Membrane distillation biofouling: Impact of feed water temperature on

Aug 6, 2018 - Membrane distillation (MD) is a temperature driven membrane separation technology that holds great potential for decentralized and ...
0 downloads 0 Views 3MB Size
Subscriber access provided by University of Sussex Library

Sustainability Engineering and Green Chemistry

Membrane distillation biofouling: Impact of feed water temperature on biofilm characteristics and membrane performance Anne Bogler, and Edo Bar-Zeev Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b02744 • Publication Date (Web): 06 Aug 2018 Downloaded from http://pubs.acs.org on August 7, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 35

Environmental Science & Technology

1

Membrane distillation biofouling: Impact of feed water temperature

2

on biofilm characteristics and membrane performance

3

Anne Bogler* and Edo Bar-Zeev*

4

Zuckerberg Institute for Water Research, The Jacob Blaustein Institutes for Desert

5

Research, Ben-Gurion University of the Negev, Sede Boker, 84990, Israel

6

* Corresponding Author: Dr. Edo Bar-Zeev; [email protected], Anne Bogler;

7

[email protected]

8

Key words

9

Membrane distillation, feed water temperature, wetting, biofouling, biofilm characteristics

10

ABSTRACT

11

Membrane distillation (MD) is a temperature driven membrane separation technology

12

that holds great potential for decentralized and sustainable wastewater treatment

13

systems. Yet, similarly to all membrane based systems, microbial fouling (biofouling)

14

might be a critical hurdle for MD wastewater treatment applications. In this study we

15

determined the impact of increasing feed water temperatures (47 °C, 55 °C and 65 °C)

16

on biofilm growth and MD performance via dynamic biofouling experiments with

17

Anoxybacillus sp. as a model bacterium. Our results indicated that cell growth was

18

reduced at 47 °C, resulting in moderate distillate water flux decline (30%). Differently,

19

extensive growth of Anoxybacillus sp. at feed water temperature of 55 °C caused severe

20

distillate water flux decline (78%). Additionally, biofouling induced membrane wetting,

1 ACS Paragon Plus Environment

Environmental Science & Technology

21

which facilitated the passage of bacteria cells and endospores through the membrane

22

structure into the distillate. Although bacteria growth was impaired at feed water

23

temperature of 65 °C, excessive production of EPS (compared to bacterial abundance)

24

crippled membrane separation due to severe pore wetting. These results underline the

25

importance of optimized operating conditions and development of anti-biofouling and

26

anti-wetting membranes for successful implementation of MD in wastewater treatment

27

with high biofouling propensity.

28

GRAPHICAL ABSTRACT

29 30

INTRODUCTION

31

Membrane distillation (MD) is a promising technology for sustainable fresh water

32

production, due to the possibility of utilizing waste heat or low-grade solar and

33

geothermal heat for separation of high quality fresh water from contaminated feed

34

solutions.1–3 Distillate water flux is driven by a water vapor pressure gradient across a

35

water-excluding microporous hydrophobic membrane.4,5 Air-filled membrane pores only

36

allow the passage of vapors that evaporate from the heated feed water and condense 2 ACS Paragon Plus Environment

Page 2 of 35

Page 3 of 35

Environmental Science & Technology

37

into the cold distillate. Therefore, all non-volatile contaminants are rejected at the vapor-

38

liquid interface.1,4 MD operates at ambient hydraulic pressure, which reduces system

39

complexity and facilitates the application of MD in decentralized wastewater treatment

40

systems.2,3,6 Such MD systems may be powered by an unlimited supply of solar energy,

41

thus provide remote communities that are not connected to the national water and

42

energy grids with potable water and reduce critical water scarcity.

43

Similarly to all membrane systems, treatment of contaminated feed water via MD

44

induces the challenge of fouling and especially microbial fouling (herein termed

45

biofouling).3,7,8 Biofouling develops as bacteria and organic material, ubiquitous in natural

46

and engineered systems, form biofilms on membrane and spacer surfaces.9–11 Biofilm

47

formation follows a phased paradigm, in which individual cells or planktonic bacterial

48

clusters (protobiofilms) adhere to an organic conditioning film.12 Following irreversible

49

attachment, bacteria and protobiofilms develop into a multi-layered biofilm structure,

50

comprising live and dead cells encased in a protective matrix of self-produced

51

extracellular polymeric substances (EPS).11,13 Despite substantial research on

52

membrane biofouling, very little is known about biofilm formation and community

53

composition in MD systems.14,15 In addition to factors that influence biofilm formation in

54

other membrane systems, the elevated feed water temperature is unique to MD.8,14,16

55

Feed water temperature of MD systems can range between 40 °C to 80 °C,3,17 leading to

56

a shift in bacterial community composition due to thermally induced succession, after

57

which thermophilic and heat resistant bacteria will constitute the majority of the bacteria

58

population.14,15,18,19

59

MD biofilm can reduce the vapor pressure driving force by hindering mass and heat

60

transport, consequently enhancing temperature and salt concentration at the membrane

61

surface.15,20,21 The hydrophilic nanoporous structure of the biofilm can further affect the 3 ACS Paragon Plus Environment

Environmental Science & Technology

62

driving force via water vapor pressure depression.21,22 Concomitantly, depending on the

63

biofilm properties (i.e., thickness, density, organic composition, etc.), hydraulic

64

resistance can also impair water transfer through the biofilm.21,23 Another fouling effect,

65

that is unique to MD, is membrane wetting, which refers to the penetration of

66

contaminated feed water through the pore structure into the distillate.15,24,25 Among other

67

mechanisms, wetting can be caused by a reduction of membrane surface hydrophobicity

68

via attachment of surface active compounds in the feed water.15,20,24 Some surface

69

active compounds, termed biosurfactants, can be actively secreted to the feed water as

70

amphiphilic EPS components by bacteria.15,25

71

In this study we identified the effects of feed water temperature on MD biofouling with a

72

monoculture of a thermophilic Anoxybacillus sp. at three feed water temperatures (47

73

°C, 55 °C and 65 °C) in a direct contact MD system containing feed and distillate

74

spacers. System performance was analyzed in real time over three days via distillate

75

water flux and distillate water quality measurements. In addition, biofilm properties were

76

characterized at the end of each experiment. Our results highlight that selection of the

77

appropriate feed water temperature is crucial for the success of MD application in

78

wastewater treatment.

79

MATERIALS AND METHODS

80

Bench-scale MD system. A custom-made bench-scale direct contact MD system with a

81

transparent polycarbonate cross flow cell was used for dynamic biofouling experiments

82

(Figures S1 and S2). Feed and distillate temperature were controlled by a recirculating

83

heater (Polyscience) and chiller (KNF Lab). Flow conditions were held constant using

84

two gear pumps with Masterflex® pump heads (Cole-Parmer). Distillate water flux was

85

monitored by weighing the distillate solution on a digital scale (Phoenix instrument)

86

interfaced with a data acquisition system. Additionally, values of feed (Sensorex) and 4 ACS Paragon Plus Environment

Page 4 of 35

Page 5 of 35

Environmental Science & Technology

87

distillate conductivity (Eutech Instruments, Thermo Scientific) as well as temperature

88

(DS18B20 Digital Temp Sensor, Adafruit) in the reservoirs and at in-/outlets of the cross

89

flow cell were collected every minute via a microprocessor (Arduino UNO). Further

90

details and experimental parameters are available in the Supporting Information.

91

Hydrophobic Durapore® membranes with nominal pore size 0.45 µm (HVHP, Merck

92

Millipore, Ireland) were used as MD membranes. The active membrane area in the cross

93

flow cell was 6.5 x 3.5 cm2 and spacers (46 mils = 1.2 mm, Conwed®, USA) determined

94

channel height on feed and distillate side. The spacer had a diamond shaped pattern

95

comprised of slightly hydrophobic (contact angel of ~94°) polypropylene filaments,

96

molded together in two layers. Filaments were oriented at a 45° angle towards the flow

97

direction (Figure S1, insert).

98

Bacteria strain and feed water medium. Thermophilic, Gram-positive, spore forming

99

Anoxybacillus sp. was isolated from effluent of an operational wastewater membrane

100

bioreactor (MBR). An MD biofouling experiment (see details below) was carried out with

101

effluent from the MBR for one day at a feed water temperature of 55 °C. Bacteria were

102

removed from the biofouled MD membrane with mild sonication and plated on Luria–

103

Bertani broth agar (LB, Becton, Dickinson and Company). Single colonies were isolated,

104

grown overnight (~12h) in LB and plated again. Isolation process was repeated three

105

times before genomic DNA was extracted from sub-samples using a phenol chloroform

106

approach.14 Amplification of the V1–V3 regions of the bacterial 16S rRNA was achieved

107

with a 28F and 519R primer pair 26 and the bacterium strain was identified by sanger-

108

sequencing (Hy-labs, Israel), with high confidence (99% similarity to the Silva database)

109

as an Anoxybacillus sp. (and most likely Anoxybacillus gonensis).

5 ACS Paragon Plus Environment

Environmental Science & Technology

110

Artificial sterile wastewater medium was prepared fresh for each experiment according

111

to Bar-Zeev et al. 2014,27 comprising 8.0 mM NaCl, 0.15 mM MgSO4, 0.50 mM NaHCO3,

112

0.20 mM CaCl2, 0.20 mM KH2PO4, 0.40 mM NH4Cl, and 0.6 mM Na3C6H5O7 (sodium

113

citrate). Each salt was dissolved in 60 mL double distilled water (DDW), individually

114

autoclaved and then added to sterile DDW (10 L). The resulting feed water medium had

115

a conductivity of 1 mS cm-1 and pH 7.

116

Biofouling procedure. Prior to each experiment, the MD system was thoroughly

117

cleaned in three steps by passing 10% bleach, Ethylenediaminetetraacetic acid solution

118

(EDTA, 5 mM) at pH 9 and 90% ethanol through the system for 30 min each. Between

119

steps, the system was rinsed twice for 5 min with DDW. Finally, the system was

120

thoroughly rinsed five times with DDW to remove any traces of the cleaning agents

121

before the membrane and spacers were inserted into the cross flow cell.

122

Initially, baseline (control) experiments were carried out for three days with artificial

123

sterile wastewater (10 L) as feed water and without bacterial inoculation to determine the

124

distillate water flux and salt passage at the different temperatures. Distillate temperature

125

was adjusted to reach the same initial distillate water flux of 23 ± 2 L m-2 h-1 for all three

126

feed water temperatures (further details on the operating parameters are provided in

127

Table S1). Every 24 h, collected distillate water was removed from the distillate

128

reservoir.

129

For each biofouling experiment a fresh and concentrated bacterial suspension was

130

prepared by inoculating 300 mL of LB broth with Anoxybacillus sp. and letting it grow

131

overnight to a mid-exponential stage (OD600 of ~0.5). Supernatant was removed and

132

replaced with sterile artificial wastewater after short centrifugation (4000 rpm for 20 min).

133

The feed reservoir was inoculated with the bacteria culture (~7x107 cells mL-1) once the

6 ACS Paragon Plus Environment

Page 6 of 35

Page 7 of 35

Environmental Science & Technology

134

initial distillate water flux was stable at 23 ± 2 L m-2 h-1. The feed water was constantly

135

aerated by a small air pump and sampled every 24 h to monitor pH and bacterial

136

concentration. At the same time, glucose (Sigma-Aldrich) was supplemented as an

137

additional carbon source to maintain a constant concentration of ~0.55 mM.

138

Real time observation with optical coherence tomography. OCT is an approach that

139

has recently gained importance for in situ non-invasive fouling observation in membrane

140

systems 28–30 and was used in this study to characterize biofilm formation and membrane

141

wetting. The scan lens (Thorlabs, LSM03-BB) fitted on a spectral domain Optical

142

Coherence Tomograph (Ganymede-II, Thorlabs, Germany) was placed above the cross

143

flow cell to allow observation through the viewing window of the top cell half. Cross

144

sectional scans were taken every 24 h between spacer filament crossings and along

145

filaments with a resolution of 2 µm/pixel. Sensitivity of image acquisition was set to

146

medium at an A-scan rate of 15 kHz with averaging over six A-scans.

147

Biofilm characterization. After three days of biofouling membrane and feed spacer

148

were removed from the cross flow cell, avoiding separation or shifting, and dissected into

149

1 cm2 coupons for subsequent analysis.27,31

150

Confocal laser scanning microscopy (CLSM). Imaging was carried out directly at the end

151

of each experiment. SYTO® 9, propidium iodide (LIVE/DEAD BacLight™, molecular

152

probes) and concanavalin A (Alexa Fluor® 633, molecular probes) were used to stain

153

membrane and spacer coupons for identification of live cells, dead cells and extracellular

154

polysaccharides as part of biofilm EPS. Stained coupons were mounted in an

155

unconfined biofilm characterization chamber 27 for image acquisition with an inverted

156

CLSM (LSM 510 META, Carl Zeiss, Inc.). Random Z stacks (7 to 14) with slice thickness

157

of 2 µm were captured for each membrane coupon using an LD C-Apochromat 40x

7 ACS Paragon Plus Environment

Environmental Science & Technology

158

magnification objective. Images were analyzed to obtain biovolume and biofilm thickness

159

of the three biofilm components. For spacer samples, a Plan-Neofluar 10x magnification

160

objective was used to capture CLSM images with 50 µm slice thickness at and between

161

each filament crossing. The resulting eight adjacent images were combined into one

162

image showing one square spacer element. Further details can be found in the

163

Supporting Information.

164

Bacterial abundance (BA). At the end of each experiment membrane and spacer

165

subsamples were re-suspended in 1 mL of sterile wastewater with 2.5 mM EDTA. Cells

166

were removed from samples by short (6 min) bath sonication and were diluted with

167

sterile wastewater. Dilutions were stained according to the manual with LIVE/DEAD™

168

BacLight™ Bacterial Viability and Counting Kit (molecular probes). BA in the distillate

169

was measured by staining with SYBR® Green II RNA gel stain (molecular probes) for

170

total bacteria count. All stained samples were measured at a flow speed of 25 µL min-1

171

using an Attune NxT flow cytometer (life technologies). Representative flow-cytometry

172

plots that exhibit the distinction between live and dead cells as well as total bacteria

173

count can be found in the Supporting Information (Figure S3).

174

Total organic carbon (TOC). Measurements were obtained from membrane and spacer

175

samples placed in acid-cleaned glass vials with 7 mL DDW and 40 µL 2 M HCl. Probe

176

sonication (Sonicator Model CL-188, QSONICA) for 3 min (six 30 s cycles) was required

177

to disperse cells from membrane and spacer surface. A TOC analyzer (Multi N/C,

178

Analytik-Jena, Germany) measured TOC using a five point calibration procedure.

179

Biofilm density. Organic carbon density was calculated by dividing TOC per area by total

180

biovolume per area obtained from the biofilm components in CLSM and is given in fg

8 ACS Paragon Plus Environment

Page 8 of 35

Page 9 of 35

Environmental Science & Technology

181

µm-3. Additionally, cell density was calculated by dividing BA per area by total biovolume

182

per area, given in cells µm-3.

183

Transmission (TEM) and scanning (SEM) electron microscopy. Samples were fixed,

184

stained and imaged according to Bar-Zeev et al. 2015 32. Briefly, membrane and spacer

185

coupons were fixed at 4 °C overnight with 2.5% glutaraldehyde fixation buffer (0.1 M

186

Cacodylate, 0.1% CaCl2, pH 7.2). Staining of bacterial cells was done with osmium

187

tetroxide followed by sequential dehydration steps. For TEM, membrane samples were

188

then infiltrated with epoxy resin at room temperature and cut into 70 nm slices before

189

imaging with an FEI Tecnai T12 G2 TWIN transmission electron microscope operating at

190

120 kV. For SEM, membrane samples after dehydration were freeze-fractured and then

191

both membrane and spacer samples were sputter coated with gold and imaged with an

192

JSM-7400F (JEOL) ultrahigh resolution cold FEG-SEM at an acceleration voltage of 3

193

KeV. Further details are available in the Supporting Information.

194

Statistical analysis. Distillate water flux values collected every minute were aggregated

195

into 4 h rolling averages. Averages were normalized to the last hour before inoculation,

196

as well as to the corresponding hour of two averaged baseline experiments (Figure S4).

197

Distillate salinity was averaged in the same manner, but normalized to the initial salinity

198

of the distillate, equaling DDW. TOC and BA were displayed as means with

199

corresponding standard deviations, obtained from three or four biologically different

200

experiments. Biofilm parameters were normalized to the area of membrane or spacer

201

coupon, measured with ImageJ software. The spacer area was measured as the area

202

covered and not the surface area of the spacer filaments, which the supplier estimated

203

to be 0.98 m2 m-2. Statistical analysis was conducted in Excel with the XLSTAT Add-In

204

using ANOVA pairwise comparison at a significance level of p