Tuning of Catalytic Property Controlled by the Molecular Dimension of

Oct 11, 2017 - The wt % data of palladium metal ions in the Pd-exchanged zeolite and encapsulated ..... Pure zeolite Y is purchased from Sigma-Aldrich...
0 downloads 4 Views 3MB Size
This is an open access article published under an ACS AuthorChoice License, which permits copying and redistribution of the article or any adaptations for non-commercial purposes.

Article Cite This: ACS Omega 2017, 2, 6636-6645

http://pubs.acs.org/journal/acsodf

Tuning of Catalytic Property Controlled by the Molecular Dimension of Palladium−Schiff Base Complexes Encapsulated in Zeolite Y Archana Choudhary, Susheela Kumari, and Saumi Ray* Birla Institute of Technology and Science, Pilani, Rajasthan 333031, India S Supporting Information *

ABSTRACT: Planar palladium−Schiff base complexes are synthesized, maintaining the order of their molecular dimensions as PdL1 < PdL2 < PdL3 < PdL4 < PdL5 in free state, as well as encapsulated in zeolite Y, where L1: N,N′-bis(salicylidene)ethylenediamine and L2, L3, L4, and L5 are derivatives of L1. All encapsulated complexes have shown better catalytic activity for the sulfoxidation of methyl phenyl sulfide in comparison to their homogeneous counter parts. These hybrid systems are characterized with the help of different characterization techniques such as X-ray diffraction analysis, scanning electron microscopy−energy-dispersive X-ray spectrometry, X-ray photoelectron spectroscopy, Fourier transform infrared, and UV−visible spectroscopy; all of these studies have suggested that the largest complex deviates by the maximum from its free-state properties, and a radical change in the reactivity of the complex is observed.



INTRODUCTION The selective oxidation of thioethers is a significant reaction in organic synthesis1 because the product sulfoxides are the important intermediate of various biological advances in natural compounds.2 These products also have versatile applications in agrochemical,3 pharmaceutical,4 and polymer5 industries and also can be used as ligands in asymmetric catalysis,6 oxotransfer reagents, and solvents.4 They often play an important role as therapeutic agents such as antiulcer,7 antibacterial, antifungal, antiatherosclerotic,8 anthelmintic,9 antihypertensive,10 and vasodilators.11 As a result, there are substantial amounts of work done to develop varieties of competent catalysts for the sulfoxidation process.12 Most of the conventional synthesis routes for the sulfoxidation process are quite efficient, but they require the use of lots of organic and inorganic oxidants and solvents which obviously leads to the production of a large amount of toxic waste.13 Consequentially, it is essential to develop a “greener approach” to synthesize the desired sulfoxidation products. To adopt the environmentally benign methodology, there should be some modification in the traditional procedures such as uses of environment-friendly oxidants, solvent-free reaction medium, and eco-friendly catalysts. Aqueous hydrogen peroxide is a most popular oxidant for the sulfoxidation process because of its easy handling, greater availability, and eco-friendly approach for the reaction due to the formation of water as the only byproduct.12h Schiff base transition-metal complexes have played a vital role in the progress of catalytic processes with greater effectiveness in biological and industrial applications.14 However, the homogeneous catalysts generally have some disadvantages in the catalytic processes such as their instability, difficulty in the separation, lack of reusability, and lack of greener approach.15 © 2017 American Chemical Society

The modern catalytic science favors those catalysts, which can conquer the limitation of these homogeneous catalysts without the loss of reactivity. In this direction, heterogenization of conventional homogeneous catalysts is a suitable route to couple the reactivity of the complex with the additional shape and size selectivity and site isolation properties appended by the host materials. Encapsulation of transition-metal complexes in different hosts such as microporous and mesoporous materials is an alternative contemporary approach to accomplish the synthesis of designer catalysts.16 To synthesize designer catalysts, especially biomimetic systems, zeolites are found as competent hosts for the encapsulation of transitionmetal complexes having a molecular dimension comparable with that of the cavity of the host zeolites.16c,17 Among those, employment of zeolite-encapsulated metal complexes in the field of oxidation or epoxidation of alkanes, alkenes, alcohols, and aromatic compounds has been extensively studied and reporte16b,d,18 but comparatively fewer reports are available on the sulfoxidation process.19 Maurya and co-workers have investigated different vanadium complexes entrapped in zeolite Y and explored their catalytic activities for the oxidation and sulfoxidation reactions.19a−d The authors have stated that the encapsulated complexes in zeolite Y have shown almost a similar reactivity for the sulfoxidation reaction when compared with their free states. However, higher turnover frequencies and reusability make the zeolite-encapsulated complexes more suitable than their free-state analogues. Received: July 26, 2017 Accepted: September 28, 2017 Published: October 11, 2017 6636

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Figure 1. Molecular dimensions of palladium complexes.

In the present work, we have synthesized some novel palladium−Schiff base complexes in the encapsulated state in zeolite Y as well as in the free state. The molecular dimensions of the complexes follow the order as PdL1 < PdL2 < PdL3 < PdL4 < PdL5 (where L1: N,N′-bis(salicylidene)ethylenediamine, L2: N,N′-bis(5-hydroxy-salicylidene)ethylenediamine, L3: N,N′-bis(5-bromo-salicylidene)ethylenediamine, L4: N,N′-bis(5-methyl-salicylidene)ethylenediamine, and L5: N,N′-bis(5methoxysalicylidene)ethylenediamine) (given in Figure 1). These systems are employed as catalysts for the sulfoxidation of methyl phenyl sulfide to study the steric and electronic effect of different substituent groups which are attached on the complexes and their consequences on the reactivity upon encapsulation. These systems are characterized by powder Xray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM)−energy-dispersive X-ray spectrometry (EDXS), IR, and UV−visible (UV−vis) spectroscopy. It is quite fascinating to observe that as compared to their neat forms, encapsulated complexes have shown quite a modified catalytic activity toward the conversion of methyl phenyl sulfide to corresponding sulfoxide, and interestingly the steric environment imposed by zeolitic topology has a significant control over the reactivity of the encapsulated systems.

Table 1. Concentration of Palladium (wt %) Content in the Different Samples s. no.

samples

palladium (wt %)

Si/Al ratio

1 2 3 4 5 6 7

parent Y Pd-Y PdL1-Y PdL2-Y PdL3-Y PdL4-Y PdL5-Y

0.65 0.51 0.27 0.27 0.26 0.22

2.90 2.79 2.85 2.89 1.28 2.78 2.79

occur which eventually leads to the reduction of the wt % of palladium in encapsulated metal complexes. Scanning Electron Microscopy. Scanning electron microscopic studies of pure zeolite Y and the Soxhlet extracted hybrid PdL1-Y, PdL2-Y, PdL3-Y, PdL4-Y, and PdL5-Y systems are carried out (the SEM images are shown in Figure 2). Zeolite boundaries are evidently observable in the SEM images of zeolite-entrapped complexes and also comparable with that of the pure zeolite Y which is a clear manifestation of the absence of unreacted species or impurities on the surface of the host lattice in the final host−guest products.20 Powder XRD Analysis. Powder XRD patterns of the parent zeolite Y, Pd-zeolite Y, and palladium−salen complexes encapsulated in zeolite Y have been recorded (shown in Figure 3). The complexes are synthesized within the supercage of zeolite Y via the flexible ligand synthesis method, and the unreacted ligands and complexes are completely removed by the Soxhlet extraction technique; however, during the whole process, the host framework is remained intact. The X-ray diffractograms of PdL1-Y, PdL2-Y, PdL3-Y, PdL4-Y, and PdL5Y samples and that of the pure zeolite Y exhibit no shift in peak positions when compared. This observation is indeed a significant one as it specifies the preservation of host lattice integrity even after the encapsulation of a large complex into it. However, XRD patterns of PdL1-Y, PdL2-Y, PdL3-Y, PdL4-Y, and PdL5-Y evidently illustrate a substantial reversal in the intensity of the peaks at 2θ = 10° and 12°, that is, I220 < I311 in comparison to those in the XRD patterns of pure and Pdexchanged zeolite Y. This intensity reversal has already been empirically correlated with the existence of the large complex



RESULTS AND DISCUSSION Elemental Analysis. The pure Na-zeolite Y has the unit cell formula as Na58Al58Si136O388·yH2O, and the Si/Al ratio is 2.34. The elemental analysis (EDXS spectra) of the encapsulated complexes PdL1, PdL2, PdL3, PdL4, and PdL5 has suggested that the Si/Al ratio remains nearly unaffected even after the encapsulation for all cases (shown in Table 1), indicating that no significant dealumination takes place during the process of encapsulation. The wt % data of palladium metal ions in the Pd-exchanged zeolite and encapsulated metal complexes (given in Table 1) highlight the reasonable observation that the concentration of palladium metal ions in Pd-exchanged zeolite Y is greater than those of all zeoliteencapsulated complexes. It is perhaps obvious because in the process of encapsulation, slight leaching of metal ions may 6637

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Figure 2. SEM images of (A) Pd-Y, (B) PdL1-Y, (C) PdL2-Y (before Soxhlet extraction), (D) PdL2-Y (after Soxhlet extraction), (E) PdL3-Y, and (F) PdL5-Y.

complexes show a very weak signal for palladium metal because of its low loading level within the host lattice. High-resolution XPS spectra of palladium in the PdL1 complex have shown two signals at the binding energies of 335.96 and 340.96 eV which are attributed to 3d5/2 and 3d3/2, respectively. However, when the complex is encapsulated in zeolite Y, 3d5/2 and 3d3/2 XPS signals are broader and appear at the almost same binding energies (335.13 and 340.49 eV) and additionally a new signal originates at a relatively higher binding energy of 347.87 eV. This additional XPS signal at a higher binding energy has been observed for all encapsulated complexes (PdL1-Y, PdL2-Y, and PdL5-Y) but not for the free-state complex (PdL1). The higher shift in binding energy is definitely a consequence of the removal of electron density from the metal center.16d,22f In this context, it could have relevant significance as the geometry which the metal complex adopts under encapsulation might play the major role in the depletion of electron density from the metal center. Furthermore, XPS signals of Na (1s), Si (2p), and Al (2p) elements are also observed at their expected positions in the XPS spectra of all encapsulated complexes. IR Spectroscopy. Fourier transform infrared (FTIR) spectral data of ligands and palladium−Schiff base complexes in neat as well as encapsulated states along with the pure zeolite Y have been recorded (Figure 6 and Table S1 in the Supporting Information). IR spectroscopic data have provided information about the retention of integrity of the zeolite Y framework and also indicated the successful complex formation within the supercage of zeolite Y. The four major zeolitic IR bands are observed in the region of 450−1200 cm−1, and two additional peaks appear at 1643 and 3500 cm−1. The IR bands at 560, 717, 786, and 1018 cm−1 are attributed to (Si/Al−O)4 bending mode, double ring, symmetric stretching, and asymmetric stretching vibrations, respectively,23 whereas IR bands at 3500 and 1643 cm−1 are assigned to surface hydroxylic group and lattice water molecules, respectively.20a All of these bands mostly remain unaffected for all of the encapsulated systems (PdL1-Y, PdL2-Y, PdL3-Y, PdL4-Y, and PdL5-Y) because the host framework does not experience any structural modifications during the process of encapsulation. However, the salen ligands and corresponding complexes are primarily identified by the IR studies as CN stretching, CC stretching, and C−O stretching vibrations of the salen ligands appear at the expected positions. Upon complexation, these FTIR bands show an essentially identical vibration with shifts to lower energies as an

Figure 3. XRD pattern of (a) pure zeolite Y, (b) Pd-exchanged zeolite Y, (c) PdL1-Y, (d) PdL2-Y, (e) PdL3-Y, (f) PdL4-Y, and (g) PdL5-Y.

inside the cavity of zeolite Y.21 Interestingly, a tethered complex on the host surface does not show such type of intensity reversal in XRD patterns. Moreover, the absence of new peaks in the XRD patterns of palladium-encapsulated complexes is a signature of the formation of the complexes in low concentrations inside the host lattice. X-ray Photoelectron Spectroscopy. XPS is an important technique which provides an indirect proof about the complex formation in free as well as encapsulated states. All core constituent elements of the complexes such as C (1s), N (1s), O (1s), and Pd (3d) of PdL1, PdL1-Y, PdL2-Y, and PdL5-Y complexes are presented in the form of survey spectra and highresolution spectra (Figures 4 and 5 and Figures S1−S3 in the Supporting Information), and the corresponding binding energy data are tabulated in Table 2. The low concentration of palladium in the encapsulated complexes makes the XPS signal for metal weak which is actually in accordance with the concentration-dependent EDXS, IR, and UV−vis spectroscopic studies. The observed data evidently indicate the presence of C, N, O, Na, Si, Al, and Pd in their respective chemical states, which is in accordance with the literature.16d,22 Intense and broad carbon (1s) XPS spectra have been observed for palladium−salen complexes in both the states, are further deconvoluted into two peaks, and confirmed the presence of sp3 and sp2 carbon atoms in those complexes. Similarly, these complexes have shown the XPS signals for nitrogen (1s), oxygen (1s), and validated for the (M−N), (NC) and (C− O), (M−O) elemental state, respectively.22e All encapsulated 6638

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Figure 4. High-resolution XPS signals of (A) Pd (3d), (B) C (1s), (C) N (1s), and (D) O (1s) for PdL1 complex (black-colored graphs are experimental data, and green- and blue-colored peaks are peak-fitted data).

Figure 5. High-resolution XPS signals of (A) Pd (3d), (B) C (1s), (C) N (1s), and (D) O (1s) for PdL1-Y complex (black-colored graphs are experimental data, and green- and blue-colored peaks are peak-fitted data).

outcome of the coordination with the metal ion. IR peaks of the encapsulated complexes are mostly difficult to identify because

of the appearance of the strong zeolitic bands in the 450−3500 cm−1 region. Advantageously, some characteristic IR peaks of 6639

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Table 2. Binding Energy Data of the Free-State and Encapsulated Complexes s. no.

samples

1 2 3 4

PdL1 PdL1-Y PdL2-Y PdL5-Y

Si (2p) 101.52 101.55 102.72

Al (2p) 75.15 72.94, 73.79 73.16, 75.47

C (1s) 284.04, 285.23, 285.23, 285.66,

N (1s)

282.82 283.65 283.65 283.64

399.11, 398.88, 398.81, 399.93,

396.54 397.72 397.76 397.88

O (1s)

Pd (3d5/2)

Pd (3d3/2)

532.84 530.96 530.95 532.63, 530.69

335.92 335.13 335.39 337.11

340.96 340.49, 347.87 340.21, 346.72 343.34, 346.64

relatively low intensities are observed in the range of 1600− 1200 cm−1 which is mainly due to the guest complex and are suitable to study because zeolitic IR bands are silent particularly in this region. These bands in encapsulated complexes have appeared with little shifts with respect to that of the nearly planar free-state complex. These shifts could be attributed to the altered geometry the complex adopts to accommodate itself in the rigid host supercage under encapsulation. Furthermore, a shift in C−H deformation bands has already been identified as an indication of the encapsulation of the complex inside the zeolite Y.24 Solid-State UV−Vis Spectroscopy. Electronic spectra of the ligand and corresponding complex in solution (Figure S4 in the Supporting Information) or solid states have been studied for the justification of complex formation. In addition to that, comparative optical spectra of palladium−Schiff base complexes in both states have been studied thoroughly to understand the nature of the geometry they adopt under encapsulation (given in Figure 7 and Table 3). Electronic transitions of the Schiff

Figure 6. FTIR spectra of encapsulated palladium−salen complexes in zeolite Y: (a) pure zeolite Y, (b) PdL1-Y, (c) PdL2-Y, (d) PdL3-Y, (e) PdL4-Y, and (f) PdL5-Y.

Figure 7. (A) UV−vis spectra of (a) PdL1 and (b) PdL1-Y; (B) UV−vis spectra of (a) PdL2 and (b) PdL2-Y; (C) UV−vis spectra of (a) PdL3 and (b) PdL3-Y; (D) UV−vis spectra of (a) PdL4 and (b) PdL4-Y; and (E) UV−vis spectra of (a) PdL5 and (b) PdL5-Y. 6640

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

of percentage conversion as well as turnover number (TON) are significantly higher than those of their corresponding free state (catalytic data are given in Table 4).

Table 3. Solid-State UV−Vis Data of Palladium−Schiff Base Complexes in Both States s. no.

samples

π−π* transitions

n−π* transitions

CT/d−d transitions

1 2 3 4 5 6 7 8 9 10

PdL1 PdL1-Y PdL2 PdL2-Y PdL3 PdL3-Y PdL4 PdL4-Y PdL5 PdL5-Y

224 222 231 225 235 220 231 217 235 224

255 262 261, 296 255 261 247 288 278 288, 366 259, 299

380−415 350−370 424−447 364, 479 404−433 323−364, 465 372−415 335−357 435−445 346−366, 470

Table 4. Oxidation of Methyl Phenyl Sulfide after 4 h Reaction Time with H2O2 as an Oxidant s. no. 1 2 3 4 5 6 7 8 9 10 11

base ligands appearing in the range of 210−240 nm are assigned to the π−π* transition and in the range of 240−300 nm are assigned to the n−π* transition. However, in the freestate transition-metal complexes, these transitions are shifted relatively toward a lower energy; π−π* transition has been observed in the range of 210−240 nm, and n−π* transition has been observed in the range of 240−300 nm. The most evident confirmation of free-state complex formation is the appearance of charge-transfer (CT) and d−d transitions bands, which are clearly observed in the solid-state electronic spectra in the range of 335−450 nm for different palladium−Schiff base complexes. However, the appearance of d−d bands in square planar palladium complexes is indistinguishable in comparison with those of nickel−salen complexes. In palladium−salen complexes, these bands appear in the range of 335−450 nm, whereas in nickel complexes, these are identified in the 510− 570 nm region.25 According to the ligand field theory, for 4d series elements, d orbital splitting is much higher as compared to that of the corresponding 3d series elements and hence d−d bands in palladium−salen complexes have shifted toward the high-energy region and merged with CT bands. After encapsulation, palladium−salen complexes have shown a comparable pattern; however, the CT and d−d bands which are instigated from the metal center are primarily affected, that is, intensified26 and blue-shifted on encapsulation.24b Such an observation eventually signifies the deviation of the free-state geometry of the complexes when encapsulated, especially around the metal center. Interestingly, PdL2-Y, PdL3-Y, PdL4Y, and PdL5-Y complexes have shown a blue shift in greater extent compared to that observed for PdL1-Y because these complexes have larger molecular dimensions and might experience more space constraint imposed by the topology of the supercage which in turn causes more distortion in the geometry of these complexes. Catalytic Study. Transition-metal complexes are efficient catalysts for sulfoxidation reaction using aqueous hydrogen peroxide as an oxidant.27 However, among the zeoliteencapsulated transition-metal complexes, palladium−Schiff base complexes are comparatively less investigated catalysts for sulfoxidation. Therefore, in the present report, free-state as well as encapsulated Pd complexes have been employed as catalysts for sulfoxidation reaction in the presence of H2O2; the objective is to, however, investigate how encapsulation affect the catalytic activity of the complex. For all cases, methyl phenyl sulfide is converted into corresponding sulfoxide selectively (Scheme 3), and it is quite interesting to note that the catalytic activities of these encapsulated complexes in terms

samples

% conversion

pure zeolite Y PdL1 PdL1-Y PdL2 PdL2-Y PdL3 PdL3-Y PdL4 PdL4-Y PdL5 PdL5-Y

7 39 48 30 60 63 71 36 76 26 86

TON

30 201 25 477 67 564 30 623 23 835

selectivity for sulfoxide

selectivity for sulfone

82.1

17.9

98.66 97.25 99.51 98.95 98.98 95.45 98.31 92.01 98.18 92.23

1.33 2.74 0.49 1.04 1.01 4.54 1.68 7.98 1.81 7.76

Surface impurities in the form of ligands and surface complexes are minimized by extensive Soxhlet extraction using different solvents, and the uncoordinated palladium ions are removed by further ion-exchange reaction with sodium ions. The exercise of removal of impurities is truly significant so as to comprehend better the origin of modified catalysis with respect to the parent zeolite Y as it has been observed that the parent zeolite Y (Na-zeolite Y) shows fairly less % conversion as well as selectivity (shown in Table 4). Though another direction of research could be with the change in Si/Al ratio as it definitely affects the catalytic activity of the encapsulated complexes,28 the present work highlights on the catalysis of hybrid host−guest systems with the Si/Al ratio of the host kept constant by taking the same lot of parent zeolite Y for the synthesis of all encapsulated complexes. The reactivity order of free-state complexes follows the order as PdL3 > PdL1 ≈ PdL4 > PdL2 > PdL5, whereas after encapsulation, the order of reactivity is just in accordance with the molecular dimension of the complexes and it is PdL5 > PdL4 > PdL3 > PdL2 > PdL1. The proposed mechanism for this catalytic reaction includes the nucleophilic attack of H2O2 on the electropositive metal center. As a result, in the transition state, electron-rich nucleophile is bonded through the axial position to the metal complex. Plausible mechanism for the oxidation of sulfides to the corresponding sulfoxides catalyzed by the PdL complexes entrapped in zeolite Y using H2O2 as an oxidant is given in Scheme 1, and it is obvious that the electropositive character of the metal drives the first step of the reaction.29 Bhadbhade and Srinivas have already reported that an electron-withdrawing group (Cl−) makes the copper−salen complex distorted from its square planar geometry,30 whereas an electron-donating group (−OCH3) on the same position tries to maintain the planarity of the complex, especially around the metal. Distortion around the metal atom by any means makes the complex more susceptible to nucleophilic attack by removing electron density from the metal center; on the contrary, the metal center in planar effectively conjugated systems becomes electron-rich and less efficient for the nucleophilic attacks. We also have observed a similar effect 6641

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Scheme 1. Possible Mechanism for the Oxidation of Sulfides (Adapted from Ref 30)

Figure 8. Recyclability of the PdL5-Y catalyst for sulfoxidation reaction.

electronic factor, whereas after encapsulation, the catalytic activity order of the complexes is in accordance with the molecular dimensions or the extent of distortion.



CONCLUSIONS Zeolite-encapsulated complexes are indeed better heterogeneous catalysts with enhanced adapted reactivity for the oxidation process, for example, sulfoxidation reaction. The comparative studies of palladium−Schiff base complexes in free as well as encapsulated states provide clear insights about the modified reactivity for the catalytic oxidation processes of such systems after encapsulation. The observed blue shift in d−d bands in the electronic spectra of encapsulated complexes has demonstrated the effect of the space restrictions imposed by rigid host frameworks on the coordination environment around the metal as space restrictions compel the encapsulated guest complex to adopt an unusual nonplanar geometry for better accommodation inside the supercage to minimize the van der Waals interaction. High-resolution XPS spectra of Pd (3d) of encapsulated complexes showing an additional signal toward a higher binding energy also confirms the change in the electronic environment around the metal upon encapsulation. Comparative catalytic studies of these hybrid systems provide a fascinating corelation between modified structural aspects and adapted functionality of complexes, and therefore it can be concluded as the degree of distortion in the structure of the encapsulated complex is the key point for the remarkable modified catalytic activity of the systems.

for the nickel−salen complexes encapsulated in zeolite with different molecular dimensions in series.25 Currently, while exploring the catalytic activity of the Pd complexes in their free states, PdL3 having electron-withdrawing (−Br) groups is identified as the most efficient catalyst which is just in line with the previous arguments. Electronwithdrawing (−Br) groups in PdL3 make the complex distorted even in the free state and subsequently more reactive. Electronreleasing groups (−OH and −OCH3 in PdL2 and PdL5, respectively) make those palladium−salen complexes less reactive. PdL1 and even PdL4 complexes showing nearly the same TON have exhibited intermediate reactivity, as they do not have a noteworthy push−pull effect of substituents. As expected, the PdL5 complex has shown most exciting modified enhancement in reactivity on encapsulation, as the complex is most distorted to be fitted into the supercage because of its largest molecular dimensions. The modified reactivity of the encapsulated complexes is indeed a consequence of the geometry they adopt under encapsulation in zeolite Y. It is quite evident and well-supported by the optical spectroscopic and XPS studies and even theoretical studies25 that the rigid spherical walls of the zeolite supercage impose significant space constraint which in turn leads the complexes to suffer from noteworthy structural distortion. The observed relative shifts toward higher values of binding energy in XPS signals for the zeolite-encapsulated complexes indicate the enhancement of the electropositive character of the metal center after encapsulation. Distortion around the metal atom by any means makes the complex more susceptible to nucleophilic attack by removing electron density from the metal center; on the contrary, the metal center in planar effectively conjugated systems becomes electron-rich and less efficient for the nucleophilic attacks. The reusability of PdL5-Y is evaluated for the same sulfoxidation reaction (shown in Figure 8); the catalyst could be effectively used for up to four cycles without much loss in catalytic activity. In conclusion, it can be stated that the reactivity of free-state complexes is mainly governed by the



EXPERIMENTAL SECTION Materials and Preparation. Pure zeolite Y is purchased from Sigma-Aldrich, India. Salicylaldehyde and its derivatives and ethylenediamine are purchased from Alfa Aesar, and palladium acetate is purchased from TCI chemicals, India. All solvents (ethanol, acetone, methanol, and diethyl ether) are purchased from S.D. Fine, India. Preparation of Ligands (L1, L2, L3, L4, and L5).24b,31 Two molar ratios of salicylaldehyde (or its derivatives) dissolved in ethanol is refluxed for 10−15 min. One molar ratio of ethylenediamine is added into it. The reaction mixture is refluxed for 30 min at 60−70 °C and then ice-cooled for an hour. Bright yellow solid flakes are obtained as a product, thoroughly washed with ethanol, and then dried in air (given in Scheme 2). Preparation of Complexes.32 Ligands (L1, L2, L3, L4, and L5 in the respective reactions) taken in ethanol are refluxed, and then aqueous solution of equimolar ratio of palladium acetate is added dropwise into them. The reaction 6642

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

Scheme 2. (a) Synthesis of Palladium−Salen Complexes, (b) Palladium-Exchanged Zeolite Y, and (c) Zeolite-Encapsulated Palladium−Salen Complexes via the Flexible Ligand Synthesis Method

mass is further refluxed for 30 min. For the synthesis of these Schiff base complexes, an inert environment is used. The final greenish-yellow colored product is recovered, washed with ethanol and diethyl ether, and then dried at room temperature (Scheme 2). Preparation of Palladium-Exchanged Zeolite Y. Pure Na-zeolite Y (10 g) (Na58Al58Si136O388·yH2O) is allowed to disperse in 0.01 M palladium salt [Pd(CH3COO)2 = 0.224 g] in 100 mL of water to acquire the required loading level of palladium ions and stirred at room temperature for 24 h. The slurry is filtered, washed repeatedly with water, and then desiccated for 12 h at 150 °C (Scheme 2). Synthesis of Encapsulated Pd(II)−Schiff Base Complexes in Zeolite Y.24b,31 Schiff base ligands are flexible in nature; thus, one of the methods of encapsulation of metal complexes inside the supercage of zeolite Y could be possible via the “flexible ligand” approach (Scheme 2). The palladiumexchanged zeolite and excess amount of the ligand (L1, L2, L3, L4, and L5 in each respective reaction) are allowed to react at 200−250 °C for 24 h under constant stirring to synthesize the complex inside the supercage of zeolite Y. The reaction mass is then recovered and further subjected to the Soxhlet extraction with the different solvents such as acetone, methanol, and diethyl ether in a sequence. The product is dried in a muffle furnace for 10−12 h at 150 °C. The recovered material is further reacted with 0.01 M NaCl solution for 12 h to remove the unreacted metal ions, followed by filtration and washing until the filtrate is negative for the chloride ion test. Sulfoxidation of Methyl Phenyl Sulfide. Aqueous 30% H2O2 (0.57 g, 5 mmol), methyl phenyl sulfide (0.62 g, 5 mmol), and the catalyst (0.015 g) are mixed in a minimum amount of solvent (3 mL of CH3CN), and the reaction mixture is stirred at 60 °C temperature for 4 h. The progress of the reaction is monitored by gas chromatography (GC) at different time intervals, and the products are identified and quantified (by using an internal standard method) with the help of GC (Scheme 3). The calibration curve of thioanisole is provided in the Supporting Information (Figure S5). To attain the maximum efficiency, reaction conditions are optimized by varying the different reaction parameters such as temperature, time duration of reaction, and amount of catalysts, considering the PdL1-Y complex as the representative catalyst (Figure S6 is given in the Supporting Information).

Scheme 3. Schematic Representation of the Sulfoxidation Reaction



ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsomega.7b01071. Physical measurements; XPS survey spectra of PdL1 and encapsulated complexes PdL1-Y, PdL2-Y, and PdL5-Y; high-resolution XPS spectra for PdL2-Y and PdL5-Y complexes; FTIR spectral data (in cm−1) for ligands and neat and encapsulated complexes; UV−vis spectra of L1 and PdL1; calibration curve of thioanisole; and % conversion of thioanisole for PdL1-Y complex with respect to the amount of catalyst, temperature of reaction, and different time durations (PDF)



AUTHOR INFORMATION

Corresponding Author

*E-mail: [email protected] (S.R.). ORCID

Saumi Ray: 0000-0002-6893-9634 Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS The authors acknowledge the DST, New Delhi, for the financial support (DST Project no. SR/FT/CS-038/2010) and for the instrumental facility funded by DST-FIST, Department of Chemistry, and Department of Physics, BITS, Pilani, for the XPS measurement, and MNIT, Jaipur. 6643

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega



Article

25, 1049−1052. (i) Reddy, R. S.; Reddy, J. S.; Kumar, R.; Kumar, P. Sulfoxidation of thioethers using titanium silicate molecular sieve catalysts. J. Chem. Soc., Chem. Commun. 1992, 84−85. (j) Legros, J.; Bolm, C. Investigations on the iron-catalyzed asymmetric sulfide oxidation. Chem.Eur. J. 2005, 11, 1086−1092. (k) Legros, J.; Bolm, C. Highly enantioselective iron-catalyzed sulfide oxidation with aqueous hydrogen peroxide under simple reaction conditions. Angew. Chem., Int. Ed. 2004, 43, 4225−4228. (l) Drago, C.; Caggiano, L.; Jackson, R. F. W. Vanadium-catalyzed sulfur oxidation/kinetic resolution in the synthesis of enantiomerically pure alkyl aryl sulfoxides. Angew. Chem., Int. Ed. 2005, 44, 7221−7223. (13) (a) Barton, D. H. R.; Li, W.; Smith, J. A. Binuclear manganese complexes as catalysts in the selective and efficient oxidation of sulfides to sulfones. Tetrahedron Lett. 1998, 39, 7055−7058. (b) Hirano, M.; Yakabe, S.; Clark, J. H.; Morimoto, T. Synthesis of sulfoxides by the oxidation of sulfides with sodium chlorite catalysed by manganese(III) acetylacetonate in acetone in the presence of alumina. J. Chem. Soc., Perkin Trans. 1 1996, 2693−2698. (14) (a) Cozzi, P. G. Metal−Salen Schiff base complexes in catalysis: Practical aspects. Chem. Soc. Rev. 2004, 33, 410−421. (b) De Rosa, M.; Lamberti, M.; Pellecchia, C.; Scettri, A.; Villano, R.; Soriente, A. An efficient solvent free catalytic oxidation of sulfides to sulfoxides with hydrogen peroxide catalyzed by a binaphthyl-bridged Schiff base titanium complex. Tetrahedron Lett. 2006, 47, 7233−7235. (c) Palucki, M.; Hanson, P.; Jacobsen, E. N. Asymmetric oxidation of sulfides with H2O2 catalyzed by (salen)Mn(III) complexes. Tetrahedron Lett. 1992, 33, 7111−7114. (d) Jeong, Y.-C.; Choi, S.; Hwang, Y. D.; Ahn, K.-H. Enantioselective oxidation of sulfides with hydrogen peroxide catalyzed by vanadium complex of sterically hindered chiral Schiff bases. Tetrahedron Lett. 2004, 45, 9249−9252. (15) (a) Chen, N. Y.; Garwood, W. E. Some catalytic properties of ZSM-5, a new shape selective zeolite. J. Catal. 1978, 52, 453−458. (b) Deshpande, S.; Srinivas, D.; Ratnasamy, P. EPR and Catalytic Investigation of Cu(Salen) Complexes Encapsulated in Zeolites. J. Catal. 1999, 188, 261−269. (c) Anderson, J. R.; Foger, K.; Mole, T.; Rajadhyaksha, R. A.; Sanders, J. V. Reactions on ZSM-5-type zeolite catalysts. J. Catal. 1979, 58, 114−130. (16) (a) Maurya, M. R.; Chandrakar, A. K.; Chand, S. Zeolite-Y encapsulated metal complexes of oxovanadium(VI), copper(II) and nickel(II) as catalyst for the oxidation of styrene, cyclohexane and methyl phenyl sulfide. J. Mol. Catal. A: Chem. 2007, 274, 192−201. (b) Jin, C.; Fan, W.; Jia, Y.; Fan, B.; Ma, J.; Li, R. Encapsulation of transition metal tetrahydro-Schiff base complexes in zeolite Y and their catalytic properties for the oxidation of cycloalkanes. J. Mol. Catal. A: Chem. 2006, 249, 23−30. (c) Balkus, K. J.; Gabrielov, A. G. Zeolite Encapsulated Metal Complexes. In Inclusion Chemistry with Zeolites: Nanoscale Materials by Design; Herron, N., Corbin, D. R., Eds.; Springer Netherlands: Dordrecht, 1995; pp 159−184. (d) Bania, K. K.; Deka, R. C. Zeolite-Y Encapsulated Metal Picolinato Complexes as Catalyst for Oxidation of Phenol with Hydrogen Peroxide. J. Phys. Chem. C 2013, 117, 11663−11678. (e) Zhu, J.; Kónya, Z.; Puntes, V. F.; Kiricsi, I.; Miao, C. X.; Ager, J. W.; Alivisatos, A. P.; Somorjai, G. A. Encapsulation of Metal (Au, Ag, Pt) Nanoparticles into the Mesoporous SBA-15 Structure. Langmuir 2003, 19, 4396−4401. (f) De Vos, D. E.; Dams, M.; Sels, B. F.; Jacobs, P. A. Ordered Mesoporous and Microporous Molecular Sieves Functionalized with Transition Metal Complexes as Catalysts for Selective Organic Transformations. Chem. Rev. 2002, 102, 3615−3640. (17) Bedioui, F. Zeolite-encapsulated and clay-intercalated metal porphyrin, phthalocyanine and Schiff-base complexes as models for biomimetic oxidation catalysts: an overview. Coord. Chem. Rev. 1995, 144, 39−68. (18) (a) Bhagya, K. N.; Gayathri, V. Metal complexes of 2methylimidazole encapsulated in zeolite-Y as efficient and reusable catalysts for oxidation of phenol and benzyl alcohol. J. Porous Mater. 2013, 20, 257−266. (b) Bunce, S.; Cross, R. J.; Farrugia, L. J.; Kunchandy, S.; Meason, L. L.; Muir, K. W.; O’Donnell, M.; Peacock, R. D.; Stirling, D.; Teat, S. J. Chiral Schiff base complexes of copper(II), vanadium(IV) and nickel(II) as oxidation catalysts. X-ray

REFERENCES

(1) Madesclaire, M. Synthesis of sulfoxides by oxidation of thioethers. Tetrahedron 1986, 42, 5459−5495. (2) (a) Carreno, M. C. Applications of Sulfoxides to Asymmetric Synthesis of Biologically Active Compounds. Chem. Rev. 1995, 95, 1717−1760. (b) Prilezhaeva, E. N. Rearrangements of sulfoxides and sulfones in the total synthesis of natural compounds. Russ. Chem. Rev. 2001, 70, 897−920. (3) (a) Prakash, G. K. S.; Hu, J.; Olah, G. A. Preparation of Tri- and Difluoromethylsilanes via an Unusual Magnesium Metal-Mediated Reductive Tri- and Difluoromethylation of Chlorosilanes Using Triand Difluoromethyl Sulfides, Sulfoxides, and Sulfones. J. Org. Chem. 2003, 68, 4457−4463. (b) Fukuda, N.; Ikemoto, T. Imide-Catalyzed Oxidation System: Sulfides to Sulfoxides and Sulfones. J. Org. Chem. 2010, 75, 4629−4631. (4) Kukushkin, V. Y. Metal-ion mediated deoxygenation of sulfoxides. Coord. Chem. Rev. 1995, 139, 375−407. (5) Schuster, M.; de Araujo, C. C.; Atanasov, V.; Andersen, H. T.; Kreuer, K.-D.; Maier, J. Highly Sulfonated Poly(phenylene sulfone): Preparation and Stability Issues. Macromolecules 2009, 42, 3129−3137. (6) Fernández, I.; Khiar, N. Recent Developments in the Synthesis and Utilization of Chiral Sulfoxides. Chem. Rev. 2003, 103, 3651− 3706. (7) (a) Lai, K. C.; Lam, S. K.; Chu, K. M.; Wong, B. C. Y.; Hui, W. M.; Hu, W. H. C.; Lau, G. K. K.; Wong, W. M.; Yuen, M. F.; Chan, A. O. O.; Lai, C. L.; Wong, J. Lansoprazole for the prevention of recurrences of ulcer complications from long-term low-dose aspirin use. N. Engl. J. Med. 2002, 346, 2033−2038. (b) Kaczorowska, K.; Kolarska, Z.; Mitka, K.; Kowalski, P. Oxidation of sulfides to sulfoxides. Part 2: Oxidation by hydrogen peroxide. Tetrahedron 2005, 61, 8315− 8327. (8) (a) Focke, M.; Feld, A.; Lichtenthaler, H. K. Allicin, a naturally occurring antibiotic from garlic, specifically inhibits acetyl-CoA synthetase. FEBS Lett. 1990, 261, 106−108. (b) Pérez-Giraldo, C.; Cruz-Villalón, G.; Sánchez-Silos, R.; Martínez-Rubio, R.; Blanco, M. T.; Gómez-García, A. C. In vitro activity of allicin against Staphylococcus epidermidis and influence of subinhibitory concentrations on biofilm formation. J. Appl. Microbiol. 2003, 95, 709−711. (9) Merino, G.; Molina, A. J.; García, J. L.; Pulido, M. M.; Prieto, J. G.; Alvarez, A. I. Effect of clotrimazole on microsomal metabolism and pharmacokinetics of albendazole. J. Pharm. Pharmacol. 2003, 55, 757− 764. (10) Kotelanski, B.; Grozmann, R. J.; Cohn, J. N. Positive inotropic effect of oral esproquin in normal subjects. Clin. Pharmacol. Ther. 1973, 14, 427−433. (11) Padmanabhan, S.; Lavin, R. C.; Durant, G. J. Asymmetric synthesis of a neuroprotective and orally active N-methyl-D-aspartate receptor ion-channel blocker, CNS 5788. Tetrahedron: Asymmetry 2000, 11, 3455−3457. (12) (a) Baeckvall, J.-E. Selective Oxidation of Amines and Sulfides; Wiley-VCH Verlag GmbH & Co. KGaA, 2010; pp 277−313. (b) Chen, C.-Y.; Zhang, H.; Zhang, L.-X.; Li, L.-D.; Yan, Y.-L. HBr/ t-BuONO catalysts for activation of oxygen to selective aerobic sulfide oxidation. Youji Huaxue 2008, 28, 1978−1981. (c) Souza, F. B.; Stefani, H. A. Synthesis and Functionalization of Vinyl Sulfoxides Halides; American Chemical Society, 2014; p ORGN-203. (d) Wheelock, K. S.; Piccone, L. A. Pharmaceutical compositions containing transition metal sulfoxides prepared from oxidation of thioethers. U.S. Patent 20,070,203,195 A1, 2007. (e) Zhang, H.; Chen, C.; Liu, R.; Xu, Q.; Zhao, W. Transition-metal-free highly efficient aerobic oxidation of sulfides to sulfoxides under mild conditions. Molecules 2010, 15, 83− 92. (f) Zhang, H.; Chen, C.-Y.; Liu, R.-H.; Xu, Q.; Liu, J.-H. DBDMH/ NaNO2 catalyst: Transition-metal-free approach to highly efficient aerobic oxidation of sulfides to sulfoxides. Synth. Commun. 2008, 38, 4445−4451. (g) Baig, N.; Madduluri, V. K.; Sah, A. K. Selective oxidation of organic sulfides to sulfoxides using sugar derived cis-dioxo molybdenum(vi) complexes: kinetic and mechanistic studies. RSC Adv. 2016, 6, 28015−28022. (h) Pitchen, P.; Kagan, H. B. An efficient asymmetric oxidation of sulfides to sulfoxides. Tetrahedron Lett. 1984, 6644

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645

ACS Omega

Article

crystal structures of [Cu(R-salpn)(OH2)] and [Cu(±-busalcx)]. Polyhedron 1998, 17, 4179−4187. (c) Feng, H.-x.; Wang, Y.; Wang, R.-m.; Wang, Y.-p. Study on the properties of catalytic oxidation of zeolite-encapsulated metal Schiff-base complex. Huaxue Shiji 2004, 26, 1−2. (d) Kuźniarska-Biernacka, I.; Biernacki, K.; Magalhães, A. L.; Fonseca, A. M.; Neves, I. C. Catalytic behavior of 1-(2-pyridylazo)-2naphthol transition metal complexes encapsulated in Y zeolite. J. Catal. 2011, 278, 102−110. (e) Maurya, M. R.; Titinchi, S. J. J.; Chand, S. Oxidation of phenol with H2O2 catalyzed by Cu(II), Ni(II) and Zn(II) complexes of N,N′-bis-(salicylidene)diethylenetriamine (H2saldien) encapsulated in Y-zeolite. J. Mol. Catal. A: Chem. 2003, 201, 119−130. (f) Raja, R.; Ratnasamy, P. Catalytic oxidation process for the preparation of cresols from toluene and oxygen. IN 192396 A1, 2004. (g) Srinivas, D.; Sivasanker, S. Biomimetic oxidations using transition metal complexes encapsulated in zeolites. Catal. Surv. Asia 2003, 7, 121−132. (h) Varkey, S. P.; Jacob, C. R. Direct catalytic oxidation of methane to methanol over zeolite encapsulated transition metal complexes. Indian J. Chem., Sect. A: Inorg., Bio-inorg., Phys., Theor. Anal. Chem. 1999, 38, 320−324. (19) (a) Maurya, M. R.; Bisht, M.; Avecilla, F. Synthesis, characterization and catalytic activities of vanadium complexes containing ONN donor ligand derived from 2-aminoethylpyridine. J. Mol. Catal. A: Chem. 2011, 344, 18−27. (b) Maurya, M. R.; Bisht, M.; Chaudhary, N.; Avecilla, F.; Kumar, U.; Hsu, H.-F. Synthesis, structural characterization, encapsulation in zeolite Y and catalytic activity of an oxidovanadium(V) complex with a tribasic pentadentate ligand. Polyhedron 2013, 54, 180−188. (c) Maurya, M. R.; Saini, P.; Haldar, C.; Avecilla, F. Synthesis, characterisation and catalytic activities of manganese(III) complexes of pyridoxal-based ONNO donor tetradenatate ligands. Polyhedron 2012, 31, 710−720. (d) Maurya, M. R.; Saini, P.; Kumar, A.; Costa Pessoa, J. Oxidovanadium(IV) Complexes of Tetradentate Ligands Encapsulated in Zeolite-Y as Catalysts for the Oxidation of Styrene, Cyclohexene and Methyl Phenyl Sulfide. Eur. J. Inorg. Chem. 2011, 4846−4861. (e) Van de Velde, F.; Arends, I. W. C. E.; Sheldon, R. A. Vanadium-catalysed enantioselective sulfoxidations: rational design of biocatalytic and biomimetic systems. Top. Catal. 2000, 13, 259−265. (20) (a) Bania, K. K.; Bharali, D.; Viswanathan, B.; Deka, R. C. Enhanced Catalytic Activity of Zeolite Encapsulated Fe(III)-SchiffBase Complexes for Oxidative Coupling of 2-Napthol. Inorg. Chem. 2012, 51, 1657−1674. (b) Jafarian, M.; Rashvand avei, M.; Khakali, M.; Gobal, F.; Rayati, S.; Mahjani, M. G. DFT and Experimental Study of the Host−Guest Interactions Effect on the Structure, Properties, and Electro-Catalytic Activities of N2O2−Ni(II) Schiff-Base Complexes Incorporated into Zeolite. J. Phys. Chem. C 2012, 116, 18518− 18532. (21) (a) Quayle, W. H.; Peeters, G.; De Roy, G. L.; Vansant, E. F.; Lunsford, J. H. Synthesis and spectroscopic properties of divalent and trivalent tris(2,2′-dipyridine)iron complexes in zeolite Y. Inorg. Chem. 1982, 21, 2226−2231. (b) Quayle, W. H.; Lunsford, J. H. Tris(2,2′bipyridine)ruthenium(III) in zeolite Y: characterization and reduction on exposure to water. Inorg. Chem. 1982, 21, 97−103. (22) (a) Reddy, G. R.; Balasubramanian, S.; Chennakesavulu, K. Zeolite encapsulated Ni(ii) and Cu(ii) complexes with tetradentate N2O2 Schiff base ligand: catalytic activity towards oxidation of benzhydrol and degradation of rhodamine-B. J. Mater. Chem. A 2014, 2, 15598−15610. (b) Silva, A. R.; Martins, M.; Freitas, M. M. A.; Valente, A.; Freire, C.; de Castro, B.; Figueiredo, J. L. Immobilisation of amine-functionalised nickel(II) Schiff base complexes onto activated carbon treated with thionyl chloride. Microporous Mesoporous Mater. 2002, 55, 275−284. (c) Dillard, J. G.; Taylor, L. T. X-Ray photoelectron spectroscopic study of schiff base metal complexes. J. Electron Spectrosc. Relat. Phenom. 1974, 3, 455−460. (d) Matienzo, L. J.; Swartz, W. E.; Grim, S. O. X-ray photoelectron spectroscopy of tetrahedral and square planar nickel(II) compounds. Inorg. Nucl. Chem. Lett. 1972, 8, 1085−1091. (e) Choudhary, A.; Das, B.; Ray, S. Enhanced catalytic activity and magnetization of encapsulated nickel Schiff-base complexes in zeolite-Y: a correlation with the adopted nonplanar geometry. Dalton Trans. 2016, 45, 18967−18976. (f) Vedrine, J.

C.; Dufaux, M.; Naccache, C.; Imelik, B. X-ray photoelectron spectroscopy study of Pd and Pt ions in type Y-zeolite. Electron transfer between metal aggregates and the support as evidenced by Xray photoelectron spectroscopy and electron spin resonance. J. Chem. Soc., Faraday Trans. 1 1978, 74, 440−449. (23) Dutta, B.; Jana, S.; Bera, R.; Saha, P. K.; Koner, S. Immobilization of copper Schiff base complexes in zeolite matrix: Preparation, characterization and catalytic study. Appl. Catal., A 2007, 318, 89−94. (24) (a) Ganesan, R.; Viswanathan, B. Physicochemical and Catalytic Properties of Copper Ethylenediamine Complex Encapsulated in Various Zeolites. J. Phys. Chem. B 2004, 108, 7102−7114. (b) Choudhary, A.; Das, B.; Ray, S. Encapsulation of a Ni salen complex in zeolite Y: an experimental and DFT study. Dalton Trans. 2015, 44, 3753−3763. (25) Choudhary, A.; Das, B.; Ray, S. Enhanced catalytic activity and magnetization of encapsulated nickel Schiff-base complexes in zeoliteY: a correlation with the adopted non-planar geometry. Dalton Trans. 2016, 45, 18967−18976. (26) Deshpande, S.; Srinivas, D.; Ratnasamy, P. EPR and Catalytic Investigation of Cu(Salen) Complexes Encapsulated in Zeolites. J. Catal. 1999, 188, 261−269. (27) Khorshidifard, M.; Rudbari, H. A.; Askari, B.; Sahihi, M.; Farsani, M. R.; Jalilian, F.; Bruno, G. Cobalt(II), copper(II), zinc(II) and palladium(II) Schiff base complexes: Synthesis, characterization and catalytic performance in selective oxidation of sulfides using hydrogen peroxide under solvent-free conditions. Polyhedron 2015, 95, 1−13. (28) (a) Xu, B.; Bordiga, S.; Prins, R.; van Bokhoven, J. A. Effect of framework Si/Al ratio and extra-framework aluminum on the catalytic activity of Y zeolite. Appl. Catal., A 2007, 333, 245−253. (b) Zhang, R.; Li, J.; Wang, B. The effect of Si/Al ratios on the catalytic activity of CuY zeolites for DMC synthesis by oxidative carbonylation of methanol: a theoretical study. RSC Adv. 2013, 3, 12287−12298. (29) (a) Noori, N.; Nikoorazm, M.; Ghorbani-Choghamarani, A. Synthesis and characterization of Co (II) and Fe (III) Schiff base complexes grafted onto mesoporous MCM-41: A heterogeneous and recyclable nanocatalysts for the selective oxidation of sulfides and oxidative coupling of thiols. Phosphorus, Sulfur, Silicon Relat. Elem. 2016, 191, 1388−1395. (b) Coletti, A.; Galloni, P.; Sartorel, A.; Conte, V.; Floris, B. Salophen and salen oxo vanadium complexes as catalysts of sulfides oxidation with H2O2: Mechanistic insights. Catal. Today 2012, 192, 44−55. (30) Bhadbhade, M. M.; Srinivas, D. Effects on molecular association, chelate conformation, and reactivity toward substitution in copper Cu (5-X-salen) complexes, salen2- = N,N′-ethylenebis(salicylidenaminato), X = H, CH3O, and Cl: synthesis, x-ray structures, and EPR investigations. [Erratum to document cited in CA119(26):285036b]. Inorg. Chem. 1993, 32, 6122−6130. (31) Bania, K. K.; Bharali, D.; Viswanathan, B.; Deka, R. C. Enhanced Catalytic Activity of Zeolite Encapsulated Fe(III)-Schiff-Base Complexes for Oxidative Coupling of 2-Napthol. Inorg. Chem. 2012, 51, 1657−1674. (32) Dewan, A.; Bora, U.; Borah, G. A simple and efficient tetradentate Schiff base derived palladium complex for Suzuki− Miyaura reaction in water. Tetrahedron Lett. 2014, 55, 1689−1692.

6645

DOI: 10.1021/acsomega.7b01071 ACS Omega 2017, 2, 6636−6645