Two-photon Microscopy and Spectroscopy Studies to Determine the Mechanism of Copper Oxide Nanoparticle Uptake by Sweetpotato Roots during Post-harvest Treatment Nestor J Bonilla-Bird, Aurelio Paez, Andres M Reyes, Jose A. HernandezViezcas, Chunqiang Li, Jose R Peralta-Videa, and Jorge L. Gardea-Torresdey Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b02794 • Publication Date (Web): 31 Jul 2018 Downloaded from http://pubs.acs.org on August 1, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

Environmental Science & Technology

1 1

Two-photon Microscopy and Spectroscopy Studies to Determine the Mechanism of Copper

2

Oxide Nanoparticle Uptake by Sweetpotato Roots during Post-harvest Treatment

3

Bonilla-Bird, N.J.,† Paez, A.,‡ Reyes, A., ‡ Hernandez-Viezcas, J.A., ║,§ Li, C.,‡ Peralta-Videa, J.R.,

4

†,║,§

Gardea-Torresdey, J.L.†,║,§*

5 6 7

† Environmental Science and Engineering PhD program, The University of Texas at El Paso; 500

8

West University Ave. El Paso, TX 79968 United States

9

║

Department of Chemistry and Biochemistry, The University of Texas at El Paso; 500 West

10

University Ave. El Paso, TX 79968 United States

11

§

12

Texas at El Paso, 500 West University Ave. El Paso, TX 79968 United States

13

‡

14

TX 79968 United States.

15

*Corresponding author: J. Gardea ([email protected]); phone 915 747 5359; fax: 915 747-5748

UC Center for Environmental Implications of nanotechnology (UC CEIN), The University of

Department of Physics, The University of Texas at El Paso, 500 West University Ave. El Paso,

16

17

ACS Paragon Plus Environment


Page 2 of 30

2 18

Abstract

19

The interaction of engineered nanoparticles with plant tissues is still not well understood. There is

20

a lack of information about the effects of curing (post-harvest treatment) and lignin content on

21

copper uptake by sweetpotato roots exposed to copper-based nanopesticides. In this study,

22

Beauregard -14 (lower lignin) and Covington (higher lignin) varieties were exposed to CuO

23

nanoparticles (nCuO), bulk CuO (bCuO), and CuCl2 at 0, 25, 75 and 125 mg/L. Cured and uncured

24

roots were submerged into copper suspensions/solutions for 30 min. Subsequently, root segments

25

were sliced for imaging with a 2-photon microscope, while other root portions were severed into

26

periderm, cortex, perimedulla, and medulla. They were individually digested and analyzed for Cu

27

content by inductively coupled plasma-optical emission spectroscopy (ICP-OES). Microscope

28

images showed higher fluorescence in periderm and cortex of roots exposed to nCuO, compared

29

with bCuO. At 25 mg/L, only bCuO showed higher Cu concentration in the periderm and cortex of

30

Beauregard -14 (2,049 mg/kg and 76 mg/kg before curing; 6,769 mg/kg and 354 mg/kg after

31

curing, respectively) and in cortex of Covington (692 mg/kg before curing and 110 mg/kg after

32

curing) compared with controls (p ≤ 0.05). In medulla, the most internal tissue, only Beauregard-

33

14 exposed to 125 mg bCuO/L showed significantly (p ≤ 0.05) more Cu before curing (17 mg/kg)

34

and after curing (28 mg/kg), compared with control. This research has shown that the 2-photon

35

microscope can be used to determine CuO particles in non-dyed plant tissues. The lack of Cu

36

increase in perimedulla and medulla, even in roots exposed to high CuO concentrations (25 mg/L),

37

suggests that nCuO may represent a good alternative to protect and increase the shelf life of

38

sweetpotato roots, without exposing consumers to excess Cu.

39

Keywords: CuO nanoparticles, ICP-Ms, 2-photon microscope, Periderm, Medulla, Curing, Cu

40

uptake


Page 3 of 30


3 41

INTRODUCTION

42

The literature indicates a rapid increase in the use of nanomaterials (NMs) in agriculture industry.

43

Currently, 9% of the nanoproducts targeted for agri/feed/food application are used in agriculture.1

44

Moreover, there are several NMs in development for application as nanopesticides or

45

nanofertilizers. Nano-compounds of zinc, iron, and copper have been shown to have great potential

46

as nanofertilizers.2 In addition, copper-based NMs, whose global production for 2010 was

47

estimated at 200 tons,3 may have additional applications, since Cu has been approved as a

48

pesticide in organic agriculture.4 The fast development of agriculture-oriented nanoproducts would

49

reduce the amount of Cu used in the production and shelf preservation of several types of produce.

50

So far, several Cu-based nanoparticles (NPs) have been tested to control fungus and bacteria, with

51

promising results. CuO NPs, (nCuO), have proven to be efficacious of controlling coliform

52

bacteria in ultra-filtrated cheese.5 It was also reported that Cu-based NPs are able to control fungi

53

at field level.6 These researchers reported that nCuO, at 150 mg/l (15 g/hl), controlled about 60%

54

of Phytophthora infestans in field grown tomato (Solanum lycopersicum).7

55

Sweetpotato (Ipomoea batatas L. Lam.) ranks seventh in the world in staple food production and

56

fifth in developing countries. The world production is around 105 million tons/year, while the

57

production in the US is around 23.8 billion tons/year.8 Sweetpotato plants have different types of

58

roots including storage, pencil, fibrous, and string roots.9 Storage roots, the edible portion of sweet

59

potato plants, are carefully cured and stored before they are exposed to the market. Curing implies

60

the storage of roots under special temperature and ventilation for three to five days right after

61

harvesting.10 During the curing, the outermost parenchyma cells wounded at harvest desiccate,

62

while the internal parenchyma cells suberize.11 These changes heal wounds and protect the roots

63

from future microbial infections throughout the storage period. Improper handling during a long



Page 4 of 30

4 64

curing period (one to four months)12 may lead to a loss of up to 65% due to a reduction of

65

freshness or fungal infestation. Several fungicides have been used to control sweetpotato fungal

66

root rots, dicloran being the most used. However, foods with dicloran residues are no longer

67

accepted in many markets including infant food, organic, and export.13 Thus, other fungicides,

68

including Cu have been tested.14 However, until now, only ionic Cu has been utilized; thus, new

69

Cu products, including nano forms, may have great potential in preserving the quality of sweet

70

potato roots, before they reach the market.

71

To the authors’ knowledge, only one publication has described the interaction of metal oxide NPs

72

with sweetpotato.15 These researchers cultivated sweetpotato slips in soil amended with either

73

CeO2, CuO, or ZnO NP (100, 500, or 1000 mg/kg of the respective metal) and evaluated treatment

74

effects on storage root production, metal concentration, and possible dietary intake of Ce, Cu, or

75

Zn. The authors reported that the peel retained more Ce than Cu or Zn; 15 however, there is no

76

information about the role of the peel components on the retention mechanism.

77

Confocal microscopy has been used to observe the root uptake of nanoparticles.16 However, this

78

technique requires the staining of non-fluorescent NPs. The Two-photon microscopy (TPM)

79

offers the advantage of observing the uptake of NPs without staining. The capacity of TPM to

80

obtain high depth of field images is greater than that of confocal microscopy. However, this is

81

limited by the thickness of the samples17 because the quality of the image depends on the

82

scattering and the absorption coefficients of the tissue, the type of fluorophore, and the objective

83

lenses.18 CuO NPs may be good candidate to treat sweetpotato roots while they are cured.

84

However, there is a lack of information concerning the penetration of the particles into the edible

85

portion of the roots. It is hypothesized that the peel constitution will affect the retention of the NPs.


Page 5 of 30


5 86

Thus, the aim of this study was to determine the role of peel tissues and the curing process on the

87

retention of CuO NPs and the possible penetration of NPs into the root.

88

Variation in the constitution of sweetpotato root peel may have differential effects on the

89

interaction with metal oxide NPs. Thus, the aim of this study was to determine the role of peel

90

tissues and the curing process on the retention of CuO NPs and the possible penetration of NPs

91

into the root. The roots of two sweetpotato varieties, with different lignin content, were exposed to

92

CuO NPs, bulk CuO, and CuCl2. Subsequently, the samples of roots were screened with a two-

93

photon microscopy and analyzed with inductively coupled plasma- optical emission spectroscopy

94

to determine the retention of CuO and the absorption of Cu. Two-photon microscope has been

95

used to track cell mobility in zebrafish.19 2-photon microscope, combined with nanoparticle-

96

assisted near-infrared has been used for in vivo image of fluorescent nanoparticles in mice ear.20

97

To the authors’ knowledge, this is the first time that a two-photon excited fluorescence and

98

second-harmonic generation (SHG) microscope has been used to image metallic particles into the

99

edible tissue.

100

MATERIAL AND METHODS

101

Characteristics of the Cu products and suspension/solution preparations. Commercial nano

102

CuO (nCuO), bulk copper oxide, (bCuO), and reagent grade salt CuCl2 (Sigma Aldrich, St. Louis,

103

MO) were used in this research. These materials were supplied by the UC Center for

104

Environmental Implications of Nanotechnology. The physicochemical properties of both the nCuO

105

and bCuO were previously determined.21, 22 Table S1 in Supporting Information (SI) shows major

106

physicochemical properties of the particles used in this study. The nCuO had 50 nm, rhombus

107

irregular, hydrodynamic diameter of 280 ± 15 nm and zeta potential of -34.4 ± 0.5 mV. bCuO had

108

particles smaller than 1 µm with diverse morphology, hydrodynamic diameter of 376 ± 26 nm, and



Page 6 of 30

6 109

zeta potential of -42.7 ± 0.153 mV.22 Suspensions/solutions of Cu NP or compounds were prepared

110

at 0, 25, 75, 125 mg/L in Millipore water (MPW) and homogenized by sonication in a water bath

111

(Crest Ultrasonics, Trenton, N) at 25 ºC for 30 min and 180 watts. The 25 mg/L treatment was

112

selected because the average Cu concentration in soil of the United States is 20 mg/kg,23 while 75

113

mg/L was selected to mimic the highest- Cu concentration reported in agricultural soils amended

114

with sewage sludge (75 mg/kg).24 The 125 mg/L treatment represents 83% of the CuO NPs used to

115

control fungi at field level.6, 24

116

Preparation of root samples and Cu treatment applications. Storage roots of Covington and

117

Beauregard-14 sweetpotato varieties varying in peel lignin content were used in this study.

118

Beauregard-14 has 156 g/kg and Covington 178 g/kg lignin in the peel; they are significantly

119

different at p ≤0.05.25 Both varieties were procured from Mississippi State University, Pontotoc

120

Experiment Station. Enough roots of both varieties were separated in two sets, one set was cured

121

and the other one was uncured. For curing, roots were set at 29 ºC and 80% relative humidity for

122

10 days in a growth chamber (Environmental Growth Chamber, Chagrin Falls, OH). Uncured roots

123

were kept in the laboratory at ~24 ºC and 47% relative humidity. At the end of the curing process,

124

uncured and cured roots were individually tied up with a cotton thread and immersed in the Cu

125

suspensions/solutions for 30 min under continuous stirring. The exposure time of 30 min was

126

selected because the treatment period before storing in the curing facility is very short. Roots were

127

kept in the laboratory for 72 h after treatment and processed for microscopy imaging and elemental

128

analyses. Each Cu treatment had three replicates and one root was used as a replicate. Three

129

replicate samples of uncured and cured roots were used as control (no Cu application).

130

Sample preparation for Cu determination. For element determination, roots were washed gently

131

with Millipore water (MPW) to remove the debris adhered to the periderm of the storage roots.


Page 7 of 30


7 132

The washing procedure was also supposed to remove most of the CuO particles adhered to the

133

roots surface. The roots were not washed with acid solution to avoid deterioration of the flesh

134

tissue. After washing, the layers of tissues from each root were pulled apart with a bistouri

135

(scalpel) in the following order: periderm, cortex, perimedulla, and medulla. Each tissue was put in

136

a paper envelop, oven dried at 70 ºC for 72 h, and manually ground using a ceramic mortar and

137

pestle. Dried samples of 0.2 g were acid digested in a block digestion system (DigiPREP MS, SCP

138

Science. Canada) with 3 mL of 30% plasma pure HNO3. Digests were adjusted to 50 mL with

139

MPW and analyzed for Cu content by using an inductively coupled plasma-optical emission

140

spectrometer (ICP-OES, Perkin-Elmer optima 4300 DV, Shelton, CT). To evaluate the digestion

141

and analytical methods, (QC/QA), spiked samples and the standard reference material 1547 from

142

the National Institute of Standards and Technology were treated and analyzed in a similar way as

143

the root samples. The recovery rate was 99%. The detection limit for copper was determined by

144

reading eight replicas of the blank. The mean plus three standard deviations (µ± 3SD) was in the

145

range of 50 µg/L.

146

Sample preparation for microscopy imaging. For microscopy observation with the 2-photon

147

microscope, fresh transversal thin slides from plants exposed to bCuO and nCuO after curing were

148

mounted in water-immersion objective lens (Olympus LUM Plan FLN) and observed in a

149

nonlinear optical microscope, which can detect both 2-photon excited fluorescence. The light

150

source is a femtosecond Ti: Sapphire laser (Spectra-Physics, Mai-Tai HP). Our experiment was set

151

at the Mai Tai at 710 nm, 200 Watts. Its pulse duration was about 100 fs width at a repetition rate

152

of 80 MHz. The wavelength of the laser was tuned from 690 to 1040 nm, with the maximum

153

power up to 2.5 Watts. The fluorescence signal from the sample was deflected with the 665 nm

154

long-pass dichroic mirror. A second long-pass dichroic beam splitter was used to separate the blue



Page 8 of 30

8 155

and green/red fluorescence signal. The blue signal was deflected by dichroic beam splitter and

156

transmitted through a 417-477 nm band-pass filter. The green signal was transmitted through a

157

500-550 nm band-pass filter, while the red signal through a 570-616 nm band-pass filter. The

158

outputs of the three signals were individually detected by photomultiplier tubes set at 0.9V, 2.20V,

159

and 2.10 V for the red, green, and blue channels, respectively. The outputs of these three signals

160

were fed into red/green/blue channels of a frame grabber installed on a computer. The images in X-

161

Y plane were acquired through a home built software program.26 Covington variety was selected

162

because its higher lignin content in periderm could limit the Cu transport to cortex.25

163

Statistics analysis. The analysis of variance (ANOVA) of the interaction between the main factors

164

(curing, varieties, treatments, and root tissues) and the Cu concentrations was performed using

165

univariate analysis (SPSS 19.0 package, Chicago, IL). The Eta-squared (kind of t-test family

166

similar to r2) was used to assign the portion of variation to each one of the factors. The differences

167

between averages of triplicate data per treatment and control was calculated with the Tukey HSD

168

multiple comparisons test. The data presented in tables and figures are means ± the standard error

169

(SE).

170

RESULT AND DISCUSIONS

171

Figure 1 shows a description of the distribution of tissues in the sweetpotato storage root. As seen

172

in this figure, the periderm has three layers of tissues, which contain lignin. Lignin is an organic

173

polymer that increases during the curing process, which has been proven to bind metals.12

174

Microscopy analysis

175

Figure 2 shows 2-photon microscopy images of the control (A) and the CuCl2 treated Covington

176

variety roots (B). The samples were from roots exposed to the CuCl2 after curing. The figures

177

show the periderm in the left part and the cortex in the right part. The autofluorescence shown in


Page 9 of 30


9 178

the control sample is due to the suberization of the cell walls, which gives firmness and resistance

179

to excoriation to the roots.23The insert in Figure 2B shows a lack of fluorescence from the CuCl2

180

solution. Figure 3 shows the 2-photon images of Covington variety roots exposed after curing to

181

75 mg/L nCuO (A) or bCuO (B) as shown in Figure 3A, less fluorescence points were observe in

182

the cortex of nCuO treated roots, compared to bCuO (Figure 3B). The inserts in both figures show

183

the fluorescence of the CuO suspensions. The areas in squares show CuO particles in the cortex

184

tissues. The 2-photon microscope images of nano CuO and bulk CuO treated samples showed

185

differences, compared with control. For instance, the root exposed to 75 mg/L of nCuO (Figure

186

3A) shows fluorescent points inside of the cortex tissue, which is located below the periderm. Cell

187

walls in the periderm show higher bright intensities than the inside cells. In the cortex tissue,

188

fluorescence from several nanoparticles stuck in intercellular spaces were observed (arrow). Due

189

to the fast flash moment of the excitation of the nanoparticles, only a few 2-photon fluorescences

190

were obtained in the image. The internal part of the root cortex (Figure 3A) shows an increase in

191

the number of 2-photon fluorescences from different bulk particles. Images of roots exposed to

192

nCuO at 75 mg/L also showed 2-photon fluorescence (Supporting Information, Figure S1),

193

indicating that these particles also penetrated the tissues, the cortex tissue in (S1-A and S1-B). In

194

addition Figure S1 (C) shows the surface graph to detect the nCuO between the cell walls. The

195

fact that the 2-photon fluorescences were observed between the cells suggests the photochemical

196

decomposition, which occurs when the particles are excited by the laser beam, allows their

197

localization within the root tissues. The molecular constitution of each material has a different

198

reaction when they are impacted by the laser beam, creating varied ranges of fluorescence.27 The

199

signal/noise ratio for nCuO were 26/25, 21/168, and 27/122 for red, green, and blue, respectively.

200

For bCuO were 22/27, 20/181, and 26/122 for red, green and blue, respectively.



Page 10 of 30

10 201

Effect of factors on Cu accumulation in roots. The statistical analysis of Cu concentration in

202

roots showed effects of single factors variety, tissue, and Cu treatments (Table S2, SI). In addition,

203

the double, triple, and quadruple interactions between curing × tissue, curing × variety × Cu

204

treatments, variety × tissue × Cu treatment, and curing × variety × tissue × Cu treatments were also

205

statistically different. The Eta-squared statistics showed that the higher variance was due to the

206

differences between tissues and the interaction tissue × Cu treatment, with 50% and 18%,

207

respectively (p ≤ 0.001). Table S2, SI, shows the Tukey test for the main factors curing, varieties,

208

and tissues. As seen in this table, the curing, as a whole, had no statistical effects; however, there

209

were effects for varieties and tissues. Beauregard-14, the variety with less lignin.25 had lower Cu

210

concentration (720 ± 108 mg/kg), with differences statistically significant at p ≤ 0.05, while

211

Covington, the variety with higher lignin, 25 had 1003 ± 148 mg/kg, with differences statistically

212

significant at p ≤ 0.005. It has been demonstrated that lignin binds metals through ion-exchange.

213

The binding strength of Cu to lignin is one the strongest.28

214

Copper concentration in individual tissues

215

The Cu concentration was analyzed from the outermost tissue, the periderm, to the innermost one,

216

the medulla. Figure 5 shows the Cu concentration in cortex, and Figure S2, SI the periderm of

217

uncured and cured storage roots of variety Beauregard-14. Before curing, at 25 mg/L, only roots

218

exposed to bCuO had significantly more Cu, 2,049 mg/kg in the periderm (the most external

219

layer). While at 75 and 125 mg/L, all treatments showed significantly more Cu. At 125 mg/L, the

220

increases from bCuO and nCuO were 6,105 mg/kg and 2,635 mg/kg. After curing, similar results

221

were observed at 25 mg/L, but not at 75 and 125 mg/L. At 75 mg/L, there was no significant

222

increase in Cu concentration, while at 125 mg/L, bCuO and nCuO showed 5,437 mg/kg and 4,147

223

mg/kg more Cu, respectively, compared with control. It is possible that the small differences in


Page 11 of 30


11 224

hydrodynamic dimeter caused the similarity in Cu accumulation. Hong et al.29 demonstrated that

225

the removal of CeO2 NPs from cucumber leaves washed with water was lower, compared to the

226

washing with CaCl2 or HNO3. As expected, less Cu was found in the cortex, the tissue beneath

227

periderm (Table 1 and Table S3). As shown in Figure 6, variety Covington before curing, Cu

228

concentration in cortex followed a similar trend than in periderm Figure S2. After curing, no

229

effects were observed at 75 mg/L, while at 25 mg/L and 125 mg/L, bCuO increased (354 mg/kg

230

and 144 mg/kg) and nCuO increased (142 mg/kg and 208 mg/kg) Cu in cortex (p ≤ 0.001). The

231

difference in Cu accumulation between uncured and cured roots was attribute to the suberization

232

and lignification of the internal parenchyma cells.11

233

Figure 6 shows data for cortex and Figure S3 shows data for periderm in Covington variety (higher

234

lignin content). As seen in this figure, before curing, exposure to 25 mg/L of the three Cu-based

235

compounds did not increase Cu in periderm, compared with control. While after curing, at 25 mg

236

bCuO/L increased Cu in periderm by 8,311 mg/kg. In addition, before curing, at 75 mg/L, only

237

nCuO increased Cu in periderm (7,803 mg/kg), and 125 mg/L, both bCuO and nCuO showed more

238

Cu in periderm (7,052 mg/kg and 9,235 mg/kg). In cortex, before curing, all the treatments

239

increased Cu. After curing, all bCuO concentrations increased Cu in periderm, and at 25 mg/L and

240

75 mg/L increased Cu in cortex- Figure 7- (110 mg/kg and 126 mg/kg, respectively). On the other

241

hand, at 75 and 125 mg/L, nCuO increased Cu in periderm (4,279 mg/kg and 7,055 mg/kg,

242

respectively) and only at 125 mg/L, increase Cu in cortex (77 mg/kg). CuCl2, at any

243

concentrations, increased Cu in periderm and cortex, before and after curing. The fact that Cu

244

concentration in cortex from particulate compounds were higher than in CuCl2 treatments may be

245

due to both the uptake of aggregates that contain a high proportion of Cu and to the high atomic

246

percentage Cu in the CuO. The lack of Cu increase in uncured roots exposed to 25 mg/L could be



Page 12 of 30

12 247

due to the lower lignin content,11 or the natural Cu accumulation from soil,28 while after curing, the

248

Cu increase was attributed to the increment in lignin, which occurs during the curing process.11

249

There were not much differences in the most internal tissues, perimedulla and medulla (Figures 8

250

and 9). Before curing, the perimedulla of Covington and medulla of Beauregard-14 showed

251

significantly higher Cu concentration, respect to control, in roots exposed to 125 mg/L of bCuO

252

After curing, none of the treatments increased Cu in perimedulla or medulla of both varieties,

253

except bCuO, which at 25 mg/L increased Cu in perimedulla of Beauregard-14 (p ≤ 0.001. The

254

fact that only bCuO showed significantly more Cu in the internal tissues might be a results of the

255

lower dissolution of bCuO, compared with nCuO.30 bCuO aggregates could remain in the tissues

256

resulting in high total Cu concentration. Thus, some of the bCuO particles that penetrated into

257

cortex dissolved, allowing the movement of the Cu ions into deeper tissues. In addition, it is

258

assumed that Cu did not increase in perimedulla and medulla of cured roots because Cu was

259

retained in suberized and lignified external tissues. Kulik et al. demonstrated that lignin in decay of

260

wood strongly bind Cu through the COO- binding group.31,32 Unfortunately, there are no previous

261

reports about the Cu uptake by non-growing plant/tissue exposed to nCuO; thus, it is difficult to

262

make comparisons. The uptake of Cu by the roots of growing plants exposed to nCuO, bCuO, and

263

CuCl2 has shown different results. For instance, Rawat et al.30 reported that the roots of bell pepper

264

cultivated in soil amended with 250 mg/kg of bCuO, nCuO, or CuCl2 had similar Cu

265

concentrations. Conversely, the roots of rice (Oryza sativa L.) plants grown in soil amended with

266

1000 mg/kg of nCuO had significantly more Cu than the roots of plants exposed to the same

267

concentration of bCuO.33 This suggest that the Cu uptake of non-growing tissues cannot be

268

compared with that of growing tissues.


Page 13 of 30


13 269

A comparison between Covington and Beauregard-14 shows some differences in Cu accumulation

270

(Table 1). The data suggests and interaction variety × treatment × tissues (Table S1). In

271

Beauregard-14, the variety with less lignin content (156 g/kg), before curing, all the compounds, at

272

the highest concentration, showed significant Cu concentration in periderm and cortex ,while after

273

curing, at 125 mg/L, both bCuO and nCuO, showed significantly more Cu in periderm and cortex,

274

compared with control. However, in uncured roots of Covington, the variety with higher lignin

275

content (178 g/kg), both bCuO and nCuO, at 125 mg/L, significantly increased Cu in the periderm

276

(p ≤ 0.001), but had no effect in cortex. While in cure roots, the same compounds, at the same

277

concentration, increased Cu in periderm but not in cortex. A comparison of the total Cu

278

contraptions, before and after curing (Table S3), shows that in Beauregard-14, only the periderm

279

showed more Cu after curing than before curing, while converse data was found in cortex,

280

perimedulla and medulla. The difference between uncured and cured roots was statistically

281

significant (p ≤ 0.05) only in medulla (Table S3); the data showed that the difference was caused

282

by bCuO (Figure 6). On the other hand, in Covington, the Cu concentrations in all tissues where

283

higher after curing; however, the differences did not show statistical significance. The data

284

suggest that the curing, lignin content, tissue, and compound influence the Cu uptake in

285

sweetpotato roots. Suberization during curing increases lignin,11 which has shown to bind Cu

286

ions;33 this could explain the reduction of Cu concentration in the ionic treatment. On the other

287

hand, Figures 2-4 show that bCuO and nCuO penetrated the tissues through the apoplast, which

288

explains the Cu increase in roots treated with such compounds.

289 290

CONCLUSIONS

291

This research has shown, for the first time, the use of the 2-photon microscope for the observation

292

of fluorescence from particulate CuO in sweetpotato root tissues. The fluorescence of the particles



Page 14 of 30

14 293

was observed in the periderm and cortex. The data showed that the nCuO and bCuO are able to

294

penetrate the tissues through the fluid uptake into the xylem of the sweetpotato roots. Results also

295

showed that lignin content has a strong effect in retaining the NPs in the exterior layers. As a

296

whole, the curing process seems to have no effect in the absorption of the copper products and the

297

copper content in internal tissues, except for bCuO treatment that at 25 mg/L caused and effect in

298

Beauregard-14, the variety with less lignin content. The Cu concentration in internal tissues of

299

roots treated with nCuO was similar than control roots, which suggests there should be no risk of

300

Cu contamination in peeled roots. This also suggests that CuO nanoparticles may be used as an

301

alternative to preserve and increase the shelf life of sweetpotato roots before they reach the market,

302

without an overload of the copper content.

303


Page 15 of 30


15 304

ACKNOWLEDGEMENTS

305

This material is based upon work supported by the National Science Foundation and the

306

Environmental Protection Agency under Cooperative Agreement Number DBI-1266377. Any

307

opinions, findings, and conclusions or recommendations expressed in this material are those of the

308

author(s) and do not necessarily reflect the views of the National Science Foundation or the

309

Environmental Protection Agency. This work has not been subjected to EPA review and no official

310

endorsement should be inferred. Authors also acknowledge the USDA grant 2016-67021-24985

311

and the NSF Grants EEC-1449500, CHE-0840525 and DBI-1429708. Partial funding was

312

provided by the NSF ERC on Nanotechnology-Enabled Water Treatment (EEC-1449500). This

313

work was also supported by the grant 2G12MD007592 from the National Institutes on Minority

314

Health and Health Disparities (NIMHD), a component of the National Institutes of Health (NIH)

315

and by the grant 1000001931 from the ConTex program. J.L. Gardea-Torresdey acknowledges the

316

Dudley family for the Endowed Research Professorship, the Academy of Applied Science/US

317

Army Research Office, Research and Engineering Apprenticeship program (REAP) at UTEP, grant

318

no. W11NF-10-2-0076, sub-grant 13-7, and the LERR and STARs programs of the University of

319

Texas System.

320 321

Supporting Information

322 323 324 325 326

The Supporting Information is available free of charge on the ACS Publications website. Two-photon microscopy images of the Covington variety root; copper concentration in periderm; Major physicochemical properties of the particles used in this study; tables of ANOVA

327 328



Page 16 of 30

16 329 330 331

References

332 333 334

1.

Iavicoli, I.; Leso, V.; Beezhold,; D.H. Shvedova, A. Nanotechnology in Agriculture: Opportunities, Toxicological Implications, and Occupational Risks. Toxicol. Appl. Pharmacol. 329, 96–111 (2017).

335 336 337

2.

Monreal, C. M.; Derosa, M.; Mallubhotla, S. C.; Bindraban, P. S.; Dimkpa, C. Nanotechnologies for Increasing the Crop use Efficiency of Fertilizer-Micronutrients. Biol. Fertil. Soils 52, 423–437 (2016).

338 339

3.

Keller, A.A.; McFerran, S.; Lazareva, A.; Suh, S. Global life cycle releases of engineered nanomaterials. J. Nanopart. Res. 15:1692. http://dx.doi.org/10.1007/s11051-0131692-4. (2013)

340 341 342 343

4.

Cabús, A.; Pellini, M.; Zanzotti, R.; Devigili, L.; Maines, R.; Giovannini, O.; Mattedi, L. Mescalchin, E. Efficacy of reduced copper dosages against Plasmopara viticola in organic agriculture. Crop Prot. 96, 103–108 (2017).

344 345 346

5.

Dizaj, S.; Lotfipour, F.; Barzegar-Jalali, M.; Zarrintan, M;. Adibkia, K. Antimicrobial Activity of the Metals and Metal Oxide Nanoparticles. Mater. Sci. Eng. C 44, 278–284 (2014).

347 348 349

6.

Giannousi, K.; Pantazaki, A.; Dendrinou-Samara, C. Copper-Based Nanoparticles as Antimicrobials. Nanostructures Antimicrob. Ther. 515–529 (2017). doi:10.1016/B978-0323-46152-8.00023-8

350 351 352

7.

Giannousi, K.; Avramidis, I.; Dendrinou-Samara, C. Synthesis, Characterization and Evaluation of Copper Based Nanoparticles as Agrochemicals Against Phytophthora Infestans. RSC Adv. 3, 21743 (2013).

353

8.

FAO. FAOSTAT CROPS. (2016). Available at: http://www.fao.org/faostat/en/#data/QC.

354 355

9.

Huaman, Z. Systematic Botany and Morphology of the Sweetpotato Plant. TechnicalInformation-Bulletin---International-Potato-Center 1–22 (1992).

356 357

10.

Edmunds, B.; Boyette, M.; Clark, C.; Ferrin, D.; Smith, T.; Holmes, G. Postharvest Handling of Sweetpotatoes. (2003). doi:8/08—5M—VB

358 359

11.

Walter, W.E. Jr.; Schadel, W. E. Structure and Composition of Normal Skin (Periderm) and Wound Tissue from Cured Sweet Potatoes. J Am. Soc. Hort. Sci. 108, 909–914 (1983).

360 361

12.

Ray, R. C.; Ravi, V. Post harvest spoilage of sweetpotato in tropics and control measures. Crit. Rev. Food Sci. Nutr. 45, 623–644 (2005).

362 363 364

13.

Edmunds, B. A.; Holmes, G. J. Evaluation of Alternative Decay Control Products for Control of Postharvest Rhizopus Soft Rot of Sweetpotatoes. Plant Health Progress. (2009). doi:10.1094/PHP-2009-0206-01-RS.


Page 17 of 30


17 365 366

14.

Eckert, J. W.; Ogawa, J. M. Chemical Control of Posharvest Diseases : Deciduous Fruits , Berries , Vegetables and Root / Tuber Crops. Annu. Rev. Phytopathol. 26, 433–469 (1988).

367 368 369

15.

Bradfield, S. J.; Kumar, P..; White, J. C.; Ebbs, S. D. Zinc, Copper, or Cerium Accumulation from Metal Oxide Nanoparticles or Ions in Sweet Potato: Yield Effects and Projected Dietary Intake From Consumption. Plant Physiol. Biochem. 110, 128–137 (2017).

370 371 372 373

16.

Zhao, L.; Peralta-Videa, J. R.; Varela-Ramirez, A.; Castillo-Michel, H.; Li, C.; Zhang, J.;Aguilera, R.J.; Keller, A. . & Gardea-Torresdey, J. L. Effect of surface coating and organic matter on the uptake of CeO2 NPs by corn plants grown in soil: Insight into the uptake mechanism. J. Hazard. Mater. 225–226, 131–8 (2012).

374 375

17.

Feijó, J.A.; Moreno, N. Imaging Plant Cells by Two-photon Excitation. Protoplasma 223, 1–32 (2004).

376 377 378

18.

So, P.T.C; Kim, D. An optical design primer for not linear optical microscope. In Masters, B.R.; So, P.T.C. Handbook of Biomedical Nonlinear Optical Microscopy, Oxford University Press, 2008.

379 380 381 382

19.

Olivier, N.; Luengo-oroz, M. A.; Duloquin, L.; Faure, E.; Savy, T.; Veilleux, I.; Solinas, X.; Débarre, D.; Bourgine, P.; Santos, A.; Peyriéras, N.; Beaurepaire, E. Cell Lineage Reconstruction of Early Zebrafish Embryos Using Label-Free Nonlinear Microscopy. Science (80-. ). 70, 967–971 (2010).

383 384 385 386

20.

Alifu, N.; Yan, L.; Zhang, H.;Zebibula, A.; Zhu, Z.; Xi, W.; Roe, A.W.; Xu, B.; Tian, W.;Qian, J. Organic dye doped nanoparticles with NIR emission and biocompatibility for ultra-deep in vivo two-photon microscopy under 1040 nm femtosecond excitation. Dye. Pigment. 143, 76–85 (2017).

387 388 389

21.

Adeleye, A. S.; Conway, J. R.; Perez, T.; Rutten, P.; Keller, A. Influence of Extracellular Polymeric Substances on the Long-term Fate, Dissolution, and Speciation of Copper-based Nanoparticles. Environ. Sci. Technol. 48, 12561–12568 (2014).

390 391 392 393

22.

Hong, J.; Rico, C.; Zhao, L.; Adeleye, A.; Keller, A.; Peralta-Videa, J.R.; GardeaTorresdey, J. L. Toxic Effects of Copper-based Nanoparticles or Compounds to Lettuce (Lactuca sativa) and Alfalfa (Medicago sativa). Env. Sci Process Impacts 23, 177–185 (2015).

394 395 396

23.

Shacklette, H.T.; Boerngen, J. G. Element concentrations in soils and other surfical materials of the conterminous United States. U.S. Geol. Surv. Prof. Pap. 1270 I, 1–63 (1984).

397

24.

EPA (US Environmental protection Agency). Land Application of Sewage Sludge. (1994).

398 399

25.

Bonilla-Bird, N. J. Morphological and Physiological Characterization of Sweetpotato Roots After Skinning. (PhD Dissertation, Mississippi State University). 1, 1–86 (2015).

400 401 402

26.

Acosta, Y.; Zhang, Q.; Rahaman, A.; Ouellet, H.; Xiao, C.; Sun, J.; Li, C. . Imaging cytosolic translocation of Mycobacteria with two-photon fluorescence resonance energy transfer microscopy. Biomed. Opt. Express 5, 3990 (2014).

403 404

27.

Gerritsen, H. C.; De Grauw, C. J. Imaging of Optically Thick Specimen Using Two-photon Excitation Microscopy. Microsc. Res. Tech. 47, 206–209 (1999).

405

28.

Crist, R.H.;Martin, J.R.; Crist, D. R. Heavy metal uptake by lignin: Comparison of biotic



Page 18 of 30

18

ligand models with an ion-exchange process. Environ. Sci. Technol. 36, 1485–1490 (2002).

406 407 408 409 410

29.

Hong, J..;Peralta-Videa, J. R.;Rico, C.;Sahi, S.;Viveros, M. N.; Bartonjo, J.;Zhao, L.;Gardea-Torresdey, J. L. Evidence of translocation and physiological impacts of foliar applied CeO2 nanoparticles on cucumber (Cucumis sativus) plants. Environ. Sci. Technol. 48, 4376–4385 (2014).

411 412 413 414

30.

Rawat, S.;Pullagurala, V.L.R.; Hernandez-Molina, M.; Sun, Y.;Niu, Genhua.;HernandezViezcas, J. A.;Peralta-Videa, J. R.;Gardea-Torresdey, J. L. Impacts of Copper Oxide Nanoparticles on Bell Pepper ( Capsicum annum L.) Plants: a Full Life Cycle Study. Environ. Sci. Nano 5, 83–95 (2018).

415 416

31.

Kulik, F.; Wieber, J.; Pethica, B.; Zuman, P. Binding of Cu(II) and Zinc(II) ions on various lignins. J. Electroanal. Chem., 214 (1986) 331-342.

417 418

32.

Thevenot, M.; Dignac, M.F.;Rumpel, C. Fate of Lignins in Soils: A Review. Soil Biol. Biochem. 42, 1200–1211 (2010).

419 420 421

33.

Peng, C.;Xu, C.;Liu, Q.;Sun, L.;Luo, Y.;Shi, J. Fate and Transformation of CuO Nanoparticles in the Soil-Rice System during the Life Cycle of Rice Plants. Environ. Sci. Technol. 51, 4907–4917 (2017).

422 423 424 425


Page 19 of 30


19 426

Figure legends

427 428 429 430 431 432 433 434 435 436 437 438 439 440 441 442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458 459 460 461 462 463 464 465 466 467 468 469

Figure 1. The positions of the tissues as seen in transverse section on sweetpotato storage root. The outermost the periderm, followed by cortex, perimedulla, and medulla or edible part. Figure 2. (A) Two-photon microscopy image of control root of the Covington variety showing the fluorescence of lignin in cell walls of periderm. The arrows are pointing the cell structures in the periderm and cortex. The opaque segment correspond to the cortex. (B) Two-photon microscopy image of the Covington variety root exposed after curing to 75 mg/L of copper chloride. The insert picture corresponds to the copper chloride solution in DI water. There was no fluorescent points. The signals were obtained at a wavelength of 710 nm and a power of 200 mW. Figure 3. (A). Two-photon microscopy image of the Covington variety root exposed to 75 mg/L of CuO nanoparticles showing the fluorescence of lignin in the periderm. The arrows are pointing out the fluorescence from the CuO nanoparticles inside the square in cortex. The insert corresponds to the nCuO suspension in DI water, the fluorescence is from the nCuO particles (B) 2-photon microscopy image of the Covington variety root exposed to 75 mg/L of bCuO showing the fluorescence of lignin in the periderm and the fluorescence of the bCuO particles. The arrow is pointing out the fluorescence from bCuO particles inside the square in cortex. The insert corresponds to the bCuO suspension in DI water, the fluorescence is from the bCuO particles. The fluorescence signals were obtained at a wavelength of 710 nm and a power of 200 mW. Figure 4. (A) Two-photon microscopy image of the Covington variety root exposed to 75 mg/L of nCuO particles showing the fluorescence (square) of the nCuO particles in the cortex tissue. The particles are located between the intercellular spaces (B) Image of the Covington variety root exposed to 75 mg/L of bCuO (square) of the bCuO particles inside of the vascular tissue. The square shows the bCuO particles between the cells walls. The signals were obtained at a wavelength of 710 nm and a power of 200 mW. Figure 5. Copper concentration (mg/kg dwt) in cortex of the Beauregard-14 roots exposed to nCuO, bCuO, and CuCl2 at 0, 25, 75, and 125 mg/L, before and after curing. Data are average of three replicates ± SE. Different letters stand for statistical differences at p ≤ 0.05, (n = 3). Figure 6. Copper concentration (mg/kg dwt) in cortex of the Covington roots exposed to nCuO, bCuO, and CuCl2 at 0, 25, 75, and 125 mg/L, before and after curing. Data are average of three replicates ± SE. Different letters stand for statistical differences at p ≤ 0.05, (n = 3); (ns) stands for not significant. Figure 7. Copper concentration (mg/kg dwt) in perimedulla and medulla of the Beauregard-14 roots exposed to nCuO, bCuO, and CuCl2 at 0, 25, 75, and 125 mg/L, before and after curing. Data are average of three replicates ± SE. Different letters stand for statistical differences at p ≤ 0.05, (n = 3); (ns) stands for not significant. Figure 8. Copper concentration (mg/kg dwt) in perimedulla and medulla of the Covington roots exposed to nCuO, bCuO, and CuCl2 at 0, 25, 75, and 125 mg/L, before and after curing. Data are



Page 20 of 30

20 470 471 472

average of three replicates ± SE. Different letters stand for statistical differences at p ≤ 0.05, (n = 3); (ns) stands for not significant.

473 474 475 476 477 478 479 480 481 482 483 484 485 486 487 488 489 490


Page 21 of 30


21 491 492

Table 1. Tukey HSD – Post Hoc test for the main factors. The sweetpotato roots were exposed to nCuO, bCuO, and CuCl2 at 0, 25, 75, and 125 mg/L.

493

Factors 1. Curing Before curing After curing

494

Copper concentration (mg/kg) 841 ± 176 882 ± 186

2.Variety Beauregard-14 Covington

720 ± 108* 1003± 148**

3.Tissues Perimederm Cortex Perimedulla Medulla

3,326 ± 261*** 99.0 ±18** 15.0±2** 6.3±1**

*significant at p