Triboelectric Nanogenerator for Harvesting Wind Energy and as Self

Sep 17, 2013 - We report a triboelectric nanogenerator (TENG) that plays dual roles as a sustainable power source by harvesting wind energy and as a s...
0 downloads 9 Views 1MB Size
Ya Yang,†,§ Guang Zhu,†,§ Hulin Zhang,† Jun Chen,† Xiandai Zhong,‡ Zong-Hong Lin,† Yuanjie Su,† Peng Bai,† Xiaonan Wen,† and Zhong Lin Wang†,‡,*

ARTICLE

Triboelectric Nanogenerator for Harvesting Wind Energy and as SelfPowered Wind Vector Sensor System †

School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332-0245, United States and ‡Beijing Institute of Nanoenergy and Nanosystems, Chinese Academy of Sciences, Beijing 100085, China. §Y. Yang and G. Zhu contributed equally to the work.

ABSTRACT We report a triboelectric nanogenerator (TENG) that plays dual roles as a sustainable power

source by harvesting wind energy and as a self-powered wind vector sensor system for wind speed and direction detection. By utilizing the wind-induced resonance vibration of a fluorinated ethylene propylene film between two aluminum foils, the integrated TENGs with dimensions of 2.5 cm  2.5 cm  22 cm deliver an output voltage up to 100 V, an output current of 1.6 μA, and a corresponding output power of 0.16 mW under an external load of 100 MΩ, which can be used to directly light up tens of commercial light-emitting diodes. Furthermore, a self-powered wind vector sensor system has been developed based on the rationally designed TENGs, which is capable of detecting the wind direction and speed with a sensitivity of 0.09 μA/(m/ s). This work greatly expands the applicability of TENGs as power sources for self-sustained electronics and also self-powered sensor systems for ambient wind detection. KEYWORDS: triboelectric nanogenerator . wind energy . self-powered . vector sensor . wind sensor

A

s one of the most important renewable and green energy sources in nature, wind energy has attracted increasing attention in the past decade due to the threat of global warming and the energy crisis.1 3 Based on electromagnetic and piezoelectric mechanisms, conventional approaches of wind energy harvesting have been developed.4 6 The main drawbacks of these wind energy harvesters are the complex structure, the large volume, and the mechanical wear induced performance degradation. Owning to the coupling between triboelectrification and electrostatic induction, triboelectric nanogenerators (TENGs), as an innovative invention, recently have been widely utilized to effectively scavenge mechanical energy from impacts,7 9 sliding,10,11 and rotations.12 These reported TENGs exhibit the remarkable characteristics of easy fabrication, low cost, and high efficiency. In this regard, developing TENG technology to harvest wind energy is of great necessity, which will not only decrease the cost of wind energy harvesting but also greatly extend the potential applications of TENGs. YANG ET AL.

Usually, a wind vector sensor system functions for wind speed and direction, which plays a critical role in weather forecasting. The working mechanisms of the designed wind sensors include mechanical rotation,13 temperature change,14 and laser Doppler.15 These sensors need to run on external power sources or conventional batteries, which will limit their applications in remote areas to collect wind information in real time. One creative approach to resolve the power limitation issue is to build up a self-powered system that operates independently, sustainably, and wirelessly by itself without using a battery.16 18 TENGs have been utilized as self-powered sensors for detecting displacement, mercury ions/catechin, and the change of magnetic field.11,19 21 In this paper, we report a triboelectric effect based wind energy harvester as a sustainable power source and a self-powered wind vector sensor system for wind speed and direction detection. The as-fabricated wind energy harvester is based on periodic contact/separation between two aluminum (Al) foils and a fluorinated ethylene propylene (FEP) film with a surface of nanowire VOL. XXX



NO. XX



* Address correspondence to [email protected]. Received for review August 18, 2013 and accepted September 13, 2013. Published online 10.1021/nn4043157 C XXXX American Chemical Society

000–000



XXXX

A www.acsnano.org

current and voltage output, a self-powered wind vector sensor system has been developed to detect the wind speed and direction. This work is important progress toward the practical applications of wind energy harvesting and the related self-powered sensor systems. RESULTS AND DISCUSSION

ARTICLE

structures. By utilizing the coupling between the triboelectric effect and the electrostatic effect, the periodic change of distance between the two Al foils and the FEP film can induce charge transfer between the Al electrode and the ground, resulting in the flow of free electrons in the external circuit as an alternating current. The integrated TENGs with a size of 2.5 cm  2.5 cm  22 cm deliver an output voltage up to 100 V and an output current of 1.6 μA, which can be used to directly drive tens of commercial light-emitting diodes (LEDs). Furthermore, relying on the wind flow induced

The fabricated TENG consists of two Al foils and a FEP film in a cuboid acrylic tube, as schematically illustrated in Figure 1a. The Al foil plays dual roles as a triboelectric

Figure 1. (a) Schematic diagram of the TENG. (b, c) Photographs of the TENG. (d) SEM image of the etched FEP film surface. (e, f) Rectified output voltage and current of one (e) and four (f) TENGs under a loading resistance of 100 MΩ. (g) Photographs of a 9-LED flashlight before and after being driven. (h) Photograph of the 40 green LEDs driven by the integrated TENGs. YANG ET AL.

VOL. XXX



NO. XX



000–000



B

XXXX www.acsnano.org

YANG ET AL.

ARTICLE

surface and as an electrode. One side of the FEP film was fixed at the middle of the end surface of the tube, leaving the other side free-standing. The distance between the two Al foils and the FEP film can be changed periodically due to the wind-induced vibration of the FEP film, resulting in an output voltage/ current across an external loading resistor. Figure 1b and c are the side view and front view of a typical as-fabricated TENG, indicating that the device has the dimensions 2.5 cm  2.5 cm  5.5 cm. The device electrode E1 or E2 is connected with an external loading resistance of 100 MΩ to the ground. To increase the triboelectric charge density, FEP nanowires are created on the surface of the FEP film via an inductively coupled plasma method, as shown in Figure 1d. To investigate the TENG's performance for harvesting wind energy, an air gun that provides uniform air flow was employed as a wind source with tunable flow speed. Figure S1 depicts the measured output voltage and current of the fabricated TENG under a wind speed of about 10 m/s, where the voltage and current are about 5 V and 0.5 μA under a loading resistance of 100 MΩ, respectively. Figure 1e presents the rectified output voltage and current of the TENG. The rectified output current of the TENG is still about 0.5 μA, while the output voltage can be increased to about 20 V, which is associated with the parasitic capacitance in the bridge rectification circuit under the high working frequency and the large loading resistance. Due to the charging effect of the parasitic capacitance, the output voltage of the TENG can be increased in this study. To increase the output power of the device, four TENGs were integrated in one acrylic tube, as illustrated in Figure S2. The top and bottom Al electrodes were connected with two bridge rectification circuits, respectively. Then the two bridge rectification circuits were connected in parallel. The measured output voltage and current of the integrated TENGs can be increased to 100 V and 1.6 μA, respectively, corresponding to an output power of 0.16 mW. The increase of the total output is due to the increase of the current flow through the external loading resistor. The output signals of the TENGs were rectified and then were connected in parallel. The total output performance can be enhanced further by connecting more TENG units. To demonstrate that the produced energy can be utilized as an effective power source, one TENG with a size of 2.5 cm  2.5 cm  5.5 cm was fixed on a car, as displayed in Figure S3. The device was then connected with a bridge rectification circuit and a 9-LED flashlight. The photograph in Figure 1g indicates that the TENG can harvest the wind energy induced by the movement of a car and light up the flashlight, which can be also seen in the movie file 1 (see the Supporting Information). Figure 1h illustrates that the produced energy of the four integrated TENGs can

Figure 2. Sketches that illustrate the electricity generation process in a full cycle under the wind-induced vibration of the FEP film between two Al foils.

be used to directly drive 40 green LEDs, as shown in movie file 2 (see the Supporting Information). A cycle of electricity generation of the fabricated TENG is illustrated in Figure 2. At the initial state, the surfaces of the bottom Al foil and the FEP film fully contact each other, inducing charge transfer between them. According to the triboelectric series,22 the electrons are injected from Al to FEP, resulting in positive and negative triboelectric charges on the Al and FEP surfaces, respectively. Figure 2a displays that the produced triboelectric charges with opposite polarities are fully balanced; no electron flow occurs in the external circuit. Once a wind flow separates the FEP film from the bottom Al, these triboelectric charges cannot be compensated. The negative ones on the FEP film will drive free electrons to flow through the external circuits, where the movement directions of electrons are opposite at the top and bottom Al electrodes, as depicted in Figure 2b. This electrostatic induction process can give the output voltage/current signals until the negative triboelectric charges on the FEP film are fully screened from the induced positive charges as well as the contact-induced triboelectric positive charges. No output voltage/current signals can be observed at this state, as illustrated in Figure 2c. When the FEP film was moved back from the top Al electrode to the bottom Al electrode, the negative triboelectric charges on the FEP film can induce the electrons to flow from the ground to the top Al electrode due to the increase of the relative separation between the top Al VOL. XXX



NO. XX



000–000



C

XXXX www.acsnano.org

ARTICLE Figure 3. (a) Schematic diagram of the model for the calculation. (b) Finite-element simulation of the potential distribution in the TENG under the different positions of the FEP film between two Al electrodes. (c) Total charges on the two Al electrodes as a function of the positions of the FEP film.

electrode and the FEP film. Moreover, the electrons can be driven to flow from the bottom Al electrode to the ground due to the decrease of the distance between the FEP and the bottom Al electrode, as shown in Figure 2d. When the FEP film is in contact with the bottom Al electrode, the negative triboelectric charges on the two surfaces of the FEP film are fully screened by the induced positive charges, resulting in no electron flow in the external circuit, as shown in Figure 2e. When the FEP film was moved again from the bottom Al electrode to the top Al electrode, Figure 2f displays that the opposite voltage/current signals can be observed in the external circuit as compared with those in Figure 2d. Therefore, when the wind flow vibrates the FEP film up and down, the TENG acts as an electron YANG ET AL.

pump that drives electrons back and forth between the Al electrodes and the ground, producing alternating current in the external circuit. As shown in Figure 2b, two circuits were used to connect the top and bottom Al electrodes, respectively. When the FEP film moved between the two Al electrodes, the output signals at both the top and bottom electrodes can be obtained by using the two circuits. The output signals were then rectified and connected in parallel, producing the largest electric output. To obtain a more quantitative understanding of the proposed electricity generation mechanism of the TENG, the electric potential distribution and the charge transfer between the Al electrodes and the FEP film can be verified through finite-element simulation using VOL. XXX



NO. XX



000–000



D

XXXX www.acsnano.org

ARTICLE Figure 4. (a) Schematic diagram of the designed double-electrode-based TENG. (b) Photograph of the TENG. (c) Measured open-circuit voltage and the short-circuit current of the TENG under a wind speed of 10 m/s. (d, e) Photographs show that the TENG was used to harvest the human mouth blowing induced wind energy to drive 10 LEDs (d) and an exit sign (e).

COMSOL. Figure 3a illustrates a schematic diagram of the constructed model including a FEP film (20 mm  30 mm  25 μm) and two Al electrodes (20 mm  30 mm  1 mm), which were grounded. The triboelectric charge densities on the two surfaces of the FEP film were assumed to be 10 μC/m2. Figure 3b shows the calculated results of the electric potential distribution in the TENG under the different positions at 6, 3, 0, 3, and 6 mm, respectively. When the FEP film occurs at the middle position between the two Al electrodes, it has the largest electrical potential, up to 9000 V. The electric potential on the FEP film was found to decrease dramatically when approaching the top or bottom Al electrode, as depicted in Figure 3b. Figure 3c shows the change of the total charge quantities on the Al electrodes at the different positions of the FEP film. When the YANG ET AL.

FEP film departs from the bottom Al electrode to the top Al electrode, the charge quantities on the top and bottom Al electrodes increase and decrease, respectively, revealing that the opposite voltage/current signals can be obtained at the top and bottom Al electrodes. Meanwhile, due to the diversity of contact electrification, an additional double-electrode-based TENG has also been developed for wind energy harvesting in this study. The working mechanism of the TENG is based on the contact/separation between two triboelectric material layers to drive the electrostatic induction charge flow in the external circuit.23 Figure 4a presents a schematic diagram of the TENG, which consists of a copper electrode, a polytetrafluoroethylene (PTFE) film, and an Al electrode on a Kapton film as the VOL. XXX



NO. XX



000–000



E

XXXX www.acsnano.org

ARTICLE Figure 5. (a) Photograph of the four TENGs arranged along four different directions. (b) Schematic diagram of the fabricated wind vector sensor system. (c, d) Measured output current (c) and voltage (d) of one TENG under different wind speeds. (e h) Measured output voltage mapping figures when the wind occurs along the four different directions.

wind-sensitive unit. As illustrated in Figure 4b, the photograph of the TENG indicates that the device has the dimensions 2.5 cm  0.6 cm  5 cm. The Al, Kapton, and the bottom acrylic can also form a single-electrodebased TENG. However, the short distance (