The Role of Structural and Compositional Heterogeneities in the

Apr 13, 2017 - ... were attached with a silver paste before running them in a He refrigerator from 300 to 25 K. The electronic structure was calculate...
2 downloads 0 Views 2MB Size
Article pubs.acs.org/IC

The Role of Structural and Compositional Heterogeneities in the Insulator-to-Metal Transition in Hole-Doped APd3O4 (A = Ca, Sr) Leo K. Lamontagne,†,‡ Geneva Laurita,‡ Michael Knight,‡ Huma Yusuf,‡ Jerry Hu,‡ Ram Seshadri,*,‡,†,¶ and Katharine Page§ †

Materials Department, ‡Materials Research Laboratory, and ¶Department of Chemistry and Biochemistry, University of California, Santa Barbara, California 93106, United States § Chemical and Engineering Materials Division, Spallation Neutron Source, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, United States S Supporting Information *

ABSTRACT: The cubic semiconducting compounds APd3O4 (A = Ca, Sr) can be hole-doped by Na substitution on the A site and driven toward more conducting states. This process has been followed here by a number of experimental techniques to understand the evolution of electronic properties. While an insulator-to-metal transition is observed in Ca1−xNaxPd3O4 for x ≥ 0.15, bulk metallic behavior is not observed for Sr1−xNaxPd3O4 up to x = 0.20. Given the very similar crystal and (calculated) electronic structures of the two materials, the distinct behavior is a matter of interest. We present evidence of local disorder in the A = Sr materials through the analysis of the neutron pair distribution function, which is potentially at the heart of the distinct behavior. Solid-state 23Na nuclear magnetic resonance studies additionally suggest a percolative insulator-to-metal transition mechanism, wherein presumably small regions with a signal resembling metallic NaPd3O4 form almost immediately upon Na substitution, and this signal grows monotonically with substitution. Some signatures of increased local disorder and a propensity for Na clustering are seen in the A = Sr compounds.



INTRODUCTION The study of insulator-to-metal transitions is an important topic in the fields of materials chemistry and condensed-matter physics. The profound change in properties associated with the transition are of great fundamental interest, even at the level of separating the elements into metals and nonmetals.1 In addition, a huge range of useful materials functionalities are often found associated with materials that display such transitions.2,3 In particular, understanding compositionally driven insulator-to-metal transitions in which carriers are doped into a material can lead to tuned carrier concentrations for optimal electrical properties in thermoelectric materials4 or elevated Tc in superconductors.5 An important question regarding the nature of the transition driven by charge carrier doping into semiconducting or insulating hosts is whether the transition is percolative (in the sense of forming as puddles of metal in the insulating background that coalesce at some concentration and drive the entire system metallic), or whether it occurs suddenly across the entirety of the material. Percolation of metallic regions is believed to lead to the colossal magnetoresistance observed in LaMnO3,6−8 and it leads to interesting magnetic and electronic properties in Srsubstituted La1−xSrxCoO3.9−12 While the change in carrier concentration can be estimated based on the amount of doping, there are other considerations that can affect the onset of an © 2017 American Chemical Society

insulator-to-metal transition. The size of the dopant ion relative to the crystallographic site, as well as complementary changes in valence to maintain neutrality, can impart local distortions that can also affect an insulator-to-metal transition.13 Many complex palladium oxides have been previously shown to undergo compositional insulator-to-metal transitions.14−18 The small bandgaps and significant Pd d states just below the Fermi level in complex palladium oxides allows for the ease of hole-doping. Previous studies have suggested that some palladium oxides may have unique gapless electronic structures that can lead to interesting physics,19,20 though these results may be influenced by the tendency of some density functional theory (DFT) functionals to underestimate bandgaps in small bandgap semiconductors.21 Furthermore, complex palladium oxides are typically diamagnetic, allowing for more detailed studies of local structural changes throughout insulator-to-metal transitions with the use of solid-state NMR, which, while useful in examining local phase separation, is difficult to utilize in magnetic oxide materials.22,23 Recently, we observed a high Seebeck coefficient with metallic conductivity in the complex palladium oxide PbPdO2 when it undergoes an insulator-tometal transition with Li substitution.24 A better understanding Received: February 3, 2017 Published: April 13, 2017 5158

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry

distribution function suggest disorder as a barrier to bulk metallicity in SrPd3O4.

of the insulator-to-metal transitions can lead to improvements in the functional properties of these and other oxide materials. CaPd3O4 and SrPd3O4 both crystallize in the cubic NaPt3O4 structure type, highlighted in Figure 1. The alkaline-earth cation



Polycrystalline samples of A1−xNaxPd3O4 (A = Ca, Sr), 0 ≤ x ≤ 0.2, were prepared by heating stoichiometric amounts of CaCO3, SrCO3, PdO, and Na2CO3 powders. The precursors were ground in an agate mortar and pestle and pressed into a pellet at 100 MPa. The pellets were placed onto beds of powder of the same composition to prevent contamination from the alumina crucible. The samples were heated at 600 °C for 12 h in a flowing O2 tube furnace. This procedure was repeated twice to ensure a complete reaction of the precursors. The end-member NaPd3O4 was prepared in a similar manner at 700 °C. The crystal structures were characterized by X-ray powder diffraction on a Panalytical Empyrean powder diffractometer with Cu Kα radiation. Lattice parameters were determined by mixing the prepared materials with a silicon standard and recording from 10°2θ to 120°2θ. The x = 0.05 and x = 0.20 samples were additionally studied through synchrotron X-ray diffraction at the 11-BM beamline at the Advanced Photon Source at Argonne National Laboratory with wavelength λ = 0.414 159 Å. Rietveld27 refinement was performed using the TOPAS academic software.28 Crystal structures were visualized using VESTA.29 Neutron scattering data for pair distribution function (PDF) analysis was collected at the NOMAD diffractometer30 at the Spallation Neutron Source, Oak Ridge National Laboratory. Least-squares refinement of the reduced PDF was performed using the PDFgui program.31 Single pulse 23Na solid-state magic-angle spinning (MAS) NMR experiments were performed at 300 K on a Bruker ASCEND III HD 400 MHz (9.4 T) spectrometer. Samples were packed into a 4 mm zirconia rotor with Kel-F caps and spun at a rate of 8 kHz. The single pulse experiment used a pulse length of 0.83 μs corresponding to a π/12 tip angle. The 23Na shifts were referenced to 1 M NaCl. For electrical resistivity measurements, the materials were sintered as bar pellets ∼9 mm in length, and four copper wires were attached with a silver paste before running them in a He refrigerator from 300 to 25 K. The electronic structure was calculated using DFT as implemented in the Vienna ab initio Simulation Package (VASP)32,33 with projector-augmented wave (PAW) pseudopotentials.34 For structure optimization, the exchange-correlation was described by Perdew−Burke−Ernzerhof within the generalized gradient approximation (GGA-PBE)35 using a Γ center k-mesh of 8 × 8 × 8 and a tetrahedron smearing method. A screened hybrid functional (HSE06)36 was used to calculate the density of states (DOS).

Figure 1. Crystal structure of APd3O4 (A = Ca, Sr) in cubic Pm3n (No. 74). Ca/Sr, Pd, and O are colored silver, blue, and orange, respectively. The PdO4 square planes in APd3O4 exhibit threedimensional corner connectivity. The alkaline-earth element sits in a symmetric, eight-coordinate, cubic site. The Wyckoff positions are A in 2a (0, 0, 0,); Pd in 6c ( 1 , 0, 1 ); and O in 8e ( 1 , 1 , 1 ). 4

2

4

4

EXPERIMENTAL AND COMPUTATIONAL METHODS

4

resides in an eight-coordinate cubic site, while the d8 palladium is in its preferred square-planar coordination. The palladium square planes are corner-connected and form a 3d network throughout the crystal.25 Given the identical crystal structures, one would expect that a compositionally driven insulator-tometal transition in both CaPd3O4 and SrPd3O4 would occur around the same dopant level assuming the electronic structures were also similar. However, insulator-to-metal transitions in these compounds have been reported to occur under a wide range of hole-dopant levels. Ichikawa and coworkers reported a transition in CaPd3O4 of ∼10 mol % Li doping onto the Ca site.16 However, when Na was used as a dopant, Itoh, Yano, and Tsuda reported 30 mol % was necessary to drive the transition and remarked how processing can affect the observed electronic properties.17,26 In the system Sr1−xNaxPd3O4, Taniguchi and co-workers reported a transition around 10 mol % Na.18 To better understand the nature of the insulator-to-metal transitions in these compounds and account for the reported differences, we prepared and processed Ca1−xNaxPd3O4 and Sr1−xNaxPd3O4 with 0 ≤ x ≤ 0.2 under identical conditions. The metallic end-member compound NaPd3O4 was also prepared and studied as a reference. We find that, while the electronic structures of CaPd3O4 and SrPd3O4 are nearly identical, CaPd3O4 is driven metallic above 10 mol % Na substitution, while SrPd3O4 remains a semiconductor with a negative dρ/dT (slope of resistivity as a function of temperature) up to 20 mol % Na substitution. X-ray diffraction studies suggest Na clustering or a distribution gradient in both compounds at high doping levels and, along with solid-state 23 Na NMR, suggest a percolative insulator-to-metal transition in CaPd3O4. However, increased local disorder observed in both NMR and analysis of total scattering data using the pair



RESULTS AND DISCUSSION Average Structure from Diffraction. Polycrystalline samples of APd3O4 (A = Ca, Sr) were prepared phase-pure with up to 20 mol % Na substitution onto the A site. The reactions were done in a flowing O2 atmosphere at 600 °C to prevent the reduction of the PdO to Pd metal. Rietveld refinements of synchrotron XRD data confirmed the phase purity, shown in Figure 2 for the highest Na substitution levels. The lattice parameters for the samples were determined through Rietveld refinement of laboratory Cu Kα radiation with a Si standard. The lattice parameters for both the Ca and Sr materials generally decrease with increasing Na doping, as shown in Figure 3. The lattice parameter for CaPd3O4 decreases from 5.743 to 5.740 Å, and the lattice parameter of SrPd3O4 decreases by an identical amount, from 5.823 to 5.820 Å. This is surprising, as the ionic radii of Na1+ in an eightcoordinate site (1.18 Å) is slightly larger than Ca2+ (1.12 Å) and smaller than Sr2+ (1.26 Å).37 This suggests that the decreasing lattice parameter does not primarily arise from the size difference of the dopant ion but by the necessary oxidation 5159

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry

transition occurs beyond 10% Na doping (Figure 4) as seen through the positive dρ/dT for the x = 0.15 and x = 0.20

Figure 2. Single-phase refinements of nominal (a) Ca0.8Na0.2Pd3O4 and (b) Sr0.8Na0.2Pd3O4 from synchrotron X-ray data. Figure 4. Resistivities of APd3O4 (A = Ca, Sr) with Na doping. CaPd3O4 undergoes an insulator-to-metal transition above x = 0.10 as seen through the decrease in resistivity with temperature at these levels. Despite similar room-temperature resistivity values, SrPd3O4 does not undergo an insulator-to-metal transition even up to x = 0.20.

compositions, similar to the substitution amount Ichikawa and co-workers reported upon Li doping in CaPd3O4.16 Unsubstituted SrPd3O4 exhibits a room-temperature resistivity almost identical to that of CaPd3O4. However, even up to x = 0.20, the material remains semiconducting with a negative dρ/dT, though the resistivity values are nearly identical to those reported by Taniguchi and co-workers.18 This result is surprising, as both materials were prepared and processed identically and, from the lattice parameter changes, appear to be incorporating the Na dopants up to 20 mol %. To explore the differing electronic behavior in these compounds, DFT calculations were performed to investigate any differences in the electronic structure. The DOS for both of the pristine materials are shown in Figure 5. It is important to note that the DOS calculations were performed using a hybrid functional to obtain a more accurate band gap value. The HSE calculations predict very small, nearly identical bandgaps of 0.25 eV for CaPd3O4 and 0.22 eV for SrPd3O4. Both compounds

Figure 3. Changes in lattice parameters for (a) Ca1−xNaxPd3O4 and (b) Sr 1−xNax Pd 3O 4 with Na substitution. Stoichiometric Na substitution levels and lattice parameters refined on a laboratory Cu Kα diffractometer with a Si standard. Refined Na occupancy values and lattice parameters from synchrotron X-ray diffraction data for the nominal x = 0.05 and x = 0.20 substitution levels. The refined Na occupancy value and lattice parameter using neutron diffraction data.

of the Pd2+ to Pd3+ to maintain charge neutrality. The slight increase in the lattice parameter with small Na substitution in CaPd3O4 may be attributed to the larger ionic size of the Na1+ ion dominating at smaller substitution levels. Refined Na occupancy values and lattice parameters from the synchrotron X-ray data are shown in Figure 3. For the nominal x = 0.05 substitution level, the refined Na occupancies are in good agreement with expectations. Peak tails, which are only seen in the high-resolution synchrotron X-ray diffraction data for the x = 0.20 materials, lead to an underestimation of the Na occupancy and a slight discrepancy in the refined lattice parameters, the details of which will be discussed presently. Refined values from neutron time-of-flight (TOF) diffraction data are used in Figure 3 for the x = 0.20 Sr sample, as the significant peak tails in the X-ray data prevented reliable refinements. Electrical Properties and Electronic Structure. To study the insulator-to-metal transitions in these materials, the electrical resistivity was measured with successive doping. Pristine CaPd3O4 displays semiconducting behavior with a room-temperature resistivity of 0.1 Ω cm. An insulator-to-metal

Figure 5. DOS calculated using a hybrid functional for (a) CaPd3O4 and (b) SrPd3O4. The calculated bandgaps are 0.25 and 0.22 eV, respectively. 5160

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry show significant Pd d states just below the Fermi level. The DOS for both compounds possess similar features both below and above the Fermi level, and the band structures for both compounds are almost indistinguishable near the Fermi level. The extreme similarities in the electronic structures of these compounds imply that the differences in the onset of the insulator-to-metal transition are not due to any fundamental differences in the physics of the materials but may be due to deviations in the local structure imparted through hole-doping. Deviations from Average Structure: Structural Heterogeneities. Close inspection of the synchrotron diffraction data reveals that the nominal Ca 0.80 Na 0.20 Pd 3 O 4 and Sr0.80Na0.20Pd3O4 samples have peak tails to higher Q on all Bragg peaks, highlighted in the (enlarged) difference curves presented in Figure 6. The tails are more pronounced in

Figure 7. Fits of the primary (021) reflections of nominal Sr0.80Na0.20Pd3O4 using (a) an Na-gradient model and (b) a twophase Na-cluster model result in a similar quality fit.

occupancy. While both models are able to capture the peak tails, there is no substantial difference between the two, and the nature of the Na substitution is still unclear from analysis of the diffraction data. The peak tails in synchrotron X-ray diffraction data of the highly substituted samples prompt a close study of the local structure in these materials to both explore the nature of the insulator-to-metal transition and to explain differences in the observed electronic properties. Neutron PDF data were utilized to investigate local deviations from the average crystallographic structure. Least-squares fits of the PDFs are shown in Figure 8. The data were fit against the crystallographic structure with nominal site occupancies over a fit range from 1.5 to 5 Å. The results of the fits are given in Table 1. When the resulting fits against the average models are compared, relative degrees of local disorder can be ascertained. As demonstrated by the goodness-of-fit parameters Rw (Table 1), the 5% substituted CaPd3O4 and SrPd3O4 are locally fit well with the average structure. Interestingly, the 20% substituted SrPd3O4 results in a poorer fit to the average model than the

Figure 6. Diffraction patterns and Rietveld fits for the 5% Nasubstituted (a) CaPd3O4 and (b) SrPd3O4 and (c, d) 20% Nasubstituted materials. While the 5% substituted compounds have symmetric peak shapes, the peaks of the 20% Na-substituted compounds have a tail to higher Q. This is clearly evident in the difference curves (enlarged for clarity), which possess a broad feature after every peak.

Sr0.80Na0.20Pd3O4. For both the Ca and Sr compounds substituted with only 5 mol % Na, the peaks appear symmetric, and the difference curves do not reveal any features. The tails in the highly substituted samples suggest a deviation from the average crystallographic structure. This may be attributed to either a gradient or clustering of the Na dopants as the dopant concentration increases, as a uniform distribution of dopant ions should produce symmetric peaks with a corresponding shift in the lattice parameters. Two different models were applied to better capture the peak tails in the 20% substituted samples. To simulate a concentration gradient of Na dopants across the material, a model was created with eight Pm3n phases with the lattice parameter and Na occupancy shifted by a constant amount between each phase. To simulate Na clustering, the second model was constructed of two phases where the Na concentration, lattice parameter, and size/strain contributions to the peak shapes were allowed to refine independently. These methods have been used in many material systems to examine phase separation and structural heterogeneity.38,39 Figure 7 illustrates the fit of each model to the main reflection (021) of Sr0.80Na0.20Pd3O4. The total Na occupancy was not fixed in either of the models and refined to between 12% and 16% total

Figure 8. PDF fits against the crystallographic structures. Both of the lightly Na-substituted (x = 0.05) samples (a, c) and the highly Nasubstituted (x = 0.20) CaPd3O4 (b, d) are well-fit with the average structure. The highly Na-substituted SrPd3O4 is comparatively more poorly fit, indicating that the local environment is more disordered. 5161

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry Table 1. Results of Fits of the Neutron PDF Data against the Pm3n Models for A1−xNaxPd3O4 with x = 0.05 and 0.20 and A = Ca and Sr A = Ca a (Å) A/Na Uiso (Å2) Pd Uiso (Å2) O Uiso (Å2) Rw (%)

A = Sr

x = 0.05

x = 0.20

x = 0.05

x = 0.20

5.759(4) 0.0078(18) 0.0042(6) 0.0070(8) 12.7

5.748(3) 0.0077(15) 0.0034(4) 0.0064(6) 11.0

5.829(3) 0.0040(7) 0.0034(4) 0.0055(5) 9.0

5.821(3) 0.0028(7) 0.0044(4) 0.0058(6) 17.7

20% substituted CaPd3O4, evidenced by a large increase in the resulting Rw value. This is indicative of a more locally disordered structure, and by examining the features of the PDF that are not being captured by the average model, the nature of the distortion may be qualitatively inferred. A significant peak shoulder occurring around 3 Å is present only in the highest substituted SrPd3O4. This correlation distance corresponds to the Pd−Pd and O−O interactions of proximal Pd square-planar units. Thus, slight distortions of the Pd square-planar network around Na dopants may be present, which is reasonable given the greater size difference between the Sr2+ and Na1+ ions. In addition to local distortions, any potential Na clustering may result in poorer fits to the local structure. A two-phase fit including the possibility of a Na2CO3 impurity was attempted, as some amount of Na2CO3 was observed in solid-state 23Na NMR (see next section), though it did not improve the fit or capture the observed peak shoulder. Deviations from Average Structure: Compositional Heterogeneities. In addition to PDF, solid-state 23Na NMR was conducted to study the resolved local environment of the Na dopants in these materials. 23Na is a spin 3/2 quadrupolar nucleus in 100% abundance, making it an attractive nucleus to study in the materials before and after an insulator-to-metal transition as well as to examine differences between the Ca and Sr compounds. As a reference, we prepared metallic NaPd3O4, which possesses the same structure as CaPd3O4 and SrPd3O4 and can be thought of as a Na substitution level of x = 1.00. The structure of NaPd3O4 has been reported previously,40,41 and reported electric properties are in agreement with our measurements.17,26 A higher preparation temperature than was used for Na substitution in CaPd3O4 and SrPd3O4 was needed for phase purity. The different panels of Figure 9 summarize the results on this interesting metallic oxide. Figure 9a displays a Rietveld refinement of X-ray diffraction data of NaPd3O4 displaying a single cubic phase with a = 5.638 Å. Figure 9b displays a dominant peak observed at −6 ppm, as is expected due to the single Na site in the structure. This peak is narrow due to the symmetric environment of the crystallographic site, despite the quadrupolar nature of the 23Na nucleus. A small amount of a potential impurity marked by * in Figure 9 may also be present. Note that despite the metallic nature of the sample, established from the resistivity versus temperature data shown in Figure 9c, that the peak is not strongly Knight-shifted by the conduction electrons.42 The 23Na Knight shift can vary widely in magnitude and direction between various types of Nasubstituted compounds,43−45 but it is generally expected to be small in a system like NaPd3O4, where the conduction states are derived from other atoms, namely, Pd. Figure 10 shows MAS spectra of various Na substitution levels in CaPd3O4 and SrPd3O4. All of the spectra display two distinct Na environments, which is surprising, as the Na

Figure 9. Results on the pure end-member (x = 1) compound NaPd3O4. (a) X-ray diffraction Rietveld refinement showing the phasepure nature of this composition. (b) 23Na solid-state single-pulse MAS NMR spectra (9.4 T, MAS at 8 kHz) showing a principle single peak corresponding to the single site in the crystal structure with a potential minor impurity on the right edge of the peak marked by (*). (c) Resistivity vs temperature for a pressed pellet of NaPd3O3 showing the highly metallic nature of this hole-doped oxide.

Figure 10. Single-pulse solid-state 23Na MAS NMR spectra (9.4 T, MAS at 8 kHz) of Na-substituted CaPd3O4 and SrPd3O4. All of the Ca and Sr samples show two distinct Na environments represented by a sharp peak at 7 ppm and a broad signal centered around −10 ppm, which grows relative to the sharp peak with increasing Na substitution. Metallic NaPd3O4 (x = 1.00) shows a single sharp peak at −6 ppm. The asterisk represents a small amount of Na2CO3 precursor.

substitutes onto only one crystallographic site in these materials. A sharp peak centered at 7 ppm and a broad peak around −10 ppm are present at all levels of Na substitution in both series. The broad peak grows in intensity relative to the sharp peak with increasing Na substitution. A small amount of Na2CO3 was detected in the SrPd3O4 samples, denoted with a star in Figure 10. On the basis of the peak shape and chemical shift of the NaPd3O4 spectrum, we conclude the sharp peaks in the Ca and Sr compounds arise from Na in an undistorted environment, that is, an isolated Na in the APd3O4 matrix. The insulating Ca/Sr matrix surrounding the isolated Na explains 5162

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry the differing chemical shifts in regard to the pure Na compound. The broad signal(s) appear at chemical shifts similar to the sharp peak of NaPd3O4, and thus we propose the origin of the broad peaks as arising from Na in metallic, Na-rich environments. The broadness may arise from a distribution in chemical shifts due to a distribution of the number of proximal Na atoms and/or a distorted Na coordination environment, leading to quadrupolar effects. In SrPd3O4, this peak is broader and more asymmetric in nature, further supporting a higher degree of disorder in comparison to the Ca sample at the same Na substitution level. Additionally, SrPd3O4 clearly shows a greater tendency for a clustering of the Na dopants at x = 0.15, as the broad peak begins to coalesce toward the NaPd3O4 (x = 1.00) peak. The CaPd3O4 samples do not show as clear a clustering at the Na substitution levels studied through NMR. The greater ionic size difference of Na and Sr most likely leads to the increased propensity for Na clustering. For both samples, the relative intensity of the broad peak grows with increasing Na concentration, suggesting a percolative insulator-to-metal transition mechanism. Even at small Na substitution levels, there is evidence of metallic domains most likely arising from Na atoms in nearby proximity. However, the local disorder present in the Sr compounds limits the domain growth, thus preventing bulk metallicity. 23 Na NMR evidence suggests the formation of what appear to be metallic regions immediately upon Na substitution, despite bulk electrical transport suggesting that the samples remain in the insulating regime. This points to metallic and insulating regions in the sample that are phase-separated. This phenomena is well-known in alkali-metal liquid NH3 solutions, where the phase separation between more metallic, high alkalicontent liquid from the insulating, less-concentrated liquid can be physically observed and has also been followed by NMR.46 The phenomena of such microscopic phase separation was predicted by Mott,47 who pointed out that the insulator and the metal must lie in separate minima of the free energy characteristic of first-order phase transitions. Similar local heterogeneity has been observed in Li NMR of 7 Lideintercalated LiCoO248 and in a study of Li-ordering in Li1−xSn2+xAs2.49 In conclusion, Na has been substituted into both CaPd3O4 and SrPd3O4 under identical conditions, and subtle differences in the local structure of these materials have been studied. Despite identical crystal and electronic structures, CaPd3O4 is more easily driven metallic with hole doping through Na substitution. Neutron pair distribution function data reveal SrPd3O4 is more locally disordered with high Na substitution. 23 Na NMR reveals an apparent percolative insulator-to-metal transition mechanism, as metallic domains in the materials grow with increasing Na substitution. Increased disorder and a tendency for the Na to cluster when substituted into SrPd3O4 are believed to act against metallicity by limiting metallic domain growth. This work highlights the need for detailed local probes to elucidate differences in observed material properties that are not easily explained by average structure techniques such as diffraction.





CIF files obtained from single-phase Rietveld refinement of synchrotron X-ray diffraction data of the nominal Ca0.80Na0.20Pd3O4 and Sr0.80Na0.20Pd3O4 compounds. As discussed in the main text, significant peak tails, particularly in the Sr sample, result in an underestimation of the Na occupancy (CIF) X-ray data (CIF)

AUTHOR INFORMATION

Corresponding Author

*E-mail: [email protected]. ORCID

Geneva Laurita: 0000-0001-9577-150X Ram Seshadri: 0000-0001-5858-4027 Katharine Page: 0000-0002-9071-3383 Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS This work was supported by the National Science Foundation (NSF) through DMR-1403862. Helpful discussions with R. Clément and R. Sangodkar are gratefully acknowledged. This manuscript has been coauthored by UT-Battelle, LLC under Contract No. DE-AC05-00OR22725 with the U.S. Department of Energy (DOE). The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy. gov/downloads/doe-public-access-plan). The computational studies reported here made use of facilities supported by the Center for Scientific Computing at UCSB, supported by NSF MRSEC (DMR-1121053) and NSF CNS-0960316 and Hewlett-Packard. The Materials Research Laboratory is a member of the NSF-supported Materials Research Facilities Network. Use of the Advanced Photon Source at Argonne National Laboratory was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357. The use of the NOMAD instrument used resources at the Spallation Neutron Source, a DOE Office of Science User Facility operated by the Oak Ridge National Laboratory.



REFERENCES

(1) Hensel, F.; Slocombe, D. R.; Edwards, P. P. On the Occurrence of Metallic Character in the Periodic Table of the Chemical Elements. Philos. Trans. R. Soc., A 2015, 373, 20140477. (2) Imada, M.; Fujimori, A.; Tokura, Y. Metal-Insulator Transitions. Rev. Mod. Phys. 1998, 70, 1039−1263. (3) Yang, Z.; Ko, C.; Ramanathan, S. Oxide Electronics Utilizing Ultrafast Metal-Insulator Transitions. Annu. Rev. Mater. Res. 2011, 41, 337−367. (4) Snyder, G. J.; Toberer, E. S. Complex Thermoelectric Materials. Nat. Mater. 2008, 7, 105−114. (5) Chu, C. W.; Deng, L. Z.; Lv, B. Hole-Doped Cuprate High Temperature Superconductors. Phys. C 2015, 514, 290−313. (6) Fäth, M.; Freisem, S.; Menovsky, A. A.; Tomioka, Y.; Aarts, J.; Mydosh, J. A. Spatially Inhomogeneous Metal-Insulator Transition in Doped Manganites. Science 1999, 285, 1540−1542. (7) Dagotto, E.; Hotta, T.; Moreo, A. Colossal Magnetoresistant Materials: The Key Role of Phase Separation. Phys. Rep. 2001, 344, 1− 153. (8) Baldini, M.; Muramatsu, T.; Sherafati, M.; Mao, H.-k.; Malavasi, L.; Postorino, P.; Satpathy, S.; Struzhkin, V. V. Origin of Colossal

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acs.inorgchem.7b00307. 5163

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164

Article

Inorganic Chemistry Magnetoresistance in LaMnO3 Manganite. Proc. Natl. Acad. Sci. U. S. A. 2015, 112, 10869−10872. (9) Raccah, P. M.; Goodenough, J. B. A Localized Electron to Collective Electron Transition in the System (La,Sr)CoO3. J. Appl. Phys. 1968, 39, 1209. (10) Wu, J.; Leighton, C. Glassy Ferromagnetism and Magnetic Phase Separation in La1−xSrxCoO3. Phys. Rev. B: Condens. Matter Mater. Phys. 2003, 67, 174408. (11) Phelan, D.; Louca, D.; Kamazawa, K.; Lee, S.-H.; Ancona, S. N.; Rosenkranz, S.; Motome, Y.; Hundley, M. F.; Mitchell, J. F.; Moritomo, Y. Spin Incommensurability and Two Phase Competition in Cobaltites. Phys. Rev. Lett. 2006, 97, 235501. (12) He, C.; El-Khatib, S.; Eisenberg, S.; Manno, M.; Lynn, J. W.; Zheng, H.; Mitchell, J. F.; Leighton, C. Transport Signatures of Percolation and Electronic Phase Homogeneity in La1−xSrxCoO3 Single Crystals. Appl. Phys. Lett. 2009, 95, 222511. (13) Page, K.; Kolodiazhnyi, T.; Proffen, T.; Cheetham, A. K.; Seshadri, R. Local Structural Origins of the Distinct Electronic Properties of Nb-Substituted SrTiO3 and BaTiO3. Phys. Rev. Lett. 2008, 101, 205502. (14) Uriu, R.; Shimada, D.; Tsuda, N. Metal to Insulator Transition in Pd1−xLixO. J. Phys. Soc. Jpn. 1991, 60, 2479−2480. (15) Ozawa, T. C.; Taniguchi, T.; Nagata, Y.; Noro, Y.; Naka, T.; Matsushita, A. Metal-Insulator Transition and Large Thermoelectric Power of a Layered Palladium Oxide: PbPdO2. J. Alloys Compd. 2005, 388, 1−5. (16) Ichikawa, S.; Terasaki, I. Metal-Insulator Transition in Ca1−xLixPd3O4. Phys. Rev. B: Condens. Matter Mater. Phys. 2003, 68, 233101. (17) Itoh, K.; Tsuda, N. Metal to Semiconductor Like Transition for Sintered Ca1−xNaxPd3O4. Solid State Commun. 1999, 109, 715−719. (18) Taniguchi, T.; Nagata, Y.; Ozawa, T. C.; Sato, M.; Noro, Y.; Uchida, T.; Samata, H. Insulator-Metal Transition Induced in Sr1−xNaxPd3O4 for Small Na-Substitutions. J. Alloys Compd. 2004, 373, 67−72. (19) Wang, X. L. Proposal for a New Class of Materials: Spin Gapless Semiconductors. Phys. Rev. Lett. 2008, 100, 156404. (20) Hase, I.; Nishihara, Y. CaPd3O4 as an Excitonic Insulator. Phys. Rev. B: Condens. Matter Mater. Phys. 2000, 62, 13426−13429. (21) Kurzman, J. A.; Miao, M.-S.; Seshadri, R. Hybrid Functional Electronic Structure of PbPdO2, a Small-Gap Semiconductor. J. Phys.: Condens. Matter 2011, 23, 465501. (22) Savosta, M. M.; Novák, P. Two-Phase Character of Metallic Ferromagnetism in Manganites. Phys. Rev. Lett. 2001, 87, 137204. (23) Kuhns, P. L.; Hoch, M. J. R.; Moulton, W. G.; Reyes, A. P.; Wu, J.; Leighton, C. Magnetic Phase Separation in La1−xSrxCoO3 by 59Co Nuclear Magnetic Resonance. Phys. Rev. Lett. 2003, 91, 127202. (24) Lamontagne, L. K.; Laurita, G.; Gaultois, M. W.; Knight, M.; Ghadbeigi, L.; Sparks, T. D.; Gruner, M. E.; Pentcheva, R.; Brown, C. M.; Seshadri, R. High Thermopower with Metallic Conductivity in pType Li-Substituted PbPdO2. Chem. Mater. 2016, 28, 3367−3373. (25) Muller, O.; Roy, R. Synthesis and Crystal Chemistry of Some New Complex Palladium Oxides. Adv. Chem. Ser. 1971, 3, 28−38. (26) Itoh, K.; Yano, Y.; Tsuda, N. Metal to Insulator Transition for Ca1−xNaxPd3O4. J. Phys. Soc. Jpn. 1999, 68, 3022−3026. (27) Rietveld, H. M. A Profile Refinement Method for Nuclear and Magnetic Structures. J. Appl. Crystallogr. 1969, 2, 65−71. (28) Coelho, A. A.; Evans, J.; Evans, I.; Kern, A.; Parsons, S. The TOPAS Symbolic Computation System. Powder Diffr. 2011, 26, S22− S25. (29) VESTA: a Three-Dimensional Visualization System for Electronic and Structural Analysis. J. Appl. Crystallogr. 2008, 41, 653−658. (30) Neuefeind, J.; Feygenson, M.; Carruth, J.; Hoffmann, R.; Chipley, K. K. The Nanoscale Ordered MAterials Diffractometer NOMAD at the Spallation Neutron Source SNS. Nucl. Instrum. Methods Phys. Res., Sect. B 2012, 287, 68−75. (31) Farrow, C. L.; Juhas, P.; Liu, J. W.; Bryndin, D.; Božin, E. S.; Bloch, J.; Proffen, T.; Billinge, S. J. L. PDFfit2 and PDFgui: Computer

Programs for Studying Nanostructure in Crystals. J. Phys.: Condens. Matter 2007, 19, 335219. (32) Kresse, G.; Furthmüller, J. Efficiency of Ab-Initio Total Energy Calculations for Metals and Semiconductors Using a Plane-Wave Basis Set. Comput. Mater. Sci. 1996, 6, 15−50. (33) Kresse, G.; Marsman, M.; Furthmüller, J. Vienna Ab-Initio Simulation Package: VASP the GUIDE; University of Wien: Austria, 2012. (34) Kresse, G.; Joubert, D. From Ultrasoft Pseudopotentials to the Projector Augmented-Wave Method. Phys. Rev. B: Condens. Matter Mater. Phys. 1999, 59, 1758−1775. (35) Perdew, J. P.; Burke, K.; Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 1996, 77, 3865−3868. (36) Heyd, J.; Scuseria, G. E.; Ernzerhof, M. Hybrid Functionals Based on a Screened Coulomb Potential. J. Chem. Phys. 2003, 118, 8207. (37) Shannon, R. D. Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides. Acta Crystallogr., Sect. A: Cryst. Phys., Diffr., Theor. Gen. Crystallogr. 1976, 32, 751−767. (38) Kaveh, S.; Tremblay, C. P.; Norhashim, N.; Curry, R. J.; Cheetham, A. K. Phase Separation in Garnet Solid Solutions and its Effect on Optical Properties. Adv. Mater. 2013, 25, 6448−6452. (39) Douglas, J. E.; Chater, P. A.; Brown, C. M.; Pollock, T. M.; Seshadri, R. Nanoscale Structural Heterogeneity in Ni-Rich HalfHeusler TiNiSn. J. Appl. Phys. 2014, 116, 163514. (40) Scheer, J. J.; Arkel, A. E. V.; Heyding, R. D. Oxide Complexes Formed in the Systems Platinum Metals: Alkali Carbonates: Oxygen. Can. J. Chem. 1955, 33, 683−686. (41) Panin, R. V.; Khasanova, N. R.; Abakumov, A. M.; Antipov, E. V.; van Tendeloo, G.; Schnelle, W. Synthesis and Crystal Structure of the Palladium Oxides NaPd3O4, Na2PdO3 and K3Pd2O4. J. Solid State Chem. 2007, 180, 1566−1574. (42) Knight, W. D. Nuclear Magnetic Resonance Shift in Metals. Phys. Rev. 1949, 76, 1259−1260. (43) Tunstall, D. P.; Ramage, W. A High-Pressure NMR Study of Sodium Tungsten Bronze: NaxWO3. J. Phys. C: Solid State Phys. 1980, 13, 725. (44) Riccó, M.; Fumera, G.; Shiroka, T.; Ligabue, O.; Bucci, C.; Bolzoni, F. Metal-to-Insulator Evolution in (NH3)xNaK2C60: An NMR study. Phys. Rev. B: Condens. Matter Mater. Phys. 2003, 68, 35102. (45) Ramachandran, G. K.; Dong, J.; Sankey, O. F.; McMillan, P. F. 23 Na and 29Si NMR Knight Shifts in the Silicon Clathrate Na16Cs8Si136. Phys. Rev. B: Condens. Matter Mater. Phys. 2000, 63, 33102. (46) Lodge, M. T. J. H.; Cullen, P.; Rees, N. H.; Spencer, N.; Maeda, K.; Harmer, J. R.; Jones, M. O.; Edwards, P. P. Multielement NMR Studies of the Liquid−Liquid Phase Separation and the Metal-toNonmetal Transition in Fluid Lithium−and Sodium−Ammonia Solutions. J. Phys. Chem. B 2013, 117, 13322−13334. (47) Mott, N. F. The Transition to the Metallic State. Philos. Mag. 1961, 6, 287−309. (48) Ménétrier, M.; Saadoune, I.; Levasseur, S.; Delmas, C. The Insulator-Metal Transition Upon Lithium Deintercalation from LiCoO2: Electronic Properties and 7Li NMR Study. J. Mater. Chem. 1999, 9, 1135−1140. (49) Lee, K.; Kaseman, D.; Sen, S.; Hung, I.; Gan, Z.; Gerke, B.; Pöttgen, R.; Feygenson, M.; Neuefeind, J.; Lebedev, O. I.; Kovnir, K. Intricate Short-Range Ordering and Strongly Anisotropic Transport Properties of Li1−xSn2+xAs2. J. Am. Chem. Soc. 2015, 137, 3622−3630.

5164

DOI: 10.1021/acs.inorgchem.7b00307 Inorg. Chem. 2017, 56, 5158−5164