Subscriber access provided by Kaohsiung Medical University

Remediation and Control Technologies

Self-Assembled Nano-FeO(OH)/Reduced Graphene Oxide Aerogel as a Reusable Catalyst for Photo-Fenton Degradation of Phenolic Organics Renlan Liu, Yiming Xu, and Baoliang Chen Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b01043 • Publication Date (Web): 25 May 2018 Downloaded from http://pubs.acs.org on May 25, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 32

Environmental Science & Technology

1

Self-Assembled Nano-FeO(OH)/Reduced Graphene Oxide Aerogel as a

2

Reusable Catalyst for Photo-Fenton Degradation of Phenolic Organics

3

Renlan Liu1,2, Yiming Xu3,4, and Baoliang Chen1,2,*

4 5

(1.Department of Environmental Science, Zhejiang University, Hangzhou, Zhejiang 310058, China; 2.

6

Zhejiang Provincial Key Laboratory of Organic Pollutant Process and Control, Zhejiang University,

7

Hangzhou Zhejiang 310058, China. 3. Department of Chemistry, Zhejiang University, Hangzhou,

8

Zhejiang 310027, China. 4. State Key Laboratory of Silica Materials, Zhejiang University, Hangzhou

9

310027, China.)

10 11 12

* Corresponding author: phone & Fax: 0086-571-88982587

13

Email: [email protected]

14 15 16 17 18 19 20 21 22 23 1

ACS Paragon Plus Environment

Environmental Science & Technology

24

Abstract

25

Fabrication of visible-light-responsive, macroscopic photo-Fenton catalysts is crucial for

26

wastewater treatment. Here, we report a facile fabrication method for nano-FeO(OH)/reduced

27

graphene oxide aerogels (FeO(OH)-rGA) equipped with a stable macrostructure and a high

28

efficiency for catalytic degradation of phenolic organics. The structure of FeO(OH)/rGA was

29

characterized by SEM, TEM, XPS, Raman analysis. The FeO(OH) is the main constituent of

30

ferrihydrite, which dispersed in the graphene aerogel with a particle size of ~3 nm can

31

efficiently activate H2O2 to generate abundant •OH. The excellent performance of the

32

FeO(OH)/rGO aerogel was specifically exhibited by the outstanding catalyst activity,

33

sustained mineralization and eminent reaction rate for phenolic organics. A synergy effect

34

between FeO(OH) and graphene aerogel was observed, which came from the extensive

35

electron transfer channels and active sites of the 3D graphene aerogel and the

36

visible-light-activated FeO(OH) and H2O2 consistently producing •OH. The FeO(OH)/rGA

37

could be reused for 10 cycles without a reduction in the catalytic activity and had less iron

38

leaching, which guarantees that the active ingredient remains in the gel. Moreover, the

39

FeO(OH)/rGA induced photo-Fenton degradation of 4-chlorophenol under near neutral pH

40

conditions because the tight connection of FeO(OH) with the rGO aerogel results in less iron

41

leaching and prevents the generation of Fe(OH)3. The 4-chlorophenol was completely

42

removed in 80 min with a 0.074 min-1 rate constant in the FeO(OH)-rGA/H2O2 photo-Fenton

43

system under visible-light irradiation, and mineralization rate was up to 80% after six hours.

44

Oxidative •OH can continuously attack 4-chlorophenol, 2,4,6-trichlorophenol and bisphenol A

45

without selectivity. These results lay a foundation for highly effective and durable

46

photo-Fenton degradation of phenolic organics at near neutral pH and sufficient activation of

47

H2O2 for future applications.

48 2

ACS Paragon Plus Environment

Page 2 of 32

Page 3 of 32

Environmental Science & Technology

49 50

TABLE OF CONTENTS

51 52

Fe-rGA 53 54 55 56 57 58 59 60 61 62 63 64 65 66 67 68 69 70 71 72 73 3

ACS Paragon Plus Environment

Environmental Science & Technology

74

1. Introduction

75

The traditional Fenton reaction is an advanced oxidation technology used for wastewater

76

treatment, and the reaction involves a mixture of hydrogen peroxide (H2O2) and ferrous iron

77

(Fe2+) in an acidic solution to generate hydroxyl radicals (·OH) for a subsequent attack of

78

tartaric acid.1 Despite its use, the homogeneous Fenton reaction has several disadvantages,

79

such as an acidic pH (pH 420 nm) in an XPA-7 type photochemical reactor (Xujiang

180

Electromechanical Plant, Nanjing, China). The temperature was maintained at 30±2ºC by

181

circulating cooling water. For the recycling, the organic compounds were added with H2O2

182

after each cycle.

183

2.5. Analytical Methods

184

The residual concentrations of 4-CP and 2,4,6-TCP were detected by high-performance liquid

185

chromatography (HPLC, Agilent 1200 Series) equipped with an ultraviolet detector with an

186

SB-C18 (4.6×150 mm) column. The optimum mobile phase for 4-CP was a mixture of

187

methanol, water and phosphoric acid (70/20/10 by volume) at a flow rate of 1.0 mL min-1 with

188

an analytical wavelength of 279 nm. For 2,4,6-TCP detection, a mobile phase containing

189

methanol and 0.02 mol/L phosphoric acid (80:20 v/v) was used at a wavelength of 285 nm.

190

BPA was detected by an HPLC equipped with a fluorescence detector with an SB-C18

191

(4.6×150 mm) column. The mobile phase was a mixture of acetonitrile and 0.01 M

192

trifluoroacetic acid (70:30, v/v), and a wavelength of 280 nm was used. The total organic

193

carbon (TOC) was measured using a TOC-V CPH TOC analyzer (SHIMADZU). The total

194

dissolved iron in the reactive solution was detected using atomic absorption spectrometry

195

(AAS, Perkin Elmer AAnalyst 700). For the different H2O2 concentrations, the potassium

196

titanium (IV) oxalate spectrophotometric method was used at a wavelength of 385 nm.33 A

197

pseudo first-order model was applied to describe the kinetics of phenolic organics

198

photo-degration by Fe-rGA.

34,35

The first-order constant k (min-1) was determined according 8

ACS Paragon Plus Environment

Page 8 of 32

Page 9 of 32

Environmental Science & Technology

199

to the following equation: ln(C0/Ct)=kt, where Ct is the concentration of phenolic organics at

200

time t, C0 is the initial concentration of phenolic organics, k is the degradation rate constant,

201

and t is the irradiation time. Hydroxyl radicals (•OH) were measured by adding methanol as

202

scavenger and obtaining electron paramagnetic resonance (EPR) spectra with DMPO forming

203

DMPO-•OH on a Bruker A300 EPR (modulation amplitude 1.00G; microwave power 20 mW;

204

modulation frequency 9.866 GH). The intermediate products were determined by liquid

205

chromatography-mass spectrometry (LC/MS) equipped with a linear ion trap interface with an

206

HPLC and quaternary pump. More details regarding the analytical methods are available in

207

the supporting information (SI).

208 209

3. Results and discussion

210

3.1. Characterization of the FeO(OH)-rGA aerogels and rGA

211

A schematic illustration of the fabrication of FeO(OH)-rGA is presented in Figure S1. Initially,

212

Fe3+ from FeCl3 can react via electrostatic interactions, cation-π interactions or metal

213

coordination with the oxygen-containing functional groups on the GO nanosheets. Second,

214

with the addition of VcNA for the chemical reduction at 95°C, the GO will transform into a

215

reduced graphene oxide hydrogel (rGH), resulting in uniform deposition of the FeO(OH)

216

nanometer structure on rGH layers. Finally, the black FeO(OH)-rGA was obtained after the

217

freeze-drying process. The simple rGA was prepared by the same procedure without the

218

addition of Fe3+. The measured density of FeO(OH)-rGA is 14.5 mg cm-3 and can be seen in

219

Figure S2a. Meanwhile, FeO(OH)-rGA can bear weight 1,800 times more than its own weight

220

without any mechanical deformation, as shown in Figure S2b. The excellent physical and

221

mechanical performances are beneficial for its practical application. Nevertheless, excessive

222

iron loading has an adverse impact on the aerogel structure stability. 25FeO(OH)-rGA

223

presented an incomplete aerogel structure (Figure S2c). 9

ACS Paragon Plus Environment

Environmental Science & Technology

224 225

Figure 1. SEM image (a), TEM image (inset SAED image) (b), HRTEM image (c) and elemental mapping

226

(d) of FeO(OH)-rGA.

227 228

SEM and TEM techniques were used to observe the lamella and pore morphology.

229

Figure 1a displays an abundant internal pore network. FeO(OH)-rGA possesses numerous,

230

more uniform and smaller pore networks than rGA (Figure S3a), which can provide an

231

extensive transportation network for electron transfer and effective reactions with H2O2.

232

Figure 1b shows the abundant tiny particles (~3 nm) on the reduced graphene oxide (rGO)

233

layers in FeO(OH)-rGA compared with that of pure rGA (Figure S3b), and the inset SAED

234

shows the crystal diffraction with a crystal ring of FeO(OH)-rGA, implying that lattice

235

striation of the particles and suggesting the generation of smaller and uniform crystals on the

236

rGO layers. By calculation, the d-spacing values were equal to 0.223 nm and 0.127 nm, which

237

were assigned to the (112) and (220) lattice planes of ferrihydrite (FeO(OH)) (JCPDS No.

238

46-1315). Ferrihydrite can enhance the decomposition of H2O2 and the oxidation of atrazine 10

ACS Paragon Plus Environment

Page 10 of 32

Page 11 of 32

Environmental Science & Technology

239

via the Fenton reaction in solution.36 Simultaneously, the elemental mapping showed C, O,

240

and Fe elements in FeO(OH)-rGA (Figure 1d).

241

To further confirm the oxygen functional groups and iron composition in the

242

FeO(OH)-rGA aerogel, XPS was employed to analyze the FeO(OH)-rGA and rGA aerogels.

243

We analyzed the C 1s spectra of the FeO(OH)-rGA and rGA aerogels and found that the

244

functional groups, such as C-C/C=C (284.3 eV), C-O (285.5 eV), C=O (287.8 eV), and

245

O-C=C (289.7 eV), were not significantly different, as shown in Figure 2a and Figure S3(c,

246

d).37 The Fe 2p XPS spectra are shown in Figure 2b. The peaks at 711.8 eV and 725.6 eV are

247

assigned to Fe(III)2p3/2 and Fe(III)2p1/2, respectively,38 which demonstrated that the iron ions

248

were successfully loaded on the rGO layers and that a possible composition was FeO(OH).

249

These XPS results demonstrated that the addition of iron did not influence the oxygen

250

functional group contents in the rGA aerogel but increased the oxygen percentage via

251

FeO(OH) generation (Figure S3 (e, f)). Meanwhile, the EDX analysis showed that the Fe

252

mass percentage was 1.63%.

253

Raman spectroscopy is an effective tool to observe ordered and disordered defects in

254

graphene. In the Raman spectra (Figure 2c), two prominent peaks were observed at 1346 cm-1

255

(D band) and 1582 cm-1 (G band), which correspond to sp3 carbon vibrational stretching and

256

sp2 carbon vibrational stretching, respectively. The intensity ratios of the D to G bands (ID/IG)

257

for the 15FeO(OH)-rGA and rGA aerogels are 1.09 and 1.24, respectively. The decrease of

258

ID/IG ratio indicates that the FeO(OH) generation can reduce the disorder and defects of

259

graphene during the synthesis process. It is possible that the iron ions easily combine with the

260

–OH and –COOH groups of GO, and thus, small FeO(OH) crystals, which can prevent defect

261

(e.g., holes) generation, form in the presence of VcNa at 95°C and are derived from the direct

262

removal of oxygen functional groups.39 The Raman spectra are consistent with the SEM

263

morphology, which also revealed that the pore network of FeO(OH)-rGA was more uniform,

264

smaller and more plentiful than that of rGA. 11

ACS Paragon Plus Environment

Environmental Science & Technology

265 266

Figure 2. XPS spectra of C 1s (a) and Fe 2p (b) for FeO(OH)-rGA. Raman spectra of FeO(OH)-rGA and

267

rGA (c). The optical contact angle of FeO(OH)-rGA (d).

268 269

The contact angle values of FeO(OH)-rGA (Figure 2d) and rGA (Figure S4) were

270

approximately 45° and 42°, which indicated hydrophilic surfaces. These surfaces are

271

favorable for adsorbing dissolved phenolic compounds. We chose VcNa as the reducing

272

reagent for a moderate reduction process compared to that with other reducing reagents (such

273

as hydrazine hydrate) to retain a portion of the oxygen functional groups in the aerogel, as can

274

be observed in the C 1s spectra of FeO(OH)-rGA and rGA from the XPS analysis. The

275

moderate chemical reduction process of the synthesized aerogel restores the sp2 correlation of

276

the π structure of the rGO layers and forms a loose porous structure, which provides more

277

reactive reaction sites and electron transfer channels for photo-Fenton catalysis. 12

ACS Paragon Plus Environment

Page 12 of 32

Page 13 of 32

Environmental Science & Technology

278

The thermograms (TG) of 15FeO(OH)-rGA and rGA in air are shown in Figure S5. From

279

room temperature to 500ºC, rGA and 15FeO(OH)-rGA exhibit a two-stage decomposition

280

pattern. The first decomposition below 120 ºC corresponds to the loss of adsorbed water. The

281

second decomposition in the range of 120-500ºC originates from the removal of labile

282

oxygen-containing functional groups as CO2, CO, and H2O vapor. 15FeO(OH)-rGA and rGA

283

have different weight losses because crystalline FeO(OH) gradually transforms into highly

284

crystalline Fe2O3, which occupies 4.175%.

285

3.2. Photo-Fenton catalytic activity of FeO(OH)-rGA aerogel

286

Control experiments were conducted to compare the removal efficiency of 4-CP by the

287

15FeO(OH)-rGA/H2O2 system at pH 3.0 with an initial 4-CP concentration of 10 mg/L and 20

288

mM H2O2. As shown in Figure 3, 15FeO(OH)-rGA can dramatically degrade 4-CP within 80

289

min under visible-light irradiation in the 15FeO(OH)-rGA/H2O2/4-CP system, whereas

290

15FeO(OH)-rGA could not remove 4-CP, which demonstrated that 15FeO(OH)-rGA did not

291

have catalytic activity without H2O2. In addition, H2O2 could not reduce 4-CP because the

292

H2O2 direct photolysis rate constant is only 1.4×10-11 M-1 s-1.40 Most importantly, the

293

visible-light adsorption of FeO(OH)-rGO after 2 h of heating presented a dramatic increase

294

(Figure S6). This was mainly due to electron transfer between the iron center and rGO layers,

295

which mobilized the FeO(OH)-producing Fe(II) in rGO. Consequently, 4-CP could not

296

degrade without visible-light irradiation because the reaction rate constant of ferric iron with

297

H2O2 is 2×10-3 M-1 s-1,41 which falls far below that of the ferrous ion reaction with H2O2 (76

298

M-1s-1).42 Consequently, H2O2 and visible light were all essential conditions for 4-CP

299

degradation. Furthermore, the reaction rate in the initial 30 min was comparatively slow

300

because the concentration of the quinone intermediate the organics generated was limited, as

301

shown in the latter HPLC analysis. According to previous reports, the coupling of visible

302

irradiation and hydroquinone resulted in strong and universal driving forces in the Fenton

303

reaction for organic pollutant degradation and mineralization.43 As the reaction proceeded, the 13

ACS Paragon Plus Environment

Environmental Science & Technology

304

4-CP removal remarkably accelerated, and the pseudo-first-order kinetic constant (k) was

305

0.0695 min-1. Compared with other Fenton-like reactions previously reported (listed in Table

306

S1),44-50 15FeO(OH)-rGA has a high degradation activity and efficiently utilizes H2O2 with

307

less iron loading under visible-light irradiation.

308 309

Figure 3. Time evolution of 4-CP removal under different conditions (reaction conditions: C0(4-CP): 10

310

mg/L, C0(H2O2): 20 mM, pH=3, 500 W xenon lamp with a UV cutoff filter (λ > 420 nm)).

311

3.3. Influence of solution conditions on degradation of phenolic organics

312

The presence of iron in aerogels plays a vital role in their reaction activity. The

313

performance of rGA changed significantly for 4-CP in the presence of iron χFeO(OH)-rGA

314

(χ=0, 4, 8, 15) (Figure 4a) (C0(H2O2): 10 mM, pH=3). 15FeO(OH)-rGA completely removed

315

4-CP within 110 min and was more efficient than the other iron-doped rGA aerogels. The

316

removal of 4-CP increased as the iron doping increased because of the importance of iron in

317

most of the catalytic components in the photo-Fenton reaction. Consequently, the addition of

318

iron resulted in the activation of H2O2 to generate •OH radicals. Nevertheless, excessive iron

319

loading will have an adverse impact on the aerogel structure stability. The probable reason is

320

that Fe3+ could generate stable coordination compounds with GO.51 In the synthesis process,

321

the excessive iron ions turn into FeO(OH) among the rGO layers, which can greatly hinder 14

ACS Paragon Plus Environment

Page 14 of 32

Page 15 of 32

Environmental Science & Technology

322

π-π stacking between the rGO layers in the aerogel, resulting in aerogel structural collapse, as

323

shown in Figure S2c. Therefore, we chose 15FeO(OH)-rGA as the optimal aerogel ratio for

324

further study.

325 326

Figure 4. Influence of the initial iron content in FeO(OH)-rGA (a), influence of the initial solution pH (b),

327

influence of the H2O2 concentration(c) on 4-CP degradation. Effectiveness for the degradation of various

328

phenolic organics (d).

329 330

The initial pH affects not only the photocatalytic performance but also the extent of iron

331

leaching and the stability of the catalyst. In consideration of the significant influence of the

332

pH on the photo-Fenton reaction, we studied the effect of the initial pH on the degradation of

333

4-CP, as shown in Figure 4b (Catalyst: 15FeO(OH)-rGA, C0(H2O2): 10 mM). Although the

334

degradation rate of 4-CP slightly declined as the pH increased from 3 to 6, approximately 15

ACS Paragon Plus Environment

Environmental Science & Technology

335

100% of 4-CP was removed within 150 min at pH=3, 4, 5, and 6, and this removal rate is

336

evidently higher than that of other reported heterogeneous Fenton-like catalysts.52 One reason

337

for the good degradation of 4-CP at near neutral pH is that the pH of the solution changed

338

after the reaction because of the generation of low molecular weight organic acids, which

339

were detected in this study, and mineralization to form CO2, which can also transform into

340

carbonic acid, resulting in a decrease in the pH. Another reason is that FeO(OH) is

341

encapsulated by graphene layers via strong π-π interactions, which could restrain ferric iron

342

from leaching and transforming into less active Fe(OH)3. As shown in Figure S7, the color of

343

the Fe3+ solution (16.4 mg/L, pH=3) changed from colorless to yellow after heating for 2 h

344

without sediment formation, but after the 1st photo-Fenton reaction, an obvious red-brown

345

precipitation was generated after 1 h, which directly proved the homogenous Fenton-like

346

reaction is not suitable for practical applications. The special internal network structure of the

347

graphene aerogels alters the state of iron in the catalyst, and the catalyst can exist at near

348

neutral pH values and displays an excellent degradation performance that is completely

349

different from that obtained with a homogeneous Fenton system. In addition, FeO(OH)-rGA

350

has outstanding photo-Fenton performance at near neutral pH, which makes FeO(OH)-rGA a

351

good candidate for the preparation of stable catalysts for industrial wastewater treatment

352

applications without drastically adjusting the pH. Moreover, the macroscopic aerogel is easier

353

to recycle, prevents sediment production, resists corrosion and possesses longer-term

354

prospects.

355

In photo-Fenton catalytic reactions, the oxidant concentration is a crucial factor that can

356

significantly influence organic matter degradation. Figure 4c shows the 4-CP degradation was

357

accelerated as the H2O2 dosage increased from 0 to 20 mM (Catalyst: 15FeO(OH)-rGA,

358

pH=3), and the degradation rate constant (k) increased from 0.040 min under 5mM H2O2, to

359

0.069 min-1 under 10mM H2O2, and to 0.074 min-1 15mM H2O2. This is because H2O2 is the 16

ACS Paragon Plus Environment

Page 16 of 32

Page 17 of 32

Environmental Science & Technology

360

precursor in the reaction to produce •OH. However, with a higher dosage (50 mM), the k

361

value obviously decreased to 0.06 min-1, which was probably caused by the excess H2O2

362

scavenging •OH, which suppressed the 4-CP degradation. Consequently, the dosage of H2O2

363

should exists in an optimum concentration range as much as possible. The demand for H2O2 is

364

always high in the traditional Fenton reaction; hence, the consumption of H2O2 is commonly

365

high in the reaction and a supply of fresh H2O2 is constantly required. As seen in Figure S8,

366

we detected the variation in the H2O2 concentration in the photo-Fenton reaction and found

367

that the concentration of H2O2 slightly decreased as the 4-CP degraded, which was mainly

368

ascribed to the nanometer, well-dispersed FeO(OH) with a small size (~3 nm) in rGA

369

effectively activating H2O2. Comparatively, the mass percentage of transition metal iron in

370

15FeO(OH)-rGA merely was approximately 5%, which was far below that of synthetic iron

371

oxide minerals. This further confirmed that the 3D macroscopic structures can disperse

372

FeO(OH) on the graphene layers to provide sufficient catalytic sites and electron transfer

373

channels for the photo-Fenton reaction.

374

The photo-Fenton catalytic efficiency was different based on the type of organic

375

compound. We selected three phenolic organics, 4-CP, 2,4,6-TCP and BPA. These organics

376

are widely used as fungicides, herbicides, and plastic materials; considered toxic organic

377

pollutants that are harmful to human health and aquatic organisms; and regarded as priority

378

organic pollutants by the US Environmental Protection Agency (USEPA). In this study, when

379

the amount of added catalyst and H2O2 were determined, the content of •OH generated was

380

simultaneously confirmed. Consequently, the difference in the degradation kinetics among

381

4-CP, 2,4,6-TCP and BPA, which is shown in Figure 4d, was ascribed to the different

382

molecular structures. The structural formulas of 4-CP, 2,4,6-TCP and BPA are shown in

383

Figure S9. 2,4,6-TCP has three chlorine substituent connections on one benzene ring, and

384

BPA has two benzene rings connected to each other in contrast with 4-CP. The photo-Fenton 17

ACS Paragon Plus Environment

Environmental Science & Technology

385

degradation kinetics of 4-CP, 2,4,6-TCP and BPA are presented in Figure 4d (Catalyst:

386

15FeO(OH)-rGA, C0(H2O2): 20 mM, pH=3). 4-CP was completely removed within 80 min,

387

and the degradation rate constant was 0.074 min-1, which was higher than that of 2,4,6-TCP

388

and BPA. 2,4,6-TCP and BPA were completely degraded after 150 min, and the degradation

389

rate constants were 0.029 min-1 and 0.031 min-1, respectively. Based on the above results, we

390

concluded that as the number of chlorine substituents on one benzene ring and the number of

391

benzene rings increase the rate of the photo-Fenton reaction decreases. Moreover, the

392

influence of the number of benzene rings was even more significant because the structure of

393

the benzene ring is very stable and not easily oxidized into an open loop. Nonetheless, •OH

394

has a strong oxidant activity (oxidation potential=2.8 V vs NHE) and is capable of oxidizing a

395

wide range of organics in wastewater. In this study, FeO(OH)-rGA, an outstanding

396

photo-Fenton catalyst, could absolutely and rapidly degrade phenolic organics. In Figure 4,

397

degradation rate of phenolic organics at the beginning was slow, which was probably because

398

the FeO(OH)-rGA has limited sorption capacity of phenolic organics. But as the quinone

399

organics produced in the reaction may be excited under visible light, and react with H2O2 to

400

generate •OH as well. This may explain the fast degradation of 4-CP, 2,4,6-TCP and BPA after

401

a short period of irradiation time.

402

3.4. Reusability and stability of the FeO(OH)-rGA aerogel

403

The reusability and stability of photo-Fenton catalysts are crucial for practical

404

applications. FeO(OH)-rGA was stored in a reaction solution for 10 cycles, and 4-CP and

405

H2O2 were added repeatedly after each cycle under visible-light irradiation. The reusability

406

performance of FeO(OH)-rGA is shown in Figure 5a. It can be seen that 4-CP was completely

407

degraded (100%) after each cycle, and the degradation continued until the 10th cycle.

408

Moreover, the morphology and internal network of FeO(OH)-rGA after 10 cycles of

409

regeneration did not show any significant changes, as shown in Figure S10. The reusability of 18

ACS Paragon Plus Environment

Page 18 of 32

Page 19 of 32

Environmental Science & Technology

410

FeO(OH)-rGA ensures its efficient performance and stability for several cycles without losing

411

its catalytic activity; thus, it is a superior candidate for the photo-Fenton process, particularly

412

for the removal of organic contaminants.

413

The stability of the photo-Fenton catalyst was also observed by examining the iron

414

leaching, which directly indicated the stability of the catalytically active component. The total

415

iron leaching after 10 cycles is displayed in Figure 5b. The total iron concentration was 16.4

416

mg/L in FeO(OH)-rGA. The range of the total iron leaching after each cycle was

417

approximately 0.4-0.6 mg/L, which accounted for only ~2.5% of 16.4 mg/L. Moreover, the

418

total iron content in solution after each cycle did not change significantly after the first cycle,

419

as shown in the inset picture (Figure 5b). We did not detect ferrous ions in the reaction

420

solution using the 1,10-phenanthroline method at a wavelength of 510 nm with a Shimadzu

421

UV-2550 spectrophotometer.53 Comparing the EDX results of 15FeO(OH)-rGA after 10

422

cycles (Figure S10d) with that of the initial 15FeO(OH)-rGA (Figure S3f), the 0.1% drop

423

suggests that the iron loss was practically negligible. Therefore, FeO(OH)-rGA is an excellent

424

photo-Fenton catalyst for practical applications in the future.

425 426

Figure 5. The reusability (a) and stability (inset of Fe(T) variation in the first cycle) (b) of the

427

FeO(OH)-rGA aerogel after 10 cycles in the FeO(OH)-rGA/H2O2/4-CP system under visible-light

428

irradiation. (Reaction conditions: C0(4-CP): 10 mg/L, C0(H2O2): 10 mM, pH=3, 500 W xenon lamp with a

429

UV cutoff filter (λ > 420 nm)). 19

ACS Paragon Plus Environment

Environmental Science & Technology

430

3.5. Photocatalytic degradation mechanisms

431

The analysis of free radical quenching is effective for real-time identification of reaction

432

species in photo-Fenton system. Therefore, the reactive species were further distinguished by

433

adding methanol as scavenger for the •OH generated in the reaction solution.54 Methanol has

434

a high reaction rate constant with •OH, up to k=9.6 ×109 M-1 s-1.55 The results achieved after

435

the methanol addition were compared to those obtained without methanol addition and are

436

shown in Figure 6a. The results clearly revealed no degradation of 4-CP after the methanol

437

addition, which suggested that the 4-CP degradation was driven by •OH derived from

438

FeO(OH)-rGA-activated H2O2 under visible-light irradiation. To further identify the radical

439

species in the reaction, EPR with DMPO as a spin-trapping agent was used to detect •OH

440

radicals

441

•OH with an intensity ratio of 1:2:2:1 were obtained in the EPR spectra of

442

FeO(OH)-rGA/H2O2, which clearly indicated •OH was generated in the FeO(OH)-rGA/H2O2

443

system under visible-light irradiation.

48,56

after 5 min of visible-light irradiation. The typical four characteristic peaks of

444 445

Figure 6. Effect of radical scavengers on the degradation of 4-CP (a). EPR spectra of DMPO-•OH adducts

446

that formed over time with visible-light irradiation of a suspension of 15FeO(OH)-rGA/H2O2 (b).

447 448

20

ACS Paragon Plus Environment

Page 20 of 32

Page 21 of 32

Environmental Science & Technology

449

The HPLC analysis is displayed in Figure 7a and shows the visual changes in the 4-CP

450

degradation. It can be concluded that A and D are 4-CP and H2O2, respectively, at t=0, and the

451

degree of 4-CP mineralization is shown in Figure 7b. The TOC removal gradually increased

452

to 80% after 6 h of reaction. The initial TOC removal was slow within 120 min, which was

453

mainly because of the intermediate product generation, i.e., quinone organics (C and D) with

454

a higher toxicity potential.57 The molecular structure of the intermediate products was

455

determined by HPLC-MS (Figure S11). These intermediate products retained the benzene ring

456

structure, which resulted in a solution with a relatively higher TOC at the beginning of the

457

reaction. The TOC removal dramatically accelerated once the reaction continued because the

458

benzene ring of the intermediate products was persistently attacked by •OH and eventually

459

transformed into low molecular weight organic acids with toxicity decreasing, which are more

460

susceptible to oxidative degradation. The possible reaction pathway for 4-CP degradation is

461

presented in Figure S12.

462 463

Figure 7. The intermediate products generation and mineralization of 4-CP. HPLC analysis of 4-CP

464

degradation within 150 min (a). TOC removal of 4-CP within 6 h of reaction (b). (Reaction conditions:

465

C0(4-CP): 10 mg/L, C0(H2O2): 10 mM, pH=3, 500 W xenon lamp with UV cutoff filter (λ > 420 nm)).

466 467 21

ACS Paragon Plus Environment

Environmental Science & Technology

468

Based on the above analysis, a possible mechanism for phenolic organic degradation by

469

FeO(OH)-rGA with H2O2 under visible-light irradiation was proposed (Figure 8). Ferric ions

470

on the GO interface can create catalyst precursors with even and uniform distributions. Once

471

sodium ascorbate was added as a reducing agent, GO gradually transforms into rGO along

472

with recovery of the sp2 regions, which are beneficial for electron transfer between the iron

473

center and H2O2. Moreover, the ferric ions turn into nanometer FeO(OH) that is firmly fixed

474

in rGA via strong π-π interaction between the rGO layers, preventing iron leaching. In

475

addition, the nanoparticles (average size ~ 3 nm) are distributed evenly on the rGO layers,

476

improving the catalytic activity of the FeO(OH)-rGA aerogel compared with that of pure

477

Fe2O3, which has a slow reaction efficiency with H2O2 even under UV-light irradiation.58

478

FeO(OH) has a special optical activity that can easily be activated by visible light and

479

transforms to Fe(II) to activate H2O2 to produce •OH. This process is than pure H2O2 direct

480

photolysis, and an extraordinary catalytic activity is displayed for phenolic organic

481

degradation along with Fe(III)/Fe(II) catalytic cycles. Furthermore, FeO(OH)-rGA can

482

generate •OH with H2O2 under visible-light irradiation due to coupling the visible irradiation

483

and intermediate quinone organics, which have strong and universal driving forces in the

484

Fenton reaction for phenolic organic degradation and mineralization. The special

485

FeO(OH)-rGA structure allows superior degradation of phenolic organics at near neutral pH

486

values and maintains the stability of the catalyst, avoiding a negative influence from catalyst

487

aggregation.

22

ACS Paragon Plus Environment

Page 22 of 32

Page 23 of 32

Environmental Science & Technology

488 489

Figure 8. Schematic illustration of the possible hydroxyl radical generation mechanism and phenolic

490

organic mineralization in the FeO(OH)-rGA/H2O2 system under visible-light irradiation.

491 492

In this study, we employed a facile synthetic method for iron-doped-rGO aerogels as an

493

effective and original photo-Fenton catalyst. The obtained aerogel not only had a stable

494

macrostructure and lighter density but also a prominent catalytic activity for phenolic organic

495

degradation at near neutral pH values with less iron leaching after 10 cycles of consecutive

496

uses. The minimal iron leaching was mainly because the smaller FeO(OH) crystals (average

497

size ~3 nm) were immobilized and dispersed on the rGO layers, and these iron crystals

498

possess a higher catalytic activity than pure iron oxides. The sp2 regions of rGO were

499

recovered by sodium ascorbate reduction to ensure fewer defects after iron doping.

500

Consequently, this FeO(OH)-rGA aerogel is an ideal photo-Fenton catalyst that overcomes the

501

disadvantages of conventional Fenton reactions and can be applied to practical applications

502

for effective removal of organic pollutants.

503 23

ACS Paragon Plus Environment

Environmental Science & Technology

504

 ASSOCIATED CONTENT

505

Supporting Information

506

LC-MS analysis and comparison of the catalytic properties of different photo-Fenton catalysts

507

(Table S-1) and Figures S1-S12 are presented. This information is available free of charge via

508

the Internet at http://pubs.acs.org.

509 510

 AUTHOR INFORMATION

511

Corresponding Author

512

*Phone: 0086-574-87609508; e-mail: [email protected]

513

Notes

514

The authors declare no competing financial interest.

515 516

 ACKNOWLEDGMENTS

517

This project was supported by the National Natural Science Foundation of China (Grant

518

21425730, 21537005, and 21621005), the National Basic Research Program of China (Grant

519

2014CB441106), and the National Key Technology Support Program of China (No.

520

2015BAC02B01).

521 522

References

523

[1] Fenton, H. J. H. Oxidation of tartaric acid in presence of iron. J. Chem. Soc. Transactions.

524 525 526 527

1894, 65, 899-910. [2] Kremer, M. L. The Fenton reaction. Dependence of the rate on pH. J. Phys. Chem. A. 2003, 107, 1734-1741. [3] Lin, S. H.; Lo, C. C. Fenton process for treatment of desizing wastewater. Wat. Res. 1997, 24

ACS Paragon Plus Environment

Page 24 of 32

Page 25 of 32

528

Environmental Science & Technology

31, 2050-2056.

529

[4] Iurascu, B.; Siminiceanu, I.; Vione, D.; Vicente, M. A.; Gild, A. Phenol degradation in

530

water through a heterogeneous photo-Fenton process catalyzed by Fe-treated laponite. Wat.

531

Res. 2009, 43, 1313-1322.

532 533

[5] Dercova, K.; Branislav, V.; Tandlich, R.; Subova, L. Fenton’s type reaction in chemical pretreatment of PCBs. Chemosphere 1999, 39, 2621-2628.

534

[6] Gao, L. Z.; Zhuang, J.; Nie, J.; Zhang, J. B.; Gu, N.; Wang, T. H.; Feng, J.; Yang, S.L.;

535

Perrett, S.; Yan, X. Y. Intrinsic peroxidase-like activity of ferromagnetic nanoparticles. Nat.

536

Nanotechnol. 2007, 2, 577-583.

537 538

[7] Xu, L. J.; Wang, J. L. Fenton-like degradation of 2,4-dichlorophenol using Fe3O4 magnetic nanometerparticles. Appl. Catal. B: Environ. 2012, 123, 117-126.

539

[8] Guo, L. Q.; Chen, F.; Fan, X. Q.; Cai, W. D.; Zhang, J. L. S-doped α-Fe2O3 as a highly

540

active heterogeneous Fenton-like catalyst towards the degradation of acid orange 7 and

541

phenol. Appl. Catal. B: Environ. 2010, 96,162-168.

542 543

[9] Lin, S. S.; Gurol, M. D. Catalytic decomposition of hydrogen peroxide on iron oxide: kinetics, mechanism, and implications. Environ. Sci. Technol. 1998, 32, 1417- 1423.

544

[10] Chen, H.; Zhang, Z. L.; Yang, Z. L.; Yang, Q.; Li, B.; Bai, Z. Y. Heterogeneous

545

Fenton-like catalytic degradation of 2,4-dichlorophenoxyacetic acid in water with FeS.

546

Chem. Eng. J. 2015, 273, 481-489.

547

[11] Segura, Y.; Martinez, F.; Melero, J. A. Effective pharmaceutical wastewater degradation

548

by Fenton oxidation with zero-valent iron. Appl. Catal. B: Environ. 2013, 136, 64-69.

549

[12] Hu, M. Q.; Xu, Y. M. Visible light induced degradation of chlorophenols in the presence 25

ACS Paragon Plus Environment

Environmental Science & Technology

550

Page 26 of 32

of H2O2 and iron substituted polyoxotungstate. Chem. Eng. J. 2014, 246, 299-305.

551

[13] Ramirez, J. H.; Costa, C. A.; Madeira, L. M.; Mata, G.; Vicente, M. A.; Rojas-Cervantes,

552

M. L.; López-Peinado, A. J.; Martín-Aranda, R. M. Fenton-like oxidation of Orange II

553

solutions using heterogeneous catalysts based on saponite clay. Appl. Catal. B: Environ.

554

2007, 71, 44-56.

555

[14] Zhang, L. L.; Xu, D.; Hu, C.; Shi, Y. L. Framework Cu-doped AlPO4 as an effective

556

Fenton-like catalyst for bisphenol A degradation. Appl. Catal. B: Environ. 2017, 207,

557

9-16.

558

[15] Coelho, J. V.; Guedes, M. S.; Prado, R. G.; Tronto, J.; Ardisson, J. D.;

Pereira, M. C.;

559

Oliveira, L. C. A. Effect of iron precursor on the Fenton-like activity of Fe2O3/

560

mesoporous silica catalysts prepared under mild conditions. Appl. Catal. B: Environ.

561

2014, 144, 792-799.

562

[16] Sun, L. J.; Yao, Y. Y.; Wang, L.; Mao, Y. J.; Huang, Z. F.; Yao, D. C.; Lu, W. Y.; Chen, W.

563

X. Efficient removal of dyes using activated carbon fibers coupled with

564

8-hydroxyquinoline ferric as a reusable Fenton-like catalyst. Chem. Eng. J. 2014, 240,

565

413-419.

566

[17] Liu, Y. Y.; Jin, W.; Zhao, Y. P.; Zhang, G. S.; Zhang, W. Enhanced catalytic degradation

567

of methylene blue by α-Fe2O3/graphene oxide via heterogeneous photo-Fenton reactions.

568

Appl. Catal. B: Environ. 2017, 206, 642-652.

569

[18] Nair, R. R.; Blake, P.; Grigorenko, A. N.; Novoselov, K. S.; Booth, T. J.; Stauber, T.;

570

Peres, N. M. R.; Geim, A. K.

571

graphene. Science 2008, 320, 1308.

Fine structure constant defines visual transparency of

26

ACS Paragon Plus Environment

Page 27 of 32

572 573

Environmental Science & Technology

[19] Moser, J.; Barreiro, A.; Bachtold, A. Current-induced cleaning of graphene. Appl. Phys. Lett. 2007, 91, 163513.

574

[20] Mayorov, A. S.; Gorbachev, R. V.; Morozov, S.V.; Britnell, L.; Jalil, R.; Ponomarenko, L.

575

A.; Blake, P.; Novoselov, K. S.; Watanabe, K.; Taniguchi, T.; Geim, A. K.

576

Micrometer-scale ballistic transport in encapsulated graphene at room temperature. Nano

577

Lett. 2011, 11, 2396-2399.

578

[21] Tang, H.; Zhao, Y.; Yang, X. N.; Liu, D. M.; Shan, S.J.; Cui, F. Y. Understanding the

579

roles of solution chemistries and functionalization on the aggregation of graphene-based

580

nanometer materials using molecular dynamic simulations. J. Phys. Chem. C. 2017, 121,

581

13888-13897.

582

[22] Garacci, M.; Barret, M.; Mouchet, F.; Sarrieu, C.; Lonchambon, P.; Flahaut, E.; Gauthier,

583

L.; Silvestre, J.; Pinelli, E. Few layer graphene sticking by biofilm of freshwater diatom

584

nitzschia palea as a mitigation to its ecotoxicity. Carbon 2017, 113, 139-150.

585

[23] Sanchís, J.; Olmos, M.; Vincent, P.; Farré, M.; Barceló, D. New Insights on the influence

586

of organic co-contaminants on the aquatic toxicology of carbon nanometermaterials.

587

Environ. Sci. Technol. 2016, 50, 961-969.

588

[24] Shen, Y.; Zhu, X.; Chen, B. Size effects of graphene oxide nanosheets on the construction

589

of three-dimensional graphene-based macrostructures as adsorbents. J. Mater. Chem. A.

590

2016, 4, 12106-12118.

591

[25] Xia, W.; Qu, C.; Liang, Z.; Zhao, B.; Dai, S.; Qiu, B.; Jiao, Y.; Zhang, Q.; Huang, X.;

592

Guo, W.; Dang, D.; Zou, R.; Xia, D.; Xu, Q.; Liu, M. High-performance energy storage

593

and conversion materials derived from a single metal-organic framework/graphene 27

ACS Paragon Plus Environment

Environmental Science & Technology

594

aerogel composite. Nanometer. Lett. 2017, 17, 2788-2795.

595

[26] Liu, X.; Sun, J.; Zhang, X. Novel 3D graphene aerogel-ZnO composites as efficient

596

detection for NO2 at room temperature. Sensor Actuat B: Chem. 2015, 211, 220-226.

597

[27] Yang, T. T.; Li, R.; Long, X. H.; Li, Z. J.; Gu, Z. G.; Wang, G.; Liu, J. K. Nitrogen and

598

sulphur-functionalized multiple graphene aerogel for supercapacitors with excellent

599

electrochemical performance. Electrochim. Acta. 2016, 187, 143-152.

600

[28] Wu, T.; Chen, M.; Zhang, L.; Xu, X.; Liu, Y.; Yan, J.; Wang, W.; Gao, J. P.

601

Three-dimensional graphene-based aerogels prepared by a self-assembly process and its

602

excellent catalytic and absorbing performance. J. Mater. Chem. A. 2013, 1, 7612-7621.

603

[29] Yang, C. X.; Liu, N. S.; Zeng, W.; Long, F.; Song, Z.; Sun, J.; Li, L.; Zou, Z.; Fang, G.;

604

Xiong, L.; Gao, Y. Superelastic and ultralight electron source from modifying 3D

605

reduced graphene aerogel microstructure. Nanometer Energy 2017, 33, 280-287.

606

[30] Cui, C.; Li, S.; Qiu, Y. W.; Hu, H. H.; Li, X. Y.; Li, C.; Gao, J.; Tang, W. Fast assembly of

607

Ag3PO4 nanometerparticles within three-dimensional graphene aerogels for efficient

608

photocatalytic oxygen evolution from water splitting under visible light. Appl. Catal. B:

609

Environ. 2017, 200, 666-672.

610

[31] Wang, C.; Yang, S.; Ma, Q.; Jia, X.; Ma, P. Preparation of carbon nanometertubes/

611

graphene hybrid aerogel and its application for the adsorption of organic compounds.

612

Carbon 2017, 118, 765-771.

613 614 615

[32] Hummer, W. S.; Offerman, R. E. Preparation of graphite oxide. J. Am. Chem. Soc. 1958, 80, 1339. [33] Sellers, R. M. Spectrophotometric determination of hydrogen peroxide using potassium 28

ACS Paragon Plus Environment

Page 28 of 32

Page 29 of 32

616

Environmental Science & Technology

titanium(IV) oxalate. Analyst 1980, 105, 950-954.

617

[34] Sun, Z.; Zhang, C., Xing, L.; Zhou, Q.; Dong, W. ; Hoffmann, M. R. Uv/nitrilotriacetic

618

acid process as a novel strategy for efficient photoreductive degradation of

619

perfluorooctanesulfonate. Environ. Sci. Technol. 2018, 52, 2953-2962.

620

[35] Yu, S.; Wang, X.; Yao, W.; Wang, J.; Ji, Y.; Ai, Y.; Alsaedi, A.; Hayat, T.; Wang, X.

621

Macroscopic, spectroscopic, and theoretical investigation for the interaction of phenol

622

and naphthol on reduced graphene oxide. Environ. Sci. Technol. 2017, 51, 3278−3286.

623

[36] Barreiro, J. C.; Capelato, M. D.; Neto, L. M.; Hansen, H. C. B. Oxidative decomposition

624

of atrazine by a Fenton-like reaction in a H2O2/ferrihydrite system. Wat. Res. 2007, 41,

625

55-62.

626

[37] Wang, J.; Chen, Z.; Chen, B. Adsorption of polycyclic aromatic hydrocarbons by

627

graphene and graphene oxide nanometersheets. Environ. Sci. Technol. 2014, 48, 4817-

628

4825.

629

[38] Lv, A.; Hu, C.; Nie, Y. L.; Qu, J. H. Catalytic ozonation of toxic pollutants over magnetic

630

cobalt and manganese co-doped γ-Fe2O3. Appl. Catal. B: Environ. 2010, 100, 62-67.

631

[39] Eigler, S.; Dotzer, C.; Hirsch, A. Visualization of defect densities in reduced graphene

632

oxide. Carbon 2012, 50, 3666-3673.

633

[40] Zellner, R.; Exner, M.; Herrmann, H. Absolute OH quantum yields in the laser photolysis

634

of nitrate, nitrite and dissolved H2O2 at 308 and 351 nm in the temperature range of

635

278-353 K. J. Atm. Chem. 1990, 10, 411-425.

636

[41] Walling, C.; Goosen, A. Mechanism of the ferric ion catalyzed decomposition of

637

hydrogen peroxide. Effect of organic substrates. J. Am. Chem. Soc. 1973, 95, 2987-2991. 29

ACS Paragon Plus Environment

Environmental Science & Technology

Page 30 of 32

638

[42] Walling, C. Fenton’s reagent revisited. Acc. Chem. Res. 1975, 8, 125-131.

639

[43] Ma, J. H.; Ma, W. H.; Song, W. J.; Chen, C. C.; Tang, Y.; Zhao, J. C.; Huang, Y. P.; Xu, Y.

640

M.; Zang, L. Fenton degradation of organic pollutants in the presence of

641

low-molecular-weight organic acids: Cooperative effect of quinone and visible light.

642

Environ. Sci. Technol. 2006, 40, 618-624.

643

[44] Qiu, B. C.; Xing, M. Y.; Zhang, J. L. Stӧber-like method to synthesize ultralight, porous,

644

stretchable Fe2O3/graphene aerogels for excellent performance in photo- Fenton reaction

645

and electrochemical capacitors. J. Mater. Chem. A. 2015, 3, 12820-12827.

646

[45] Qiu, B. C.; Li, Q. Y.; Shen, B.; Xing, M. Y.; Zhang, J. L. Stöber-like method to

647

synthesize ultradispersed Fe3O4 nanometerparticles on graphene with excellent

648

Photo-Fenton reaction and high-performance lithium storage. Appl. Catal. B: Environ.

649

2016, 183, 216-223.

650

[46] Zhou, Y.; Xiao, B.; Liu, S. Q.; Meng, Z.; Chen, Z. G.; Zou, C. Y.; Liu, C. B.; Chen, F.;

651

Zhou, X. Photo-Fenton degradation of ammonia via a manganese-iron double-active

652

component catalyst of graphene-manganese ferrite under visible light. Chem. Eng. J.

653

2016, 283, 266-275.

654

[47] Boruah, P. K.; Sharma, B.; Karbhal, I.; Shelke, M. V.; Das, M. R. Ammonia-modified

655

graphene sheets decorated with magnetic Fe3O4 nanometerparticles for the photocatalytic

656

and photo-Fenton degradation of phenolic compounds under sunlight irradiation. J.

657

Hazard. Mater. 2017, 325, 90-100.

658 659

[48] Li, X. Y.; Pi, Y. H.; Wu, L. Q.; Xia, Q. B.; Wu, J. L.; Li, Z.; Xiao, J. Facilitation of the visible

light-induced

Fenton-like

excitation

of

30

ACS Paragon Plus Environment

H2O2

via

heterojunction

of

Page 31 of 32

Environmental Science & Technology

660

g-C3N4/NH2-Iron terephthalate metal-organic framework for MB degradation. Appl.

661

Catal. B: Environ. 2017, 202, 653-663.

662

[49] Nguyen, X. S.; Zhang, G. K.; Yang, X. F. Mesocrystalline Zn-doped Fe3O4 hollow sub-

663

microspheres: Formation mechanism and enhanced photo-Fenton catalytic performance.

664

ACS Appl. Mater. Interfaces. 2017, 9, 8900-8909.

665

[50] Zhao, Y. B.; Pan, F.; Li, H.; Niu, T. C.; Xu, G. Q.; Chen, W. Facile synthesis of uniform

666

α-Fe2O3 crystals and their facet-dependent catalytic performance in the photo-Fenton

667

reaction. J. Mater. Chem. A. 2013, 1, 7242-7246.

668 669

[51] Liu, R.; Zhu, X.; Chen, B. A new insight of graphene oxide-Fe(III) complex photochemical behaviors under visible light irradiation. Sci. Rep. 2017, 7, 40711.

670

[52] Xu, L. J.; Wang, J. L. Magnetic Nanometerscaled Fe3O4/CeO2 composite as an efficient

671

Fenton-like heterogeneous catalyst for degradation of 4-chlorophenol. Environ. Sci.

672

Technol. 2012, 46, 10145-10153.

673

[53] Tamura, H.; Goto, K.; Yotsuyanagi, T.; Nagayama, M. Spectrophotometric determination

674

of iron(II) with 1,10-phenanthroline in the presence of large amounts of iron(III). Talanta

675

1974, 21, 314-318.

676

[54] Lin, Y. M.; Li, D. Z.; Hu, J. H.; Xiao, G. C. Highly efficient photocatalytic degradation of

677

organic pollutants by PANI-modified TiO2 composite. J. Phys. Chem. C. 2012, 116,

678

5764-5772.

679

[55] Sun, L. Z.; Bolton, J. R. Determination of the quantum yield for the photochemical

680

generation of hydroxyl radicals in TiO2 suspensions. J. Phys. Chem. 1996, 100,

681

4127-4134. 31

ACS Paragon Plus Environment

Environmental Science & Technology

682

[56] Malka, E.; Pereshtein, I.; Lipovsky, A.; Shalo, Y. K.; Naparstek, L.; Perkas, N.; Patick, T.;

683

Lubart, R.; Nitzan, Y.; Banin, E.; Gedanken, A. Eradication of multi-drug resistant

684

bacteria by a novel Zn-doped CuO nanometercomposite. Small 2016, 9, 4069-4076.

685

[57] Miller, R. M.; Singer, G. M.; Rosen, J. D.; Bartha. R. Sequential degradation of

686

chlorophenols by photolytic and microbial treatment. Environ. Sci. Technol. 1988, 22,

687

1215-1219.

688

[58] Wang, Y.; Sun, Y.; Li, W.; Tian, W.; Irini, A. High performance of nanometerscaled Fe2O3

689

catalyzing UV-Fenton under neutral condition with a low stoichiometry of H2O2: Kinetic

690

study and mechanism. Chem. Eng. J. 2015, 267, 1-8.

32

ACS Paragon Plus Environment

Page 32 of 32