. The production rates of H2 and S were maintained at

276

~0.0131 mmol h-1 cm-2 and ~0.0135 mmol h-1 cm-2, respectively, suggesting that H2S was

277

completely converted into H2 and S (Table S1). Moreover, the Faradaic efficiency for H2

278

was calculated to be ~99% through the formula below.

279

Faraday Efficiency =

m ( H 2 ) ⋅ n (e) ⋅ F ( F , Faradaycon s tan t ) I ⋅T

280

The m(H2) represent the molar number of hydrogen, n(e) represent the reaction 281

electron number. I and T represent the photocurrent of the system and operation time of 282

the system, respectively.

283

In contrast, the production of sulfur was examined with 0.1 M H2S pumping into the

284

I3- solution. We found that the productivity of S was ~0.09 M, which means S was

285

absolutely generated by I3-. The effect of the photoanode on the elemental S before S was

286

filtered from the solution was also investigated. Similarly, SO42- can react with Ba2+ and

287

generate BaSO4 precipitate. The amount of SO42- was calculated by weighing the weight

288

of BaSO4. When S was filtered from the solution, ~11.5 g of BaSO4 was obtained after

289

ample BaCl2 was added. However, it yielded ~60 g of BaSO4 when S remained in the

290

system, which means that S was transformed into SO42- if it remained in the solution.



291

In addition, the test also demonstrates that the system possesses good stability and

292

reusability. The electricity generation was investigated by evaluating the output power

293

density (Pmax) of the PEC-H2S system as shown in Figure 6b. Pmax can be calculated using

294

the following formula:

Pmax=FF×JSCVOC

295

296

Pmax and JSC represent the real maximum power density and theoretical maximum

297

power density yielded from the PEC-H2S system, respectively. JSC, VOC and FF are the

298

short-circuit current density, the open-circuit voltage and fill factor of the PEC-H2S

299

system. As shown, the maximum output power density of the PEC-H2S system was ~0.11

300

mW cm-2. The illuminated area of anode and cathode are both 2 cm2. The light energy

301

conversion efficiency was 0.56%.

302

Overall, we described a novel self-driven PEC-H2S system using a WO3 nanoplate

303

as the photoanode and a Pt-decorated Si photovoltaic cell (Pt/SiPVC) as the photocathode

304

for decomposing H2S and obtaining H2 and S with simultaneous electricity production.

305

The performance of the self-driven PEC-H2S system was studied by measuring the

306

photoelectric effect and the production of S and H2. The results demonstrated that the

307

photocurrent and the open-circuit potential could reach 0.7 mA cm-2 and 0.36 V,

308

respectively. Meanwhile, H2 bubbles were observed in the cathode cell, and the unique

309

solid S product was recovered via an external centrifugal circulation system. The novel

310

self-driven PEC-H2S system is promising for sustainable waste recovery and green


Page 16 of 24

Page 17 of 24


311

energy generation.

312

ASSOCIATED CONTENT

313

Supporting Information is available free of charge on the ACS Publications website.

314

Figures S1−S6 and Table S1 (PDF)

315

AUTHOR INFORMATION

316

Corresponding Author

317

E-mail: [email protected]; [email protected];

318

phone: 021-54747351; 021-54747364

319

Notes

320

The authors declare no competing financial interests.

321

ACKNOWLEDGEMENTS

322

The authors would like to acknowledge the National Natural Science Foundation of

323

China (No. 21507085), the Shanghai Yangfan Program (14YF1401500) and the

324

SJTU-AEMD for support.

325

REFERENCES

326

1.

327

fumed silica. Fuel 2016, 168, 47-53, DOI: 10.1016/j.psep.2017.01.008.

Yoosuk, B.; Wongsanga, T.; Prasassarakich, P., CO2 and H2S binary sorption on polyamine modified



328

2.

Nunnally, T.; Gutsol, K.; Rabinovich, A.; Fridman, A.; Starikovsky, A.; Gutsol, A.; Potter, R. W.,

329

Dissociation of H2S in non-equilibrium gliding arc “tornado” discharge. Int. J. Hydrogen Energy 2009, 34,

330

(18), 7618-7625, DOI: 10.1016/j.ijhydene.2009.07.045.

331

3.

332

simultaneous removal of hydrogen sulphide and ammonia at a wastewater treatment plant. Biochem. Eng. J.

333

2016, 107, 1-,10, DOI: 10.1016/j.bej.2015.11.018.

334

4.

335

Oxidation. Cat. Rev. - Sci. Eng. 1998, 40, (4), 409-450, DOI: 10.1080/01614949808007113.

336

5.

337

six fatal hydrogen sulfide poisonings in quick succession. Forensic Sci. Int. 2016, 260, e7-10, DOI:

338

10.1016/j.forsciint.2016.01.021.

339

6.

340

Haas-Santo, K.; Konsolakis, M.; Figen, H. E.; Güldal, N. O.; Baykara, S. Z., An electrocatalytic

341

membrane-assisted process for hydrogen production from H2S in Black Sea: Preliminary results. Int. J.

342

Hydrogen Energy 2015, 40, (24), 7530-7538, DOI: 10.1016/j.ijhydene.2014.12.017.

343

7.

344

1972, 238, (5358), 37-38, DOI: 10.1038/238037a0.

345

8.

346

self-doped Bi2WO6 under visible light by generating more superoxide ions. Environ. Sci. Technol. 2014, 48,

347

(10), 5823, DOI: 10.1021/es405714q.

348

9.

349

morphology and crystallite phases of titanium oxide on the catalytic ozonation of phenol. Environ. Sci.

350

Technol. 2010, 44, (10), 3913, DOI: 10.1021/es100456n.

351

10. Guo, Y.; Lou, X.; Fang, C.; Xiao, D.; Wang, Z.; Liu, J., Novel Photo-Sulfite System: Toward

352

Simultaneous Transformations of Inorganic and Organic Pollutants. Environ. Sci. Technol. 2016, 47, (19),

353

11174-11181, DOI: 10.1021/es403199p.

354

11. Coskun, I.; Tollefson, E. L., Oxidation of low concentrations of hydrogen sulfide over activated

355

carbon. Can. J. Chem. Eng. 2010, 58, (1), 72-76, DOI: 10.1002/cjce.5450580111.

356

12. Zhu, L.; Hong, M.; Ho, G. W., Fabrication of wheat grain textured TiO2/CuO composite nanofibers for

357

enhanced solar H2 generation and degradation performance. Nano Energy 2015, 11, 28-37, DOI:

Rabbani, K. A.; Charles, W.; Kayaalp, A.; Cord-Ruwisch, R.; Ho, G., Pilot-scale biofilter for the

PiÉPlu, A.; Saur, O.; Lavalley, J.-C.; Legendre, O.; NÉDez, C., Claus Catalysis and H2S Selective

Barbera, N.; Montana, A.; Indorato, F.; Arbouche, N.; Romano, G., Domino effect: An unusual case of

Ipsakis, D.; Kraia, T.; Marnellos, G. E.; Ouzounidou, M.; Voutetakis, S.; Dittmeyer, R.; Dubbe, A.;

Fujishima, A.; Honda, K., Electrochemical photolysis of water at a semiconductor electrode. Nature

Ding, X.; Zhao, K.; Zhang, L., Enhanced photocatalytic removal of sodium pentachlorophenate with

Shuang, S.; Liu, Z. W.; He, Z. Q.; Zhang, A. L.; Chen, J. M.; Yang, Y. P.; Xu, X. H., Impacts of


Page 18 of 24

Page 19 of 24


358

10.1016/j.nanoen.2014.09.032.

359

13. Yang, J.; Zhang, X.; Liu, H.; Wang, C.; Liu, S.; Sun, P.; Wang, L.; Liu, Y., Heterostructured TiO2/WO3

360

porous microspheres: Preparation, characterization and photocatalytic properties. Catal. Today , 2013, 201,

361

195-202, DOI: 10.1016/j.cattod.2012.03.008.

362

14. Gong, J.; Tian, F.; Peng, D.; Li, A.; Zhang, L., A highly sensitive photoelectrochemical detection of

363

perfluorooctanic acid with molecularly imprined polymer-functionalized nanoarchitectured hybrid of AgI–

364

BiOI composite. Biosens. Bioelectron. 2015, 73, 256, DOI: 10.1016/j.bios.2015.06.008.

365

15. Liu, D.; Jing, L.; Peng, L.; Tang, J.; Fu, H., Enhancement Effects of Cobalt Phosphate Modification on

366

Activity for Photoelectrochemical Water Oxidation of TiO2 and Mechanism Insights. ACS Appl. Mat.

367

Interfaces 2013, 5, (10), 4046, DOI: 10.1021/am400351m.

368

16. Zhang, X.; Cui, H.; Humayun, M.; Yang, Q.; Fan, N.; Sun, X.; Jing, L., Exceptional performance of

369

photoelectrochemical water oxidation of single-crystal rutile TiO2 nanorods dependent on the hole trapping

370

of modified chloride. Sci. Reports 2016, 6, 21430, DOI: 10.1038/srep21430.

371

17. Jing, L.; Zhou, J.; Durrant, J. R.; Tang, J.; Liu, D.; Fu, H., Dynamics of photogenerated charges in the

372

phosphate modified TiO2 and the enhanced activity for photoelectrochemical water splitting. Energy

373

Environ. Sci. 2012, 5, (4), 6552-6558, DOI: 10.1039/C2EE03383F.

374

18. Noh, S. Y.; Sun, K.; Choi, C.; Niu, M.; Yang, M.; Xu, K.; Jin, S.; Wang, D., Branched TiO2/Si

375

nanostructures for enhanced photoelectrochemical water splitting. Nano Energy 2013, 2, (3), 351-360, DOI:

376

10.1016/j.nanoen.2012.10.010.

377

19. Wang, G.; Ling, Y.; Wheeler, D. A.; George, K. E.; Horsley, K.; Heske, C.; Zhang, J. Z.; Li, Y., Facile

378

synthesis of highly photoactive alpha-Fe(2)O(3)-based films for water oxidation. Nano Lett 2011, 11, (8),

379

3503-9, DOI: 10.1021/nl202316j.

380

20. Bhirud, A. P.; Sathaye, S. D.; Waichal, R. P.; Ambekar, J. D.; Park, C. J.; Kale, B. B., In-situ

381

preparation of N-TiO2/graphene nanocomposite and its enhanced photocatalytic hydrogen production by

382

H2S splitting under solar light. Nanoscale 2015, 7, (11), 5023-5034, DOI:10.1039/c4nr06435f.

383

21. Zong, X.; Han, J.; Seger, B.; Chen, H.; Lu, G. M.; Li, C.; Wang, L., An integrated

384

photoelectrochemical-chemical loop for solar-driven overall splitting of hydrogen sulfide. Angew Chem Int

385

Ed Engl 2014, 53, (17), 4399-403, DOI: 10.1002/anie.201400571.

386

22. Wang, H., Hydrogen production from a chemical cycle of H2S splitting. International Journal of

387

Hydrogen Energy 2007, 32, (16), 3907-3914, DOI: 10.1016/j.ijhydene.2007.05.030.



388

23. Dubois, P.; Lelieur, J. P.; Lepoutre, G., Identification and characterization of lithium polysulfides in

389

solution in liquid ammonia. Cheminform 1988, 19, (15), 1883-1890.

390

24. Shin, S. W.; Lee, J. Y.; Ahn, K.-S.; Kang, S. H.; Kim, J. H., Visible Light Absorbing TiO2 Nanotube

391

Arrays by Sulfur Treatment for Photoelectrochemical Water Splitting. J. Phys. Chem. C 2015, 119, (24),

392

13375-13383, DOI: 10.1021/acs.jpcc.5b01104.

393

25. Solarska, R.; Jurczakowski, R.; Augustynski, J., A highly stable, efficient visible-light driven water

394

photoelectrolysis system using a nanocrystalline WO3 photoanode and a methane sulfonic acid electrolyte.

395

Nanoscale 2012, 4, (5), 1553-6, DOI: 10.1039/c2nr11573e.

396

26. Kang, M. J.; Kang, Y. S., Ultrathin insulating under-layer with a hematite thin film for enhanced

397

photoelectrochemical (PEC) water splitting activity. J. Mater. Chem. A 2015, 3, (30), 15723-15728, DOI:

398

10.1039/c5ta03468j, DOI: 10.1039/c5ta03468j.

399

27. Selvan, M. S.; Mckinley, M. D.; And, R. H. D.; Atwood, J. L., Liquid−Liquid Equilibria for Toluene +

400

Heptane + 1-Ethyl-3-methylimidazolium Triiodide and Toluene + Heptane + 1-Butyl-3-methylimidazolium

401

Triiodide†. J. Chem. Eng. Data 2000, 45, (5), 841-845, DOI: 10.1063/1.3474571.

402

28. Gomes, A. S. P.; Visscher, L.; Bolvin, H.; Saue, T.; Knecht, S.; Fleig, T.; Eliav, E., The electronic

403

structure of the triiodide ion from relativistic correlated calculations: A comparison of different

404

methodologies. J. Chem. Phys. 2010, 133, (6), 272, DOI: http://dx.doi.org/10.1063/1.3474571.

405

29. Svensson, P. H.; Kloo, L., A vibrational spectroscopic, structural and quantum chemical study of the

406

triiodide ion. J. Chem. Soc., Dalton Trans. 2000, 41, (14), 2449-2455, DOI: 10.1039/b002492i.

407

30. Ejigu, A.; Lovelock, K. R. J.; Licence, P.; Walsh, D. A., Iodide/triiodide electrochemistry in ionic

408

liquids: Effect of viscosity on mass transport, voltammetry and scanning electrochemical microscopy.

409

Electrochim. Acta 2011, 56, (28), 10313-10320, DOI: 10.1016/j.electacta.2011.03.108.

410

31. Reza-Dávila, J. C.; Avilés-Rodríguez, D.; Gomez, M.; Cortés-Arroyo, A. R.; Domínguez-Ramírez, A.

411

M., Evaluation of antioxidant capacity by triiodide methods. Ecs Transactions 2008, 15, (1), DOI:

412

10.1149/1.3046662.

413

32. Zeng, Q.; Li, J.; Bai, J.; Li, X.; Xia, L.; Zhou, B., Preparation of vertically aligned WO3 nanoplate

414

array films based on peroxotungstate reduction reaction and their excellent photoelectrocatalytic

415

performance. Appl. Catal., B 2017, 202, 388-396, DOI: 10.1016/j.apcatb.2016.09.045.

416

33.

417

oxygen evolution from water. Rsc Advances 2014, 5, (9), 6543-6552, DOI: 10.1039/c4ra09546d.

Pan, H.; Zhu, S.; Lou, X.; Mao, L.; Lin, J.; Tian, F.; Zhang, D., Graphene-based photocatalysts for


Page 20 of 24

Page 21 of 24


418

34. Chen, Q. P.; Li, J. H.; Li, X. J.; Huang, K.; Zhou, B. X.; Shangguan, W. F., Self-Biasing

419

Photoelectrochemical Cell for Spontaneous Overall Water Splitting under Visible-Light Illumination.

420

Chemsuschem 2013, 6, (7), 1276-1281, DOI: 10.1002/cssc.201200936.

421

35. Kamata, K.; Hirano, T.; Kuzuya, S.; Mizuno, N., ChemInform Abstract: Hydrogen-Bond-Assisted

422

Epoxidation

423

Selenium-Containing

424

10.1021/ja901289r.

425

36. Lillard, R. S.; Kanner, G. S. J.; Butt, D. P., The nature of oxide films on tungsten in acidic and alkaline

426

solutions. J. Electrochem. Soc. 1998, 145, (8), 2718-2725, DOI: 10.1149/1.1838704.

427

37. Takase, A.; Miyakawa, K., Raman Study on Sol-Gel Derived Tungsten Oxides from Tungsten

428

Ethoxide. J. Appl. Phys. 1991, 30, (30), L1508-L1511, DOI: 10.1143/JJAP.30.L1508.

429

38. Quanpeng, C.; Jinhua, L.; Baoxue, Z.; Mingche, L.; Hongchong, C.; Yanbiao, L.; Weimin, C.;

430

Wenfeng, S., Preparation of well-aligned WO3 nanoflake arrays vertically grown on tungsten substrate as

431

photoanode for photoelectrochemical water splitting. Electrochem. Commun. 2012, 20, 153-156, DOI:

432

10.1016/j.elecom.2012.03.043.

433

39. Qiang, L.; Quanpeng, C.; Jing, B.; Jianyong, L.; Jinhua, L.; Baoxue, Z., Enhanced

434

photoelectrocatalytic performance of nanoporous WO3 photoanode by modification of cobalt-phosphate

435

(Co-Pi) catalyst. J. Solid State Electrochem. 2014, 18, (1), 157-61, DOI: 10.1007/s10008-013-2228-7.

436

40. Matthews, R. W., ChemInform Abstract: Photocatalytic Oxidation of Organic Contaminants in Water:

437

An

438

https://doi.org/10.1351/pac199264091285.

439

41. Zhu, H.; Anders Hagfeldt, A.; Boschloo, G., Photoelectrochemistry of Mesoporous NiO Electrodes in

440

Iodide/Triiodide Electrolytes. J.phys.chem.c 2007, 111, (47), 17455-17458, DOI: 10.1021/jp077134k.

Aid

of

to

Homoallylic Dinuclear

Environmental

and

Allylic

Alcohols

Peroxotungstate.

Preservation.

with

Hydrogen

Cheminform

Cheminform

2009,

2009,

441


64,

Peroxide 131,

(9),

(20),

Catalyzed 6997,

1285-1290,

by

DOI:

DOI:


442 443 444 445

Figure 1. (a) SEM image of WO3/FTO; (b)chopped JSC -Potential curves of WO3 under visible light illumination; (c) schematic diagram of the Si/PVC cathode; (d) chopped JSC-Potential curves of the Si/PVC photoanode photocathode system.

446 447 448

Figure 2. (a) Band-Energy diagram of the PEC system comprising the WO3/FTO photoanode and Pt/SiPVC photocathode; (b) schematic diagram of the PEC-H2S system.


Page 22 of 24

Page 23 of 24


449

450

Figure 3. (a) Ion percentage of I- and I3- during the operation of the system; (b) ion

451

percentage of I- and I3- during the operation of the system with a scavenger in the anodic

452

cell.

453

454

Figure 4. Current and open-circuit potential under different concentrations of

455

sulfuric acid and potassium I-; (a) current histogram; (b) VOC of the PEC under different

456

conditions.



457 458 459

Figure 5. (a) Change in current during the system operation; (b) color change of the electrolyte in the anode chamber and sulfur compounds separated via centrifugation.

460 461 462

Figure 6. (a) Production of hydrogen and sulfur during long-term operation; (b) I–V characteristic curve and power density curve of the PEC-H2S system.


Page 24 of 24