Solar Water Oxidation by an InGaN Nanowire ... - ACS Publications

Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Letter

Solar Water Oxidation by InGaN Nanowire Photoanode with a Bandgap of 1.7 eV Sheng Chu, Srinivas Vanka, Yichen Wang, Jiseok Gim, Yongjie Wang, Yong-Ho Ra, Robert Hovden, Hong Guo, Ishiang Shih, and Zetian Mi ACS Energy Lett., Just Accepted Manuscript • DOI: 10.1021/acsenergylett.7b01138 • Publication Date (Web): 02 Jan 2018 Downloaded from http://pubs.acs.org on January 2, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Energy Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Solar Water Oxidation by InGaN Nanowire Photoanode with a Bandgap of 1.7 eV Sheng Chu1, Srinivas Vanka1,2, Yichen Wang1, Jiseok Gim3, Yongjie Wang2, Yong-Ho Ra1, Robert Hovden3, Hong Guo4, Ishiang Shih1, and Zetian Mi1,2 1

Department of Electrical and Computer Engineering, McGill University, 3480 University Street,

Montreal, Quebec H3A 0E9, Canada 2

Department of Electrical Engineering and Computer Science, University of Michigan, Ann

Arbor, 1301 Beal Avenue, Ann Arbor, MI 48109, USA 3

Department of Materials Science and Engineering, University of Michigan, Ann Arbor, 1301

Beal Avenue, Ann Arbor, MI 48109, USA 4

Department of Physics, McGill University, 3600 University Street, Montreal, Quebec H3A 2T8,

Canada

Corresponding Author *E-mail: [email protected]; Phone: 1 734 764 3963

ACS Paragon Plus Environment

1

ACS Energy Letters 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 29

ABSTRACT The performance of overall solar water splitting has been largely limited by the half-reaction of water oxidation. Here, we report a 1.7 eV bandgap InGaN nanowire photoanode for efficient solar water oxidation. It produces a low onset potential of 0.1 V versus reversible hydrogen electrode (RHE) and a high photocurrent density of 5.2 mA cm-2 at a potential as low as 0.6 V versus RHE. The photoanode yields a half-cell solar energy conversion efficiency up to 3.6%, a record for a single-photon photoanode to our knowledge. Furthermore, in the presence of hole scavengers, the photocurrent density of InGaN photoanode reaches 21.2 mA/cm2 at 1.23 V versus RHE, which approaches the theoretical limit for a 1.7 eV InGaN absorber. The InGaN nanowire photoanode may serve as an ideal top cell in a photoelectrochemical tandem device when stacked with a 0.9-1.2 eV bandgap bottom cell, which can potentially deliver solar-tohydrogen efficiency over 25%.

TOC GRAPHICS


2

Page 3 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

The availability of solar energy far exceeds global energy demands, but to date only provides a small fraction in the world energy market. A major hurdle to the widespread use of solar energy is the variability due to its intermittent and fluctuating nature, which requires a cost-effective energy storage for on-demand usage.1 Photoelectrochemical (PEC) water splitting, which combines photovoltaics and electrolysis into a simple and fully integrated unit, is a promising approach to directly store solar energy in the form of energy-rich hydrogen fuel in a scalable and low-cost manner.2-4 Among the proposed PEC cell configurations, the tandem device consisting of a p-type photocathode and an n-type photoanode with complementary bandgap absorption is advantageous for encompassing a substantial part of the solar spectrum while providing sufficient photovoltage to drive unassisted water splitting.5-8 In the PEC tandem cell, the maximum operating current density is the intersection of the overlapped current–potential curves of photocathode and photoanode. Compared to proton reduction on the photocathode, the water oxidation on the photoanode is more kinetically challenging due to the complicated four-electron transfer process. To date, the performance of PEC tandem devices has been largely limited by inefficient photoanodes, which are unable to offer high photocurrent density at low bias potential – for example, below 0.6 V versus reversible hydrogen electrode (RHE) to pair with highperformance photocathodes (e.g. Si).9-12 Si13-15 (Eg ~1.1 eV), Fe2O316,17 (Eg ~2.0 eV) and Ta3N51820

(Eg ~2.1 eV) photoanodes promise high theoretical photocurrent densities (Figure 1), but their

applications in PEC tandem cell have been largely limited by undesired high onset potentials, which were reported typically in the range of 0.9-1.1 V, 0.8-1.0 V and 0.6-0.8 V versus RHE, respectively. To date, BiVO4 is the favorable photoanode material for PEC tandem cell due to its relatively high performance with negative onset potentials (0.2-0.3 V versus RHE).21-26 BiVO4, however, is not ideal as the top light absorber in PEC tandem cell due to its wide bandgap of 2.4


3


Page 4 of 29

eV that limits the efficient utilization of solar spectrum. Recent theoretical modeling studies, by considering current matching conditions and kinetic overpotentials for water splitting, have shown that the optimal top and bottom light absorbers in a tandem cell are with bandgaps of 1.61.8 eV and 0.9-1.2 eV, respectively, which can yield a potential solar-to-hydrogen efficiency over 25%.27-32 Therefore, it is highly desirable to develop photoanode material with a lower bandgap and high performance working at low applied potentials. InGaN, a widely used semiconductor for solid-state lighting and power electronics, is a promising material as the top light absorber because of its tunable bandgap from 3.4 to 0.65 eV by increasing the indium content, as well as high absorption coefficient and large charge carrier mobility.33-36 The conduction and valence band edges of InGaN straddle the water redox potentials for an indium composition up to ~50%, corresponding to an energy bandgap of ~1.7 eV with a theoretical photocurrent density of 22 mA cm-2 (Figure 1).37-38 To date, however, previously reported InGaN photoanodes generally exhibit very poor performance for water oxidation (typically sub-mA cm-2 at 1.23 V versus RHE under simulated 1-sun illumination),39-40 which is largely limited by the inefficient light absorption due to low indium concentration, the presence of extensive recombination centers, and poor surface reaction kinetics for water oxidation. In the present study, we demonstrate highly efficient water oxidation using an In-rich InGaN nanowire photoanode with a bandgap of 1.7 eV. With the incorporation of an oxygen evolution co-catalyst, the InGaN nanowire photoanode produces a low onset potential of 0.1 V versus RHE and a high photocurrent density of 5.2 mA cm-2 at a potential as low as 0.6 V versus RHE. Moreover, a benchmarking half-cell solar energy conversion efficiency of 3.6% is achieved, which is the highest among single-photon photoanodes reported to date. In addition, using H2O2 or Na2SO3 as hole scavengers, the photocurrent density of InGaN nanowire


4

Page 5 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

photoanode reaches over 21 mA cm-2 at 1.23 V versus RHE, which approaches the theoretical limit for a 1.7 eV InGaN absorber. InGaN nanowire arrays were grown on a large area Si substrate (Figure 2a, 2-inch wafer, diameter ~5 cm) by plasma-assisted molecular beam epitaxy (MBE) (see the Supporting Information). The cross-sectional electron microscopy of InGaN/Si reveals that the InGaN nanowires are vertically aligned to the Si substrate with an approximate diameter of ~200 nm (±40 nm) and height of ~700 nm (±50 nm)—shown by scanning electron microscopy (SEM) in Figure 2b and scanning transmission electron microscopy (STEM) in Figure S1 in the Supporting Information. The crystalline nanowires extend atop a polycrystalline growth layer of ~650 nm (±50 nm) where early growth of nanowires may have competed and coalesced. Highresolution transmission electron microscopy (HRTEM) image (Figure 2c) indicates uniform crystallinity near the termination of the nanowires where catalytic activity is expected to be highest. A lattice spacing of 0.27 nm uniquely corresponds to the (002) lattice plane of InGaN with the orientation that indicates preferred growth along direction (c-axis) (Figure 2c, Figure S2, Supporting Information). The orientation of InGaN nanowires is also confirmed by the presence of a predominant (002) diffraction peak in the X-ray diffraction (XRD) measurement (Figure S3a, Supporting Information). The electron-diffraction pattern from the growth surface is consistent with the single-crystal observation of terminal nanowire segments (Figure S3b, Supporting Information). Room temperature photoluminescence (PL) measurement shows a single optical emission peak at 720 nm (Figure S4, Supporting Information), corresponding to a bandgap of ~1.7 eV and indium composition of ~50%.36,38 The coexistence of Ga, N, and In was confirmed from electron energy-loss spectroscopy (EELS) taken on a cross-sectional InGaN nanowire (Figure S5, Supporting Information). The low


5


Page 6 of 29

substrate temperature (530 oC) and optimal N2 flow rate (~0.5 sccm) used in the InGaN growth, together with the nanowire geometry allows for effective strain relaxation and reduces phase separation.41-43 An IrO2 co-catalyst, which is known as a highly active oxygen evolution catalyst with a low overpotential over a wide pH range,44 was loaded on InGaN nanowires by a simple photodeposition process (see the Supporting Information). As revealed by dark-field TEM (DFTEM) (Figure 2d) and SEM (Figure S6, S7a, Supporting Information), IrO2 nanoparticles are uniformly loaded on the InGaN nanowire surface. The atomic concentration of Ir compared to InGaN nanowire is only a few percent—estimated to be ~2% from EDX analysis (Figure 2e). Bright-field scanning-TEM (BF-STEM) and high-angle annular dark field (HAADF-STEM) show IrO2 nanoparticles with a size of 1-2 nm and density consistent with the heavier atomic weight of IrO2 (Figure 2f, Figure S7b-f, Supporting Information). While some larger IrO2 nanoparticles present partially crystallinity (Figure S7b, d, Supporting Information, red arrows), smaller particles often appear amorphous (Figure S7b-f, Supporting Information, yellow arrows). The X-ray photoemission spectroscopy (XPS) analysis indicates Ir4+ and is the expected valence for IrO2 (Figure S8, Supporting Information). PEC performance of InGaN nanowire photoanode was investigated in 0.5 M H2SO4 under air mass 1.5 global (AM 1.5G) simulated 1-sun illumination in a conventional three-electrode cell (Figure 3a). Figure 3b shows the current-potential (J-V) curves of InGaN sample with and without IrO2 deposition. In the dark, the electrodes show negligible current. Under AM 1.5G simulated 1-sun illumination, compared to the bare InGaN, IrO2 modification produces ~500 mV cathodic shift in the onset potential and a large increase in the photocurrent, indicating enhanced charge separation and water oxidation reaction after IrO2 loading. The substantially lower


6

Page 7 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

photocurrent density and larger overpotential of bare InGaN photoanode are ascribed mainly to the poor kinetics for water oxidation that leads to higher charge carrier recombination at the surface, which requires larger bias to achieve appreciable charge transfer across the semiconductor−electrolyte interface for the oxygen evolution reaction. In addition, the excessive accumulation of holes at the surface with bare InGaN may cause the self-oxidation of InGaN absorber, which is detrimental to the photoelectrode stability. The modification of InGaN with IrO2 water oxidation co-catalyst enhances the reaction kinetic with reduced hole accumulation at the surface, which improves both the activity and photostability of the photoelectrode. A similar loading effect of IrO2 co-catalyst was also observed for other photoanode materials.45-48 The IrO2/InGaN sample provides an onset potential of 0.1 V versus RHE (measured at 0.2 mA cm-2), which is remarkable considering the small bandgap of InGaN (1.7 eV). The impressively low onset potential is largely attributed to the favorable conduction band position of InGaN that locates slightly above the water reduction potential, as determined by Mott−Schottky measurements (Figure S9, Supporting Information). Considering the bandgap energy of 1.7 eV, the valance band edge position of InGaN is estimated to be lower than the water oxidation potential (1.23 V versus RHE) by about 0.4 V. The conduction and valence band edges of InGaN that straddle the water redox potentials for an indium composition of ~50% is consistent with previous theoretical calculation.37 In addition to the low onset potential, the photocurrent density of IrO2/InGaN sample reaches 10.9 mA cm-2 at 1.23 V versus RHE, a 3.4-fold improvement compared to bare InGaN photoanode (Figure 3b). The maximum applied bias photon-to-current efficiency (ABPE) of IrO2/InGaN photoanode calculated from the J-V curve is 3.6% (Figure 3c), which is the highest among those of previously reported photoanodes including 2.2-2.3% for BiVO4-based


7


Page 8 of 29

materials,49-51 2.5% for Ir, Co complex/Ni(OH)2/Fh/TiOx/Ta3N5,52 2.7% for Coox/Fe2TiO5-TiO253 and 3.3% for NiFe/SiOx/np+-Si54 (Table S1, Supporting Information). Moreover, the PEC performance in the InGaN photoanode prepared here is much improved in comparison to the previously reported InGaN photoanodes,39-40 and the underlying mechanisms are described. The main processes that affect the PEC performance are light absorption, charge carrier transfer, and surface redox reaction. (i) The small energy bandgap of 1.7 eV for the InGaN in this work results in much enhanced light absorption towards longer wavelength and thus higher achievable photocurrent density; (ii) The presented nanowires were grown by MBE using a self-catalytic growth process,55 i.e. without the incorporation foreign metal catalysts, which together with the relatively low growth temperature, ultrahigh vacuum, and precisely controlled molecular beam flux allows for the synthesis of In-rich InGaN nanowires with drastically reduced defect densities and impurity incorporation,56 compared to the conventional chemical vapor deposition (CVD) growth processes39-40, thereby leading to significantly reduced charge recombination. The superior crystallinity of InGaN nanowires grown by MBE is further evidenced by the demonstration of high efficiency nanowire light emitting diodes and laser diodes.56-58 (iii) During the MBE growth, the use of Ga seeding layer to initiate the nanowire nucleation, together with a N-rich growth condition, leads to the formation of InGaN nanowires with N-terminated surface, not only for their top faces but also for their side faces, which is different from the Ga-terminated top surface grown by CVD.59 The N-terminated surfaces can help protect against photocorrosion, and provide polarization effect for efficient transport of photogenerated charge carriers. (iv) The surface reaction kinetics were further improved by coupling with efficient water oxidation cocatalyst (i.e. IrO2 in this work), while no co-catalyst was applied in the previous reports.39-40 It is worth noting that although we have previously reported efficient two-electron Br- oxidation with


8

Page 9 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

bare InGaN,34,38,43 the application of InGaN on more thermodynamically and kinetically challenging four-electron water oxidation has not been achieved prior to this work. This indicates the critical role of modification with efficient water oxidation catalyst to improve the surface kinetics. Significantly, the photocurrent density produced by the IrO2/InGaN photoanode in the low bias region is particularly outstanding. For example, a photocurrent density of 5.2 mA cm-2 is achieved at 0.6 V versus RHE, which is the highest among any single-photon photoanodes reported to date at such a low potential (Table S1, Supporting Information). This characteristic promises a high operating point (zero bias) when paired with a high-performance photocathode for PEC tandem system (Figure S10, Supporting Information). The 1.7 eV bandgap InGaN nanowire presented here is highly suited for the top light absorber of the PEC tandem device.27-32 Compared to other reported photoanodes with bandgaps in the range of 1.6-1.8 eV, InGaN nanowire photoanode shows an efficiency at least one or two orders of magnitude higher and stands out as the best top absorber reported to date (Table S2, Supporting Information). It is worth noting that the loading amount of IrO2 plays a significant role on the photoanode performance. An optimum content of 2 at% IrO2 on InGaN was found for the maximum activity of the photocurrent (Figure S11, Supporting Information). As shown by the SEM images in Figure S12 in the Supporting Information, a lower loading amount produces less reactive sites for water oxidation, while excessive loading forms aggregated clusters, which may shield light absorption and act as recombination centers.60 Figure 3d shows the wavelength dependence of the incident photon-to-current conversion efficiency (IPCE) for the IrO2/InGaN photoanode at 1.23 V versus RHE. A maximum IPCE of 93% is achieved at 440 nm, and then gradually decreases to 63% at 500 nm, 33% at 600 nm and


9


Page 10 of 29

10% at 700 nm. By integrating the IPCE spectrum with the standard solar spectrum of AM 1.5G, a photocurrent density of 10.3 mA cm-2 was obtained (Figure S13, Supporting Information), which is close to the measured value in Figure 3b. The photocurrent response of IrO2/InGaN agrees well with the absorption edge of InGaN, indicating the photocurrent is originated from the bandgap transition of InGaN. This is further supported by control experiment showing that negligible photocurrent is produced by the IrO2/Si photoanode in the absence of InGaN nanowires (Figure S14, Supporting Information). The stability of photoanodes for water oxidation was evaluated by chronoamperometry (J-t) under continuous illumination at 0.8 V versus RHE (Figure 3e). For the bare InGaN, the photocurrent decayed rapidly to nil within 5 min. After modification of InGaN with IrO2 cocatalyst, the stability was improved to some extent but obvious photocurrent decay was still observed with the photocurrent decreased to a negligible level after 30 min. In contrast, significant improvement was achieved by coating the IrO2/InGaN photoanode with 18 atomic layer deposition (ALD) cycles (total thickness ~1 nm) of TiO2 (see the Supporting Information). ALD is a known technique for conformal coating with precise control over thickness.61-63 XPS analysis confirmed the signal of Ti4+ from ALD TiO2 (Figure S15, Supporting Information). The binding energy of 464.0 eV and 458.2 eV correspond to Ti 2p1/2 and Ti 2p3/2 orbitals of Ti4+ from TiO2, respectively, consistent with previous reports.64-65 A prolonged stability test of TiO2/IrO2/InGaN was also examined, showing that the photoanode remained active after 4 h continuous illumination (Figure S16, Supporting Information). The Faradaic efficiencies of H2 and O2 were measured to be about 96% and 88%, respectively (Figure S17, Supporting Information). It is seen that the TiO2 protection layer plays a vital role in improving the PEC stability by preventing the underlying InGaN from direct contact with the electrolyte, while not


10

Page 11 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

compromising charge carrier transport or mass transport of reactant and product species related to the oxygen evolution reaction. Increasing the TiO2 overlayer thickness beyond 2 nm resulted in diminished photocurrent (Figure S18, Supporting Information), which can be ascribed to the limited mass transport or large tunneling resistance to charge transport associated with thick TiO2 layer.65-67 The holes can be transported by tunneling mechanism through the ultrathin TiO2 layer to the electrolyte, while large resistance occurs on layers thicker than a few nm. In addition, we note that the loss of IrO2 nanoparticles during the PEC operation was largely suppressed by adding the TiO2 overlayer, evidenced by XPS analysis (Table S3, Supporting Information). Therefore, TiO2 overlayer may also serve as a “glue” to stabilize the IrO2 nanoparticles adhered on InGaN nanowire surface to keep the high activity for water oxidation reaction. Despite the stability of InGaN photoanode is much improved with the protection of TiO2 layer, the device performance does decrease during the test. SEM and TEM images of TiO2/IrO2/InGaN after the PEC stability test were examined, as shown in Figure 4. It revealed some parts of the InGaN nanowire were photocorroded and etched away during the long-term stability testing, possibably caused by the oxidation of the electrode (via oxidation of N3-) and eventual dissolution of InGaN.68-69 It is likely that the ultrathin 1 nm TiO2 coating contains some pinholes that electrolyte can penetrate through to oxidize the underlying InGaN. This is in line with a recent study showing that a thick TiO2 protection layer of at least 40 nm is required to acheive pinholefree films.70 Indeed, literature reports show that relatively thick layers (at least 40 nm) were applied for the protection of group III-V photoanodes to achieve long-term stability (in the range of hours to days, see Table S4, Supporting Information), in which the holes are transported via electrically defective TiO2 or band edge of p-type hole conducting materials.71-74 However, compared to other III-V photoanodes, the InGaN presented here features an extremely low onset


11


Page 12 of 29

potential of 0.1 V versus RHE, which is advantageous to pair with a photocathode for unassisted solar water splitting. Ongoing work is to investigate the protection of InGaN with optimally designed TiO2 layers (together with oxygen evolution catalysts) to achieve simultaneously high activity and stability for water oxidation. The maximum attainable photocurrent density for the InGaN with a 1.7 eV bandgap is ∼22 mA/cm2 under AM 1.5G solar irradiation. At 1.23 V versus RHE, our sample reaches half of this maximum. In order to gain more information about the photocurrent loss and rate-limiting factor, PEC performance of InGaN photoanode was also studied in the presence of H2O2 hole scavenger. As shown in Figure 5a, the photocurrent density of InGaN photoanode for H2O2 oxidation reaches as high as 21.2 mA/cm2 at 1.23 V versus RHE, which exceeds 96% of the theoretical maximum for a 1.7 eV InGaN absorber. The attained near-theoretical photocurrent indicates the apparent quantum yield is nearly ideal over the wide wavelength range up to ~720 nm. This can be attributed to the enhanced light trapping due to the anti-reflection effects of nanowire geometry,75-76 efficient charge carrier transport within low dimensional nanowires, improved charge separation efficiency due to the short radial diffusion distance in nanowire geometry for the minority carriers (holes) toward the electrolyte solution, and extremely fast surface reaction rate for H2O2 oxidation owing to its rapid oxidation kinetics (2-electron transfer) and favorable oxidation potential (+0.68 V versus RHE for the O2/H2O2 couple, inset of Figure 5a).77-78 Notably, the photocurrent density of InGaN photoanode reached 20.4 mA/cm2 at 0.6 V versus RHE, which is the highest for any photoanodes reported to date at such a low potential to our knowledge. The lower photocurrent for water oxidation compared to that for H2O2 oxidation is mainly ascribed to the sluggish surface reaction kinetics. The catalytic efficiency for water oxidation was calculated to be only ~50% at 1.23 V versus RHE and even lower at low bias


12

Page 13 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

region (Figure S19, Supporting Information). Moreover, the J-t test showed the InGaN photoanode exhibited excellent stability during 10 h operation in the presence of H2O2 (Figure 5b). In addition to H2O2, a high photocurrent density of 21.2 mA/cm2 at 1.23 V versus RHE and excellent stability were also observed using Na2SO3 as a hole scavenger (Figure S20, Supporting Information). The studies in the presence of hole scavengers imply the possibility of developing highly efficient and stable water oxidation system based on InGaN nanowires if coupled with suitable water oxidation co-catalyst with fast reaction kinetics. In addition, it is noted that the presence of phase separation may exist in highly disordered regions of the InGaN wafer, offering opportunities to further optimize the growth conditions. Further improvement of the quality of the nanowire wafer is expected to enhance the performance (e.g. photovoltage) for solar water oxidation. In summary, we have demonstrated efficient solar water oxidation by InGaN nanowire photoanode with a bandgap of 1.7 eV. Owing to the low dimensional nanowire structure, appropriate band edge positions to straddle the redox potentials of water splitting, together with the effective coupling with an efficient water oxidation co-catalyst (i.e. IrO2), the InGaN photoanode produced a low onset potential of 0.1 V versus RHE and a record half-cell solar energy conversion efficiency of 3.6%. The InGaN nanowire can be leveraged with new high performing water oxidation co-catalysts as they become available, improving the performance towards the theoretical maximum for a 1.7 eV light absorber.

ASSOCIATED CONTENT Supporting Information


13


Page 14 of 29

Experimental methods, additional figures and tables. AUTHOR INFORMATION Corresponding Author *E-mail: [email protected]; Phone: 1 734 764 3963 Notes The authors declare no competing financial interest. ACKNOWLEDGMENT S. Chu and S. Vanka contributed equally to this work. This work was supported by the Natural Sciences and Engineering Research Council of Canada (NSERC) and US Department of Energy EERE Program (Grant #: EE0008086). Part of the work was conducted in the Microfabrication Facility at McGill University and the Michigan Center for Materials Characterization at the University of Michigan (NSF #DMR-0723032).

REFERENCES (1) Lewis, N. S.; Nocera, D. G. Powering The Planet: Chemical Challenges in Solar Energy Utilization. Proc. Natl. Acad. Sci. U. S. A. 2006, 103, 15729−15735. (2) Walter, M. G.; Warren, E. L.; Mckone, J. R.; Boettcher, S. W.; Mi, Q. X.; Santori, E. A.; Lewis, N. S. Solar Water Splitting Cells. Chem. Rev. 2010, 110, 6446-6473. (3) Li, Z.; Luo, W., Zhang, M.; Feng, J.; Zou, Z. Photoelectrochemical Cells for Solar Hydrogen Production: Current State of Promising Photoelectrodes, Methods to Improve Their Properties, and Outlook. Energy Environ. Sci. 2013, 6, 347-370.


14

Page 15 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

(4) Sivula, K.; Van De Krol, R. Semiconducting Materials for Photoelectrochemical Energy Conversion. Nature Rev. Mater. 2016, 1, 15010. (5) Nozik, A. J. P-N Photoelectrolysis Cells. Appl. Phys. Lett. 1976, 29, 150-153. (6) Bolton, J. R.; Strickler, S. J.; Connolly, J. S. Limiting and Realizable Efficiencies of Solar Photolysis of Water. Nature 1985, 316, 495-500. (7) Prevot, M. S.; Sivula, K. Photoelectrochemical Tandem Cells for Solar Water Splitting. J. Phys. Chem. C 2013, 117, 17879-17893. (8) Chu, S.; Li, W.; Yan, Y.; Hamann, T.; Shih, I.; Wang, D. W.; Mi, Z. Roadmap on Solar Water Splitting: Current Status and Future Prospects. Nano Futures, 2017, 1, 022001. (9) Wang, H. L.; Deutsch, T.; Turner, J. A. Direct Water Splitting under Visible Light with Nanostructured Hematite and WO3 Photoanodes and a GaInP2 Photocathode. J. Electrochem. Soc. 2008, 155, F91-F96. (10) Liu, C.; Tang, J. Y.; Chen, H. M.; Liu, B.; Yang, P. D. A Fully Integrated Nanosystem of Semiconductor Nanowires for Direct Solar Water Splitting. Nano Lett. 2013, 13, 29892992. (11) Jang, J. W.; Du, C.; Ye, Y. F.; Lin, Y. J.; Yao, X. H.; Thorne, J.; Liu, E.; Mcmahon, G.; Zhu, J. F.; Javey, A.; et al. Enabling Unassisted Solar Water Splitting by Iron Oxide and Silicon. Nat. Commun. 2015, 6, 7447. (12) Lai, Y. H.; Palm, D. W.; Reisner, E. Multifunctional Coatings from Scalable Single Source Precursor Chemistry in Tandem Photoelectrochemical Water Splitting. Adv. Energy Mater. 2015, 5, 1501668.


15


Page 16 of 29

(13) Zhou, X.; Liu, R.; Sun, K.; Papadantonakis, K. M.; Brunschwig, B. S.; Lewis, N. S. 570 mV Photovoltage, Stabilized n-Si/CoOx heterojunction Photoanodes Fabricated Using Atomic Layer Deposition. Energy Environ. Sci. 2016, 9, 892-897. (14) Yang, J.; Cooper, J. K.; Toma, F. M.; Walczak, K. A.; Favaro, M.; Beeman, J. W.; Hess, L. H.; Wang, C.; Zhu, C.; Gul, S.; et al. A Multifunctional Biphasic Water Splitting Catalyst Tailored for Integration with High-Performance Semiconductor Photoanodes. Nat. Mater. 2017, 16, 335-341 (15) Mei, B.; Seger, B.; Pedersen, T.; Malizia, M.; Hansen, O.; Chorkendorff, I.; Vesborg, P. C. K. Protection of p+-n-Si Photoanodes by Sputter-Deposited Ir/IrOx Thin Films. J. Phys. Chem. Lett. 2014, 5, 1948-1952. (16) Sivula, K.; Le Formal, F.; Gratzel, M. Solar Water Splitting: Progress Using Hematite (α-Fe2O3) Photoelectrodes. Chemsuschem 2011, 4, 432-49. (17) Shen, S.; Lindley, S. A.; Chen, X.; Zhang, J. Z. Hematite Heterostructures for Photoelectrochemical Water Splitting: Rational Materials Design and Charge Carrier Dynamics. Energy Environ. Sci. 2016, 9, 2744-2775. (18) Li, M. X.; Luo, W. J.; Cao, D. P.; Zhao, X.; Li, Z. S.; Yu, T.; Zou, Z. G. A Co-CatalystLoaded Ta3N5 Photoanode with a High Solar Photocurrent for Water Splitting upon Facile Removal of the Surface Layer. Angew. Chem. Int. Ed. 2013, 52, 11016-11020. (19) He, Y.; Thorne, James E.; Wu, Cheng H.; Ma, P.; Du, C.; Dong, Q.; Guo, J.; Wang, D. What Limits the Performance of Ta3N5 for Solar Water Splitting? Chem 2016, 1, 640655. (20) Zhong, M.; Hisatomi, T.; Sasaki, Y.; Suzuki, S.; Teshima, K.; Nakabayashi, M.; Shibata, N.; Nishiyama, H.; Katayama, M.; Yamada, T.; et al. Highly Active GaN-


16

Page 17 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Stabilized Ta3N5 Thin-Film Photoanode for Solar Water Oxidation. Angew. Chem. Int. Ed. 2017, 56, 4739-4743. (21) Park, Y.; Mcdonald, K. J.; Choi, K.-S. Progress in Bismuth Vanadate Photoanodes for Use in Solar Water Oxidation. Chem. Soc. Rev. 2013, 42, 2321−2337. (22) Sharp, I. D.; Cooper, J. K.; Toma, F. M.; Buonsanti, R. Bismuth Vanadate as a Platform for Accelerating Discovery and Development of Complex Transition-Metal Oxide Photoanodes. ACS Energy Lett. 2017, 2, 139-150. (23) Bornoz, P.; Abdi, F. F.; Tilley, S. D.; Dam, B.; Van De Krol, R.; Graetzel, M.; Sivula, K. A Bismuth Vanadate-Cuprous Oxide Tandem Cell for Overall Solar Water Splitting. J. Phys. Chem. C 2014, 118, 16959-16966. (24) Xu, P.; Feng, J.; Fang, T.; Zhao, X.; Li, Z.; Zou, Z. Photoelectrochemical Cell for Unassisted Overall Solar Water Splitting Using a BiVO4 Photoanode and Si Nanoarray Photocathode. RSC Adv. 2016, 6, 9905. (25) Zhao, J.; Guo, Y.; Cai, L.; Li, H.; Wang, K. X.; Cho, I. S.; Lee, C. H.; Fan, S.; Zheng, X. High-Performance Ultrathin BiVO4 Photoanode on Textured Polydimethylsiloxane Substrates for Solar Water Splitting. ACS Energy Lett. 2016, 1, 68-75. (26) Chakthranont, P.; Hellstern, T. R.; Mcenaney, J. M.; Jaramillo, T. F. Design and Fabrication of a Precious Metal-Free Tandem Core–Shell p+-n Si/W-Doped BiVO4 Photoanode for Unassisted Water Splitting. Adv. Energy Mater. 2017, 7, 1701515. (27) Hu, S.; Xiang, C. X.; Haussener, S.; Berger, A. D.; Lewis, N. S. An Analysis of the Optimal Band Gaps of Light Absorbers in Integrated Tandem Photoelectrochemical Water-Splitting Systems. Energy Environ. Sci. 2013, 6, 2984-2993.


17


Page 18 of 29

(28) Doscher, H.; Geisz, J. F.; Deutsch, T. G.; Turner, J. A., Sunlight Absorption in Water Efficiency and Design Implications for Photoelectrochemical Devices. Energy Environ. Sci. 2014, 7, 2951-2956. (29) Seitz, L. C.; Chen, Z.; Forman, A. J.; Pinaud, B. A.; Benck, J. D.; Jaramillo, T. F. Modeling Practical Performance Limits of Photoelectrochemical Water Splitting Based on the Current State of Materials Research. Chemsuschem 2014, 7, 1372-1385. (30) Fountaine, K. T.; Lewerenz, H. J.; Atwater, H. A. Efficiency Limits for Photoelectrochemical Water-Splitting. Nat. Commun. 2016, 7, 13706. (31) Seger, B.; Hansen, O.; Vesborg, P. C. K., A Flexible Web-Based Approach to Modeling Tandem Photocatalytic Devices. Solar RRL 2017, 1, E201600013; (32) Montoya, J. H.; Seitz, L. C.; Chakthranont, P.; Vojvodic, A.; Jaramillo, T. F.; Norskov, J. K. Materials for Solar Fuels and Chemicals. Nat. Mater. 2017, 16, 70-81. (33) Luo, W. J.; Liu, B.; Li, Z. S.; Xie, Z. L.; Chen, D. J.; Zou, Z. G.; Zhang, R. Stable Response to Visible Light of InGaN Photoelectrodes. Appl. Phys. Lett. 2008, 92, 262110. (34) Alotaibi, B.; Nguyen, H. P. T.; Zhao, S.; Kibria, M. G.; Fan, S.; Mi, Z. Highly Stable Photoelectrochemical Water Splitting and Hydrogen Generation Using a Double-Band InGaN/GaN Core/Shell Nanowire Photoanode. Nano Lett. 2013, 13, 4356-4361. (35) Kibria, M. G.; Chowdhury, F. A.; Zhao, S.; Alotaibi, B.; Trudeau, M. L.; Guo, H.; Mi, Z. Visible Light-Driven Efficient Overall Water Splitting Using P-Type Metal-Nitride Nanowire Arrays. Nat. Commun. 2015, 6, 6797. (36) Wu, J.; Walukiewicz, W.; Yu, K. M.; Ager, J. W.; Haller, E. E.; Lu, H.; Schaff, W. J. Small Band Gap Bowing in In1-XGaxN Alloys. Appl. Phys. Lett. 2002, 80, 4741-4743.


18

Page 19 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

(37) Moses, P. G.; Van De Walle, C. G. Band Bowing and Band Alignment in InGaN Alloys. Appl. Phys. Lett. 2010, 96, 021908; (38) Fan, S.; Shih, I.; Mi, Z. A Monolithically Integrated InGaN Nanowire/Si Tandem Photoanode Approaching the Ideal Bandgap Configuration of 1.75/1.13 eV. Adv. Energy Mater. 2017, 7, 1600952. (39) Hwang, Y. J.; Wu, C. H.; Hahn, C.; Jeong, H. E.; Yang, P. D. Si/ InGaN Core/Shell Hierarchical Nanowire Arrays and Their Photoelectrochemical Properties. Nano Lett. 2012, 12, 1678-1682. (40) Caccamo, L.; Hartmann, J.; Fabrega, C.; Estrade, S.; Lilienkamp, G.; Prades, J. D.; Hoffmann, M. W. G.; Ledig, J.; Wagner, A.; Wang, X.; et al. Band Engineered Epitaxial 3D GaN-InGaN Core-Shell Rod Arrays as an Advanced Photoanode for Visible-LightDriven Water Splitting. ACS Appl. Mater. Inter. 2014, 6, 2235-2340. (41) Kuykendall, T.; Ulrich, P.; Aloni, S.; Yang, P. Complete Composition Tunability of InGaN Nanowires Using a Combinatorial Approach. Nat. Mater. 2007, 6, 951-956. (42) Pendyala, C.; Jasinski, J. B.; Kim, J. H.; Vendra, V. K.; Lisenkov, S.; Menon, M.; Sunkara, M. K. Nanowires as Semi-Rigid Substrates for Growth of Thick, InxGa1-XN (X > 0.4) Epi-Layers without Phase Segregation for Photoelectrochemical Water Splitting. Nanoscale 2012, 4, 6269-6975. (43) Fan, S.; Woo, S. Y.; Vanka, S.; Botton, G. A.; Mi, Z. An In0.5Ga0.5N Nanowire Photoanode for Harvesting Deep Visible Light Photons. APL Mater. 2016, 4, 076106. (44) Mccrory, C. C. L.; Jung, S. H.; Peters, J. C.; Jaramillo, T. F. Benchmarking Heterogeneous Electrocatalysts for the Oxygen Evolution Reaction. J. Am. Chem. Soc. 2013, 135, 16977-16987.


19


Page 20 of 29

(45) Tilley, S. D.; Cornuz, M.; Sivula, K.; Gratzel, M. Light-Induced Water Splitting with Hematite: Improved Nanostructure and Iridium Oxide Catalysis. Angew. Chem., Int. Ed. 2010, 49, 6405-6408. (46) Abe, R.; Higashi, M.; Domen, K. Facile Fabrication of an Efficient Oxynitride TaON Photoanode for Overall Water Splitting into H2 and O2 under Visible Light Irradiation. J. Am. Chem. Soc. 2010, 132, 11828-11829. (47) Bledowski, M.; Wang, L. D.; Neubert, S.; Mitoraj, D.; Beranek, R. Improving the Performance of Hybrid Photoanodes for Water Splitting by Photodeposition of Iridium Oxide Nanoparticles. J. Phys. Chem. C 2014, 118, 18951-18961. (48) Li, W.; He, D.; Sheehan, S. W.; He, Y.; Thorne, J. E.; Yao, X.; Brudvig, G. W.; Wang, D. Comparison of Heterogenized Molecular and Heterogeneous Oxide Catalysts for Photoelectrochemical Water Oxidation. Energy Environ. Sci. 2016, 9, 1794-1802. (49) Kim, T. W.; Ping, Y.; Galli, G. A.; Choi, K. S. Simultaneous Enhancements in Photon Absorption and Charge Transport of Bismuth Vanadate Photoanodes for Solar Water Splitting. Nat. Commun. 2015, 6, 8769. (50) Kuang, Y. B.; Jia, Q. X.; Nishiyama, H.; Yamada, T.; Kudo, A.; Domen, K. A FrontIlluminated Nanostructured Transparent BiVO4 Photoanode for > 2% Efficient Water Splitting. Adv. Energy Mater. 2016, 6, 1501645. (51) Ye, K.-H.; Wang, Z.; Gu, J.; Xiao, S.; Yuan, Y.; Zhu, Y.; Zhang, Y.; Mai, W.; Yang, S. Carbon Quantum Dots as a Visible Light Sensitizer to Significantly Increase the Solar Water Splitting Performance of Bismuth Vanadate Photoanodes. Energy Environ. Sci. 2017, 10, 772-779.


20

Page 21 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

(52) Liu, G. J.; Ye, S.; Yan, P. L.; Xiong, F. Q.; Fu, P.; Wang, Z. L.; Chen, Z.; Shi, J. Y.; Li, C. Enabling an Integrated Tantalum Nitride Photoanode to Approach the Theoretical Photocurrent Limit for Solar Water Splitting. Energy Environ. Sci. 2016, 9, 1327-1334. (53) Liu, Q. H.; He, J. F.; Yao, T.; Sun, Z. H.; Cheng, W. R.; He, S.; Xie, Y.; Peng, Y. H.; Cheng, H.; Sun, Y. F.; et al. Aligned Fe2TiO5-Containing Nanotube Arrays with Low Onset Potential for Visible-Light Water Oxidation. Nat. Commun. 2014, 5, 5122. (54) Yu, X.; Yang, P.; Chen, S.; Zhang, M.; Shi, G. NiFe Alloy Protected Silicon Photoanode for Efficient Water Splitting. Adv. Energy Mater. 2016, 6, 1601805. (55) Chang, Y. L.; Li, F.; Fatehi, A.; Mi, Z. Molecular Beam Epitaxial Growth and Characterization of Non-Tapered InN Nanowires on Si (111). Nanotechnology 2009, 20, 345203. (56) Zhao, S.; Nguyen, H. P. T.; Kibria, M. G.; Mi, Z. III-Nitride Nanowire Optoelectronics. Prog. Quant. Electron. 2015, 44, 14-68. (57) Nguyen, H. P. T.; Zhang, S.; Cui, K.; Han, X.; Fathololoumi, S.; Couillard, M.; Botton, G. A.; Mi, Z. p-Type Modulation Doped InGaN/GaN Dot-in-a-Wire White-LightEmitting Diodes Monolithically Grown on Si(111). Nano Lett. 2011, 11, 1919-1924. (58) Ra, Y.; Wang, R., Woo, S. Y.; Djavid, M.; Sadaf, S. M.; Lee, J.; Gianluigi A. Botton, G. A.; Mi, Z. Full-Color Single Nanowire Pixels for Projection Displays. Nano Lett. 2016, 16, 4608-4615. (59) Kibria, M. G.; Qiao, R.; Yang, W. L.; Boukahil, I.; Kong, X. H.; Chowdhury, F. A.; Trudeau, M. L.; Ji, W.; Guo, H.; Himpsel, F. J.; et al. Atomic-Scale Origin of Long-Term Stability and High Performance of p-GaN Nanowire Arrays for Photocatalytic Overall Pure Water Splitting. Adv. Mater. 2016, 28, 8388-8397.


21


Page 22 of 29

(60) Ran, J. R.; Zhang, J.; Yu, J. G.; Jaroniec, M.; Qiao, S. Z. Earth-Abundant Cocatalysts for Semiconductor-Based Photocatalytic Water Splitting. Chem. Soc. Rev. 2014, 43, 7787-7812. (61) Hu, S.; Lewis, N. S.; Ager, J. W.; Yang, J. H.; Mckone, J. R.; Strandwitz, N. C. ThinFilm Materials for the Protection of Semiconducting Photoelectrodes in Solar-Fuel Generators. J. Phys. Chem. C 2015, 119, 24201-24228 (62) Scheuermann, A. G.; Mcintyre, P. C. Atomic Layer Deposited Corrosion Protection: A Path to Stable and Efficient Photoelectrochemical Cells. J. Phys. Chem. Lett. 2016, 7, 2867-2878. (63) Bae, D.; Seger, B.; Vesborg, P. C. K.; Hansen, O.; Chorkendorff, I. Strategies for Stable Water Splitting via Protected Photoelectrodes. Chem. Soc. Rev. 2017, 46, 1933-1954. (64) Zhang, P.; Wang, T.; Gong, J. L. Passivation of Surface States by ALD-Grown TiO2 Overlayers on Ta3N5 Anodes for Photoelectrochemical Water Oxidation. Chem. Commun. 2016, 52, 8806-8809. (65) Mcdowell, M. T.; Lichterman, M. F.; Spurgeon, J. M.; Hu, S.; Sharp, I. D.; Brunschwig, B. S.; Lewis, N. S. Improved Stability of Polycrystalline Bismuth Vanadate Photoanodes by Use of Dual-Layer Thin TiO2/Ni Coatings. J. Phys. Chem. C 2014, 118, 19618-19624. (66) Chen, Y. W.; Prange, J. D.; Duhnen, S.; Park, Y.; Gunji, M.; Chidsey, C. E. D.; Mcintyre, P. C. Atomic Layer-Deposited Tunnel Oxide Stabilizes Silicon Photoanodes for Water Oxidation. Nat. Mater. 2011, 10, 539-544. (67) Kim, H. J.; Kearney, K. L.; Le, L. H.; Haber, Z. J.; Rockett, A. A.; Rose, M. J. ChargeTransfer through Ultrathin Film TiO2 on n-Si(111) Photoelectrodes: Experimental and


22

Page 23 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Theoretical Investigation of Electric Field-Enhanced Transport With a Nonaqueous Redox Couple. J. Phys. Chem. C 2016, 120, 25697-25708. (68) Kamimura, J.; Bogdanoff, P.; Lahnemann, J.; Hauswald, C.; Geelhaar, L.; Fiechter, S.; Riechert, H. Photoelectrochemical Properties of (In,Ga)N Nanowires for Water Splitting Investigated by in Situ Electrochemical Mass Spectroscopy. J. Am. Chem. Soc. 2013, 135, 10242-10245. (69) Caccamo, L.; Cocco, G.; Martin, G.; Zhou, H.; Fundling, S.; Gad, A.; Mohajerani, M. S.; Abdelfatah, M.; Estrade, S.; Peiro, F.; et al. Insights into Interfacial Changes and Photoelectrochemical Stability of InxGa1-xN (0001) Photoanode Surfaces in Liquid Environments. ACS Appl. Mater. Inter. 2016, 8, 8232-8238. (70) Moehl T.; Suh J.; Severy L.; Wick-Joliat R.; Tilley S. D. Investigation of (Leaky) ALD TiO2 Protection Layers for Water-Splitting Photoelectrodes. ACS Appl. Mater. Inter. 2017, 9, 43614-43622. (71) Hu, S.; Shaner, M. R.; Beardslee, J. A.; Lichterman, M.; Brunschwig, B. S.; Lewis, N. S., Amorphous TiO2 Coatings Stabilize Si, GaAs, and GaP Photoanodes for Efficient Water Oxidation. Science 2014, 344, 1005-1009. (72) Verlage, E.; Hu, S.; Liu, R.; Jones, R. J. R.; Sun, K.; Xiang, C. X.; Lewis, N. S.; Atwater, H. A., A Monolithically Integrated, Intrinsically Safe, 10% Efficient, SolarDriven Water-Splitting System Based on Active, Stable Earth-Abundant Electrocatalysts in Conjunction with Tandem III-V Light Absorbers Protected by Amorphous TiO2 Films. Energy Environ. Sci. 2015, 8, 3166-3172.


23


Page 24 of 29

(73) Sun, K.; Kuang, Y. J.; Verlage, E.; Brunschwig, B. S.; Tu, C. W.; Lewis, N. S., Sputtered NiOx Films for Stabilization of p+n-InP Photoanodes for Solar-Driven Water Oxidation. Adv. Energy Mater. 2015, 5, 1402276. (74) Chen, L.; Yang, J. H.; Klaus, S.; Lee, L. J.; Woods-Robinson, R.; Ma, J.; Lum, Y.; Cooper, J. K.; Toma, F. M.; Wang, L. W.; et al. p-Type Transparent Conducting Oxide/nType Semiconductor Heterojunctions for Efficient and Stable Solar Water Oxidation. J. Am. Chem. Soc. 2015, 137, 9595-9603. (75) Liu, C.; Dasgupta, N. P.; Yang, P. D. Semiconductor Nanowires for Artificial Photosynthesis. Chem. Mater. 2014, 26, 415-422. (76) Mozharov, A. M.; Bolshakov, A. D.; Kudryashov, D. A.; Kryzhanovskaya, N. V.; Cirlin, G. E.; Mukhin, I. S.; Harmand, J. C.; Tchernysheva, M. Modeling, Synthesis and Study of Highly Efficient Solar Cells Based on III-Nitride Nanowire Arrays Grown on Si Substrates. J. Phys. Conf. Ser. 2015, 643, 012115. (77) Dotan, H.; Sivula, K.; Gratzel, M.; Rothschild, A.; Warren, S. C. Probing the Photoelectrochemical Properties of Hematite (α-Fe2O3) Electrodes Using Hydrogen Peroxide as a Hole Scavenger. Energy Environ. Sci. 2011, 4, 958-964. (78) Abdi, F. F.; Van De Krol, R. Nature and Light Dependence of Bulk Recombination in Co-Pi-Catalyzed BiVO4 Photoanodes. J. Phys. Chem. C 2012, 116, 9398-9404.


24

Page 25 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Figures

Figure 1. The maximum theoretical photocurrent densities of different photoanode materials under AM 1.5G 1-sun illumination. The conduction band (red bar) and valance band (blue bar) positions associated with the water redox potentials are also shown (pH = 0).


25


Page 26 of 29

Figure 2. (a) Photograph, (b) 45°-tilted SEM, and (c) HRTEM images of InGaN nanowire sample. (d) Dark-field TEM image, (e) EDX and (f) HAADF-STEM image of IrO2/InGaN sample.


26

Page 27 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Figure 3. PEC water oxidation performance. (a) Schematic illustration of the three-electrode cell for PEC measurements. InGaN nanowire photoanode, Pt wire and Ag/AgCl were employed as working electrode (WE), counter electrode (CE) and reference electrode (RE), respectively. (b) J-V curves of InGaN and IrO2/InGaN photoanodes in 0.5 M H2SO4 under AM 1.5G simulated 1sun illumination. (c) ABPE of the photoanodes derived from the J-V curves. (d) IPCE of IrO2/InGaN photoanode at 1.23 V versus RHE. (e) J-t curves of InGaN, IrO2/InGaN and TiO2/IrO2/InGaN photoanodes in 0.5 M H2SO4 at 0.8 V versus RHE under AM 1.5G simulated 1-sun illumination.


27


Page 28 of 29

Figure 4. (a) 45o-tilted SEM and (b) TEM images of TiO2/IrO2/InGaN photoanode after PEC stability test for 4 h.


28

Page 29 of 29 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Energy Letters

Figure 5. PEC performance in the presence of H2O2 hole scavenger. a) J-V curves of TiO2/IrO2/InGaN photoanode under AM 1.5G simulated 1-sun illumination in 0.5 M H2SO4 containing 0.5 M H2O2 hole scavenger. The data in 0.5 M H2SO4 without any scavengers is also shown for comparison. The inset illustrates the potentials of H2O, and H2O2 oxidation, indicating H2O2 oxidation are more feasible from the view of both thermodynamic and kinetic. b) J-t curve of TiO2/IrO2/InGaN photoanode at 0.8 V versus RHE under AM 1.5G simulated 1-sun illumination in 0.5 M H2SO4 containing 0.5 M H2O2 hole scavenger. The fluctuation of photocurrent density was ascribed to the formation of O2 bubbles on the photoanode surface.


29