Metal-Organic Framework-Derived Nickel-Cobalt Sulfide on Ultrathin Mxene Nanosheet for Electrocatalytic Oxygen Evolution Haiyuan Zou, Bowen He, Panyong Kuang, Jiaguo Yu, and Ke Fan ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b06272 • Publication Date (Web): 11 Jun 2018 Downloaded from http://pubs.acs.org on June 11, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Metal-Organic Framework-Derived Nickel-Cobalt Sulfide on Ultrathin Mxene Nanosheet for Electrocatalytic Oxygen Evolution ＊＊ Haiyuan Zou,† Bowen He,† Panyong Kuang,† Jiaguo Yu,*,†,§ Ke Fan*,†

†

State Key Laboratory of Advanced Technology for Materials Synthesis and

Processing, Wuhan University of Technology, Wuhan 430070, P. R. China §

Department of Physics, Faculty of Science, King Abdulaziz University, Jeddah 21589, Saudi Arabia

＊These authors contributed equally.

ABSTRACT: Water oxidation is the key process for many sustainable energy technologies containing artificial photosynthesis and metal-air batteries. Engineering inexpensive yet active electrocatalysts for water oxidation is mandatory for the costeffective generation of solar fuels. Herein, we propose a novel hierarchical porous NiCo mixed metal sulfides (denoted as NiCoS) on Ti3C2Tx MXene via a metal-organic framework (MOF)-based approach. Benefiting from the unique structure and strong interfacial interaction between NiCoS and Ti3C2Tx sheets, the hybrid guarantees an enhanced active surface area with prominent charge-transfer conductivity, thus a superior activity toward oxygen evolution reaction (OER). Impressively, the hierarchical NiCoS in the hybrid is converted to nickel/cobalt oxyhydroxide-NiCoS assembly (denoted as NiCoOOH-NiCoS) by OER measurement, where NiCoOOH on the surface is confirmed as the intrinsic active species for the consequent water oxidation. The hybrid material is further applied to an air cathode for a rechargeable zinc-air battery, which exhibits low charging/discharging overpotential and long-term 1

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 27

stability. Our work underscores the tuned structure and electrocatalytic OER performance of MOF-derivative by the versatility of MXenes, and provides insight into the structure-activity relationship for noble metal-free catalysts. KEYWORD: MOF-derivative, MXenes, oxygen evolution reaction (OER), post-OER analysis, zinc-air battery

2


Page 3 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


INTRODUCTION Sustainable routes for renewable energy to mitigate the reliance on the combustion of traditional fossil fuels trigger extensive attention.1-5 Recent innovative strategies for electrochemical energy conversion via water splitting and metal-air batteries offer significant potentials for addressing this issue.6-10 An essential process in these energy conversion systems is greatly dependent on the rate-limiting step of anodic oxygen evolution reaction (OER), in which a multiple-electron-proton process and large overpotential are required for its sluggish kinetics.11-15 Although precious Ru/Ir oxides are regarded as the benchmark catalysts toward OER, widespread implementation is hampered by their scarcity and high cost. Within this context, increasing efforts have been devoted to developing highly efficient, stable and inexpensive electrocatalysts for OER. Currently, low-cost metalorganic frameworks (MOFs) that can serve as promising precursors or templates to engineer robust electrocatalysts have ignited significant interest.16-18 The good compatibility of MOFs with diverse metal ions facilitates to construct homogenous multi-metallic materials.19,20 Moreover, MOFs not only can tune the inherent electronic and/or surface structures of the yielded derivatives, but also endow the resultant products with hollow and/or porous nanostructure, which can contribute to better catalytic activity.21-25 Unfortunately, these derivatives are commonly prone to aggregate during electrocatalysis, which leads to the decreased active surface area, and their intrinsic poor electrical conductivity severely restricts the electrocatalytic activity, stimulating the urgent requirement for efficient synthetic strategies to improve the moderate performance of MOF-derivatives for electrocatalysis. Combining

MOF-derivative

electrocatalysts

with

two-dimensional

(2D)

materials, such as graphene, is an effective strategy to solve the aforementioned 3



Page 4 of 27

problems.26-29 As a newly emerging group in two-dimensional (2D) material family with unique structure and electronic properties, MXenes have shed new light on the energy-related applications.30-36 MXenes are generally prepared by selectively removing the A layers from the bulk MAX phase, where M is an early transition metal, A is an A-group element, and X is C and/or N element.37-40 During etching, the A atoms between MAX layers are substituted by terminated functional groups such as fluorine, hydroxyl, and oxygen groups, rendering the etched MXenes with high hydrophilic surface, tunable properties, and superior electrical conductivity, which provide the feasibility for engineering novel hybrid systems with wider flexibility.41-44 Additionally, comparing with the conventional 2D materials such as graphene, layered double hydroxides and transition-metal dichalcogenides, besides the high conductivity, MXene ultrathin nanosheets can give extra merits of large active surface area, fast charge transfer kinetics, and strong interfacial coupling for the energy conversion process (e.g., artificial photosynthetic systems, electronic apparatus, the catalysis, etc).45-47 On the basis of these premises, it is anticipated that coupling of MOF-derivatives with conductive MXenes could boost the catalytic properties and circumvent weaknesses of the dilemma above. In this research, we report a MOF-derivative/2D MXene hybrid by in situ nucleation and conversion of ZIF-67 (ZIF indicates zeolitic imidazolate framework) to hierarchical porous Ni-Co mixed metal sulfides on exfoliated Ti3C2Tx (Tx represents surface terminal groups like -(Fx) and -(OH)x) MXene sheets (denoted as NiCoS/Ti3C2Tx hereinafter). The unique hybrid structure and intimate interfacial interaction between the two components not only ensure favorable electrical conductance and enlarged surface area, but also provide sufficient active sites and superior activity toward OER. Specially, post-catalytic analysis reveals that the hybrid 4


Page 5 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


catalyst of NiCoS/Ti3C2Tx undergoes a chemical-structure transformation during water oxidation, with the rise of valence states of metal ions and in situ formation of nickel cobalt oxyhydroxides/NiCoS (denoted as NiCoOOH-NiCoS) assembly on Ti3C2Tx sheets, where NiCoOOH on the surface serves as the intrinsic active species for OER. Furthermore, as a proof-of-concept application, the rechargeable Zn-air battery fabricated by NiCoS/Ti3C2Tx exhibits a small charging/discharging voltage gap and excellent operation durability. This work highlights the optimized structure and electrocatalytic performance of MOF-derivative by the versatility of MXenes, and provides insight into the structure-activity relationship for noble metal-free catalysts for OER.

RESULTS AND DISCUSSION A two-step process was applied to prepare the few-layer MXene Ti3C2Tx sheets, as schematically illustrated in Figure 1a (see the Experimental section for details). The Al layers of the pristine bulk Ti3AlC2 was first selectively etched by HF to yield the accordion-like Ti3C2Tx, as displayed in the scanning electron microscopy (SEM) images in Figure 1b and 1c. Subsequently, the resulting Ti3C2Tx was further delaminated by dimethyl sulfoxide (DMSO) under nitrogen atmosphere to give isolated Ti3C2Tx sheets (Figure 1d). Transmission electron microscopy (TEM) image of the as-exfoliated Ti3C2Tx shows a lateral size of hundreds of nanometers with a very low contrast to the background, indicating its ultrathin thickness (Figure 1e). High-resolution TEM (HRTEM) image taken on the edge of the exfoliated sheets presents few layers thick, revealing its ultrathin nature again (Figure 1f). In addition, atomic force microscopy (AFM) image indicates that the exfoliated Ti3C2Tx sheet renders a height of 3.66 nm, which is only ~ 4 layers of Ti3C2Tx. 5



Page 6 of 27

Figure 1. (a) Scheme for synthesis of Ti3C2Tx sheets. SEM images of (b) bulk Ti3AlC2, (c) accordion-like Ti3C2Tx and (d) exfoliated Ti3C2Tx sheets. TEM (e), HRTEM (f) and AFM (g) images of Ti3C2Tx sheets.

To integrate with MOF-derivatives, the obtained Ti3C2Tx sheets were used as a synthetic substrate for the in situ nucleation and conversion of ZIF-67 by MOF-based strategy. The zeta potential of the prepared Ti3C2Tx sheets is -19.9 mV (Figure S1), which is ascribed to the functional groups (e.g., -(Fx) and -(OH)x) on the surface. The negative charge on the surface of Ti3C2Tx sheets could absorb Co2+ ions by electrostatic interaction. Then, the surface-anchored Co2+ could coordinate with 2methylimidazole (MeIM) molecules, and form the ZIF-67/Ti3C2Tx hybrid. After reaction for 15 min, ZIF-67 crystals were uniformly coated on both sides of Ti3C2Tx 6


Page 7 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


sheets (Figure 2b). When an appropriate amount of Ni(NO3)2 was reacted with ZIF67/Ti3C2Tx hybrid, Ni2+ ions will etch ZIF-67 and the Co2+/Co3+ ions would coprecipitate with Ni2+ ions to form Ni-Co mixed layered double hydroxide (LDH) (Figure 2a), which was denoted as NiCo-LDH/Ti3C2Tx (the ratio of Ni and Co here does not indicate the stoichiometric ratio). A typical SEM image (Figure 2c) of the asformed product presents hierarchical porous NiCo-LDH (inset Figure 2c) on Ti3C2Tx sheets, forming a unique hybrid structure. Energy-dispersive X-ray element mapping images confirm that Ni, Co, Ti, C, O, and F are homogeneously distributed (Figure S2a-2h), suggesting the successful synthesis of the hybrid. After the sulfuration, NiCo-LDH/Ti3C2Tx was converted to NiCoS/Ti3C2Tx with good preservation of the hierarchical porous structure (Figure 2d and inset). The TEM image (Figure 2e) clearly demonstrates that NiCoS is strongly anchored on the Ti3C2Tx sheets and presents continuous macropores (inset Figure 2e), which could greatly facilitate the electrolyte diffusion. The HRTEM image of NiCoS/Ti3C2Tx (Figure 2f) shows that NiCoS is assembled by NiCoS nanoparticles hierarchically, where the lattice constants of 0.34 nm and 0.24 nm can be corresponded to (220) and (400) planes of Ni3S4, respectively. High angle annular dark-field (HAADF) image (Figure 2g) and the associated energy-dispersive X-ray spectroscopy (EDS) mapping images (Figure 2h-2m) of NiCoS/Ti3C2Tx further confirm the spatial dispersion of the elements in the composite, where the Ni, Co, S are homogeneously coated on the Ti-C-O composite, suggesting the successful hybridization of Ti3C2Tx with NiCoS. In contrast, the etching and sulfuration treatments of pristine ZIF-67 crystals give agglomerated polyhedron particles, which is unfavorable for the accessibility of electrolyte (Figure S3a-S3c). TEM image confirms the hollow structure of the bare NiCoS with an even size of ~ 200 nm, whose surface is constituted by nanosheets (Figure S3d). Therefore, 7



Page 8 of 27

above evidences indicate that Ti3C2Tx sheets can serve as a highly conducted matrix to homogeneously deposit and distribute hierarchical NiCoS.

Figure 2. (a) Scheme of the preparation process of NiCoS/Ti3C2Tx. SEM images of (b) ZIF-67/Ti3C2Tx, (c) NiCo-LDH/Ti3C2Tx and (d) NiCoS/Ti3C2Tx. Inset: the highmagnification SEM images of the samples. (e) TEM (Inset: the high-magnification TEM image) and (f) HRTEM images of NiCoS/Ti3C2Tx. (g) HAADF and (h-m) EDS images of NiCoS/Ti3C2Tx.

The X-ray diffraction patterns (XRD) were performed for detailed structural characterization of the samples. The diffraction peak for the (104) planes of bulk 8


Page 9 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Ti3AlC2 is absent in the XRD pattern of Ti3C2Tx sheets, suggesting the successful etching of the Al layers (Figure S4a). Moreover, the (002) diffraction peak of Ti3C2Tx sheets shifts to lower angle in comparison with that of bulk Ti3AlC2, verifying the enlarged interlayer distance of the exfoliated MXene Ti3C2Tx sheets. Figure 3a shows the X-ray diffraction (XRD) patterns of ZIF-67/Ti3C2Tx and the derived products of NiCo-LDH/Ti3C2Tx and NiCoS/Ti3C2Tx. Notably, the XRD pattern of ZIF-67/Ti3C2Tx presents a superimposition of ZIF-67 phase and Ti3C2Tx phase (Figure S4a and S4b), indicating the effective combination of ZIF-67 and Ti3C2Tx. After etched by Ni2+, the original peaks of ZIF-67 disappear and are replaced by Ni(OH)2 phase, forming the NiCo-LDH/Ti3C2Tx hybrid. In the XRD pattern of NiCoS/Ti3C2Tx, the diffraction peaks for NiCoS can be indexed to the cubic structure of Ni3S4 (PDF No. 76-1813), while the shift of the diffraction peaks to higher angle in comparison with that of Ni3S4 verifies the successful substitution of partial Ni ions by Co ions.48,49 This is consistent with the result of HRTEM image (Figure 2f), which shows clear (220) and (400) planes of Ni3S4. In Raman spectra (Figure S5), compared to the bulk Ti3AlC2, peaks I and II in Raman spectrum of Ti3C2Tx sheets are vanished, while the peak III is broadened and downshifted. Such downshifting in Raman spectra verifies the successful exfoliation of bulk to very thin sheets, which is in good agreement with the reported literatures.50 Notably, the Raman spectra of NiCoS/Ti3C2Tx present the peaks both originate from Ti3C2Tx and NiCoS. Moreover, the peaks in the hybrid are shifted relative to those in the bare ones, suggesting the strong interaction of Ti3C2Tx and NiCoS (Figure 3b).32 Furthermore, the bare Ti3C2Tx, NiCoS and NiCoS/Ti3C2Tx exhibit the same type IV nitrogen adsorption-desorption curves (Figure 3c) in nitrogen adsorption-desorption isotherms, indicating mesopores within them. Impressively, NiCoS/Ti3C2Tx gives a Brunauer-Emmett-Teller (BET) surface area 9



Page 10 of 27

about 55 m2 g-1 with a pore volume of 0.08 m3 g-1 (Table 1), much higher than those of the bare Ti3C2Tx (15 m2 g-1, 0.04 m3 g-1) and NiCoS (8 m2 g-1, 0.02 m3 g-1) counterparts. Additionally, the pore size distribution curves confirm that NiCoS/Ti3C2Tx possesses hierarchical pores containing mesopores (pore size ca. 3 nm) and macropores (pore size ca. 70 nm) simultaneously (inset of Figure 3c). Such hierarchical porosity of NiCoS/Ti3C2Tx with high surface area and pore volume can provide abundant active sites on the surface and is favorable for accessibility of electrolyte, and thus enhance the catalytic performance.

Figure 3. (a) XRD patterns of ZIF-67/Ti3C2Tx and derived NiCo-LDH/Ti3C2Tx and NiCoS/Ti3C2Tx products. (b) Raman spectra and (c) N2 sorption isotherms (inset: the pore size distribution) of Ti3C2Tx, NiCoS and NiCoS/Ti3C2Tx.

10


Page 11 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Table 1. Physical properties of the as-prepared samples. Samples

SBET (m2 g-1)

Vpore (m3 g-1)

dpore (nm)

NiCoS

8.0

0.02

6.1

Ti3C2Tx

15

0.04

9.9

NiCoS/Ti3C2Tx

55

0.08

7.9

The electrochemical characterizations were conducted on a typical threeelectrode cell in 1.0 M KOH (pH 13.6) electrolyte with 0.21 mg cm-2 catalysts loading on glassy carbon electrodes. Before the electrochemical test, the electrodes underwent an activation treatment by several linear sweep voltammetry (LSV) until a stable curve was achieved, unless noted otherwise. Figure 4a presents the iR-corrected LSV curves of all the samples at a scan rate of 5 mV s-1. Apparently, Ti3C2Tx shows no OER activity. While, compared with the bare NiCo-LDH and NiCoS, both NiCoLDH/Ti3C2Tx and NiCoS/Ti3C2Tx hybrids exhibit enhanced catalytic activities with larger current densities and lower onset potentials, suggesting the positive effects of Ti3C2Tx matrix to OER activity. Among these five electrocatalysts, NiCoS/Ti3C2Tx provides the best catalytic activity with a small overpotential (η) of 365 mV to deliver the current density of 10 mA cm-2, which is even smaller than the commercial RuO2 (397 mV). Notably, the OER performance of the physical mixture of NiCoS and Ti3C2Tx (NiCoS+ Ti3C2Tx) is much lower than that of NiCoS/Ti3C2Tx (Figure S6), implying the weak synergetic effect between physically mixed NiCoS and Ti3C2Tx. Furthermore, the Tafel slope of NiCoS/Ti3C2Tx is 58.2 mV dec-1 (Figure 4b), which is obviously smaller than that of NiCoS (73.7 mV dec-1), NiCo-LDH/Ti3C2Tx (153.1 mV dec-1), NiCo-LDH (85.0 mV dec-1), RuO2 (88.3 mV dec-1) and Ti3C2Tx (227.3 mV 11



Page 12 of 27

dec-1), revealing the higher OER rate and favorable kinetics of NiCoS/Ti3C2Tx. According to the inductively coupled plasma atomic emission spectrometry (ICP-AES, Figure S7), the content of Ni and Co in NiCoS/Ti3C2Tx is 44.59 wt.% and 21.22 wt.%, respectively, showing the molar ratio of Ni/Co ~ 2. Thus, the turnover frequency (TOF) of NiCoS/Ti3C2Tx is calculated to be 0.009 s-1 and 0.036 s-1 at overpotentials of 350 mV and 400 mV, respectively, assuming that all the metal sites (Ni and Co) in the catalysts are active (Figure 4c). These values are much higher than those of the commercial RuO2 (0.007 s-1 and 0.017 s-1 at 350 mV and 400 mV overpotentials, respectively), further confirming the high electrocatalytic activity of NiCoS/Ti3C2Tx hybrid. Note that these TOF values in our case are conservatively estimated because not all the metal sites are electrochemically accessible. Furthermore, the durability of the catalysts was measured under a constant current density of 10 mA cm-2. As shown in the chronopotentiometry curves (Figure 4d), the required potential of NiCoS/Ti3C2Tx remains nearly constant under the continuous electrolysis reaction for ~ 6 h, which is superior to NiCoS, NiCo-LDH/Ti3C2Tx, NiCo-LDH and commercial RuO2, confirming the excellent stability of NiCoS/Ti3C2Tx. Actually, NiCoS/Ti3C2Tx hybrid can be comparable to or even better than the most Ni-Co based OER catalysts (Table S1). To understand the high catalytic performance of the NiCoS/Ti3C2Tx, electrochemically active surface area (ECSA) was estimated for the catalysts for OER. Normally, ECSA shows a positive correlation with the electrochemical double-layer capacitance (Cdl). Therefore, to evaluate the ECSA, Cdl is computed by the cyclic voltammetry (CV) curves under different scan rates in a proper potential range (Figure S8a-8f). NiCoS/Ti3C2Tx exhibits much higher Cdl (2.4 mF cm-2) than NiCoS (1.2 mF cm-2), NiCo-LDH/Ti3C2Tx (0.58 mF cm-2), NiCo-LDH (0.27 mF cm-2), RuO2 12


Page 13 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


(1.8 mF cm-2) and Ti3C2Tx (0.21 mF cm-2) (Figure 4e), suggesting the more active sites of NiCoS/Ti3C2Tx. Furthermore, electrochemical impedance spectroscopy (EIS) measurement is performed to analyze the interfacial resistance for the electrocatalysts. Distinguished semicircles can be observed in Nyquist plots (Figure 4f) of the electrocatalyst, which should be ascribed to the charge transfer resistance (Rct) at the interface of catalyst/electrolyte.51 NiCoS/Ti3C2Tx presents the smallest Rct, suggesting an optimized charge-transfer capacity during OER process. This result is in good agreement with the Bode modulus plots (Figure S9), in which NiCoS/Ti3C2Tx shows the lowest resistance in various frequencies among our four electrodes. The high conductivity and fast charge transfer of NiCoS/Ti3C2Tx must be another important contributor to its enhanced water oxidation performance.

Figure 4. (a) LSV curves and (b) Tafel plots of NiCoS/Ti3C2Tx, NiCoS, NiCoLDH/Ti3C2Tx, NiCo-LDH and RuO2. (c) TOFs at η = 350 and 400 mV and (d) Chronopotentiometry curves at 10 mA cm-2 of NiCoS/Ti3C2Tx, NiCoS, NiCoLDH/Ti3C2Tx, NiCo-LDH and RuO2. (e) ∆J (= Ja-Jc) plotted scan rates and (f) Nyquist plots at 350 mV bias for different catalysts. 13



Page 14 of 27

The aforementioned results validate that the electrocatalytic activity of bare NiCo-LDH can be significantly tailored by the corporation with Ti3C2Tx and sulfuration treatment. To get insight into the activity-structure relationship of NiCoS/Ti3C2Tx,

the

X-ray

photoelectron

spectroscopy

(XPS)

spectra

of

NiCoS/Ti3C2Tx before and after OER were analyzed and compared (Figure S10a and Figure 5). In Ni 2p XPS spectra for NiCoS/Ti3C2Tx before OER, two peaks at 853.28 eV and 870.55 eV could be assigned to Ni-S bond,52,53 signifying the formation of nickel sulfide. Impressively, the Ni 2p XPS spectrum of NiCoS/Ti3C2Tx after OER test shows no Ni-S bond and the pair peaks of Ni 2p3/2 and Ni 2p1/2 shift to 855.5 eV and 873.1 eV, respectively, which is ascribed to the oxidized Ni species (Ni-O bond), demonstrating the surface oxidation of NiCoS/Ti3C2Tx.54 Moreover, the Ni 2p spectra of NiCoS/Ti3C2Tx after OER apparently shift to higher binding energies compared with the as-prepared NiCo-LDH/Ti3C2Tx before OER, suggesting its higher valence state of Ni, which is highly valuable for enhancement of the electrocatalytic activity. Similarly, the Co 2p spectra show the formation of Co-S bond in NiCoS/Ti3C2Tx before OER and a higher valence state of Co is achieved after OER (Figure 5b). Furthermore, the O 1s spectrum of NiCo-LDH/Ti3C2Tx before OER can be deconvoluted into two species (Figure 5c), whereby the O2- at 529.2 eV and OH- at 531.0 eV.55,56 While, the chemical state of O 1s in NiCoS/Ti3C2Tx is mainly attributed to the adsorbed H2O (H2Oads, 532 eV).57,58 After OER, the S signal on the surface of NiCoS/Ti3C2Tx disappeared and is substituted by OH-, O2- and H2Oads instead (Figure 5c

and

Figure

S10b),

which

reveals

the

formation

of

nickel-cobalt

oxides/hydroxides(very likely nickel cobalt oxyhydroxide, denoted as NiCoOOH). Therefore, the XPS analysis manifests that the surface of NiCoS/Ti3C2Tx undergoes an irreversible chemical-structure transformation process during OER, and the 14


Page 15 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


resulting oxides/hydroxides act as the intrinsic catalytically active species to afford water oxidation.

Figure 5. High-resolution XPS spectrum of (a) Ni 2p, (b) Co 2p and (c) O 1s for NiCo-LDH/Ti3C2Tx, NiCoS/Ti3C2Tx and NiCoS/Ti3C2Tx after OER.

The SEM and TEM images of NiCoS/Ti3C2Tx after OER shows that the nanosheets of NiCoS are transformed into a number of nanoparticles anchored on the surface of Ti3C2Tx (Figure 6a and 6b). The corresponding interplanar spacing of 0.24 nm and 0.14 nm is referred to (101) and (110) facets of NiOOH (Figure 6c). Cleary, the HAADF-STEM and EDS mapping images demonstrate the uniform-spatial distribution of Ni, Co, Ti, C, O and only a trace of S elements, revealing the transformation of NiCoS to nickel cobalt oxides/hydroxides (Figure 6d-6j). This is another strong evidence for the in situ irreversibly chemical-structure transformation of the catalyst during OER process, consistent with other reports. On the other hand, the post-OER NiCoS still maintains the initial hollow structure when the nanosheets are converted into nanoparticles (Figure S11a-S11c). Overall, by integrating the 15



Page 16 of 27

analyses of XPS and electron microscopy above, it is reasonably concluded that the initial NiCoS in the hybrid is partially converted to NiCoOOH on Ti3C2Tx irreversibly, which is the true intrinsic active phase to afford OER measurement. Interestingly, pioneer work has verified that such electrochemical transformation during water oxidation not only can take place in sulfide catalysts, but also in the MOFs.59 Inspired by these discoveries, the OER performance of ZIF-67/Ti3C2Tx and ZIF-67 is preliminarily studied (Figure S12). The overpotentials to achieve 10 mA cm-2 for ZIF67/Ti3C2Tx and ZIF-67 are 387 mV and 416 mV, respectively, again, confirming the merit of Ti3C2Tx for OER. The obtained OER performance of ZIF-67 and ZIF67/Ti3C2Tx is very likely derived from the water-oxidized Co hydroxideoxyhydroxides, rather than ZIF-67 itself. The detailed transformation of ZIF-67 in OER is in progress.

Figure 6. (a) SEM, (b) TEM, (c) HRTEM and (d-j) HAADF and EDS images of NiCoS/Ti3C2Tx after OER.

Based on the promising OER performance, a proof-of-concept test was carried out to evaluate the feasibility of NiCoS/Ti3C2Tx in a rechargeable Zn-air battery. As 16


Page 17 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


shown in Figure 7a, a homemade Zn-air battery device was assembled with a zinc plate as the anode, NiCoS/Ti3C2Tx coupled with Pt/C (the mass ratio of NiCoS/Ti3C2Tx : Pt/C was 1:1) loaded on a nickel foam (mass loading: 2 mg cm-2) as the cathode, and 6 M KOH with 0.2 M zinc acetate as the electrolyte. For compassion, Pt/C and RuO2 mixed catalyst with the same proportion was utilized as the rechargeable noble metal-air cathode. The battery fabricated from NiCoS/Ti3C2Tx + Pt/C can work with a high open-circuit of 1.43 V (Figure S13a), even slightly superior to that of the RuO2 + Pt/C air cathode (1.4 V). Figure 7b shows the charging and discharging polarization curves. Impressively, when the current density is raised to 50 mA cm-2, the voltage gap of charging (1.85 V) and discharging (1.15 V) for NiCoS/Ti3C2Tx + Pt/C-based battery is 0.7 V, which was 0.14 V lower than that of the noble metal-air cathode based one, demonstrating a low voltage even at higher current density for NiCoS/Ti3C2Tx + Pt/C. Furthermore, the cycle discharging-charging measurement is recorded at 10 mA cm-2 to assess the stability of the constructed Znair battery. After 8 h galvanostatic charge-discharge test, NiCoS/Ti3C2Tx + Pt/C shows virtually negligible voltage fading (Figure 7c), demonstrating the excellent stability of the battery, identical to RuO2 + Pt/C. By merely charging the NiCoS/Ti3C2Tx + Pt/C-based Zn-air battery for 5 min, the device can power a red light-emitting diode (LED) array (Figure S13b), implying its highly competitive potential for renewable energy applications.

17



Page 18 of 27

Figure 7. (a) Scheme of a homemade rechargeable Zn-air battery. (b) Charging and discharging polarization curves of the rechargeable Zn-air batteries. (c) Cycling performance at the current density of 10 mA cm-2.

CONCLUSION In summary, hierarchical porous NiCoS strongly coupled with exfoliated Ti3C2Tx MXene sheets were realized via MOF-based strategy. The excellent activity and stability of NiCoS/Ti3C2Tx hybrid in both OER and Zn-air battery are comparable to those of noble-metal based catalysts. The outstanding activity of NiCoS/Ti3C2Tx hybrid is mainly attributed to the strong interaction between NiCoS and Ti3C2Tx, giving high conductivity for the efficient electron transport, and tailored composite structure for more active sites by the Ti3C2Tx matrix. Specifically, morphological and chemical conversions are confirmed by post-catalytic analysis, where NiCoS on Ti3C2Tx is transformed to NiCoOOH active phase on the parent catalyst surface to 18


Page 19 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


afford water oxidation. This study highlights the tuned structure and electrocatalytic performance of MOF-derivative by the versatility of MXenes, and provides insight into the structure-activity relationship for noble metal-free catalysts in a wide range energy-related applications.

ASSOCIATED CONTENT Supporting Information The supporting information is available free of charge on the ACS Publication website at DOI: Experimental section; Structure characterizations; Electrochemical measurements; Zeta potential; EDX; SEM; XRD; Raman spectra; ICP-AES; CV curves; Bode modulus plots; Open-circuit plots and photograph of the rechargeable Zn-air batteries; XPS spectra; TEM; Performance comparison Table (Table S1).

AUTHOR INFORMATION Corresponding Author * E-mail: [email protected] * E-mail: [email protected]; Tel: 0086-27-87871029; Fax: 0086-27-87879468

Notes The authors declare no competing financial interest.

Acknowledgements This work was supported by National Natural Science Foundation of China (51320105001, 21433007, 51772234, and U1705251), the Natural Science Foundation of Hubei Province(2015CFA001), Innovative Research Funds of 19



Page 20 of 27

SKLWUT (2017-ZD-4), and the Fundamental Research Funds for the Central Universities (WUT: 2017 IVA 092).

References [1] Seh, Z. W.; Kibsgaard, J.; Dickens, C. F.; Chorkendorff, I. B.; Norskov, J. K.; Jaramillo, T. F. Combining Theory and Experiment in Electrocatalysis: Insights into Materials Design. Science 2017, 146, 355-367. [2] Fu, J.; Yu, J.; Jiang, C.; Cheng, B. g-C3N4-Based Heterostructured Photocatalysts. Adv. Energy Mater. 2018, 8, 1701503. [3] Mabayoje, O.; Shoola, A.; Wygant, B. R.; Mullins, C. B. The Role of Anions in Metal Chalcogenide Oxygen Evolution Catalysis: Electrodeposited Thin Films of Nickel Sulfide as "Precatalysts". ACS Energy Lett. 2016, 1, 195-201. [4] Cheng, H.; Li, M.-L.; Su, C.-Y.; Li, N.; Liu, Z.-Q. Cu-Co Bimetallic Oxide Quantum Dot Decorated Nitrogen-Doped Carbon Nanotubes: A High-Efficiency Bifunctional Oxygen Electrode for Zn–Air Batteries. Adv. Funct. Mater. 2017, 27, 1701833. [5] Liu, T.; Zhang, L.; You, W.; Yu, J. Core-Shell Nitrogen-Doped Carbon Hollow Spheres/Co3O4 Nanosheets as Advanced Electrode for High-Performance Supercapacitor Small 2018, 14, 1702407. [6] Fan, K.; Chen, H.; Ji, Y.; Huang, H.; Claesson, P. M.; Daniel, Q.; Philippe, B.; Rensmo, H.; Li, F.; Luo, Y.; Sun, L. Nickel-Vanadium Monolayer Double Hydroxide for Efficient Electrochemical Water Oxidation. Nat. Commun. 2016, 7, 11981. [7] Kuang, P.; Tong, T.; Fan, K.; Yu, J. In Situ Fabrication of Ni–Mo Bimetal Sulfide Hybrid as an Efficient Electrocatalyst for Hydrogen Evolution Over a Wide pH Range. ACS Catal. 2017, 7, 6179-6187. [8] Zeng, S.; Chen, H.; Wang, H.; Tong, X.; Chen, M.; Di, J.; Li, Q. Crosslinked Carbon Nanotube Aerogel Films Decorated with Cobalt Oxides for Flexible Rechargeable Zn–Air Batteries. Small. 2017, 13, 1700518.

20


Page 21 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


[9] Kuang, P.; Zhu, B.; Li, Y.; Liu, H.; Yu, J.; Fan, K. Graphdiyne: A Superior Carbon Additive to Boost Water Oxidation Catalyst. Nanoscale Horiz. 2018, 3, 317-326. [10] Daniel, Q.; Anabre, R. B.; Zhang, B.; Philippe, B.; Chen, H.; Li, F.; Fan, K.; Ahmadi, S.; Rensmo, H.; Sun, L. Re-Investigation of Cobalt Porphyrin for Electrochemical Water Oxidation on FTO Surface: Formation of CoOx as Active Species. ACS Catal. 2017, 7, 1143-1149. [11] Fan, K.; Ji, Y.; Zou, H.; Zhang, J.; Zhu, B.; Chen, H.; Daniel, Q.; Luo, Y.; Yu, J.; Sun, L. Hollow Iron-Vanadium Composite Spheres: A Highly Efficient Iron-Based Water Oxidation Electrocatalyst without the Need for Nickel or Cobalt. Angew. Chem., Int. Ed. 2017, 56, 32893293. [12] Zhang, B.; Zheng, X.; Voznyy, O.; Comin, R.; Bajdich, M.; Garcia-Melchor, M.; Han, L.; Xu, J.; Liu, M.; Zheng, L.; Arquer, F. P. G. de; Dinh, C. T.; Fan, F.; Yuan, M.; Yassitepe, E.; Chen, N.; Regier, T.; Liu, P.; Li, Y.; De Luna, P.; Janmohamed, A.; Xin, H. L.; Yang, H.; Vojvodic, A.; Sargent, E. H. Homogeneously Dispersed Multimetal Oxygen-Evolving Catalysts. Science 2016, 352, 333-337. [13] Wang, Y.; Liu, Q.; Hu, T.; Zhang, L.; Deng, Y. Appl. Surf. Sci. Carbon Supported MnO2CoFe2O4 with Enhanced Electrocatalytic Activity for Oxygen Reduction and Oxygen Evolution. 2017, 403, 51-56. [14] Yang, Y.; Zhang, K.; Ling, H.; Li, X.; Chan, H. C.; Yang, L.; Gao, Q. MoS2– Ni3S2 Heteronanorods as Efficient and Stable Bifunctional Electrocatalysts for Overall Water Splitting. ACS Catal. 2017, 7, 2357-2366. [15] Huang, J.; Chen, J.; Yao, T.; He, J.; Jiang, S.; Sun, Z.; Liu, Q.; Cheng, W.; Hu, F.; Jiang, Y.; Pan, Z.; Wei, S. CoOOH Nanosheets with High Mass Activity for Water Oxidation. Angew. Chem., Int. Ed. 2015, 54, 8722-8727. [16] Lu, X.-F.; Gu, L.-F.; Wang, J.-W.; Wu, J.-X.; Liao, P.-Q.; Li, G.-R. Bimetal-Organic Framework Derived CoFe2O4/C Porous Hybrid Nanorod Arrays as High-Performance Electrocatalysts for Oxygen Evolution Reaction. Adv. Mater. 2017, 29, 1604437. [17] Bai, S.; Liu, C.; Luo, R.; Chen, A. Metal Organic Frameworks-Derived Sensing Material of SnO2/NiO Composites for Detection of Triethylamine. Appl. Surf. Sci. 2018, 437, 304-313.

21



Page 22 of 27

[18] Wang, S.; X. Wang, Multifunctional Metal-Organic Frameworks for Photocatalysis. Small. 2015, 11, 3097-3112. [19] Xu, X.; Liang, H.; Ming, F.; Qi, Z.; Xie, Y.; Wang, Prussian Blue Analogues Derived Penroseite (Ni,Co)Se2 Nanocages Anchored on 3D Graphene Aerogel for Efficient Water Splitting. Z. ACS Catal. 2017, 7, 6394-6399. [20] Zhang, X.; Hou, F.; Yang, Y.; Wang, Y.; Liu, N.; Chen, D.; Yang, Y. A Facile Synthesis for Cauliflower Like CeO2 Catalysts from Ce-BTC Precursor and Their Catalytic Performance for CO Oxidation. Appl. Surf. Sci. 2017, 423, 771-779. [21] Zou, G.; Hou, H.; Ge, P.; Huang, Z.; Zhao, G.; Yin, D.; Ji, X. Metal-Organic FrameworkDerived Materials for Sodium Energy Storage. Small. 2017, 14, 1702648. [22] Zhang, X.; Zhang, J.; Hu, Q.; Cui, Y.; Yang, Y.; Qian, G. Postsynthetic Modification of Metal–Organic Framework for Hydrogen Sulfide Detection. Appl. Surf. Sci. 2015, 355, 814-819. [23] Liu, J.; Wu, C.; Xiao, D.; Kopold, P.; Gu, L.; Aken, P. A. van; Maier, J.; Yu, Y. MOFDerived Hollow Co9S8 Nanoparticles Embedded in Graphitic Carbon Nanocages with Superior LiIon Storage Small 2016, 12, 2354. [24] Zhang, H.; Liu, X.; Yue, Y.; Guan, C.; Cheetham, A. K.; Wang, J. MOF-Derived Nanohybrids for Electrocatalysis and Energy Storage: Current Status and Perspectives. Chem. Commun. 2018, DOI:10.1039/c8cc00789f. [25] Wu, H. Bin; Lou, X. W. Metal-Organic Frameworks and Their Derived Materials for Electrochemical Energy Storage and Conversion: Promises and Challenges. Sci. Adv. 2017, 3, eaap9252. [26] Zhong, H.-x.; Wang, J.; Zhang, Y.-w.; Xu, W.-l.; Xing, W.; Xu, D.; Zhang, Y.-f.; Zhang, X.b. ZIF-8 Derived Graphene-Based Nitrogen-Doped Porous Carbon Sheets as Highly Efficient and Durable Oxygen Reduction Electrocatalysts. Angew. Chem., Int. Ed. 2014, 53, 14235-14239. [27] Qu, C.; Zhang, L.; Meng, W.; Liang, Z.; Zhu, B.; Dang, D.; Dai, S.; Zhao, B.; Tabassum, H.; Gao, S.; Zhang, H.; Guo, W.; Zhao, R.; Huang, X.; Liu, M.; Zou, R. MOF-Derived alpha-NiS Nanorods on Graphene as an Electrode for High-Energy-Density Supercapacitors. J. Mater. Chem. A 2018, 6, 4003-4012.

22


Page 23 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


[28] Li, Z.; Shao, M.; Zhou, L.; Zhang, R.; Zhang, C.; Wei, M.; Evans, D. G.; Duan, X. Directed Growth of Metal-Organic Frameworks and Their Derived Carbon-Based Network for Efficient Electrocatalytic Oxygen Reduction. Adv. Mater. 2016, 28, 2237-2344. [29] Yu, M.; Zhou, S.; Wang, Z.; Zhao, J.; Qiu, J. Boosting Electrocatalytic Oxygen Evolution by Synergistically Coupling Layered Double Hydroxide with MXene. Nano Energy 2018, 44, 181190. [30] Naguib, M.; Mochalin, V. N.; Barsoum, M. W.; Gogotsi, Y. 25th Anniversary Article: MXenes: A New Family of Two-Dimensional Materials. Adv. Mater. 2014, 26, 992-1005. [31] Low, J.; Zhang, L.; Tong, T.; Shen, B.; Yu, J. TiO2/MXene Ti3C2 composite with excellent photocatalytic CO2 reduction activity. J. Catal. 2018, 361, 255-266. [32] Anasori, B.; Lukatskaya, M. R.; Gogotsi, Y. 2D Metal Carbides and Nitrides (MXenes) for Energy Storage. Nat. Rev. Mater. 2017, 2, 16098. [33] Lin, H.; Wang, X.; Yu, L.; Chen, Y.; Shi, J. Two-Dimensional Ultrathin MXene Ceramic Nanosheets for Photothermal Conversion. Nano Lett. 2017, 17, 384-391. [34] Cao, S.; Shen, B.; Tong, T.; Fu, J.; Yu, J. 2D/2D Heterojunction of Ultrathin MXene/Bi2WO6 Nanosheets for Improved Photocatalytic CO2 Reduction. Adv. Funct. Mater. 2018, 29, 1800136. [35] Halim, J.; Cook, K. M.; Naguib, M.; Eklund, P.; Gogotsi, Y.; Rosen, J.; Barsoum, M. W. XRay Photoelectron Spectroscopy of Select Multi-Layered Transition Metal Carbides (MXenes). Appl. Surf. Sci. 2016, 362, 406-417. [36] Ghidiu, M.; Lukatskaya, M. R.; Zhao, M.-Q.; Gogotsi, Y.; Barsoum, M. W. Conductive TwoDimensional Titanium Carbide 'Clay' with High Volumetric Capacitance. Nature 2014, 516, 78-81. [37] Wu, X.; Wang, Z.; Yu, M.; Xiu, L.; Qiu, J. Stabilizing the MXenes by Carbon Nanoplating for Developing Hierarchical Nanohybrids with Efficient Lithium Storage and Hydrogen Evolution Capability. Adv. Mater. 2017, 29, 1607017. [38] Lukatskaya, M. R.; Mashtalir, O.; Ren, C. E.; Dall'Agnese, Y.; Rozier, P.; Taberna, P. L.; Naguib, M.; Simon, P.; Barsoum, M. W.; Gogotsi, Y. Cation Intercalation and High Volumetric Capacitance of Two-Dimensional Titanium Carbide. Science 2013, 341, 1502-1505. [39] Berdiyorov, G. R.; Mahmoud, K. A. Effect of Surface Termination on Ion Intercalation Selectivity of Bilayer Ti3C2T2 (T= F, O and OH) MXene. Appl. Surf. Sci. 2017, 416, 725-730. 23



Page 24 of 27

[40] Zhao, L.; Dong, B.; Li, S.; Zhou, L.; Lai, L.; Wang, Z.; Zhao, S.; Han, M.; Gao, K.; Lu, M.; Xie, X.; Chen, B.; Liu, Z.; Wang, X.; Zhang, H.; Li, H.; Liu, J.; Zhang, H.; Huang, X.; Huang, W. Interdiffusion Reaction-Assisted Hybridization of Two-Dimensional Metal-Organic Frameworks and Ti3C2Tx Nanosheets for Electrocatalytic Oxygen Evolution. ACS Nano 2017, 11, 5800-5807. [41] Wang, H.; Zhang, J.; Wu, Y.; Huang, H.; Li, G.; Zhang, X.; Wang, Z. Surface Modified MXene Ti3C2 Multilayers by Aryl Diazonium Salts Leading to Large-Scale Delamination. Appl. Surf. Sci. 2016, 384, 287-293. [42] Wu, Y.; Nie, P.; Wang, J.; Dou, H.; Zhang, X. Few-Layer MXenes Delaminated via HighEnergy Mechanical Milling for Enhanced Sodium-Ion Batteries Performance. ACS Appl. Mater.

Interfaces 2017, 9, 39610-39617. [43] Xue, Q.; Pei, Z.; Huang, Y.; Zhu, M.; Tang, Z.; Li, H.; Huang, Y.; Li, N.; Zhang, H.; Zhi, C. Mn3O4 nanoparticles on layer-structured Ti3C2 MXene towards the oxygen reduction reaction and zinc–air batteries. J. Mater. Chem. A 2017, 5, 20818-20823. [44] Liu, J.; Zhang, H.; Sun, R.; Liu, Y.; Liu, Z.; Zhou, A.; Yu, Z. Hydrophobic, Flexible, and Lightweight MXene Foams for High-Performance Electromagnetic-Interference Shielding. Adv. Mater. 2017, 29, 1702367. [45] Ling, Z.; Ren, C. E.; Zhao, M.-Q.; Yang, J.; Giammarco, J. M.; Qiu, J.; Barsoum, M. W.; Gogotsi, Y. Flexible and Conductive MXene Films and Nanocomposites with High Capacitance. Proc. Natl. Acad. Sci. USA 2014, 111, 16676-16681. [46] Zhao, M.; Xie, X.; Ren, C.; Makaryan, T.; Anasori, B.; Wang, G.; Gogotsi, Y. Hollow MXene Spheres and 3D Macroporous MXene Frameworks for Na-Ion Storage. Adv. Mater. 2017, 29, 1702410. [47] Yang, Y.; Umrao, S.; Lai, S.; Lee, S. Large-Area Highly Conductive Transparent TwoDimensional Ti2CTx Film. J. Phys. Chem. Lett. 2017, 8, 859-865. [48] Liu, B.; Zhao, Y.-F.; Peng, H.-Q.; Zhang, Z.-Y.; Sit, C.-K.; Yuen, M.-F.; Zhang, T.-R.; Lee, C.-S.; Zhang, W.-J. Nickel-Cobalt Diselenide 3D Mesoporous Nanosheet Networks Supported on Ni Foam: An All-pH Highly Efficient Integrated Electrocatalyst for Hydrogen Evolution. Adv. Mater. 2017, 29, 1606521.

24


Page 25 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


[49] Sivanantham, A.; Ganesan, P.; Shanmugam, S. Hierarchical NiCo2S4 Nanowire Arrays Supported on Ni Foam: An Efficient and Durable Bifunctional Electrocatalyst for Oxygen and Hydrogen Evolution Reactions. Adv. Funct. Mater. 2016, 26, 4661-4672. [50] Naguib, M.; Kurtoglu, M.; Presser, V.; Lu, J.; Niu, J.; Heon, M.; Hultman, L.; Gogotsi, Y.; Barsoum, M. W. Two-Dimensional Nanocrystals Produced by Exfoliation of Ti3AlC2. Adv. Mater. 2011, 23, 4248-4253. [51] Chauhan, M.; Reddy, K. P.; Gopinath, C. S.; Deka, S. Copper Cobalt Sulfide Nanosheets Realizing a Promising Electrocatalytic Oxygen Evolution Reaction. ACS Catal. 2017, 7, 58715879. [52] Zou, H.; He, B.; Kuang, P.; Yu, J.; Fan, K. NixSy Nanowalls/Nitrogen-Doped Graphene Foam Is an Efficient Trifunctional Catalyst for Unassisted Artificial Photosynthesis. Adv. Funct. Mater. 2018, 28, 1706917. [53] Li, X.; Shang, X.; Rao, Y.; Dong, B.; Han, G. Q.; Hu, W. H.; Liu, Y. R.; Yan, K. L.; Chi, J. Q.; Chai, Y. M.; Liu, C. G. Tuning Crystal Phase of NiSx Through Electro-Oxidized Nickel Foam: A Novel Route for Preparing Efficient Electrocatalysts for Oxygen Evolution Reaction. Appl. Surf. Sci. 2017, 396, 1034-1043. [54] Liu, T.; Jiang, C.; Cheng, B.; You, W.; Yu, J. Hierarchical Flower-Like C/NiO Composite Hollow Microspheres and Its Excellent Supercapacitor Performance. J. Power Sources 2017, 359, 371-378. [55] Weidler, N.; Paulus, S.; Schuch, J.; Klett, J.; Hoch, S.; Stenner, P.; Maljusch, A.; Broetz, J.; Wittich, C.; Kaiser, B.; Jaegermann, W. CoOx Thin Film Deposited by CVD as Efficient Water Oxidation Catalyst: Change of Oxidation State in XPS and Its Correlation to Electrochemical Activity. Phys. Chem. Chem. Phys. 2016, 18, 10708-10718. [56] Kuang, P.; Zhang, L.; Cheng, B.; Yu, J. Enhanced Charge Transfer Kinetics of Fe2O3/CdS Composite Nanorod Arrays using Cobalt-Phosphate as Cocatalyst. Appl. Catal. B 2017, 218, 570580. [57] Fu, J.; Zhu, B.; Jiang, C.; Cheng, B.; You, W.; Yu, J. Hierarchical Porous O-Doped gC3N4 with Enhanced Photocatalytic CO2 Reduction Activity. Small. 2017, 13, 1603938.

25



Page 26 of 27

[58] Favaro, M.; Yang, J.; Nappini, S.; Magnano, E.; Toma, F. M.; Crumlin, E. J.; Yano, J.; Sharp, I. D. Understanding the Oxygen Evolution Reaction Mechanism on CoOx using Operando Ambient-Pressure X-ray Photoelectron Spectroscopy. J. Am. Chem. Soc. 2017, 139, 8960-8970. [59] Indra, A.; Paik, U.; Song, T. Boosting Electrochemical water oxidation with metal Hydroxide Carbonate Templated Prussian BlueAnalogues. Angew. Chem., Int. Ed. 2018, 57, 1241-1245.

26


Page 27 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


Table of Content and Abstract Graphics

27


Metal-Organic Framework-Derived Nickel-Cobalt ... - ACS Publications

Recommend Documents